本発明は、高膨張圧炭を含む配合炭をコークス炉に装入する高炉用コークスの製造方法において、高膨張圧炭に対して粘結材を添加、混練し、当該粘結材が添加、混練された高膨張圧炭を成形することにより成形炭とし、当該成形炭を、前記成形炭とは異なる他の原料炭と配合することにより配合炭を構成することを特徴とする。例文帳に追加
The method for producing coke for a blast furnace comprises charging a coke oven with a blended coal containing a high coking pressure coal, and the method is characterized by adding a caking additive to the high coking pressure coal and kneading them, forming the high coking pressure coal with the caking additive added and kneaded thereto to obtain a formed coal, and blending the formed coal with other raw material coal different from the formed coal to constitute the blended coal. - 特許庁
予め減容処理を行った廃プラスチックを石炭に混合して成形炭を製造し、成形炭を石炭に配合して、コークス炉に装入して乾留を行う。例文帳に追加
This method for producing the coke from the formed coal containing the waste plastics is characterized by mixing coal with the waste plastics preliminarily subjected to a volume-reducing treatment, forming the mixture, compounding the formed coal with coal, and then carbonizing the mixture in a coke oven. - 特許庁
熱伝導性成形体は、黒鉛化炭素粉末が配合された熱伝導性高分子組成物を所定の形状に成形してなる。例文帳に追加
The thermal conductive molded body is obtained by molding a thermal conductive polymer composition blended with graphitized carbon powder into a prescribed shape. - 特許庁
粘結性の乏しい又は粘結性のない劣質炭(主に、非微粘結炭)を多量に配合した原料炭に粘結材を配合して成形した成形炭を、竪型シャフト炉で乾留して、耐衝撃性に優れた高炉用コークスを製造する。例文帳に追加
To produce a blast furnace coke excellent in shock resistance by subjecting a formed coal to dry distillation in a vertical shaft furnace, wherein the formed coal is formed by containing a caking additive in a raw material coal having a large amount of low-grade coal of no or slight caking properties, mainly a non- or slightly-caking coal, contained therein. - 特許庁
粒径が0.046mm以上の維管束植物炭化炭粉末を55から82体積%、可塑剤を12.5から17.5体積%、樹脂微粉末を残りの体積%配合し、樹脂微粉末に対する可塑剤の体積比(可塑剤体積/樹脂微粉末体積)を0.45〜2.33とすることにより、高い吸着活性と疎水性と水蒸気透過性を有する炭配合樹脂ペースト組成物並びに該炭配合樹脂ペースト組成物を成形した成形体が得られる。例文帳に追加
A molding is obtained by molding the charcoal-mixed paste composition. - 特許庁
樹脂部材としてのハウジング部7は、PPSをベース樹脂とし、炭素繊維を配合した樹脂組成物を射出成形することで得られる。例文帳に追加
A housing part 7 as a resin member is formed by injection-molding resin composition using PPS as a base resin and containing carbon fibers. - 特許庁
-
履歴機能過去に調べた
単語を確認! -
語彙力診断診断回数が
増える! -
マイ単語帳便利な
学習機能付き! -
マイ例文帳文章で
単語を理解!
「成形炭配合」の部分一致の例文検索結果
該当件数 : 91件
フェノール樹脂及び炭素質粉末を配合した原材料を、金型に振動を加えつつ板状に圧縮成形することを特徴とする。例文帳に追加
A raw material in which phenol resin and carbonaceous powder are mixed is compressed and molded in a plate while applying oscillation to a die. - 特許庁
石炭と鉄鉱石とを混合して成形した成形炭を、竪型炉を用いて連続的に乾留してフェロコークスを製造するにあたり、棚吊りの原因となる成形炭の相互溶着やコークス割れの発生を抑制することを可能とする原料配合の調整方法を提供することを課題とする。例文帳に追加
To provide a preparation method of a raw material mixture capable of suppressing the occurrence of mutual welding and coke cracking of formed coal, which causes bridging, when producing ferrocoke by continuously distilling the formed coal, obtained by mixing coal with ironstone and forming the mixture, by using a vertical furnace. - 特許庁
炭素繊維を特定量配合してなる炭素繊維強化熱可塑性樹脂成形体に、導電性膜を膜厚0.01〜10μmで形成してなる導電性樹脂成形体。例文帳に追加
This electroconductive resin molding is obtained by forming an electroconductive film having 0.01-10 μm thickness on a carbon fiber- reinforced thermoplastic resin molding obtained by blending carbon fiber in a specific amount. - 特許庁
上記配合比率の炭化珪素粉末原料に、ホウ素化合物粉末と無機系炭素粉末からなる焼結助剤を含む泥漿を鋳込み成形し、生成された成形体を焼結する。例文帳に追加
A slip comprising a silicon carbide powder raw material having the mixing ratio and a sintering auxiliary composed of boron compound powder and inorganic carbon powder is subjected to slip casting and the formed molding is sintered. - 特許庁
炭素繊維を特定量配合してなる炭素繊維強化熱可塑性樹脂成形体に、導電塗料を1〜15μm塗装してなる導電性樹脂成形体。例文帳に追加
This electroconductive resin molded body is obtained by blending carbon fiber in a specific amount to obtain a carbon fiber reinforced thermoplastic resin molded body which is painted and coated with an electroconductive paint in 1-15 μm thickness. - 特許庁
ゴム、熱可塑性樹脂、熱可塑性エラストマー等のポリマー成分100質量部に対して活性炭および/または木炭等の調湿性能を有する材料の粉末を30〜200質量部配合し、成形した調湿用成形品。例文帳に追加
This humidity conditioning molding is molded by compounding powder 30-200 pts.wt. of the material having humidity conditioning performance such as activated carbon and/or charcoal for polymer component 100 pts.wt. such as rubber, thermoplastic resin and thermoplastic elastomer. - 特許庁
また、焼結鉱の配合原料のうち、粉鉄鉱石と炭材との一部から形成された成形体の表面に前記配合原料の残部を外装した擬似粒子であって、前記成形体の炭材含有量が10mass%以上であることを特徴とする焼結鉱の製造用擬似粒子を用いる。例文帳に追加
Further, the pseudo particles for producing sintered ore are obtained by externally charging the remainder of the blending raw materials to the surface of a compact formed from a part of powder iron ore and a carbonaceous material among blending raw materials for sintered ore, and the content of the carbonaceous material in the compact is ≥10 mass%. - 特許庁
ケース1内に、成形蓄熱剤(A)を平均で20wt%の配合割合となるように成形活性炭と混合して充填するが、大気開放口6側部分では30wt%、蒸気流入口4側部分では10wt%となるように、配合割合が連続的に変化している。例文帳に追加
Although shaped activated carbon is mixed and filled in a case 1 to make blend ratio of the shaped heat accumulating agent A average 20 wt%, the blend ratio continuously changes to be 30wt% at an atmospheric air release opening 6 side part and 10 wt% at a vapor flow inlet 4 side part. - 特許庁
|
意味 | 例文 (91件) |
|
ピン留めアイコンをクリックすると単語とその意味を画面の右側に残しておくことができます。 |
ログイン |
Weblio会員(無料)になると 検索履歴を保存できる! 語彙力診断の実施回数増加! |
-
1xenophobia
-
2decal
-
3xenophobic
-
4gold
-
5leave
-
6believe
-
7while
-
8present
-
9heaven
-
10address
weblioのその他のサービス
ログイン |
Weblio会員(無料)になると 検索履歴を保存できる! 語彙力診断の実施回数増加! |