The catalyst for water-gas-shift reaction is characterized in that Pt is present in a solid solution of oxides of zirconium and cerium with iron and/or yttrium, and at the same time, particles of one or more kinds of metal elements A selected from Au, Ag, Cu, Fe, Pd, Ni, Ir, Rh, Co, Os, and Ru are present by being partly buried in the oxide solid solution.例文帳に追加

ジルコニウム及びセリウムと、鉄及び／又はイットリウムとの酸化物の固溶体に、Ｐｔを存在させるとともに、Ａｕ，Ａｇ，Ｃｕ，Ｆｅ，Ｐｄ，Ｎｉ，Ｉｒ，Ｒｈ，Ｃｏ，Ｏｓ，Ｒｕの中から選ばれる１種または２種以上の金属元素Ａの粒子が該酸化物固溶体に一部埋まって存在する水性ガスシフト反応用触媒によって達成される。 - 特許庁

The magnesium alloy is essentially composed of magnesium, and in the magnesium alloy, the crystal structure thereof has high-angle grain boundaries, and the insides of the crystal grains surrounded by the high-angle grain boundaries is composed of sub-crystal grains, and one kind selected from calcium, tin and yttrium capable of being made into solid solution in magnesium is contained as an additional element.例文帳に追加

マグネシウムを主成分とし、その結晶構造が大傾角粒界を有し、この大傾角粒界に囲まれた結晶粒の内部が亜結晶粒にて構成されているマグネシウム合金であって、添加元素としてマグネシウムに固溶可能なカルシウム、スズ、イットリウムの一種を含有させる。 - 特許庁

This method for producing an asymmetrical dialkyl polycarbonate by an ester-interchange reaction between different kinds of symmetrical dialkyl carbonates in the presence of a solid catalyst containing an oxide of an element selected from group III elements (the short period periodic table) comprising lanthanide, scandium and yttrium, comprises bringing the solid catalyst separated from a liquid produced by the reaction into contact with an alcohol, and reusing resultant solid catalyst in the ester-interchange reaction.例文帳に追加

本発明によれば、ランタニド及びアクチニド並びにスカンジウム及びイットリウムからなるIII 族元素（短周期型周期律表）から選ばれる元素の酸化物を活性成分として含む固体触媒の存在下に、異種の対称ジアルキルカーボネート間のエステル交換反応により非対称ジアルキルカーボネートを製造するに際し、反応生成液から分離した固体触媒をアルコールと接触した後、エステル交換反応に再使用することを非対称ジアルキルカーボネートの製造方法。 - 特許庁

A mixed aqueous solution of ions of a rare earth metal such as europium and yttrium ions is adjusted to a pH of ≥8 using an alkali aqueous solution, and hydrothermally reacted at 360 to 500°C in a short time to thereby manufacture a rare earth metal ion-dissolved yttria solid solution microparticle having a primary particle diameter of ≤100 nm and a high crystallinity degree.例文帳に追加

ユーロピウムなどの希土類金属イオンとイットリウムイオンとの混合水溶液をアルカリ水溶液でｐＨ８以上に調製し、３６０−５００℃で短時間水熱反応させて、一次粒子径が１００ｎｍ以下であり、その粒子は結晶化度が高い希土類金属イオン固溶イットリア微粒子を製造する。 - 特許庁

Powder of Ce_0.8Y_0.2O_2 (YDC: solid solution of ceria doped with yttrium oxide) with an average particle size of 0.2 μm is dispersed in a prescribed medium and slurry is prepared, and this slurry is applied on the face of an electrolyte layer 101 by a screen printing method and dried, thereby, ceria system material coating film is formed.例文帳に追加

平均粒径０．２μｍのＣｅ_0.8Ｙ_0.2Ｏ_2（ＹＤＣ：セリアに酸化イットリウムがドープされた固溶体）の粉体を所定の媒体に分散させてスラリーを作製し、このスラリーをスクリーン印刷法により電解質層１０１の他方の面に塗布して乾燥し、セリア系材料塗布膜が形成された状態とする。 - 特許庁

Solid solution particles, containing nickel hydroxide as a main component, have surface areas whose 1-30% is covered with at least one type of oxide particles selected from among yttrium, scandium and lanthanide, and whose outer peripheries are covered with cobalt oxide having a cobalt average valence number which is larger than 3.0 valence.例文帳に追加

水酸化ニッケルを主成分とする固溶体粒子において、前記固溶体粒子の表面積の１〜３０％をイットリウム、スカンジウムまたはランタノイドから選ばれる少なくとも一種の酸化物粒子にて被覆し、かつ、その外周をコバルト平均価数が３．０価より大であるコバルト酸化物にて被覆する。 - 特許庁

In this case, the films 3, 4 are capable of being at least one of strontium oxide, magnesium oxide, cerium oxide, zirconium oxide, yttrium stabilized zirconium oxide, and a strontium titanate, the inorganic amorphous layer or the organic solid layer 2 are capable of being silicon oxide, and a piezoelectric or ferroelectric material, for example, is used as the thin film 5.例文帳に追加

ここで前記酸化物薄膜層３、４は酸化ストロンチウム、酸化マグネシウム、酸化セリウム、酸化ジルコニウム、イットリウム安定化酸化ジルコニウム、チタン酸ストロンチウムのうち少なくとも一つであり得、また上記無機アモルファス層又は有機固体層２は酸化シリコンであり得、また前記ペロブスカイト型酸化物薄膜５には、例えば圧電材料又は強誘電体を用いる。 - 特許庁

A gadolinium-yttrium-oxyborate single crystal being a rare earth-calcium-oxyborate-based crystal can be grown by pulverizing boron oxide under an atmosphere of reduced humidity for 24 h using a ball mill, then adding a rare earth oxide and calcium carbonate, mixing the obtained mixture for 84 h for subjecting it to solid state reaction and heating/melting the reaction product by a high frequency induction heating-type Czochralski method.例文帳に追加

湿度を低減した雰囲気でボールミルを用いて酸化硼素を２４時間粉砕後、希土類酸化物及び炭酸カルシウムを加え、８４時間混合して固相反応させた材料を高周波誘導加熱型チョクラルスキー法により加熱溶融することで、希土類・カルシウム・オキシボレート系結晶であるガドリニウム・イットリウム・オキシボレート単結晶を育成することができる。 - 特許庁