二次再結晶粒の英語

質量％で、Ｃ：0.005％以上 0.030％以下およびSi：2.0％以上 4.5％以下を含有し、フォルステライト膜を有しない二次再結晶後の方向性電磁鋼板を、50％以上の圧下率で圧延したのち、再結晶焼鈍を行い、再結晶後の結晶粒径を最終板厚の1/2以下とする。例文帳に追加

A grain oriented silicon steel sheet after secondary recrystallization which comprises, by mass, 0.005 to 0.030% C and 2.0 to 4.5% Si, and does not have a forsterite film is rolled at a draft of ≥50%, and is thereafter subjected to recrystallization annealing so as to control the crystal grain size after the recrystallization to ≤1/2 of the final sheet thickness. - 特許庁

従来よりも低い温度で二次再結晶を引き起すことが可能で、且つ二次再結晶後の組織が粒界の少ない巨大な結晶粒からなり耐クリープ特性に優れるようにすることが可能な工業的に優位性のあるモリブデン材を提供する。例文帳に追加

To provide an industrially advantageous molybdenum material which is capable of secondary recrystallization at a temperature lower than that of a conventional molybdenum material and which can be converted through the secondary recrystallization into a material that has a structure comprising very large grains with reduced grain boundaries and thus exhibits excellent creep resistance. - 特許庁

二次再結晶開始温度に達した時点で温度勾配が鋼帯コイルに付与されていれば、二次再結晶粒が圧延方向と交差する歪付与領域に沿って成長し、歪取り焼鈍でも消失しない磁区細分化効果が得られる。例文帳に追加

According to give the temperature gradient to a steel strip coil at the time of reaching to the starting temperature of a secondary recrystallization, the secondary recrystallized grains are grown along the strain-giving region crossed with the rolling direction, and thus the subdividing effect, that the magnetic domain does not dissipate even after performing the strain-removal annealing, is obtained. - 特許庁

一次熱処理で窒素富化層を形成し、二次熱処理で再焼入れする熱処理システムにおいて、二次熱処理での加熱温度を厳密に管理することにより、部品全体で結晶粒を均一に微細化する。例文帳に追加

To uniformly micronize crystal grains in the whole body of a part by strictly controlling the heating temperature in secondary heat treatment in a heat treatment system in which a nitrogen-enriched layer is formed in primary heat treatment and a re-quenching is applied in the secondary heat treatment. - 特許庁

これにより、冷延後の一次再結晶集合組織において、素材粒界近傍から発生する｛１１１｝＜１１２＞方位が増え、その結果、｛１１０｝＜００１＞方位二次再結晶の集積度が上がり、磁気特性の優れた一方向性電磁鋼板を製造できる。例文帳に追加

Thus, in the primary recrystallization texture after cold rolling, the {111}<112> direction generated from the vicinity of a material grain boundary increases, and as a result, the integration degree of the {110}<001> direction secondary recrystallization increases to allow the unidirectional magnetic steel sheet excellent in magnetic properties to be produced. - 特許庁

冷延後の鋼板に脱炭焼鈍を施し、その後仕上げ焼鈍を施すにあたり、仕上げ焼鈍の昇温過程において鋼板の粒径を測定し、測定した前記粒径の変化から二次再結晶の開始を検知し、二次再結晶の開始を検知した後、昇温速度を２０℃／ｈｒ以下に変更する。例文帳に追加

When the cold-rolled steel sheet is subjected to decarburization annealing then to the finish-annealing, the grain diameter in the steel sheet is measured at the temperature raising process of the finish-annealing, and the starting timing of the secondary recrystallization is detected from a change in the measured grain diameter, and after detecting the start of the secondary recrystallization, the temperature raising speed is changed to ≤20°C/hr. - 特許庁

高温の熱履歴が加わる環境下でも二次再結晶化といわれる結晶粒の粗大化を防止し、高輝度化や低消費電力化のための放電特性、および製品寿命を向上させた有底円筒状の冷陰極蛍光ランプ用電極を提供する。例文帳に追加

To provide a bottomed cylindrical electrode for a cold cathode fluorescent lamp, wherein coarsening of crystal grains called secondary recrystallization is prevented even under an environment in which high temperature heat history is applied, to enhance discharge characteristics for realizing high luminance and low power consumption and a product life. - 特許庁