曲げ耐力比の英語

地震時の変形や曲げ加工のごとく鋼板表層部に塑性歪が集中する変形に耐えうる優れた曲げ加工性能を有する引張強度が５７０ＭＰａ以上の低降伏比型高張力鋼板を提供する。例文帳に追加

To provide a low yield ratio high-tensile steel plate of the tensile strength of ≥570 MPa having excellent bending performance capable of withstanding deformation in which plastic distortion is concentrated in a face layer part of the steel plate such as deformation or bending during an earthquake. - 特許庁

りん脱酸銅管における破壊圧力／引張り強さの比（Ｐｆｄ／σｄ）を上回る破壊圧力／引張り強さの比を有し、且つ曲げ加工性及び耐熱性が優れた熱交換器用銅合金管を提供する。例文帳に追加

To provide a copper alloy tube for a heat exchanger having a ratio of fracture pressure/tensile strength exceeding the ratio of fracture pressure/tensile strength (Pfd/σd) in a phosphorous deoxidized copper tube, and also having excellent bending workability and heat resistance. - 特許庁

りん脱酸銅管に対する破壊圧力と引張り強さとの比（ＰＦｄ）／（σｄ）を上回る破壊圧力／引張り強さの比（ＰＦａ）／（σａ）を有し、且つ曲げ加工性及び耐熱性が優れた熱交換器用銅合金管を提供する。例文帳に追加

To provide a copper alloy tube for heat exchanger having a ratio of burst pressure to tensile strength (PFa)/(σa) more than the ratio of burst pressure to tensile strength (PFd)/(σd) for a phosphorus-deoxidized copper tube, and superior in bending property and heat resistance. - 特許庁

メタル配線、コンタクトのバラツキ要因による電圧分圧比の精度の劣化を回避すると共に、曲げ応力の耐力を低下させることなく精度を向上させたラダー抵抗を形成した半導体装置を提供すること。例文帳に追加

To provide a semiconductor device which avoids the deterioration of accuracy of a voltage dividing ratio due to the variation factor of metal wirings and contacts, and which forms a ladder resistance improved in the accuracy without reducing yield strength against bending stress. - 特許庁

従来の黄銅材に比べ、応力緩和特性を劣化させずに、リン青銅に匹敵する耐力と良好な曲げ加工性を持った強化α黄銅材及びその製造方法の提供を目的とする。例文帳に追加

To provide a reinforced α-brass that as compared with conventional brass material, realizes an excellent balance of high proof stress and moldability without deterioration of stress relaxation characteristics, and to provide a process for producing the same. - 特許庁

また、本発明のばね用ステンレス鋼線の製造方法によれば、鋼線の製造において、最終ダイスを通過した後の鋼線に、曲げ加工変形を付与することによって、鋼線の０．２％耐力比を調整する。例文帳に追加

Moreover, in the method for manufacturing the stainless steel wire for spring, bending deformation is applied, when manufacturing the steel wire, to the steel wire after being passed through a final die to control the 0.2% yield ratio of the steel wire. - 特許庁

言い換えると、塔状構造体１００の上下方向にのみプレストレスが導入された構成と比較し、曲げ破壊に対する耐力が向上する。例文帳に追加

In other words, the strength against the bending fracture is improved compared to the constitution in which prestress is introduced only in a vertical direction of the tower-like structural body 100. - 特許庁