鋳込み成形体の英語

電気石を主成分とする泥奨の鋳込み成形により得られた所望の形態の鋳込み成形体を、仮焼成及び本焼成して得られた成型品であることを特徴とする。例文帳に追加

The burial article is characterized by being a shaped article obtained by temporarily baking and baking a casting compact in a required shape obtained by casting/compacting slurry comprising tourmaline as the main component. - 特許庁

得られたスラリーを型成形用母型の成型用空間に鋳込み、硬化させ、脱型して成形体（成形用型）を得る。例文帳に追加

The obtained slurry is cast in the molding space of a matrix for molding a mold and cured and demolded to obtain a molded object (mold). - 特許庁

成形性がよく、鋳込み時の強度や形状保持性に優れ、且つ鋳込み後の鋳型の除去性にも優れた、鋳物製造用構造体を提供すること。例文帳に追加

To provide a structural body for casting, excellent in the formability and the strength at casting time and the shape-holdability and removability from a mold after casting. - 特許庁

成形性が良く、軽量で鋳込み時においても十分な熱間強度及び形状保持性を有し、鋳物の表面平滑性並びに鋳込み後の除去性に優れる鋳物製造用の鋳型及び構造体を提供すること。例文帳に追加

To provide a mold and a structural body for producing a casting, having good formability and light weight and sufficient hot-strength and shape-holding property at the casting time and excellent surface smoothness of the casting and excellent removability after casting. - 特許庁

酸化インジウムと酸化錫の混合粉末、水、分散剤、バインダーを含むＩＴＯスラリーを鋳込み成形するＩＴＯ成形体の製造方法において、カルボキシル基を有する分散剤を添加して、ＩＴＯスラリーの鋳込み前のスラリー粘度を２５℃で１.０〜５０ｄＰａ・ｓに調整する。例文帳に追加

The method for manufacturing an ITO molded form by slip casting of ITO slurry containing a mixture of indium oxide powder and tin oxide powder, water, a dispersing agent and a binder comprises adding a dispersing agent having a carboxylic group and controlling slurry viscosity prior to ITO slurry casting at 1.0-50 dPa.s at 25°C. - 特許庁

成形性がよく、軽量で炭素当量が４．２％以下の溶融金属の鋳込みにおいても精度及び表面平滑性の高い鋳物を製造することができ、且つ鋳込み後の鋳型の除去性にも優れた、鋳物製造用の鋳型又は構造体を提供すること。例文帳に追加

To provide a mold or a structural body for producing a casting which has good formability, is of light weight and has high precision and surface flatness, even in the case of casting molten metal having ≤4.2% carbon equivalent, and has excellent removability of the mold after casting. - 特許庁

生産性を維持ないし向上させつつ、成形体強度自体を向上させてクラックの発生を防止して、安定した生産が可能な鋳込み成形によるＩＴＯ成形体の製造方法を提供する。例文帳に追加

To provide a method for manufacturing an ITO molded form by slip casting capable of maintaining or improving productivity, improving molded form strength to prevent crack initiation and realizing stable production. - 特許庁

本発明は、鋳込み成形方法において得られる含水成形体が充分な保形性を保有するに好適な優れた成形体製造方法を提供せんとするものである。例文帳に追加

To provide a method for producing an excellent molding, desirable in that a water-containing molding obtained by casting can sufficiently retain its shape. - 特許庁