solidification sampleとは 意味・読み方・使い方

Subsequently, the zeolitization of a sample is facilitated by performing an alkali treatment comprising immersing the sample in a 3.5 N sodium hydroxide solution at 80°C for 24-72 h after taking the sample out of the mold or in a state that the sample is filled in the mold after curing and solidification.例文帳に追加

次に、養生固化後の試料を型から外して、もしくは型に詰めたまま、８０℃の３．５Ｎの水酸化ナトリウム溶液に２４〜７２時間浸漬してアルカリ処理を行い試料のゼオライト化を促した。 - 特許庁

When the collected unconsolidated sample satisfies a "clod state B", "reference specific gravity C" and "reference solidification strength D", the main construction is performed under the conditions.例文帳に追加

採取した未固結試料が「土塊の状態Ｂ」「基準比重Ｃ」「基準固化強度Ｄ」を満たした場合に、前記条件で本施工を行う。 - 特許庁

In the method of detecting the solidification structure of steel, a cross-section of a sample of a steel casting piece is polished, a surface other than a polished surface 2 of a sample 1 is electrically insulated to be an electrically insulated surface 3, and the polished surface 2 is corroded.例文帳に追加

鋼鋳片の試料の断面を研磨し、試料１の研磨面２以外の面を電気絶縁処理して電気絶縁処理面３とし、研磨面２を腐食することを特徴とする鋼の凝固組織検出方法である。 - 特許庁

The sample was floated in an air atmosphere of 4.5 atm, and a quench-solidification and melting process in the first example (manipulating the sample under a temperature gradient of about 700 K/sec) was repeated thrice.例文帳に追加

試料を4.5気圧の空気雰囲気中で浮遊させ、第１実施例における急冷凝固及び溶融プロセス（約700K/secの温度勾配での試料の操作）を３回繰り返した。 - 特許庁

The solidification structure is revealed even in the grade in which the solidification structure is previously difficult to be revealed, especially in low carbon steel with carbon concentration of ≤0.01 mass%, by electrically insulating the surface other than the polished surface (corroded surface) of the sample, and advancing corrosion only on the polished surface.例文帳に追加

試料の研磨面（腐食面）以外の面を電気絶縁処理することにより、研磨面のみで腐食を進行させることにより、従来は凝固組織の顕出が困難であった品種、特に炭素濃度が０．０１質量％以下の低炭素鋼についても、凝固組織を顕出できる。 - 特許庁

To provide a diffusion testing device capable of reducing a composition ratio change and a volumetric change caused by evaporation of a sample and capable of more accurately measuring a diffusion factor by sharply reducing solidification when steam of the sample having high steam pressure infiltrates into clearance between rotary shafts and share cells.例文帳に追加

蒸気圧の高い試料の蒸気が回転軸やシェアセルの隙間等に侵入して凝固するのを大幅に低減でき、これにより、試料の蒸発に伴う組成比率の変化や体積変化を低減し、拡散係数をより正確に測定することができる拡散試験装置を提供する。 - 特許庁

To provide a control method of an immersion depth of a molten metal measuring probe capable of surely performing measurements, for example, a molten temperature, a solidification temperature, and sample properties by precisely controlling the immersion depth in a molten metal layer.例文帳に追加

溶融金属層への浸漬深さをより正確に制御することで、例えば溶鋼温度や凝固温度、サンプル性状などの測定をより確実に行うことができる溶融金属測定用プローブの浸漬深さ制御方法を提供せんとする。 - 特許庁