The diamond film coated member is put in a vacuum sintering furnace, and subjected to heat treatment in a carbonizing atmosphere or vacuum atmosphere to remove the diamond film.例文帳に追加

ダイヤモンド膜被覆部材を真空焼結炉に入れ、浸炭雰囲気または真空雰囲気で熱処理することによりダイヤモンド膜を除去する。 - 特許庁

After that, the unsintered compact is charged to a sintering furnace, and its temperature is raised to 1,200°C at a temperature rising rate of 10°C per minute in a vacuum.例文帳に追加

その後、未焼成の成形体を焼成炉に入れ、真空下毎分１０℃の昇温速度で１２００℃まで昇温させた。 - 特許庁

This is attained by performing defatting and sintering processes of the binder in a vacuum sintering furnace as a single process (One-Step), and a device for forming a complicated shape by an insert (a placed core) and removing it by solvent.例文帳に追加

これらは、バインダーと真空焼結炉内でのプロセスである脱脂、焼結を一つの工程内（Ｏｎｅ−Ｓｔｅｐ）で行う事と、複雑な形状はインサート（置き中子）し、それを溶媒で除去する装置。 - 特許庁

In the method for manufacturing the glass preform comprising: storing the glass particulate deposit 2 in the furnace core pipe 6 of a vacuum heating furnace, and then sintering the deposit so as to transparently vitrifying it, the surface temperature of the glass particulate deposit 2 or the glass preform is measured through an opening 6a provided at the side face of the furnace core pipe 6.例文帳に追加

ガラス微粒子堆積体２を真空加熱炉の炉心管６内に収納し、焼結して、透明ガラス化するガラス母材の製造方法であって、炉心管６の側面に設けた開口６ａを通してガラス微粒子堆積体２又はガラス母材の母材表面温度を測定する。 - 特許庁

In a sintering stage for a compact finally made into a magnetostriction element, when the inside of a furnace is heated-up, in a temperature region where a hydride included in the compact is thermally decomposed and gaseous hydrogen is dissipated, the atmosphere in the furnace is sucked with a vacuum pump, the pressure in the furnace is held to the negative one, and the dissipation of hydrogen from the compact is promoted.例文帳に追加

最終的に磁歪素子となる成形体の焼結工程にて、炉内を昇温するに際し、成形体に含まれる水素化物が熱分解して水素ガスが放散される温度領域にて、炉内雰囲気を真空ポンプで吸引し、炉内の圧力を負圧に維持し、成形体からの水素の放散を促進するようにした。 - 特許庁

To provide a one chamber type vacuum furnace securing cleanliness of the atmosphere in a heating chamber even in a sintering process after a degreasing process, improving durability of the heating chamber itself, and uniformly cooling a material in a short period of time during a cooling process.例文帳に追加

脱脂工程後の焼結工程時においても加熱室内の雰囲気の清浄性を確保することができ、また、加熱室自体の耐久性を向上させることができ、さらに、冷却工程時、材料を短時間で均一に冷却することができる一室型真空炉を提供する。 - 特許庁