To provide a fatigue strength increasing method favorable when it is used for the hammer peening, and capable of increasing the fatigue strength of a weld zone in a steel structure such as a steel bridge by introducing the compressive residual stress without imparting any deformation forming a new stress concentration part in the weld zone.例文帳に追加

ハンマーピーニングに用いて好適な、鋼橋など鋼構造物における溶接部の疲労強度を、溶接部に新たな応力集中部となる変形を与えずに圧縮残留応力を導入して向上させる疲労強度向上方法を提供する。 - 特許庁

To provide a structure welding method which is performed by calculating through an analytical method, a welding condition causing residual stress in a proximity to a weld zone to be compressive residual stress, before actual welding is implemented.例文帳に追加

実際の溶接を実施する以前に溶接部の近傍を圧縮残留応力にする溶接条件を解析的手法により算出して行う構造物の溶接方法を提供する。 - 特許庁

To prevent the generation of a transition zone formed around a coarse aggregate as one of factors reducing the compressive strength and tensile strength of concrete.例文帳に追加

コンクリートの圧縮強度や引張強度を低減させる要因の一つが，粗骨材の周りに形成される遷移帯である．本発明は遷移帯の発生を防止するものである． - 特許庁

In the warm shot-peening step S4, shots are projected while the spring element wire after the tempering is in the warm zone exceeding 100°C, and the compressive residual stress is generated to the deep position from the surface of the spring element wire.例文帳に追加

温間ショットピーニング工程Ｓ４では、焼戻し後のばね素線が１００℃を越える温間域にあるうちにショットが投射され、ばね素線の表面から深い位置まで圧縮残留応力が生じる。 - 特許庁

When a part 15a of a backfilling part 15 contacts with the fracture zone 17, a pile structure 18 is arranged for transmitting compressive force so as to reach up to a bed rock 16 from a part 15a of the backfilling part 15.例文帳に追加

裏込め充填部１５の一部１５ａが、破砕帯１７に対して接している場合に、裏込め充填部１５の一部１５ａから岩盤部１６にまで至るように、圧縮力を伝達可能な杭構造体１８を設けた。 - 特許庁

The surface of the weld zone is improved into a state where deformation is elastically recovered from the partially yield state and tensile stress is mitigated, or a compressive residual stress state.例文帳に追加

溶接部表面は部分的降伏状態から弾性的に変形が戻り引張り応力が緩和された状態もしくは圧縮残留応力状態に改善される。 - 特許庁

The welding material consists of an iron based alloy containing Si in the range of 0.6 to 2.0 wt.%, and improves the strength of a welded joint by the introduction of compressive residual stress into the vicinity of the weld zone by transformation expansion.例文帳に追加

Ｓｉを０．６〜２．０重量％の範囲で含有する鉄基合金であって、変態膨張により溶接部近傍に圧縮残留応力を導入して溶接継手強度を向上させる溶接材料を提供する。 - 特許庁

To provide a thermoplastic elastomer composition capable of obtaining compressive permanent set at a high temperature well even with a low Mooney viscosity rubber, having good compatibility, excellent in compressive permanent set in a short and long term high temperature zone by using smaller amounts of an accelerator, etc., than those of conventional using amounts, and excellent in extrusion and injection molding properties.例文帳に追加

低ムーニー粘度のゴムでも高温の圧縮永久歪みを良好に得ることができ、相容性が良く、促進剤等を従来の使用量より少量用いることにより、短期および長期の高温領域における圧縮永久歪みに優れ、押出及び射出成形性に優れる熱可塑性エラストマー組成物の提供。 - 特許庁

The belt 4 is enabled for displacement in the radial direction of the drum 3 by way of the compressive stresses of molten polypropylene resin 2 during the pressure welding treatment with the belt 4 and drum 3 in the entire zone to be pressure-welded by the drum 3 and the belt 4.例文帳に追加

キャストドラム３と金属無端ベルト４とで圧接される全区間において、金属無端ベルト４とキャストドラム３とで圧接加工中に溶融ポリプロピレン樹脂２の圧縮応力により金属無端ベルト４はキャストドラム３の半径方向に変位可能としてある。 - 特許庁

To provide a method capable of adjusting an amount of additives such as bentonite, new sand, and fine powder before occurrence of defected castings by observing compressive strength and a permeable degree as a property of casting sand and by giving a warning before an effective clay content/ grain size distribution enter into a danger zone.例文帳に追加

鋳物砂特性である圧縮強度、通気度を監視し、有効粘土分／粒度分布が危険域に入る前に警告を出し鋳物不良の発生する前にベントナイト、新砂、微粉などの添加量を調整できる方法を提供する。 - 特許庁

Plastic working in excess weld metal toe part 7a on the upper face of the rail bottom in a thermit weld zone 2 of a rail 1 increases hardness, yield strength and tensile strength in the excess plastically worked weld metal toe part 7a as a result of work hardening and, imparts compressive residual stress, resulting in improved fatigue strength of the thermit weld zone.例文帳に追加

レール１のテルミット溶接部２のうち、レール底部上面の余盛止端部７ａに、塑性加工を施すことにより、この塑性加工を施された余盛止端部７ａが加工硬化によって、硬度、降伏強度、引張強さが増大し、さらに圧縮残留応力が付与されるので、テルミット溶接部の疲労強度が向上する。 - 特許庁