A steel sheet containing, by mass, <4% Si is subjected to siliconizing treatment under the conditions in which siliconizing temperature is controlled to 1,023 to 1,025°C, and the concentration of silicon tetrachloride in an inert gas atmosphere is controlled to >35 vol.%, preferably to >40 vol.% to form a high silicon magnetic steel sheet.例文帳に追加

質量％で、Ｓｉ含有量が４％未満の鋼板を、浸珪処理温度を１０２３℃以上、１２５０℃以下、無活性ガス雰囲気中の四塩化珪素濃度を３５ｖｏｌ％超え、好ましくは４０ｖｏｌ％超え、とする条件で浸珪処理し、高珪素電磁鋼板とする。 - 特許庁

Consequently, the amount of the perlite structure contained in the first powder can be increased when the second heating process is performed to increase the siliconizing speed.例文帳に追加

そのため、第２加熱工程を実行する際に、第１粉末に含まれるパーライト組織の量を増大させておくことができ、浸珪速度を上昇させることができる。 - 特許庁

To stably produce a high silicon steel strip in which the concentration of Si in the sheet width direction is uniform without generating the breaking of the steel strip and edge cracking by a continuous gas siliconizing treating method.例文帳に追加

連続気体浸珪処理法により、鋼帯の破断やエッジ割れを生じることなく、板幅方向のＳｉ濃度が均一な高珪素鋼帯を安定して製造する。 - 特許庁

In the high silicon steel sheet obtained by subjecting a steel sheet containing ≤4 wt% Si to heating treatment, siliconizing treatment, diffusion soaking treatment and cooling treatment in succession, the average concentration of C in the steel sheet after the diffusion soaking treatment is ≤90 ppm.例文帳に追加

Si：4wt％以下を含む鋼板に、加熱処理、浸珪処理、拡散均熱処理及び冷却処理を順次施すことにより得られる高けい素鋼板において、前記拡散均熱処理後の鋼板平均C濃度が90ppm以下である高けい素鋼板。 - 特許庁

To provide a method for producing powder for dust core, in which secondary particles are prevented from being produced upon siliconizing treatment, to improve the quality and productivity of the powder for dust core, and an apparatus for producing the powder for dust core.例文帳に追加

浸珪処理時に二次粒子が生成されることを防ぎ、圧粉磁心用粉末の品質と生産性を向上させることができる圧粉磁心用粉末製造方法及び圧粉磁心用粉末製造装置を提供すること。 - 特許庁

To provide a method for producing powder for a dust core and a device for producing the powder for the dust core, allowing improvement of productivity and quality of the powder for the dust core by preventing that secondary particles are generated in time of siliconizing treatment.例文帳に追加

浸珪処理時に二次粒子が生成されることを防ぎ、圧粉磁心用粉末の品質と生産性を向上させることができる圧粉磁心用粉末の製造方法及び圧粉磁心用粉末製造装置を提供すること。 - 特許庁

To provide an extra-thin silicon steel sheet which is less in the quantity of coarse grains even when being subjected to heat treatment at ≥1,100°C, has high B8/Bs and is suitable to siliconizing treatment, and to provide a manufacturing method therefor,.例文帳に追加

1100℃以上で熱処理しても粗大粒が少なく、且つ高いB8/Bsを示す、浸珪処理に適した極薄珪素鋼板およびその製造方法を提供する。 - 特許庁

A grain oriented silicon steel sheet composed of secondarily recrystallized grains comprising 25 to 300 ppm Sol.Al is subjected to cold rolling, and is subjected to siliconizing treatment and Si diffusion treatment at ≥1,050°C.例文帳に追加

Sol.Alを25ppm以上、300ppm以下含有する二次再結晶粒より構成された一方向性電磁鋼板に冷間圧延を施し、1050℃以上の温度で浸珪処理、Si拡散処理を施す。 - 特許庁