| 例文 (8件) |
melt-quenching alloyの部分一致の例文一覧と使い方
該当件数 : 8件
A dual phase type hydrogen permeable alloy membrane composed of a phase bearing hydrogen permeability and a phase bearing hydrogen embrittlement resistance is produced by a melt quenching method.例文帳に追加
水素透過性を担う相と耐水素脆性を担う相で構成された複相型水素透過合金膜を液体急冷法により作製する。 - 特許庁
To provide a molten metal injection nozzle capable of preventing generation of cast cavity defects in manufacturing amorphous alloy bulk material by means of a method of rapid cooling of melt into casting mold using a melt quenching apparatus.例文帳に追加
液体急冷装置を用いた鋳型液体急冷法により、アモルファス合金のバルク材を作製する際において、鋳巣欠陥の発生を防止することが可能な融解金属噴射ノズルを提供する。 - 特許庁
A method of manufacturing an iron-based alloy magnet comprises a quenching process (primary roll period) of forming the supercooled liquid of a material alloy by quenching the melt of an iron-based alloy magnet material alloy, and a temperature control process (secondary roll period) of temporarily heating the supercooled liquid before the temperature of the supercooled liquid drops to a glass transition point Tg or below.例文帳に追加
本発明による鉄基合金磁石の製造方法は、鉄基合金磁石用原料合金の溶湯を急冷することによって原料合金の過冷却液体を形成する急冷工程（１次ロール期間）と、この過冷却液体の温度がガラス転移点Ｔ_g以下に低下する前に過冷却液体を一時的に加熱する温度調節工程（２次ロール期間）とを包含している。 - 特許庁
To produce a high permeability metallic glass alloy for high-frequency extremely wide in the temp. intervals δTx in a supercooled liq. region, exhibiting soft magnetism at a room temp., producible more thickly than an amorphous alloy this strip obtainable by the conventional melt quenching method, moreover low in magnetostriction, high in specific resistance and high in permeability in a high-frequency region.例文帳に追加
過冷却液体領域の温度間隔ΔＴxが極めて広く、室温で軟磁性を示し、従来の液体急冷法で得られる非晶質合金薄帯より厚く製造でき、しかも磁歪が低く、比抵抗が高く、高周波領域での透磁率が高い高周波用高透磁率金属ガラス合金の提供。 - 特許庁
Reactive gas is made to exist in the atmosphere at quenching treatment from the melt of the noble metal-based alloy containing ≥50at% noble metal element and containing at least either one of an oxide film forming element or nitride forming element.例文帳に追加
貴金属元素を５０ａｔ％以上含有し、かつ酸化物皮膜形成元素又は窒化物形成元素の内の少なくともいずれか一方を含有する貴金属基合金の溶湯から急冷処理する際の雰囲気に反応性ガスを存在させる。 - 特許庁
The fine crystal particles in bccFe are deposited by heating the amorphous phase up to crystallization temperature or more and then cooling it, after quenching alloy melt with above mentioned composition into substantially amorphous single-phase structure.例文帳に追加
（Ｆｅ_1-a Ｑ _a）_b Ｂ_x Ｍ_y Ｚｎ_z 但しＱはＣｏ、Ｎｉのいずれかまたは両方、ＭはＴｉ、Ｚｒ、Ｈｆ、Ｖ、Ｎｂ、Ｔａ、Ｍｏ、Ｗの中から選ばれた１種又は２種以上の元素であり、a≦０.０５、８０原子％≦b、５原子％≦ｘ≦１２.５原子％、５原子％≦ｙ≦７.５原子％、０.０２５原子％≦ｚ≦０.２原子％である。 - 特許庁
In the nanocrystal soft magnetic alloy obtained by subjecting a rapidly cooled thin strip alloy produced by a melt quenching method to heat treatment, and consisting of a fine bcc phase of Fe having a grain size of ≤100 nm as the main phase, an element Q having the positive value of a mixed enthalpy ΔH with Fe is contained by ≥0.01 atomic % as an essential component.例文帳に追加
本発明は、液体急冷法により作製した急冷薄帯合金を熱処理することにより得られる粒径１００ｎｍ以下のＦｅの微細なｂｃｃ相を主相としたナノ結晶軟磁性合金において、Ｆｅとの混合エンタルピーΔＨが正の値を有する元素である元素Ｑを０.０１原子％以上必須成分として含むことを特徴とする。 - 特許庁
For example, an alloy melt composed of 6 mol% Nd, 91 mol% Fe, and 3 mol% B is filled in a nozzle 21 heated with a heating coil 24 and discharged out through the nozzle tip 22 at a proper flow rate onto the surface of the rotary metal roll which rotates at a high speed for forming amorphous thin pieces 25 through a quenching method.例文帳に追加
この例として、Ｎｄ６ｍｏｌ％、Ｆｅ９１ｍｏｌ％、Ｂ３ｍｏｌ％の組成からなる合金溶湯１を、ノズル２１に注入して加熱コイル２４で加熱しながら、ノズル口２２から高速回転している回転金属ロール２３上に適量づつ排出させて急冷法でアモルファス薄片２５を作成する。 - 特許庁