The hollow fiber membranes of polyvinylidene fluoride are provided having inner diameters of 0.4-2.3 mm, a porosity of 60-90%, a tensile break strength of 7-20 Mpa, a tensile modulus of elasticity of 10-80 MPa, and an instantaneous compressive strength of 0.3-3.0 MPa.例文帳に追加

内径０．４ｍｍ以上２．３以下、空孔率が６０％以上９０％以下であり、引っ張り破断強度が７ＭＰａ以上２０ＭＰａ以下であり、引っ張り弾性率が１０ＭＰａ以上８０ＭＰａ以下であり、瞬時耐圧縮強度が０．３ＭＰａ以上３．０ＭＰａ以下であるポリフッ化ビニリデン中空糸膜。 - 特許庁

The negative electrode for a nonaqueous electrolyte secondary battery includes a negative electrode active material layer containing a negative electrode active material, a polyvinylidene fluoride component (A), a styrene butadiene component (B), a nonionic surfactant (C) having an HLB of 10-15, and N-methylpyrrolidone (D); and a foil-shaped negative electrode current collector having the negative electrode active material layer provided on at least one principal surface of the collector.例文帳に追加

非水電解質二次電池用負極は、負極活物質と、ポリフッ化ビニリデン系成分（Ａ）と、スチレンブタジエン系成分（Ｂ）と、ＨＬＢが１０〜１５の非イオン系界面活性剤（Ｃ）と、Ｎ−メチルピロリドン（Ｄ）と、を含む負極活物質層と、この負極活物質層を少なくとも一方の主面に有する箔状の負極集電体と、を備える。 - 特許庁

The electrode sheet is obtained through a drying process, after applying the coating fluid which is mixed with an organic solvent and a solid component containing active carbon at a fixed ratio of 85 to 92 wt.%, carbon black at a fixed ratio of 2 to 7 wt.%, to an aluminum foil with a conductive adhesive layer and polyvinylidene fluoride at a fixed ratio of 4 to 9 wt.%.例文帳に追加

活性炭を８５〜９２ｗｔ％、カーボンブラックを２〜７ｗｔ％、及びポリフッ化ビニリデンを４〜９ｗｔ％の含有率で含む固形成分と、有機溶媒を混合して得られる塗液を、導電性接着層を形成したアルミ箔に塗布した後、乾燥して得られる電極シートとする。 - 特許庁

In the surface coating film, PTFE is incorporated into at least one resin selected from a polyester resin, a linear polyester resin, an acrylic resin, a urethane resin, a phenoxy resin, a phenol resin, a polyvinylidene fluoride resin/an acrylic resin, and a vinyl chloride resin, and the back coating film is formed from a resin similar to that of the surface into which no PTFE is added.例文帳に追加

また、表面塗膜がポリエステル樹脂、線状高分子ポリエステル樹脂、アクリル樹脂、エポキシ樹脂、ウレタン樹脂、フェノキシ樹脂、フェノール樹脂、ポリフッ化ビニリデン樹脂／アクリル樹脂、塩化ビニル樹脂の中から選ばれた少なくとも１種にＰＴＦＥを配合し、裏面塗膜は表面と同系の樹脂でＰＴＦＥ無配合のものでもよい。 - 特許庁

In the resin-coated metal plate comprising a colored acrylic resin film 13 and a transparent resin film 14 sequentially laminated and integrated on a metal plate of a base material 11 via an adhesive 12; the film 14 is formed of a blended composition of a polyvinylidene fluoride resin and an acrylic resin.例文帳に追加

基材の金属板上に接着剤を介して、着色されたアクリル系樹脂フィルム（Ａ）と、透明樹脂フィルム（Ｂ）とが順次積層一体化されてなる樹脂被覆金属板において、透明樹脂フィルム（Ｂ）がポリフッ化ビニリデン系樹脂とアクリル系樹脂とのブレンド組成物よりなるフィルムである耐候性樹脂被覆金属板を要旨とする。 - 特許庁

The polymer compositions are based on a PVDF (polyvinylidene fluoride) homopolymer(s) and a fluorocopolymer, composed of (A) 25-75 mass% of one or more PVDF homopolymer(s) and (B) 25-75 mass% of one or more thermoplastic copolymer(s) and comprises fluoropolymer mixtures comprising a vinylidene fluoride (VF_2) and the thermoplastic copolymers containing 5-25 mass% of chlorotrifluoroethylene.例文帳に追加

PVDFホモポリマー及びフルオロコポリマーを基剤とするポリマー組成物であって、（Ａ）２５〜７５質量％の１種以上のPVDFホモポリマー；及び（Ｂ）２５〜７５質量％の１種以上の熱可塑性コポリマーであって、ビニリデンフルオライド（ＶＦ_2）と５〜２５質量％のクロロトリフルオロエチレンとを含む該熱可塑性コポリマーを含むフルオロポリマーの混合物を含むことを特徴とするポリマー組成物。 - 特許庁

To provide a coating composition, an anode plate using the coating composition, and a nonaqueous electrolyte solution secondary battery using the anode plate, excellent in pot life and coating aptitude, as well as in adhesion to a collector after film coating, film density, and battery capacity even in the case of a small volume of a polyvinylidene fluoride binder.例文帳に追加

ポリフッ化ビニリデン系バインダーの量が少なくても、ポットライフや塗工適性、及び、塗膜化後における集電体に対する密着性、塗膜密度、電池容量に優れる塗工組成物、当該塗工組成物を用いた負極板、当該負極板を用いた非水電解液二次電池を提供する。 - 特許庁

A porous membrane is characterized in that a porous resin layer is stacked on a porous base material and the porous resin layer has a polyvinylidene fluoride-based resin, a polyvinylpyrrolidone resin, a polyacrylic acid ester resin which weight average molecular weight is equal to or more than 10,000 and equal to or less than 200,000 and/or a polymethacrylic acid ester resin.例文帳に追加

多孔質基材に多孔質樹脂層が積層されてなる多孔質膜であって、該多孔質樹脂層がポリフッ化ビニリデン系樹脂と、ポリビニルピロリドン系樹脂と、重量平均分子量が１万以上２０万以下のポリアクリル酸エステル系樹脂および／またはポリメタクリル酸エステル系樹脂とを有することを特徴とする多孔質膜。 - 特許庁

The nonaqueous electrolyte secondary battery includes a positive electrode having a positive electrode active material layer, a negative electrode having a negative electrode active material layer as well as electrolyte, and at least either the positive electrode active material layer or the negative electrode active material layer includes a binding agent containing polyvinylidene fluoride resin with a mass average molecular weight of ≥500,000, as well as polyvinyl pyrrolidone.例文帳に追加

正極活物質層を有する正極および負極活物質層を有する負極と共に電解液を備えた非水電解液二次電池であって、正極活物質層及び負極活物質層の少なくとも何れかに質量平均分子量が５０万以上のポリフッ化ビニリデン系樹脂を含む結着剤とポリビニルピロリドンとを含む非水電解質二次電池。 - 特許庁

By this, since adhesive property to the conductive base body becomes good comparing with the electrode-applied film of which the binder is constituted from the polyvinylidene fluoride system polymer independent, cell capacity reduction by degrading of the electric junction between the electrode-applied film and the conductive base body, according to the repetitions of a charge/discharge electricity, can inhibited.例文帳に追加

これにより、バインダーがポリビニリデンフルオライド系ポリマー単独で構成された電極塗膜に比べ導電性基体との接着性が良好となるので、充放電の繰り返しにより、電極塗膜と導電性基体の間の電気的接合が劣化して電池容量が減少するのを抑制することができる。 - 特許庁

This electrode is for the electric double-layered capacitor which has a positive electrode, a negative electrode, the electricity collector, and an electrolyte, and characterized in that (1) the positive and negative electrodes contain at least activated carbon and a binder, and (2) the binder is polyvinylidene fluoride containing calboxylic acid.例文帳に追加

正極、負極、集電体および電解液を備えた電気二重層キャパシタ用の電極であって、（１）正極および負極が、少なくとも活性炭とバインダ−とを含み、（２）バインダーが、カルボン酸を含むポリフッ化ビニリデンであることを特徴とする電気二重層キャパシタ用電極、及び該電極を用いた電気二重層キャパシタ。 - 特許庁

Acrylic elastomer contained in the intermediate layer 2 can produce good adhesiveness to the polyvinylidene fluoride of the inner layer 1, and olefin resin contained in the intermediate layer 2 can produce good adhesiveness to the olefin resin as constitutive material of the outer layer 3, acrylic elastomer, mixed material of acrylic elastomer and acrylic resin, olefin elastomer or styrene elastomer.例文帳に追加

更に中間層２に含まれるアクリル系エラストマーにより、内層１のポリフッ化ビニリデンとの接着性が良好であると共に、中間層２に含まれるオレフィン系樹脂により、外層３の構成材料であるオレフィン系樹脂又はアクリル系エラストマー又はアクリル系エラストマーとアクリル樹脂の混合材料又はオレフィン系エラストマー又はスチレン系エラストマーとの接着性が良好である。 - 特許庁

The porous sheet is obtained by coating inorganic fiber nonwoven fabric with a high molecular nanofiber layer, the heat resistance of the porous sheet is 300°C or more, and a material of the high molecular nanofiber layer is a mixture of one sort or a plurality of sorts selected from thermoplastic polymers of polyvinyl alcohol, polyvinylidene fluoride, polyacrylonitrile, polyvinyl chloride, polyethylene, polypropylene, polyethylene terephthalate, and polyimide.例文帳に追加

無機繊維不織布に高分子ナノファイバー層を被覆した多孔質シートであり、多孔質シートの耐熱性が３００℃以上であり、高分子ナノファイバー層は、材質がポリビニルアルコール、ポリフッ化ビニリデン、ポリアクリロニトリル、ポリ塩化ビニル、ポリエチレン、ポリプロピレン、ポリエチレンテレフタレート及びポリイミドの熱可塑性高分子から選ばれる１種類または複数種類の混合物である。 - 特許庁

The nonaqueous electrolyte battery includes a positive electrode, a negative electrode having a negative electrode active material layer provided on a negative electrode current collector and a nonaqueous electrolyte, wherein the negative electrode active material layer contains a polyvinylidene fluoride-containing binder and nano ceramic particles having a primary particle size of not more than 100 nm; and the binder and the nano ceramic particle are complexed.例文帳に追加

正極と、負極活物質層が負極集電体上に設けられた負極と、非水電解質とを備えた非水電解質電池であって、 前記負極活物質層は、ポリフッ化ビニリデンを含む結着剤および一次粒子径１００ｎｍ以下のナノセラミック粒子を含有し、 前記結着剤とナノセラミック粒子とが複合化していることを特徴とする非水電解質電池。 - 特許庁

In the negative electrode for the lithium ion secondary battery having a current collector and a negative electrode active material layer which is arranged on the current collector and which contains the hard carbon as the negative electrode active material, this is the negative electrode for the lithium ion secondary battery in which the negative electrode active material furthermore contains polyvinylidene fluoride and carbon black.例文帳に追加

集電体と、前記集電体上に配置された、負極活物質としてハードカーボンを含有する負極活物質層と、を有するリチウムイオン二次電池用負極において、前記負極活物質層は、ポリフッ化ビニリデンおよびカーボンブラックをさらに含有する、リチウムイオン二次電池用負極である。 - 特許庁

A solution containing a polymer matrix containing a polyvinylidene fluoride system compound, a support electrolyte, and an electrolytic solution at least containing a phosphoric ester class and having a viscosity of 2 to 30 Pa s at 25°C is coated on a substrate, which is then put under a drying treatment.例文帳に追加

ポリフッ化ビニリデン系高分子化合物を含有する高分子マトリックス、支持電解質、および少なくともリン酸エステル類を含有する電解液を含有し、かつ２５℃における粘度が２〜３０Ｐａ・ｓである溶液を、基板上に塗布したのち、乾燥処理することを特徴とするイオン伝導性フィルムの製造方法。 - 特許庁

In this solid electrolytic membrane, void parts in a macromolecular porous membrane such as a polyvinylidene fluoride membrane are filled with a gel material retaining an electrolyte in a network structure of a polyaddition compound of a compound such as a glycolic polymer having two or more hydroxyl groups in a molecule with a compound such as tolylene diisocyanate having two or more isocyanate groups in a molecule.例文帳に追加

分子内に２個以上の水酸基を有するグリコールポリマーのような化合物と分子内に２個以上のイソシアネート基を有するトリレンジイソシアネートのような化合物との重付加物の網目構造内に電解質を保持するゲル体が、ポリフッ化ビニリデン膜のような高分子多孔質膜の空隙部内に充填されている固体電解質膜。 - 特許庁

The lithium secondary battery and an electric double layer capacitor are manufactured with a solid polyelectrolyte containing an electrolyte salt, solvent and a polymer to be as an polymer alloy of vinylidene fluoride-acetone hexafluoride copolymer and one or more kinds of a polyvinylidene fluoride, a polycarbonate, an ethylene-vinylacetate copolymer and a poly(metha)acrylate, and with electrodes using compositions of the solid polyelectrolyte and electrode active materials.例文帳に追加

ふっ化ビニリデン−６ふっ化アセトン共重合体と、ポリふっ化ビニリデン、ポリカーボネート、エチレン酢酸ビニル共重合体およびポリ（メタ）アクリレートの１種または２種以上とのポリマーアロイである高分子、電解質塩および溶媒を有する高分子固体電解質と、この高分子固体電解質電極活物質との組成物を用いた電極とでリチウム２次電池、電気２重層キャパシタを作製する。 - 特許庁

Carbon nanotubes as conductive particles, and polyvinylidene fluoride or the like as a piezoelectric polymer are packed at a fixed weight ratio and are subjected to kneading, hot press molding and cold pressing at respective temperatures and pressures to provide a sheetlike molding, which is in turn uniaxially drawn and then impressed with a high electric field for polarization so as to be converted into the piezoelectric damping material.例文帳に追加

導電性粒子としてカーボンナノチューブを、圧電性ポリマーとして例えばポリフッ化ビニリデンを一定重量比率で充填し、これらを各温度、圧力の下で混練、加熱プレス成型、冷却プレスしてシート状に成型したものを、さらに一軸延伸した後、高電界を印加して分極処理を行い圧電制振材料に変換する。 - 特許庁

The charging member is constituted by covering a semiconductor silicone elastic body layer with a resin layer and charges the object to be charged by being made to abut the object to be charged and applying voltage between itself and the object to be charged, wherein polyol crosslinked or peroxide crosslinked polyvinylidene fluoride and/or polyol crosslinked or peroxide crosslinked polyvinyl fluoride are used as the resin for forming the resin layer.例文帳に追加

半導電性シリコーン弾性体層に樹脂層を被覆してなり、被帯電体に当接させ、該被帯電体との間に電圧を印加することにより、被帯電体を帯電させる帯電部材において、樹脂層を形成する樹脂としてポリオール架橋又は過酸化物架橋したポリフッ化ビニリデン及び／又はポリオール架橋又は過酸化物架橋したポリフッ化ビニルを用いる。 - 特許庁

The nonaqueous electrolyte battery includes a positive electrode having a positive electrode active material layer provided on a positive electrode current collector, a negative electrode and a nonaqueous electrolyte, wherein the positive electrode active material layer contains a polyvinylidene fluoride-containing binder and nano ceramic particles having a primary particle size of not more than 100 nm; and the binder and the nano ceramic particle are made to be complex.例文帳に追加

正極活物質層が正極集電体上に設けられた正極、負極および非水電解質を備えた非水電解質電池であって、 前記正極活物質層は、ポリフッ化ビニリデンを含む結着剤および一次粒子径１００ｎｍ以下のナノセラミック粒子を含有し、 前記結着剤とナノセラミック粒子とが複合化していることを特徴とする非水電解質電池。 - 特許庁

The sensor for measuring hair characteristics includes a support having a comb-shaped part for combing the hair, a detecting means arranged on the support and includes polyvinylidene fluoride as a piezoelectric converting material for converting vibrations generated when the support body combs the hair into electric signals, and an output means for outputting the signal generated by the detecting means.例文帳に追加

毛髪を梳かすための櫛型形状部を有する支持体と、前記支持体上に配置され、前記支持体が前記毛髪を梳かす際に生じる振動を電気信号に変換するポリフッ化ビニリデンを圧電変換材とする検出手段と、前記検出手段の発生する信号を出力する出力手段と、を有する毛髪特性測定用センサであることを特徴とする。 - 特許庁

The resin composition for the porous filtering membrane contains polyvinylidene fluoride and a hydrophobic calcium carbonate particulate with the BET relative surface area of 5-75 m^2/g and in which the total of 11 μm or more in a laser diffraction system (micro track FRA) particle size distribution is 25% or less, or further contains an organic liquid body.例文帳に追加

ポリフッ化ビニリデン樹脂と、ＢＥＴ比表面積５〜７５ｍ^2 / ｇ、レーザー回折式（マイクロトラックＦＲＡ）粒度分布における１１μｍ以上の累計が２５％以下である疎水性炭酸カルシウム微粒子を含有する多孔質濾過膜用樹脂組成物、又は、更に有機液状体を含有する多孔質濾過膜用樹脂組成物である。 - 特許庁

In the nonaqueous electrolyte secondary battery 10, the negative electrode mix layer 12b constituting a negative electrode 12 is formed by holding, to a negative electrode core body 12a, active material slurry formed by adding and mixing a mixture binder comprising a rubber-based resin in a dispersion state and a polyvinylidene fluoride resin (PVdF) in a powder state in graphite used at least as a negative electrode active material.例文帳に追加

本発明の非水電解質二次電池１０においては、負極１２を構成する負極合剤層１２ｂは少なくとも負極活物質となる黒鉛に、ディスパージョン状態のゴム系樹脂と粉末状態のポリフッ化ビニリデン樹脂（ＰＶｄＦ）とからなる混合結着剤を添加、混合して形成された活物質スラリーが負極芯体１２ａに保持されるように形成されたものである。 - 特許庁

To provide a method for continuously producing a polyvinylidene fluoride (PVDF) homopolymer or copolymer, wherein comonomer is selected from compounds containing polymerizable vinyl capable of being activated by the action of free radicals, the comonomer has at least one fluorine atom, fluoroalkyl or fluoroalkoxy directly bonded to the vinyl and the ratio of the comonomer is 0-50 wt.%.例文帳に追加

フリーラジカルの作用で開いて重合可能なビニル基を含む化合物からコモノマーが選択され、このコモノマーは上記のビニル基に直接結合された少なくとも一つのフッ素原子、フルオロアルキル基またはフルオロアルコキシ基を有し、コモノマーの比率が０〜５０重量％である、ＰＶＤＦのホモポリマーまたはコポリマーの連続製造方法。 - 特許庁

An endless power transmission belt 20 is provided that is equipped with a tension part 21, a cushioned part 22, a loaded part 23 located between the tension part and the cushioned part, and at least one driving surface 29 that is bonded with a cloth layer 25 on which the outer surface has undergone improvement by being coated with polyvinylidene fluoride.例文帳に追加

張力部２１と、クッション部２２と、前記張力部と前記クッション部との間に配置されている負荷部２３と、ポリふっ化ビニリデンのコーティング層を設ける改良を施したベルトの外側表面に織物層２５が接着されている少なくとも１つの駆動面２９とを備えたエンドレスの動力伝達ベルト２０を提供する。 - 特許庁

By adding such an external additive containing fine particulate silica, coarse particulate silica, silicon carbide, magnesium stearate and polyvinylidene fluoride in a predetermined component ratio to a toner composition, a toner composition is obtained by which the image density is maintained stably, the fog phenomenon does not occur, a feeding property is very effective, and the filming phenomenon does not occur, so that high quality images may be provided.例文帳に追加

トナー組成物に，小粒子シリカ，大粒子シリカ，シリコンカーバイド，マグネシウムステアレート，及びポリビニリデンフルオライドを所定の成分比で含有する外添剤を添加することにより，画像濃度が安定的に維持され，フォグ現象が発生せず，供給性に優れ，フィルミング現象も発生しない高品質の画像を提供するトナー組成物を提供することができる。 - 特許庁

Polymer such as polyacrylonitirile(PAN), polyvinylidene fluoride(PVdF) or the like, an organic solvent such as propylene carbonate(PC), ethylene carbonate(EC), γ-butyrolactone(GBL) or the like, and salt making an electrolytic capacitor function as a capacitor are mixed together and heated into a high- molecular gel electrolyte film, and the film is irradiated with an electron beam to be improved in thermal resistance.例文帳に追加

ポリアクリロニトリル（ＰＡＮ）、ポリビニリデンフルオライド（ＰＶｄＦ）等のポリマーとプロピレンカーボネート（ＰＣ）、エチレンカーボネート（ＥＣ）、γブチロラクトン（ＧＢＬ）等の有機溶媒、そしてキャパシタとして作用させるための塩を加熱混合し製膜した高分子ゲル電解質に電子線を照射して耐熱性向上させたことを特徴とする。 - 特許庁

A rolling bearing 10 constituted by interposing a rolling element 50 such as a ball, a roller, etc., and a retainer 70 between an inner ring 20 and an outer ring 30 is constituted by manufacturing all members to constitute it of the same kind or different kinds of resin materials selected from polyvinylidene fluoride, polyether ether ketone and polyphenylene sulphide.例文帳に追加

内輪（２０）と外輪（３０）との間にボール、ローラ等の転動体（５０）及び保持器（７０）が介装されてなる転がり軸受（１０）であって、それを構成する全部材が、ポリフッ化ビニリデン、ポリエーテルエーテルケトン、及び、ポリフェニレンスルフィドから選ばれる同一種類又は異種類の樹脂素材で作製されてなる。 - 特許庁

The polyvinylidene fluoride is obtained by polymerizing vinylidene fluoride and has a polymer chain comprising a vinylidene fluoride monomer unit, where the number X of normal bonds per 100 vinylidene fluoride monomer units and the number Y of branchings per 10,000 vinylidene fluoride monomer units satisfy the following expression (a) or (b): 0≤Y≤380-4.125X例文帳に追加

ビニリデンフルオライドの重合により得られるポリビニリデンフルオライドであって、上記ポリビニリデンフルオライドは、ポリマー鎖がビニリデンフルオライドモノマー単位からなるものであり、上記ビニリデンフルオライドモノマー単位１００個あたりの正常結合数Ｘ個と、上記ビニリデンフルオライドモノマー単位１００００個あたりの分岐数Ｙ個とが、下記式（ａ）又は下記式（ｂ）を満たすものであることを特徴とするポリビニリデンフルオライド。 - 特許庁

In the decorative sheet composed of at least a transparent thermoplastic resin layer and a colored thermoplastic resin base material layer, the transparent thermoplastic resin layer comprises at least two layers and characterized in that the glass transition point of the resin of the outermost layer is lower than that of the resin of the inside layer thereof, the outermost layer comprises a fluoroplastic being a polyvinylidene fluoride resin and the inside layer comprises an acrylic resin.例文帳に追加

少なくとも透明熱可塑性樹脂層と着色熱可塑性樹脂基材層からなる化粧シートにおいて、前記透明熱可塑性樹脂層が２層以上であり、最外層の樹脂のガラス転移点がその内側層の樹脂のガラス転移点より低い透明熱可塑性樹脂からなること、また外層がフッ素樹脂からなること、また前記フッ素樹脂がポリフッ化ビニリデン樹脂であること、またその内側層がアクリル樹脂からなることを特徴とする。 - 特許庁