極限点の英語

したがって、部品点数を極限まで減らした高精度な記録紙の残量検知により、底板５上に積載された記録紙Ｐを少数枚でも正確に検知することができる。例文帳に追加

Even a small number of the recording paper P piled on the bottom plate 5 can be accurately detected by accurately detecting the residual quantity of the recording paper with the parts reduced to the minimum number. - 特許庁

単焦点標準レンズ程度まで小型化され、かつ非球面を使用せず、非常に少ない構成枚数で、極限までコストダウンされた、変倍比２．２倍程度でかつ高性能なズームレンズを提供すること。例文帳に追加

To provide a high-performance zoom lens having a power variation ratio of about 2.2, which is miniaturized as small as a single focus standard lens, which is constituted of a very small number of lenses without using an aspherical lens and whose cost is reduced to the minimum. - 特許庁

缶内面に当たる側のポリエステル樹脂フィルムは厚み１５〜５０μｍ、融点が２２５〜２６０℃、極限粘度が０．６０以上で、非晶質化されている。例文帳に追加

The polyester resin film on the side in contact with the inside surface of the can has a thickness of 15 to 50 μm, a melting point 225 to 260°C and an ultimate viscosity of ≥0.60 and is made amorphous. - 特許庁

チタン−マグネシウム複合型チーグラー触媒の存在下に、エチレンおよび１−ブテンを共重合させることによって得られる共重合体であって、極限粘度が５ｄｌ／ｇ以上であり、冷キシレン可溶部と示差走査熱量測定による融点が下記の関係式を満たす超高分子量エチレン−１−ブテン共重合体。例文帳に追加

The ultrahigh molecular weight copolymer is obtained by copolymerizing ethylene and 1-butene in the presence of a titanium-magnesium complex type Ziegler catalyst. - 特許庁

ポリエチレンテレフタレート主体のポリエステル（I）からなるフィルムであって、２４６〜２５２℃に融点を有し、極限粘度が０．７０〜０．８５であり、２００℃における熱収縮率が２０〜３５％であることを特徴とする金属板ラミネート用フィルム。例文帳に追加

The polyester film for lamination of the metal plate comprises a polyester consisting essentially of a polyethylene terephthalate, and has 246-252°C melting point, 0.70-0.85 intrinsic viscosity and 20-35% heat shrinkage at 200°C. - 特許庁

現在公的に定められているゴム物性規格以外に、積層体として影響を受けると考えられる物性を見つけることで、ゴム物性と積層体の極限性能レベルが一致しない現状の問題点を解決する。例文帳に追加

To solve the present problem, in which the ultimate performance levels of a rubber material feature and of a laminate do not agree with each other, by finding a material feature considered as being a the laminate which will be influenced, other than the standard of the rubber material feature which is officially ordained at present. - 特許庁

厚さ１.０ｍｍ以下のＰＥＴ薄片を主たる出発原料として融点以下の温度で真空下或いは乾燥した不活性気体気流下で固相重合させ、極限粘度０.８以上の高ＩＶのＰＥＴ薄片の製造方法。例文帳に追加

High-IV thin PET chips having an intrinsic viscosity of 0.8 or higher are produced by subjecting thin PET chips having a thickness of 1.0 mm or lower, as the main starting material, to solid phase polymerization at the melting point or lower under vacuum or in dry inert gas stream. - 特許庁

ジカルボン酸成分が、芳香族ジカルボン酸８０〜９９ｍｏｌ％、不飽和ジカルボン酸１〜１０ｍｏｌ％、グリコール成分が、１，２−プロピレングリコール６０〜１００ｍｏｌ％からなり、極限粘度が０．３５以上、ガラス転移点温度が４０℃以上であるポリエステル樹脂。例文帳に追加

The polyester resin comprises 80-99 mol% aromatic dicarboxylic acid and 1-10 mol% unsaturated dicarboxylic acid as the dicarboxylic acid component and 60-100 mol% 1,2-propylene glycol as the glycol component, and has an intrinsic viscosity of ≥0.35 and a glass transition temperature of ≥40°C. - 特許庁