急速熱焼鈍の英語

脱炭焼鈍工程において、急速加熱して一次再結晶集合組織を調整した後に、低酸化度雰囲気で焼鈍し、アルミナを主成分とする焼鈍分離剤を塗布する。例文帳に追加

In a decarburizing annealing stage, rapid heating is performed to control a primarily recrystallized texture, thereafter, annealing is performed in an atmosphere with a low oxidizing degree, and a separation agent for annealing essentially consisting of alumina is applied. - 特許庁

方向性電磁鋼板の製造において、脱炭焼鈍の昇温過程の急速加熱領域を、誘導加熱が利用できる温度に低下させる。例文帳に追加

To reduce the rapid heating region in the heating step in decarburization/annealing to the temperature at which induction heating can be used in the production of a grain-oriented magnetic steel sheet. - 特許庁

本発明の鋼板の製造方法は、鋼板を連続焼鈍するにあたり、水焼入れ後、再加熱帯炉温をT_1（℃）とした時、0.7×T_1（℃）以上まで鋼板を急速加熱し、次いで鋼板を再加熱帯にて焼戻し熱処理する。例文帳に追加

The method for producing the steel sheet includes: rapidly heating the steel sheet to ≥0.7×T_1(°C) when continuously annealing the steel sheet after water-quenching, wherein T_1(°C) represents the furnace temperature in the reheating zone; and applying tempering heat-treatment to the steel sheet in the reheating zone. - 特許庁

インヒビターフリー系の素材による方向性電磁鋼板の製造方法において、急速加熱処理を含む一次再結晶焼鈍を行う場合に、急速加熱処理による鉄損低減効果を安定して得る方途について提案する。例文帳に追加

To provide a method for manufacturing a grain-oriented electromagnetic steel sheet from an inhibitor-free base material, which can stably obtain an effect of reducing iron loss by rapid heating treatment, when subjecting a cold-rolled sheet to primary recrystallization annealing including the rapid heating treatment. - 特許庁

方向性電磁鋼板の製造において、脱炭焼鈍の昇温過程の急速加熱領域を、誘導加熱装置を用いて制御して磁束密度の高い方向性電磁鋼板を安定して製造する方法を提案する。例文帳に追加

To provide a process for stably producing a grain-oriented steel sheet with high magnetic flux density by controlling the rapid heating region in the heating step in decarburization/annealing using induction heating devices in the production of a grain-oriented magnetic steel sheet. - 特許庁

鏡面方向性電磁鋼板の製造において、脱炭焼鈍の昇温過程の急速加熱領域を、誘導加熱が利用できる温度に低下させる。例文帳に追加

To reduce the rapid heating region in the heating step in decarburization/annealing to the temperature at which induction heating can be used in the production of a mirror-finished grain-oriented magnetic steel sheet. - 特許庁

一次再結晶焼鈍時の急速加熱による鉄損低減効果を最大限発揮させることにより、所期した鉄損低減効果を安定して発現させる。例文帳に追加

To stably obtain an expected core-loss reducing effect by displaying the core-loss reducing effect to the maximum with quick-heating when a primary recrystallize-annealing is applied. - 特許庁