The no-separator type thermosensitive recording label is formed by laminating a thermosensitive color developing layer and a release layer on one surface of a base material and providing another one surface of the base material with an adhesive layer, in which pigments 20b treated with a silane coupling agent are incorporated into the release layer 20 in order to prevent sticking and the continuous body of such no-separator type thermosensitive recording labels.例文帳に追加

基材の片面に、感熱発色層、剥離層が積層され、基材の他の片面に接着剤層が設けられてなるノーセパレータ型感熱記録ラベルにおいて、スティックを防止するために、剥離層２０にシランカップリング剤処理顔料２０ｂが混入された、ノーセパレータ型感熱記録ラベルおよびノーセパレータ型感熱記録ラベル連続体である。 - 特許庁

To provide a laminated roller reconciling a good permanent compressive strain characteristic and hardness, abrasion resistance, electric conductivity, and pollution resistance and to provide its manufacturing method by arranging an elastic body layer for a shaft, then forming a continuous metal layer on the outer surface of the elastic body layer by plating, and laminating the elastic body layer and the metal layer.例文帳に追加

シャフトに対して弾性体層を配した後、該弾性体層の外表面にメッキにより連続した金属層を形成して、弾性体層および金属層を積層させることで、良好な永久圧縮歪み特性と、硬度、耐摩耗性、電気伝導性および耐汚染性とを両立させた積層ローラおよびその製造方法を提供する。 - 特許庁

In the method for manufacturing the lithographic printing plate material prepared by laminating and coating a hydrophilic layer and an image forming layer on a continuous transparent plastic film, the method for manufacturing the lithographic printing plate material controls the product processing conditions based on optical density distribution information obtained by measuring optical densities to a transmitted light and a reflected light of a coated film during coating process.例文帳に追加

連続した透明のプラスチックフィルム上に親水性層及び画像形成層を積層塗布してなる平版印刷版材料の製造方法において、塗布工程中に塗布済フィルムの透過光及び反射光に対する光学濃度を測定して得た光学濃度分布情報に基づき製品加工条件を制御することを特徴とする平版印刷版材料の製造方法。 - 特許庁

A glass rod prepared by concentrically laminating a plurality of glass materials having different refractive indices is set with the axis of the concentric circles substantially horizontal and then heated while being rotated around the axis so that the compositions included in the glass materials in the adjacent glass material layers are made to diffuse into each other to generate the continuous distribution of the refractive index in the radial direction.例文帳に追加

屈折率の互いに異なる複数のガラス材料を同心円状に積層したガラスロッドを、その同心円の軸が実質上水平になるように設置し、該軸を中心として回転させながら加熱処理して、隣接するガラス材料層間でガラス材料中に含まれる前記成分を相互拡散させ、半径方向に連続的な屈折率分布を形成させる。 - 特許庁

The prepreg is produced by applying the epoxy resin composition to a release paper to form a film, laminating the film with the reinforcing fibers consisting of the continuous fibers so that the fiber METSUKE is 10-200 g/m^2 and the fiber content is 70-87 wt%, and heating and/or pressing the resultant laminate to impregnate the resin composition into the reinforcing fibers.例文帳に追加

このプリプレグは、エポキシ樹脂組成物を離型紙の上にコーティングして樹脂フィルムとし、該樹脂フィルムと、上記連続繊維からなる強化繊維を積層し、繊維目付が１０〜２００ｇ／ｍ^２の範囲内であって、かつ繊維含有率が７０〜８７重量％の範囲内とし、続いて加熱および／または加圧することで前記強化繊維に前記樹脂組成物を含浸させたプリプレグ。 - 特許庁

In the decorative sheet constituted by laminating at least a pattern ink layer, a transparent thermoplastic resin layer and a surface protective layer on a thermoplastic resin sheet base material in this order, the thermoplastic resin sheet base material is constituted of at least the polylactic acid type resin and a polyolefinic resin and has a phase structure wherein the polylactic acid type resin becomes a disperse phase and the polyolefinic resin becomes a continuous phase.例文帳に追加

熱可塑性樹脂シート基材上に、少なくとも絵柄インキ層と透明熱可塑性樹脂層と表面保護層がこの順に積層されてなる化粧シートにおいて、該熱可塑性樹脂シート基材が少なくともポリ乳酸系樹脂とポリオレフィン系樹脂から構成され、ポリ乳酸系樹脂が分散相、ポリオレフィン系樹脂が連続相となる相構造であることを特徴とする化粧シートを提供する。 - 特許庁

In the polypropylene resin laminated foamed sheet constituted by laminating a polypropylene resin extruded foamed sheet and a polypropylene resin film, on which a pattern repeated at a definite cycle in the extrusion direction is printed, through a polypropylene resin layer by extrusion lamination, the fluctuation in width of the interval between the patterns in the extrusion direction is set to 5% or below to continuously mold the molded product by the continuous molding machine.例文帳に追加

ポリプロピレン系樹脂押出発泡シートと、押出方向に一定周期で繰り返される模様を印刷したポリプロピレン系樹脂フィルムを、押出ラミネートによりポリプロピレン系樹脂層を介して積層してなるポリプロピレン系樹脂積層発泡シートであって、押出方向における前記模様の間隔の変動幅を５％以下とすることにより、上記成形体を連続成形機にて連続的に成形することができる。 - 特許庁

To provide a method for manufacturing a glass ceramic substrate for laminating a restraining sheet, made of an inorganic composition which is not sintered at the baking temperature of the ceramic substrate on at least one of surfaces of a green sheet laminate for baking, for obtaining the glass ceramic substrate suppressing dimensional variations within the substrate, even when baking in a continuous furnace and having high dimensional accuracy.例文帳に追加

セラミック基板の焼成温度では焼結しない無機組成物よりなる拘束シートをグリーンシート積層体の少なくとも一方の表面に積層し焼成処理を行う多層セラミック基板の製造方法において、連続炉で焼成を行う際でも基板内の寸法ばらつきを抑制し、高い寸法精度を有するセラミック基板を得るためのセラミック基板の製造方法を提供する。 - 特許庁