「X-ray fiber diffraction」に関連した英語例文の一覧と使い方 - Weblio英語例文検索

The tire cord is composed of a fiber containing a polyethylene naphthalate fiber having a crystal volume of 550-1,200 nm^3 determined by wide angle X-ray diffraction of the polyethylene naphthalate fiber and a crystallinity of 30-60%.例文帳に追加

ポリエチレンナフタレート繊維を含む繊維から構成されたタイヤコードであって、該ポリエチレンナフタレート繊維のＸ線広角回折より得られる結晶体積が５５０〜１２００ｎｍ^３であり、かつ結晶化度が３０〜６０％であることを特徴とするタイヤコード。 - 特許庁

The graphitized carbon fiber to be incorporated into a thermally conductive polymeric composition has a spacing (d002) of graphite layers, measured by the X-ray diffraction method, of <0.3370 nm and, at the same time, a peak intensity ratio (P101/P100) of the (101) diffraction peak (101) to the (100) diffraction peak of ≥1.15.例文帳に追加

熱伝導性高分子組成物に含有される黒鉛化炭素繊維は、Ｘ線回折法による黒鉛層間の面間隔（ｄ００２）が０．３３７０ｎｍ未満で、かつ、（１０１）回折ピークと（１００）回折ピークのピーク強度比（Ｐ１０１／Ｐ１００）が１．１５以上である。 - 特許庁

This industrial fibrous structural material containing a polyethylene naphthalate fiber has 100-200 nm^3 crystal volume and 30-60% degree of crystallization, as obtained by the X-ray wide angle diffraction of the polyethylene naphthalate fiber.例文帳に追加

ポリエチレンナフタレート繊維を含む産業繊維構造体であって、該ポリエチレンナフタレート繊維のＸ線広角回折より得られる結晶体積が１００〜２００ｎｍ^３であり、かつ結晶化度が３０〜６０％である産業繊維構造体。 - 特許庁

This fibrous sheet containing a polyethylene naphthalate fiber is characterized by having 550 to 1,200 nm^3 crystal volume and 30-60% degree of crystallization, as obtained by the X-ray wide angle diffraction of the polyethylene naphthalate fiber.例文帳に追加

ポリエチレンナフタレート繊維を含む繊維シートであって、該ポリエチレンナフタレート繊維のＸ線広角回折より得られる結晶体積が５５０〜１２００ｎｍ^３であり、かつ結晶化度が３０〜６０％であることを特徴とする繊維シート。 - 特許庁

This fiber-reinforced resin composition comprises a thermoplastic resin and a polyethylene naphthalate fiber and has a crystal volume obtained by an X-ray wide-angle diffraction of a fiber of 550 to 1,200 nm^3 and a crystallinity of 30 to 60%.例文帳に追加

熱可塑性樹脂とポリエチレンナフタレート繊維からなる繊維補強樹脂組成物であって、繊維のＸ線広角回折より得られる結晶体積が５５０〜１２００ｎｍ^３であり、結晶化度が３０〜６０％であることを特徴とする繊維補強樹脂組成物。 - 特許庁

The invention provides a fine carbon fiber having a layer spacing d_002 of 0.337 nm measured by X-ray diffraction method, a fiber diameter of ≤1,000 nm and a compact specific resistance of ≤0.02 Ω.cm and a fine carbon fiber having a metal content of ≤500 mass ppm.例文帳に追加

Ｘ線回折法で求めた層面間隔ｄ_002が０．３３７ｎｍを超え、繊維径１０００ｎｍ以下、圧密比抵抗が０．０２Ω・ｃｍ以下の微細な炭素繊維及び金属含有量が５００質量ｐｐｍ以下である微細な炭素繊維である。 - 特許庁

In the thermoplastic resin composition comprising at least a carbon fiber and a thermoplastic resin, the size of the crystals of the carbon fiber measured by the broad-angle X-ray diffraction method is within a range of 1.4-4.5 nm and the diameter of the cross section of the fiber is within a range of 3-15 μm.例文帳に追加

少なくとも炭素繊維と熱可塑性樹脂とを含む熱可塑性樹脂組成物において、広角Ｘ線回折法で測定した炭素繊維の結晶サイズが1.4〜4.5nmの範囲内であり、かつ繊維断面の直径が3〜15μmの範囲内であることを特徴とする熱可塑性樹脂組成物。 - 特許庁

This method for carbon fiber of vapor phase method comprises activating carbon fiber of vapor phase method having ≥0.33 nm lattice spacing (d_002) of crystal measured by X-ray diffraction method in the presence of an alkali metal compound at ≤1,000°C temperature.例文帳に追加

Ｘ線回折法で測定した結晶格子面間隔（ｄ_002）が０．３３ｎｍ以上の気相法炭素繊維をアルカリ金属化合物の存在下、１０００℃以下の温度で賦活することを特徴とする気相法炭素繊維の製造方法。 - 特許庁

The high-modulus carbon fiber has ≥1,000Å spread La in the a-axis direction of a graphite crystal obtained from a powder X-ray diffraction spectrum, >104 ton/mm^2 tensile modulus and ≥15 μm fiber diameter.例文帳に追加

粉末Ｘ線スペクトルから求めた、黒鉛結晶のａ軸方向の広がりＬａが１０００Å以上であって、引張弾性率が１０４ｔｏｎ／mm^２より大きく繊維径が、１５μｍ以上であることを特徴とする高弾性率炭素繊維。 - 特許庁

A polyester filament is a fiber made of polyester having specific intrinsic viscosity containing ethylene terephthalate as a main repeating unit, and formed of a polyester fiber in which a terminal carboxy group amount in the fiber and a long period by small-angle X-ray diffraction each fall within a specific range, and a surface treatment agent having an epoxy group adheres to the surface of the fiber.例文帳に追加

ポリエステルフィラメントが、エチレンテレフタレートを主たる繰り返し単位とする特定の固有粘度のポリエステルからなる繊維であって、繊維中の末端カルボキシ基量およびＸ線小角回折による長周期が特定範囲で、表面にエポキシ基を有する表面処理剤が付着したポリエステル繊維よりなる。 - 特許庁

Hydrogen is brought into contact with the carbon fiber interlaminar reaction product, which contains a carbon structure wherein a diffraction peak position (2θ) due to wide angle X-ray diffraction analysis appears at 9-14° and obtained by electrochemically treating carbon fibers in an acidic solution, is brought into contact with hydrogen to be occluded by the carbon fiber interlaminar reaction product.例文帳に追加

炭素繊維を酸性溶液中にて電気化学処理してなる、広角Ｘ線回折分析による回折ピーク位置（２θ）が９°〜１４°に現れる炭素構造を含有する炭素繊維層間反応生成物に、水素を接触させて炭素繊維層間反応生成物に水素を吸蔵させる。 - 特許庁

A fiber has a mean diameter of about 1 to about 4 μm, and a degree of crystallization of at least about 5 to about 50% that can be detected by an X-ray diffraction, and has a size of crystal of about 50 to about 500 A.例文帳に追加

ファイバーは約１〜約１４μｍの平均直径を有し、Ｘ線回折により検出される少なくとも約５〜約５０％の結晶化度を有し、かつ約５０〜約５００Ａの結晶の大きさを有する。 - 特許庁

The third carbonizing step is separated to the primary treatment and the secondary treatment, and the specific resistance value, the specific gravity, the N/C, the single fiber elongation and the crystal size by a wide angle x-ray measurement (at 26° diffraction angle) of the fiber, and the temperature and the draw ratio are regulated in each treatment.例文帳に追加

第三炭素化工程では、一次処理と二次処理とに分け、それぞれの処理における繊維の比抵抗値、比重、Ｎ／Ｃ、単繊維伸度、並びに、広角Ｘ線測定(回折角２６°)での結晶子サイズと、温度と、延伸倍率とを制御する。 - 特許庁

In the graphitized fiber, the spacing d(002) between graphitized layers according to an X-ray diffraction method is within the range of ≥0.3354 to ≤0.3366 nm; and the crystallite size Lc(002) of graphite crystals is ≥60 nm.例文帳に追加

この黒鉛化繊維によれば、Ｘ線回折法による黒鉛化層間の面間隔ｄ（００２）が０．３３５４ｎｍ以上０．３３６６ｎｍ以下の範囲であり、かつ黒鉛結晶の結晶子サイズＬｃ（００２）が６０ｎｍ以上である。 - 特許庁

This heat-conductive polymer composition comprises a polymer material and a graphitized carbon fiber as a heat-conductive filler, the graphitized carbon fiber contains boron and interplanar spacing (d002) between graphite layers exhibiting a degree of graphitization by an X-ray diffraction method of a graphitized carbon fiber is <0.3360 nm.例文帳に追加

熱伝導性高分子組成物は、高分子材料と、熱伝導性充填剤として黒鉛化炭素繊維とを含有し、その黒鉛化炭素繊維はホウ素を含有し、かつ黒鉛化炭素繊維のＸ線回折法による黒鉛化度を表す黒鉛層間の面間隔（ｄ００２）は０．３３６０ｎｍ未満である。 - 特許庁

The composite yarn for forming composite materials is constituted with polybenzazole fiber that has the half value width of ≤0.3°/GPa in the X-ray meridian diffraction and the proton T1H relaxation time of ≥5.0 sec. and the matrix fiber made of a thermoplastic polymer melting at 200-600°C.例文帳に追加

Ｘ線子午線回折半値幅因子が０．３゜／ＧＰａ以下でプロトンのＴ1H緩和時間が５．０秒以上であるポリベンザゾール繊維と融点が２００〜６００℃の熱可塑性重合体からなるマトリックス繊維とで構成されてなる複合材成形用複合糸条。 - 特許庁

A polyester textured yarn, having fluff consisting of polyethylene naphthalate fiber on the surface, is characterized in that a crystal volume obtained by the X-ray wide angle diffraction of the polyethylene naphthalate fiber is ranging from 550 to 1,200 nm^3, and in that crystallinity is ranging from 30 to 60%.例文帳に追加

ポリエチレンナフタレート繊維からなる毛羽を表面に有するポリエステル加工糸であって、該ポリエチレンナフタレート繊維のＸ線広角回折より得られる結晶体積が５５０〜１２００ｎｍ^３であり、かつ結晶化度が３０〜６０％であることを特徴とするポリエステル加工糸。 - 特許庁

The PVA-based fiber is composed of a PVA-based polymer and a phyllosilicate finely dispersed in the polymer and has ≥20Å average interlayer distance of the phyllosilicate measured by a wide angle x-ray diffraction and has ≥40% crystallinity and ≥60% degree of orientation.例文帳に追加

ＰＶＡ系ポリマーと、ポリマー中に微細に分散した層状ケイ酸塩からなり、広角Ｘ線回折で測定した層状ケイ酸塩の平均層間距離が２０Å以上であり、かつ結晶化度が４０％以上、配向度が６０％以上であることを特徴とするＰＶＡ系繊維。 - 特許庁

This thermoplastic resin composition produced by using at least carbon fiber and a thermoplastic resin, manifests 1.6-3 nm of crystal size measured in a wide angle x-ray diffraction method, and 0.03-0.08 of oxygen to carbon (O/C) ratio measured by ESCA and 3-15 μm of mean single fiber diameter.例文帳に追加

少なくとも炭素繊維と熱可塑性樹脂とを用いてなる熱可塑性樹脂組成物において、広角Ｘ線回折法にて測定される結晶サイズが１．６〜３ｎｍの範囲内であり、かつＥＳＣＡにて測定される（Ｏ／Ｃ）が０．０３〜０．０８の範囲内であり、さらに平均単繊維直径が３〜1５μｍの範囲内であることを特徴とする熱可塑性樹脂組成物。 - 特許庁

The braid and the electrically insulated protective sleeve, having the excellent electrically insulating properties, heat resistance and melting resistance, can be obtained by using a polyphenylene sulfide oxide fiber having ≥10% crystallinity in the measurement by wide angle X-ray diffraction, ≤15 J/g amount of heat of fusion in the measurement by differential scanning calorimeter (DSC), and 10-50 dtex fineness.例文帳に追加

広角Ｘ線回折の測定における結晶化度が１０％以上であり、かつ示差走査熱量計（ＤＳＣ）の測定における融解熱量が１５Ｊ／ｇ以下であり、繊度が１０〜５０dtexであることを特徴とするポリフェニレンスルフィド酸化物繊維を用いることにより、電気絶縁性に優れ、耐熱、耐溶融性に優れる組紐、電気絶縁保護スリーブを得ることができる。 - 特許庁