plating bath compositionとは 意味・読み方・使い方

As the plating bath composition, sulfamate nickel is contained as much as 150-650 g/l and citrate is contained as much as 5-60 g/l.例文帳に追加

メッキ浴組成として、スルファミン酸ニッケル１５０〜６５０ｇ/l、クエン酸塩５〜６０ｇ/lを含むものである。 - 特許庁

Pseudo whiskers in the tin film are prevented and the appearance of the film can satisfactorily be held by the combination of the control of the film thickness in the plating stage using the first bath and the plating in the second bath different in the composition.例文帳に追加

第１浴を用いたメッキ工程での膜厚制御と、組成の異なる第２浴でのメッキの組み合わせにより、スズ皮膜の疑似ホイスカーを防止し、皮膜外観を良好に保持できる。 - 特許庁

To provide a photosensitive resin composition excellent in resolution, adhesion, sensitivity, plating bath contaminating property and product stability.例文帳に追加

解像度、密着性、感度、めっき浴汚染性及び製品安定性に優れる感光性樹脂組成物を提供する。 - 特許庁

To provide a photosensitive resin composition excellent in resolution, adhesion, sensitivity, strippability, etc., and having a low plating bath contaminating property.例文帳に追加

解像性、密着性、感度、剥離特性等に優れ、めっき浴汚染性が低い感光性樹脂組成物を提供する。 - 特許庁

To provide a tin- and copper-containing plating bath which hardly gives rise to substitution deposition of copper to a tin anode, is low in the dependence of a plating film composition on current density, is good in bath stability and hardly gives rise to clouding.例文帳に追加

スズ陽極への銅の置換析出が生じ難く、メッキ皮膜組成の電流密度依存性が低く、浴安定性が良好で濁りが生じ難い、スズ及び銅を含有するメッキ浴を提供する。 - 特許庁

To provide a photosensitive resin composition excellent in resolution, adhesion, sensitivity and peeling property or the like and having low plating bath soiling property.例文帳に追加

解像性、密着性、感度、剥離特性等に優れ、めっき浴汚染性が低い感光性樹脂組成物を提供する。 - 特許庁

PLATED STEEL WIRE WITH HIGH CORROSION RESISTANCE AND HIGH WORKABILITY, PLATING BATH COMPOSITION, METHOD FOR MANUFACTURING PLATED STEEL WIRE WITH HIGH CORROSION RESISTANCE AND HIGH WORKABILITY, AND METAL GAUZE PRODUCT例文帳に追加

高耐食・高加工性メッキ鋼線、メッキ浴組成物、高耐食・高加工性メッキ鋼線の製造方法、及び金網製品 - 特許庁

The Rh-Re alloy plating thin film having the alloy ratio Rh:Re of 1.0:(0.1-1.0) and 0.1-10.0 μ film thickness using a plating bath having a Rh-Re alloy composition prepared by adding Re to a Rh plating bath, is formed.例文帳に追加

Ｒｈめっき浴にＲｅを添加したＲｈ−Ｒｅ合金めっき浴組成とし、当該めっき浴から電解により合金比率Ｒｈ：Ｒｅが１．０：０．１〜１．０、かつ膜厚が０．１〜１０．０ミクロンとなるＲｈ−Ｒｅ合金めっき薄膜を形成する。 - 特許庁