「ash brick」に関連した英語例文の一覧と使い方 - Weblio英語例文検索

In the method of producing light and pale colored fired brick by using the red brick clay as the raw material and mixing 3-10% zinc or zinc compound with the same, the color of the brick is accelerated to become pale and the cost is reduced by mixing 20-60 wt.% coal ash containing ≤8 wt.% iron oxide per the whole weight of the brick.例文帳に追加

また、赤煉瓦用粘土を原料として、これに、３〜１０重量％の亜鉛または亜鉛化合物を混合して明るく淡い色調の焼成煉瓦を製造する方法において、酸化鉄の含有量が８重量％以下の石炭灰を煉瓦全体に対して２０〜６０重量％混合することで淡色化を促進し、低コスト化を図る。 - 特許庁

On the working surface side of the aluminum ash, Al2O3-SiO2 sintered layer 2 in the aluminum ash components is formed with the radiation heat in the molten iron vessel and also, it is considered that AlN formed by reacting the metallic Al in the aluminum ash and the air has the molten iron resistance and the erosion of the refractory brick 3 on the bed is prevented.例文帳に追加

アルミ灰の稼働面側には溶銑容器内の輻射熱でアルミ灰成分であるＡｌ_2 Ｏ_3 ，ＳｉＯ_ 2の焼結層２が形成されるとともに、アルミ灰中の金属Ａｌと空気とが反応して形成されるＡｌＮが耐溶銑性を有し敷の耐火れんが３の溶損を防止すると思われる。 - 特許庁

To manufacture a stabilizer for steelmaking slag containing fluorine inexpensively using inexpensive molten blast furnace slag as a raw material and effectively utilizing particles or powder comprised of industrial wastes such as broken alumina brick pieces, a low-grade aluminum ash and the like.例文帳に追加

低コストの高炉スラグの融体を原料として、アルミナレンガ屑や低品位アルミ灰等の産業廃棄物からなる粒子または粉末を有効に利用して、フッ素を含む製鋼スラグの安定化剤を、安価に製造する。 - 特許庁

To provide a refractory brick used as a lining material of a furnace such as an ash melting furnace or a melting furnace and having high stability to low basicity slag even under an oxidative atmosphere.例文帳に追加

灰溶融炉や溶解炉などの炉の内張り材として使用される耐火れんがであって、酸化雰囲気下であっても低塩基度スラグに対する安定性の高い耐火れんがを提供する。 - 特許庁

The high-water absorbing, water-permeable and water-retentive brick is obtained by adding volcanic ash soil SHIRASU, a material such as bone ash or incineration ash containing phosphate and calcium oxide, a hollow material such as SHIRASU baloon or pearlite and a combustible material such as charcoal or wood chips into a ceramic material such as clay or feldspar consisting essentially of silicate and alumina, mixing, shaping and firing at a high temperature.例文帳に追加

粘土、長石などのケイ酸とアルミナを主成分とする窯業用原料に、火山灰土壌「シラス」、リン酸と酸化カルシウムを含有するや骨灰、焼却灰などの物質や、シラスバルーン、パーライトなどの中空材料、或いは炭、木屑などの可燃性材料を添加して混合成形し、高温で焼成することによって、高吸水性の透水性、保水性を有するレンガが得られる。 - 特許庁