A rack 21 of the rack and pinion type steering device is manufactured in a manner that a raw material made of steel is molded in a prescribed shape by cold forging, and is further subjected to induction hardening.例文帳に追加

ラックアンドピニオン式ステアリング装置のラック２１は、鋼からなる素材を冷間鍛造により所定の形状に成形し、さらに高周波焼入れを施すことにより製造されている。 - 特許庁

A hub ring 2 of the rolling bearing unit 1 for supporting the wheel is provided by induction hardening after a steel element is treated by hot forging, molded in a predetermined shape and cooled.例文帳に追加

車輪支持用転がり軸受ユニット１のハブ輪２を、鋼製素材に熱間鍛造を施して所定の形状に成形し冷却した後に、高周波焼入れを施すことにより得る。 - 特許庁

To provide a method and an apparatus for induction-heating with which in the method and the apparatus for induction-heating of a billet for forging by heating a columnar billet 13, especially the columnar billet 13 having large weight and diameter, a scratch generated in a billet conveying way in the induction-heating apparatus 1 is restrained and diffusion-joining of both billets 13 is restrained.例文帳に追加

円柱状ビレット１３、特に重量及び直径の大きい円柱状ビレット１３を加熱する鍛造用ビレット誘導加熱方法及び装置において、誘導加熱装置１内のビレット搬送路に発生する摺動傷を抑制し、ビレット１３同士の拡散接合を抑制する誘導加熱方法及び装置を提供することを目的とする。 - 特許庁

That is, the rack is manufactured in a manner that it is molded by cold forging after rod-like or tubular material made of steel is soft-annealed, and is further subjected to induction hardening.例文帳に追加

すなわち、上記鋼からなる棒状素材又は管状素材に軟化焼鈍しを施した後に冷間鍛造により成形し、さらに高周波焼入れを施すことにより製造されている。 - 特許庁

To provide steel having cold forgeability more excellent than that of steel for machine structures such as S53C without performing complicated heat treatment before cold forging, particularly improved in limit upsetting ratio and having induction hardenability.例文帳に追加

複雑な冷鍛前の熱処理を施すことなく、Ｓ５３Ｃ等の機械構造用鋼より優れた冷間鍛造性、特に限界据込率が向上し、高周波焼入性を有する鋼を提供する。 - 特許庁

That is, the rack is manufactured in such a manner that it is molded into a prescribed shape by cold forging after rod-like or tubular material made of the steel is softened and annealed, and is further subjected to induction hardening.例文帳に追加

すなわち、上記鋼からなる棒状素材又は管状素材に軟化焼鈍しを施した後に冷間鍛造で所定の形状に成形し、さらに高周波焼入れを施すことにより製造されている。 - 特許庁

In the induction hardening after the cold forging, valley parts between teeth and core parts are not subjected to hardening, and in the rack 21, the Vickers hardness HV of a non-hardened part including the valley parts is ≥180 and ≤300.例文帳に追加

冷間鍛造後の高周波焼入れでは歯と歯の間の谷部や芯部には焼入れは施されないので、ラック２１においては、谷部をはじめとする非焼入れ部のビッカース硬さＨＶは１８０以上３００以下となる。 - 特許庁

The rack 21 of the rack-and-pinion type steering apparatus is formed by cold forging after a material made of steel is subjected to softening, and manufactured by executing recrystallization, induction hardening, and tempering.例文帳に追加

ラックアンドピニオン式ステアリング装置のラック２１は、鋼からなる素材に軟化焼鈍しを施した後に冷間鍛造により成形し、さらに再結晶処理，高周波焼入れ，及び焼戻しを施すことにより製造されている。 - 特許庁