The phosphor is constructed of ZnS, which is coated with the CuS layer on the surface and contains needle-shaped Cus inside, for example, when a firing process is carried out following a kneading process after CuS is added to the ZnS particles containing CuS.例文帳に追加

該蛍光体は、例えばＣｕＳを含有するＺｎＳ粒子にＣｕＳを添加して混練した後、焼成することにより、表面がＣｕＳ層でコーティングされ、針状のＣｕＳを内部に含有したＺｎＳで構成される。 - 特許庁

To provide an extrusion molding machine constituted so as to continuously form an extrusion molded product having an embossed pattern on its decorative surface without causing strain by the extrusion molding of a raw material comprising an inorganic kneading material, for example, a raw material based on clay.例文帳に追加

本発明は、無機質混練材料よりなる原料、例えば粘土を主成分とする原料を押出成形し、化粧面に凹凸模様を形成した押出成形体を歪み無く連続的に形成する押出成形装置に関するものである。 - 特許庁

A manufacturing method of a flame retardant resin comprises blending 5-40 mass% of urea in a flammable resin such as a polyolefinic resin followed by heat-kneading this mixture at a softening temperature or higher of the flammable resin and at lower than degradation temperature of urea to convert the urea into a polymer, for example a biuret.例文帳に追加

ポリオレフィン系樹脂の如き可燃性樹脂中に、５〜４０質量％の尿素を配合し、これを、上記可燃性樹脂の軟化温度以上で且つ尿素の分解温度未満の温度で加熱混練し、尿素をその多量体、例えばビウレットに変換する。 - 特許庁

Thereafter, the fine aggregate 12b, the self-hardening powder aggregate 13 and water 14 are kneaded by, for example, a mixer, to thereby form a kneaded material 17, and the kneaded material 17 is inputted into a container 16 into which the coarse aggregate 12a is inputted beforehand, (a kneading process and an input process).例文帳に追加

次いで、例えばミキサーで細骨材１２ｂと自硬性を有する粉材１３’と水１４とを混練して混練材１７を形成し、あらかじめ粗骨材１２ａを入れた容器１６に、上記混練材１７を入れる（混練工程および投入工程）。 - 特許庁

A bamboo powder-thermoplastic resin composite material (bamboo powder: 80 pts.) is obtained by adding 20 pts. of polypropylene and 2 pts. of a maleic acid-modified polypropylene as a compatibilizer to 80 pts. of Phyllostachys pubescens bamboo powder passed through a 100 mesh stainless steel net, kneading the mixture with a super mixer, and semi-solidifying and molding the kneaded mixture, for example, with a conical type extruder.例文帳に追加

１００メッシュのステンレス網を通過したモウソウチクの竹粉８０部に対して、ポリプロピレンを２０部、それに相溶化剤としてマレイン酸変性のポリプロピレンを２部加え、スーパーミキサーにて混練した後、例えば、コニカルタイプの押出成形機を用いて、半固化成形により、竹粉・熱可塑性樹脂複合体（竹粉８０部）を得た。 - 特許庁

The dry coating drug can be mass-produced more efficiently than usual by a method for kneading a raw material containing a seed particle and a dry binder (for example, lauric acid and myristic acid) in a biaxial kneader to manufacture a dry binder particle in which the surface of the seed particle is coated dryly with the dry binder.例文帳に追加

核粒子及び乾式バインダー（ラウリン酸、ミリスチン酸など）を含有する原料を二軸混練機にて混練することによって、核粒子表面に乾式バインダーが乾式コーティングされた乾式バインダー粒子を製造する方法は、乾式コーティング製剤を従来よりも効率的に大量に製造できる。 - 特許庁

To provide a salt-resistant water-absorbent that has excellent water absorption property to high-concentration salt solution, for example, sea water, calcium chloride deliquescent solution or the like and has excellent mechanical stability and heat stability and causes no coagulation in the production, mixing, dispersing or kneading rubber or plastic into a variety of binders and provide the production method.例文帳に追加

海水や塩化カルシウム潮解水溶液等の高濃度の含塩溶液に対しても、優れた吸液性を有し、かつ機械的安定性や熱安定性に優れ、製造時あるいはゴムやプラスチック等の各種バインダーへの混練分散時等に凝集することのない耐塩性吸水剤及びその製造方法を提供することにある。 - 特許庁