「SILICONIZING」に関連した英語例文の一覧と使い方 - Weblio英語例文検索

To provide a method for producing by siliconizing a high silicon magnetic steel sheet having uniform distribution of Si in the width direction of the seet.例文帳に追加

この発明は、浸珪法により、板幅方向のＳｉ分布が均一な高珪素電磁鋼板を製造する方法を提供する。 - 特許庁

To provide a method for producing powder for a dust core for producing a dust core with high specific resistance where, even in the case siliconizing treatment is performed under the atmospheric pressure, a desired silicon-containing layer can be formed on the surface layer of soft magnetic metal powder, thus, while time required for the siliconizing treatment is reduced, a dust core having a high specific resistance is produced.例文帳に追加

大気圧下で浸珪処理をおこなった場合でも所望の珪素含有層を軟磁性金属粉末の表層に形成することができ、もって浸珪処理に要する時間を短縮しながら、高比抵抗な圧粉磁心を製造するための圧粉磁心用粉末を製造する方法を提供する。 - 特許庁

A steel sheet containing, by mass, <4% Si is subjected to siliconizing treatment under the conditions in which siliconizing temperature is controlled to 1,023 to 1,025°C, and the concentration of silicon tetrachloride in an inert gas atmosphere is controlled to >35 vol.%, preferably to >40 vol.% to form a high silicon magnetic steel sheet.例文帳に追加

質量％で、Ｓｉ含有量が４％未満の鋼板を、浸珪処理温度を１０２３℃以上、１２５０℃以下、無活性ガス雰囲気中の四塩化珪素濃度を３５ｖｏｌ％超え、好ましくは４０ｖｏｌ％超え、とする条件で浸珪処理し、高珪素電磁鋼板とする。 - 特許庁

Consequently, the amount of the perlite structure contained in the first powder can be increased when the second heating process is performed to increase the siliconizing speed.例文帳に追加

そのため、第２加熱工程を実行する際に、第１粉末に含まれるパーライト組織の量を増大させておくことができ、浸珪速度を上昇させることができる。 - 特許庁

To stably produce a high silicon steel strip in which the concentration of Si in the sheet width direction is uniform without generating the breaking of the steel strip and edge cracking by a continuous gas siliconizing treating method.例文帳に追加

連続気体浸珪処理法により、鋼帯の破断やエッジ割れを生じることなく、板幅方向のＳｉ濃度が均一な高珪素鋼帯を安定して製造する。 - 特許庁

In the high silicon steel sheet obtained by subjecting a steel sheet containing ≤4 wt% Si to heating treatment, siliconizing treatment, diffusion soaking treatment and cooling treatment in succession, the average concentration of C in the steel sheet after the diffusion soaking treatment is ≤90 ppm.例文帳に追加

Si：4wt％以下を含む鋼板に、加熱処理、浸珪処理、拡散均熱処理及び冷却処理を順次施すことにより得られる高けい素鋼板において、前記拡散均熱処理後の鋼板平均C濃度が90ppm以下である高けい素鋼板。 - 特許庁

To provide a method for producing powder for dust core, in which secondary particles are prevented from being produced upon siliconizing treatment, to improve the quality and productivity of the powder for dust core, and an apparatus for producing the powder for dust core.例文帳に追加

浸珪処理時に二次粒子が生成されることを防ぎ、圧粉磁心用粉末の品質と生産性を向上させることができる圧粉磁心用粉末製造方法及び圧粉磁心用粉末製造装置を提供すること。 - 特許庁

To provide a method for producing powder for a dust core and a device for producing the powder for the dust core, allowing improvement of productivity and quality of the powder for the dust core by preventing that secondary particles are generated in time of siliconizing treatment.例文帳に追加

浸珪処理時に二次粒子が生成されることを防ぎ、圧粉磁心用粉末の品質と生産性を向上させることができる圧粉磁心用粉末の製造方法及び圧粉磁心用粉末製造装置を提供すること。 - 特許庁

To provide an extra-thin silicon steel sheet which is less in the quantity of coarse grains even when being subjected to heat treatment at ≥1,100°C, has high B8/Bs and is suitable to siliconizing treatment, and to provide a manufacturing method therefor,.例文帳に追加

1100℃以上で熱処理しても粗大粒が少なく、且つ高いB8/Bsを示す、浸珪処理に適した極薄珪素鋼板およびその製造方法を提供する。 - 特許庁

A grain oriented silicon steel sheet composed of secondarily recrystallized grains comprising 25 to 300 ppm Sol.Al is subjected to cold rolling, and is subjected to siliconizing treatment and Si diffusion treatment at ≥1,050°C.例文帳に追加

Sol.Alを25ppm以上、300ppm以下含有する二次再結晶粒より構成された一方向性電磁鋼板に冷間圧延を施し、1050℃以上の温度で浸珪処理、Si拡散処理を施す。 - 特許庁

Since an Al amount is controlled, problems that a siliconizing rate varies and an effective Si concentration gradient is not obtained in a plate thickness direction are solved to obtain the unidirectional electromagnetic steel plate having an average Si concentration of 5.5 to 7 mass% on a steel plate surface and an average Si concentration of 3 to 5.5 mass% in the center of the plate thickness.例文帳に追加

Al量が制御されているため、浸珪速度が変動したり、板厚方向に有効なSi濃度勾配を実現できないという問題が解消され、鋼板表面の平均Si濃度が5.5〜7mass%、板厚中心の平均Si濃度が3〜5.5mass%である一方向性電磁鋼板が得られる。 - 特許庁

In the method for producing the high silicon electromagnetic steel sheet, a steel sheet having an Si content of <4 wt.% is subjected to siliconizing-diffusion treatment to obtain steel having a C content of 0.001 to 0.02 wt.%, an Si content of 4 to 10 wt.% and a Cr content of 1 to 20 wt.%, and the steel is thereafter annealed at 150 to 350°C.例文帳に追加

Si含有量が４wt％未満の鋼板を、浸珪・拡散処理して、Ｃ含有量が0.001wt％以上0.02wt％以下、Si含有量が４wt％以上10wt％以下、Cr含有量が１wt%以上20wt％以下の鋼を得、その後に150〜350℃で焼鈍することを特徴とする高珪素電磁鋼板の製造方法。 - 特許庁

In the method by which a base metal steel sheet containing <4 wt.% Si is subjected to heating treatment, siliconizing treatment, diffusion soaking treatment and cooling treatment in succession to produce a high silicon steel sheet, the having treatment is performed in an atmosphere satisfying the following inequality and at the temperature rising rate of ≥50°C/min at a temp of ≥500°C.例文帳に追加

Si：4wt％未満の母材鋼板に対して、加熱処理、浸珪処理、拡散均熱処理及び冷却処理を順次行い、高けい素鋼板を製造する方法において、前記加熱処理を下式を満足する雰囲気中でかつ500℃以上での昇温速度が50℃／min以上となるように加熱する。 - 特許庁

After secondary recrystallization annealing is applied to intermediate stock at 800-1,100°C for carrying out suppression of grain growth with an inhibitor and Goss integration, siliconizing treatment is performed and then purification annealing for removing the unnecessary inhibitor from the steel is done at ≥1,200°C.例文帳に追加

中間材にインヒビターにより結晶粒成長を抑制し、Ｇｏｓｓ方位に集積させる二次再結晶焼鈍を８００〜１１００℃で行った後、浸珪処理し、その後不要となったインヒビターを鋼より除去するための純化焼鈍を１２００℃以上で行う。 - 特許庁

The high-silicon electromagnetic steel sheet with excellent soft magnetic properties can be obtained by subjecting a steel sheet having <4 wt.% Si content to siliconizing treatment in a gaseous atmosphere containing silicon compounds and has 4-10 wt.% Si content, 1-20 wt.% Cr content and ≤0.01 wt.% Al content.例文帳に追加

Si含有量が４wt％未満の鋼板を、珪素化合物を含むガス雰囲気中で浸珪処理して得られる高珪素電磁鋼板であって、Si含有量が４wt％以上10wt％以下、Cr含有量が１wt％以上20wt％以下、Al含有量が0.10wt％以下であることを特徴とする軟磁気特性に優れた高珪素電磁鋼板。 - 特許庁

To provide a method of producing powder for dust cores for preventing production of a secondary particle in siliconizing treatment and for increasing quality and productivity of powder for dust cores; to provide a dust core using powder for dust cores produced by the method of producing powder for dust cores; and to provide an apparatus for producing powder for dust cores.例文帳に追加

浸珪処理時に二次粒子が生成されることを防ぎ、圧粉磁心用粉末の品質と生産性を向上させることができる圧粉磁心用粉末の製造方法、その圧粉磁心用粉末の製造方法により製造された圧粉磁心用粉末を用いた圧粉磁心、及び、圧粉磁心用粉末製造装置を提供すること。 - 特許庁

A carbon fiber reinforced silicon carbide base material is formed by mixing a plurality of kinds of carbon fibers each having different reactivity with silicon, graphite powder and powdery resin and heating and press-forming to form a carbon fiber reinforced base material and carbonizing the carbon fiber reinforced base material and siliconizing the carbon fiber reinforced carbon base material to form the carbon fiber reinforced silicon carbide base material.例文帳に追加

シリコンとの反応性が異なる複数種の炭素繊維、黒鉛粉末及び粉末樹脂を混合して加熱加圧成形を施して炭素繊維強化基材を形成し、この炭素繊維強化基材を炭化した炭素繊維強化炭素基材を炭化ケイ素化して炭素繊維強化炭化ケイ素基材を形成する。 - 特許庁