high-tensile cast ironとは 意味・読み方・使い方

To produce high strength spheroidal graphite cast iron having high tensile strength and good elongation in a state of as-cast and imparted with strong hardenability.例文帳に追加

鋳放しで高い引張り強さと良好な伸びを有し、且つ強力な焼入れ性を付与した高強度球状黒鉛鋳鉄を提供する。 - 特許庁

To eliminate inconveniences that the tensile strength and elongation of high-strength ductile cast iron are considerably reduced when it is wet in water, and embrittlement occurs.例文帳に追加

高強度ダクタイル鋳鉄が、水に濡れると引張り強度及び伸びが著しく低下し、脆化現象を生じるという不都合を解消する。 - 特許庁

To provide a thick high strength spherical graphite cast iron product, as cast, which has high strength satisfying the tensile strength of ≥750 MPa and high ductility satisfying the elongation of ≥1.5%, further is excellent in wear resistance, and also has a thickness of ≥100 mm.例文帳に追加

鋳放しのままで、引張強さ：750MPa以上の高強度と、伸び：1.5％以上の高延性とを有し、さらに耐摩耗性に優れ、かつ肉厚：100mm以上の厚肉高強度球状黒鉛鋳鉄品を提供する。 - 特許庁

To provide a thick high-strength spherical graphite cast iron product with a thickness of ≥100 mm, as cast, which has high strength satisfying the tensile strength of ≥750 MPa and high ductility satisfying the elongation of ≥1.5%, and further has excellent wear resistance.例文帳に追加

鋳放しのままで、引張強さ：750MPa以上の高強度と、伸び：1.5％以上の高延性とを有し、さらに耐摩耗性に優れる肉厚：100mm以上の厚肉高強度球状黒鉛鋳鉄品を提供する。 - 特許庁

To provide a high strength spheroidal graphite cast iron article having a high tensile strength almost satisfying >900 N/mm^2 and excellent wear resistance as cast, and in which the carbidization in the thin part with a thickness of ≤10 mm is prevented.例文帳に追加

鋳放しのままで、おおよそ引張強さ：900Ｎ/mm^2超の高強度と、優れた耐摩耗性を有し、かつ肉厚：10mm以下の薄肉部における白銑化を防止した、高強度球状黒鉛鋳鉄品を提供する。 - 特許庁

In this way, a high strength spheroidal graphite cast iron article having both of a tensile strength of >900 MPa and an elongation of ≥3% as cast, having excellent wear resistance as well, and free from carbidization in the thin part with a thickness of ≤10 mm is obtained.例文帳に追加

これにより、鋳放しままでおおよそ900MPa超の引張強さと３％以上の伸びとを兼備し、耐摩耗性にも優れ、肉厚部10mm以下の薄肉部の白銑化も生じない高強度球状黒鉛鋳鉄品となる。 - 特許庁

To obtain high strength spheroidal graphite cast iron as cast which includes a dense structure free from bainite and cementite and having satisfactory machinability, includes high strength satisfying the tensile strength of ≥900 MPa and satisfactory elongation of ≥4% even without the addition of Al, includes excellent machinability, is substitutible for forged steel, cast steel and austemper spheroidal graphite cast iron, and can contribute to the service life and lightening as parts.例文帳に追加

鋳放しで、ベイナイトやセメンタイトのない被削性の良好な緻密な組織からなり、Ａｌの添加なしでも、引張強さ９００ＭＰａ以上の高強度と、４％以上の良好な伸びを有し、優れた被削性を有し、鍛鋼や鋳鋼、オーステンパ球状黒鉛鋳鉄の代替化、部品としての寿命や軽量化に寄与できる鋳放し高強度球状黒鉛鋳鉄を得ることを目的とする。 - 特許庁