The method for growing the fluoride crystal is carried out by using a Bridgman furnace 10 and by housing a crystal raw material 3, in which a fluoride raw material is compounded, in a crucible 2, fusing the material and cooling to solidify the melt, wherein a fluoride having the total mass concentration of iron and zinc of less than 1.5 ppm is compounded as the fluoride raw material.例文帳に追加

ブリッジマン炉１０を用い、フッ化物原料が配合された結晶原料３をルツボ２に収容し、溶融後、融液を冷却固化してフッ化物結晶を育成する方法であって、フッ化物原料として、鉄及び鉛の合計質量濃度が１．５ｐｐｍ未満であるフッ化物を配合する。 - 特許庁

The vinylidene fluoride-based resin composition comprises 100 pts.wt. of vinylidene fluoride polymer having not less than 55% of stable terminal groups and 0.01-0.1 pt.wt. of at least one compound selected from hydroxides and oxides of magnesium and zinc.例文帳に追加

安定末端基を５５％以上有するフッ化ビニリデン重合体１００重量部と、マグネシウムおよび亜鉛の水酸化物および酸化物から選ばれる少なくとも一種の化合物の０．０１〜０．１重量部とからなるフッ化ビニリデン系樹脂組成物。 - 特許庁

The optical parts for an IR laser consist of an optical substrate 200 having a principal surface, a barium fluoride film 210 formed on the principal surface of the substrate 200 and a zinc selenide film 220 formed on the barium fluoride film 210, and the principal surface of the optical substrate 200 is subjected to smoothening treatment.例文帳に追加

赤外線レーザ用光学部品は、主表面を有する光学基材２００と、光学基材２００の主表面上に形成された弗化バリウム膜２１０と、弗化バリウム膜２１０の上に形成されたセレン化亜鉛膜２２０とを備え、光学基材２００の主表面は平滑化処理されている。 - 特許庁

For example, when the single crystal of calcium fluoride is produced, the furnace is heated in the presence of a fluoride of zinc having electronegativity of 1.6, lead having electronegativity of 1.8, carbon having electronegativity of 2.5 or the like because the electronegativities of Ca and oxygen are 1.0 and 3.5, respectively.例文帳に追加

例えば、フッ化カルシウムの単結晶を製造する場合、Ｃａの電気陰性度が１．０、酸素の電気陰性度は３．５であるから、電気陰性度が１．６の亜鉛、１．８の鉛、２．５の炭素などのフッ化物の存在下に炉を加熱する。 - 特許庁

A transmission spectrum of calcium fluoride singe crystal is measured, an absorption wavelength that is a reference transmittance for evaluating a zinc impurity concentration in the transmission spectrum is determined from within an absorption wavelength range of 120 to 200 nm in the transmission spectrum, and the zinc impurity concentration in the calcium fluoride singe crystal is determined using a change in the absorption wavelength.例文帳に追加

フッ化カルシウム単結晶の透過スペクトルを測定し、前記透過スペクトルにおける、亜鉛不純物濃度を評価するための基準透過率となる吸収波長を、該透過スペクトルにおける吸収波長が１２０〜２００ｎｍの範囲から決定し、該吸収波長の変化により、前記フッ化カルシウム単結晶中の亜鉛不純物濃度を決決定する。 - 特許庁

A base coating layer containing a binder resin such as polyvinylidene fluoride resin, vinylidene fluoride-trifluoroethylene copolymer resin and vinylidene fluoride-hexafluoropropylene copolymer resin and an inorganic pigment such as titanium oxide and zinc oxide is formed between a conductive supporting body and a photosensitive layer of an electrophotographic photoreceptor.例文帳に追加

電子写真感光体の導電性支持体と感光層との間に、ポリフッ化ビニリデン樹脂、フッ化ビニリデン−トリフルオロエチレン共重合体樹脂およびフッ化ビニリデン−ヘキサフルオロプロピレン共重合体樹脂などの結着樹脂と、酸化チタンおよび酸化亜鉛などの無機顔料とを含有する下引き層を設ける。 - 特許庁

The aluminum-added zinc oxide-based transparent conductive film is deposited on a substrate by a vacuum vapor deposition method while a zinc oxide sintered body containing at least 0.01-10 wt.% aluminum fluoride as impurity dopant is a target material.例文帳に追加

不純物ドーパントとして少なくともフッ化アルミニウムを０．０１〜１０重量％の割合で含む酸化亜鉛焼結体をターゲット材料とした真空蒸着法により、基板上に成膜されることを特徴とするアルミニウム添加酸化亜鉛系透明導電膜。 - 特許庁

In the middle of the passivation and the zinc substitution plating, activation suppression treatment with an aqueous solution comprising sodium pyrophosphate, sodium tetraborate and sodium fluoride can be performed.例文帳に追加

不働態化処理と亜鉛置換めっきの中間にピロリン酸ナトリウム、四ホウ酸ナトリウム及びフッ化ナトリウムを含有する水溶液による活性化抑制処理を行なうことができる。 - 特許庁