austenite regionとは 意味・読み方・使い方

The above prehardened steel is obtained by performing quenching at a cooling rate of 5 to 0.06°C/s from an austenite region to 600°C and successively at a cooling rate of 5 to 0.02°C/s from 600°C to 200°C, and performing tempering.例文帳に追加

本発明鋼は、オーステナイト領域から６００℃までを５〜０．０６℃／ｓ、続く６００℃から２００℃までを５〜０．０２℃／ｓの冷却速度で焼入れし、焼戻すことで得られる。 - 特許庁

For obtaining the steel structure in a transferring section, treatment where the stock is heated to a two phase region of austenite and spheroidized carbides, is thereafter rapidly cooled, and is quenched is performed for two or more times.例文帳に追加

このような鋼組織を得るため、素材をオーステナイトと球状化炭化物の２相域に加熱後、急冷して焼き入れる処理を２回以上行う。 - 特許庁

The method for manufacturing the above iron-based alloy comprises the first heat treatment process for obtaining a mixed structure of martensite, matrix of retained austenite, and unmelted carbides, by solution treatment of rapidly cooling from the higher temperature than austenitizing temperature, and the second heat treatment process for precipitating the low carbon austenite by cooling after precipitating MC type carbides in a temperature region of eutectoid transformation.例文帳に追加

オーステナイト化温度以上の温度から急冷して固溶化処理を施し、これによってマルテンサイトと残留オーステナイトの基地組織と未溶解炭化物の混合組織を得る第１の熱処理工程と、共析変態温度区間でＭＣ型炭化物を析出させた後に冷却し、これによって低炭素オーステナイトを析出させる第２の熱処理工程とにより、上記鉄基合金を得る。 - 特許庁

The method comprises heating a steel slab, hot-rolling the heated slab, subjecting the hot-rolled slab to accelerated cooling from the austenitic temperature region to a middle temperature in bainite transformation, immediately re-heating the cooled slab after the accelerated cooling to concentrate C in the untransformed austenite to realize a metal structure containing a martensite-austenite constituent after the cooling subsequent to the re-heating.例文帳に追加

鋼スラブを加熱、熱間圧延後、オーステナイト温度域からベイナイト変態途中温度まで加速冷却を行い、加速冷却後直ちに再加熱を行い、未変態オーステナイト中にＣを濃化せしめることによって、再加熱後の冷却後に島状マルテンサイトを含んだ金属組織とする製造方法を用いる。 - 特許庁

The method for manufacturing the iron alloy comprises the first heat treatment step of conducting solution treatment of rapidly cooling from a higher temperature than an austenitizing temperature, to obtain a mixed structure consisting of the matrix of martensite and retained austenite, and undissolved carbides, and the second heat treatment step of precipitating M_2C carbides at a eutectoid transformation temperature region and cooling it, thereby precipitating a low carbon austenite.例文帳に追加

オーステナイト化温度以上の温度から急冷して固溶化処理を施し、これによってマルテンサイトと残留オーステナイトの基地組織と未溶解炭化物の混合組織を得る第１の熱処理工程と、共析変態温度区間でＭ_２Ｃ型炭化物を析出させた後に冷却し、これによって低炭素オーステナイトを析出させる第２の熱処理工程とにより、上記鉄基合金を得る。 - 特許庁

In the high strength welded steel pipe having excellent weld zone toughness, the tensile strength of a steel sheet and a weld metal is ≥800 MPa, and the area ratio of a mixture of martensite and austenite present on the grain boundaries and in the grains of old austenite in a coarse-grained region of a weld heat affected zone is ≤10%.例文帳に追加

鋼板および溶接金属の引張強さが８００ＭＰａ以上で、かつ溶接熱影響部粗粒域の旧オーステナイト粒界および粒内に存在するマルテンサイトとオーステナイトの混成物が面積率で１０％以下であることを特徴とする溶接部靱性に優れた高強度溶接鋼管。 - 特許庁

In the step of induction-hardening the steel member, a region including a part to be the rolling surface of the rolling member is further quench-hardened to control an amount of retained austenite in a region between the surface to be the rolling surface and a plane of a 0.3 mm or less in depth therefrom to 50 vol.% to 70 vol.%.例文帳に追加

さらに、高周波焼入工程では、転動部材の転走面となる部分を含む領域がさらに焼入硬化されることにより、転走面となるべき面からの深さが０．３ｍｍ以下の領域における残留オーステナイト量が５０体積％以上７０体積％以下とされる。 - 特許庁

In the high-frequency hardening step, a region including a part to be a rolling face of the needle-like roll bearing raceway member is further quenched and hardened so that a remaining amount of austenite in a region having a depth of ≤0.3 mm from the face to be the rolling face is ≥50 vol.% and ≤70 vol.%.例文帳に追加

高周波焼入工程では、針状ころ軸受用軌道部材の転走面となる部分を含む領域がさらに焼入硬化されることにより、転走面となるべき面からの深さが０．３ｍｍ以下の領域における残留オーステナイト量が５０体積％以上７０体積％以下とされる。 - 特許庁