CHATTER MARKとは 意味・読み方・使い方

To provide a hot rolled steel sheet for working in which the generation to chatter mark defects is eliminated by using low-cost B-added low carbon steel and sufficiently reducing the content of solid solution C and the content of solid solution N, and further, sufficient ductility is secured, and to provide its production method.例文帳に追加

本発明は、低コストのＢ添加低炭素鋼を用い、固溶Ｃ量と固溶Ｎ量を十分に低減して腰折れの発生をなくした上で十分な延性を確保した加工用熱延鋼板およびその製造方法を提供する。 - 特許庁

To provide a hot rolled steel sheet for working in which the generation of chatter mark defects is eliminated by using low-cost B-added low carbon steel and sufficiently reducing the content of solid solution C and the content of solid solution N, and further, sufficient ductility is secured and to provide its producing method.例文帳に追加

本発明は、低コストのＢ添加低炭素鋼を用い、固溶Ｃ量と固溶Ｎ量を十分に低減して畳じわの発生をなくした上で十分な延性を確保した加工用熱延鋼板およびその製造方法を提供する。 - 特許庁

To provide a method for producing a hot dip plated metal band where, in the case support rolls in a bath are made into a non-driving state, chatter mark-shaped adhesion amount nonuniformity and the generation of abrasions caused by the support rolls can be prevented, and to provide a hot dip plated metal band production device.例文帳に追加

浴中のサポートロールを非駆動にした場合に、該サポートロールに起因するチャターマーク状の付着量むらや擦り疵の発生を防止できる溶融めっき金属帯の製造方法および溶融めっき金属帯製造装置を提供する。 - 特許庁

To compose the whole body of the device compact as well as to prevent the generation of a chatter mark by constraining a roll chock securely, and to carry out the replacing a brush roll, in a device to brush or polish the surface of the metal slip during passing in a line by the rotating brush roll.例文帳に追加

通板中の金属スリップの表面を、回転するブラシロールによってブラッシングや研磨する装置において、ロールチョックの拘束をより確実に行うことによりチャタマークの発生を防止すると共に、装置全体をコンパクトに構成し、かつブラシロールの組替を容易に行う。 - 特許庁

Moreover, in the method for producing the high workability hot rolled steel sheet free from the generation of chatter mark defects, a slab having the above components is reheated, is thereafter finished with rolling at the Ar3 transformation point of above, is cooled at a cooling rate of ≥30°C/sec and is coiled at ≥580°C.例文帳に追加

また、前記成分の鋼片を再加熱した後、Ａｒ_3 変態点以上で圧延を完了し、３０℃／秒以上の冷却速度で冷却して５８０℃以上で巻き取ることを特徴とする畳じわの発生しない高加工性熱延鋼板の製造方法。 - 特許庁

To inexpensively and stably manufacture a lithographic printing plate substrate for forming uniform pits and well keeping the quality level and the printing performance level of a chatter mark in a process of electrochemical surface roughening of an aluminum plate as one of the lithographic printing plate manufacturing processes.例文帳に追加

平版印刷版の製造工程の一つであるアルミニウム板の表面を電気化学的に粗面化処理する工程において、均一なピットを生成できるとともに、チャターマークの品質レベル及び印刷性能レベルを良好に維持した平版印刷版用支持体を安価かつ安定的に製造することができるようにする。 - 特許庁