アルデヒド類とメラミンとをアルカリ触媒存在下で、２５℃における白濁法による濁度が１０〜２０倍となるまで反応させて初期反応物を得る第一次反応と、該初期反応物にアルデヒド類および／またはメラミンを添加して更にアルデヒド類とメラミンとを反応させる第二次反応とを含有することを特徴とする水溶性メラミン系樹脂の製造方法。例文帳に追加

The method for the production of a water-soluble melamine resin contains a primary reaction stage to react an aldehyde with melamine in the presence of an alkali catalyst until the turbidity at 25°C becomes 10-20 times determined by a clouding method and the secondary reaction stage to add an aldehyde and/or melamine to the initial reaction product and further perform the reaction of the aldehyde with melamine. - 特許庁

平均粒子径 100ｎｍ以下の銀を含む微粒子と、水性あるいは水溶性のアクリル樹脂あるいはアクリルメラミン樹脂の少なくとも１種と、殺菌剤とを混合するように構成する。例文帳に追加

This residue-type germicide is prepared by formulating finely divided particles each containing silver having an average particle diameter of ≤100 nm, at least one selected from the group consisting of an aqueous or water-soluble acrylic resin and an acrylic melamine resin, and a germicide. - 特許庁

メラミン系化合物および／またはメラミン樹脂の粉末（ａ）と、アミノ基を有する化合物の水溶液（ｂ）からなる木質板用接着剤にアミノ系化合物と酸性物質からなる塩を添加することを特徴とする無臭木質板製板用接着剤とすることにより解決される。例文帳に追加

This adhesive for use in manufacturing an odorless wood board is obtained by adding a salt made from an amino compound and an acidic material to an adhesive for a wood board comprising (a) a powder of a melamine compound and/or a melamine resin, and (b) an aqueous solution of an amino group-containing compound. - 特許庁

二軸延伸ポリアミドフィルムの少なくとも片面に、水溶性または水分散性ポリエステル樹脂（Ａ）とメチル化メラミン樹脂（Ｂ）とからなる耐熱性樹脂層が形成され、（Ａ）と（Ｂ）の質量比（Ａ／Ｂ）が９８／２〜７０／３０であることを特徴とする包装袋用ポリアミドフィルム。例文帳に追加

The polyamide film for packaging bag is constituted by forming a heat-resistant resin layer, which is composed of a water soluble or water dispersible polyester resin (A) and a methylated melamine resin (B), at least on one side of a biaxially stretched polyamide film and characterized in that the mass ratio (A/B) of (A) and (B) is 98/2-70/30. - 特許庁

アクリル樹脂エマルジョン、合成ゴムラテックス、水溶性アクリル樹脂溶液、水性ポリウレタン分散液等の熱可塑性樹脂水性分散液と、水性エポキシ樹脂、水分散イソシアネート、および低ホルムアルデヒドのメラミン樹脂等の熱硬化性樹脂プレポリマーとの混合物を含浸させて強化した原紙を用いる。例文帳に追加

This method for producing a decorative paper comprises using a base paper reinforced by impregnation with a mixture of an aqueous dispersion of a thermoplastic resin such as an acrylic resin emulsion, a synthetic rubber latex, a water-soluble acrylic resin solution, an aqueous polyurethane dispersion, etc., and a thermosetting resin prepolymer such as an aqueous epoxy resin, a water dispersion isocyanate and a melamine resin of low formaldehyde, etc. - 特許庁

特定構造のポリイミドユニットからなるポリイミド樹脂と、メラミンシアヌレート類縁体と、ジアゾアフトキノン類縁体とを含有し、該メラミンシアヌレート類縁体が、ポリイミド樹脂１００重量部に対し５〜５０重量部である弱アルカリ性水溶液でポジ型現像が可能で且つ有機溶媒に可溶な感光性ポリイミド樹脂組成物。例文帳に追加

A photosensitive polyimide resin composition comprises a polyimide resin comprising a polyimide unit of specific structure, a melamine cyanurate analogue and a diazonaphthoquinone analogue, which can be positive-tone developable with a weakly alkaline aqueous solution, and which is soluble in an organic solvent; and in the composition, the melamine cyanurate analogue is contained in an amount of 5-50 parts by weight, relative to 100 parts by weight of the polyimide resin. - 特許庁

水溶性に富み、溶出性の成分を含有する水性塗料であっても、回収及び濃縮する過程において硬化性が低下したり、硬化塗膜の硬度、耐水性、耐候性等の膜特性が悪化することのない、メラミン樹脂硬化系水性塗料の再使用方法を提供すること。例文帳に追加

To provide a recycle method for a melamine resin curing type water-base coating in which a curing property is not reduced at processes for recovery and concentration and film characteristics such as hardness, a water-proof property and weather-resistance of a cured coating film are not deteriorated even in a water-base coating having rich water-solubility and containing an eluting component. - 特許庁

台板に、カルボキシル基変性スチレン−ブタジエン系共重合体のラテックスをプライマーとして塗布し、然る後、スチレン−ブタジエン共重合体の水溶性ラテックスと尿素メラミン縮合樹脂と増量剤とを有する接着剤で、台板と突板とを接着する。例文帳に追加

A latex of a modified styrene carboxylate-butadiene based copolymer as a primer is applied to a base plate and thereafter the base plate is bonded to the sliced veneer by adhesives having a water soluble latex of a styrene-butadiene copolymer, an urea melamine condensed resin and an extender. - 特許庁