To provide a method for leaching pyrite containing chalcopyrite, which can leach pyrite containing chalcopyrite with a bacterium, in a practically versatile condition.例文帳に追加

黄銅鉱を含む硫化鉱を実操業レベルで汎用性ある条件でバクテリア浸出することができる黄銅鉱を含む硫化鉱の浸出方法を提供する。 - 特許庁

In the method for treating the zinc leaching residue, with which granulated material of the zinc leaching residue and carbonaceous material are prepared and valuable metals are recovered by heating this granulated material in a rotary hearth furnace, the rotary hearth furnace is driven under the condition of 0.9-1.1 air ratio in a burner and 1150-1250°C temperature in the furnace.例文帳に追加

亜鉛浸出残渣と炭材との造粒物を調製し、その造粒物を回転床炉内で加熱して有価金属を回収する亜鉛浸出残渣の処理方法であって、回転床炉は、バーナの空気比：０．９〜１．１、炉内温度：１１５０〜１２５０℃の条件下で運転される。 - 特許庁

To provide a method of efficiently leaching copper from copper concentrate comprising copper sulfide ore containing a relatively large amount of enargite that is hardly-soluble and difficult to physically separate at an actual operation level and in a versatile condition.例文帳に追加

実操業レベルで汎用性ある条件で、難溶性で物理的分離も困難な硫砒銅鉱を比較的多量に含む、硫化銅鉱からなる銅精鉱から銅を効率よく浸出する方法を提供する。 - 特許庁

Step (3): a cementation deposit containing nickel in a metal form is obtained by adding alkali into the leaching solution, under a condition of solution temperature: 25-100°C and while adjusting pH to 1-5, adding iron powder to be served in cementation.例文帳に追加

工程（３）：前記浸出液中に、液温度：２５〜１００℃の条件下にアルカリを添加してｐＨを１〜５に調整しながら、鉄粉末を添加してセメンテーションに付し、ニッケルを金属形態で含むセメンテーション殿物を得る。 - 特許庁

There is also provided a method for selective separation of TiO_2-rich oxides from titaniferrous ore/residue materials via oxidative roasting in the presence of alkali carbonate or carbonates followed by aqueous leaching of the roasted material and selective precipitation of TiO_2 under controlled condition below pH=4.例文帳に追加

炭酸アルカリの存在下で酸化的焙焼を行い、焙焼物の水浸出を行い、ＴｉＯ_2をｐＨ４未満の調節条件下で選択的に沈殿させ、ＴｉＯ_2に富む酸化物をチタニア鉄鉱石／残渣物質から選択的に分離する方法も提供される。 - 特許庁

The non-leaching adhesive system comprises at least one monomer selected from the group comprising acrylate and methacrylate monomers, allylic monomers, norbornene monomers, hybrid monomers thereof containing chemically-different polymerizable groups, and multifunctional thiol monomers on condition that the thiol monomer is used in combination with at least one of these non-thiol monomers, and a polymerization initiator.例文帳に追加

その接着剤系は、アクリラート及びメタクリラート単量体、アリル系の単量体、ノルボルネン単量体、化学的に異なる重合性基を含有する、それらのハイブリッド単量体、並びに、前記の非チオール単量体の少なくとも一つとの組み合わせで使用されるとの条件で、多官能性のチオール単量体の群の間より選択された、少なくとも一つの単量体、並びに、重合開始剤を含む。 - 特許庁