Then, these constituent glaze powders are mixed to compose prepared glaze powders, and by coating them on an insulator and making the glost firing, the glazed layer is obtained.例文帳に追加

そして、これらの要素釉薬粉末を混合して調整釉薬粉末となし、絶縁体に塗布して釉焼することにより、釉薬層を得る。 - 特許庁

This decorated earthen ware is characterized in that different kinds of compounded clay (2), (3), (4) and (5) are inlaid in the surface of the earthen ware according to a design and are developed into desired colors respectively after glost firing.例文帳に追加

調合済みの粘土（２）、（３）、（４）、（５）を陶器面上にデザインに従って埋め込み、本焼き後希望する色に発色させることを特徴とする。 - 特許庁

To provide a spark plug having a glaze layer in which the content of Pb component is less, and further which is superior in fluidity in glost firing, and which is superior in an anti-flashover property with a high insulation resistance.例文帳に追加

Ｐｂ成分の含有量が少なく、しかも釉焼時の流動性に優れ、高絶縁抵抗で耐フラッシュオーバ性に優れた釉薬層を有するスパークプラグを提供する。 - 特許庁

The inner chamber of the kiln for multistage ceramic industry is divided into four chambers consisting of a first combustion chamber 57, a second combustion chamber 59, a glost firing chamber 67, and a biscuit firing chamber 89.例文帳に追加

そして、多段窯業用窯内室が、下から第１燃焼室５７、第２燃焼室５９、本焼き室６７、素焼き室８９と４室に分けられている。 - 特許庁

To provide a manufacturing method of a spark plug, wherein the glost firing in which residues of air bubbles or the like are hardly generated can be performed at a relatively low temperature, and then a glazed layer of a superior anti-chipping property is obtained.例文帳に追加

気泡等の残留を生じ難い釉焼を比較的低温にて行なうことができ、ひいては耐チッピング性の良好な釉薬層が得られるスパークプラグの製造方法を提供する。 - 特許庁

To provide a manufacturing method of a spark plug wherein the glost firing in which residues of bubbles or the like are difficult to be generated can be carried out relatively at low-temperatures, and wherein a glaze layer of superior anti-chipping property is obtained in its turn.例文帳に追加

気泡等の残留を生じ難い釉焼を比較的低温にて行なうことができ、ひいては耐チッピング性の良好な釉薬層が得られるスパークプラグの製造方法を提供する。 - 特許庁

White clay is filled into a star-shaped mold to mold the artificial star sand and the molded star sand is glost fired at 1,250°C to make the high heat resistant artificial star sand without being eluted and deformed with water in the glaze.例文帳に追加

星型の型材に白粘土を詰め込み人造星砂を成形し１２５０℃で本焼き焼成を行い釉薬などの水分で溶け出し変形することも無く耐熱性の高い人造星砂を作ることを可能とする。 - 特許庁

To provide a kiln for ceramics capable of shortening a series of firing time by simultaneously conducting firing processes of biscuit firing, glost firing and decorating firing, and improving heat efficiency in firing.例文帳に追加

陶芸作品の素焼き、本焼き、上絵焼付けなどの各焼成工程を同時に進行させて一連の焼成時間を短縮できると共に、焼成の際の熱効率を向上することができる陶芸窯を提供する。 - 特許庁

The worked veining, to which the water glass aqueous solution adheres, is placed on the ceramic ware heated in advance up to 80-200°C so as to be temporarily baked under the state of being held down in order to complete the ceramic ware at a glost firing at 1,000-1,200°C.例文帳に追加

この加工済葉脈に水ガラスの水溶液を付着させて、これを、あらかじめ８０°〜２００°に加熱しておいた陶磁器上に配置して、上から押さえて仮焼き付け終了後、本焼き１，０００°〜１，２００°で完成させる。 - 特許庁

To make artificial star sand rise up white to the surface without dyeing a color of glost firing glaze by pottery-making the artificial star sand having high strength and heat resistance and integrating a pottery body and the artificial star sand with glass powder or the glaze.例文帳に追加

強度も耐熱性も高い人造星砂を陶磁器製造し陶磁器本体と人造星砂をガラス粉又は釉薬を用い一体化させる事を可能とし人造星砂を本焼き釉薬の色に染まる事なく白く浮かび上がらせる。 - 特許庁

The mixture formed by mingling the clay and the titanium oxide powder with the water is held on the surface of the biscuit firing plate having the plural flow holes consisting of the clay as the chief material and thereafter the biscuit firing plate holding the mixture is subjected to glost firing, by which the photocatalyst is obtained.例文帳に追加

水に粘土と酸化チタン粉体とを混ぜ合わせてなる混合物を、粘土を主材とする複数の流通孔を有する素焼板の表面に保持させた後、混合物を保持した素焼板を本焼きすることによって得ることができる。 - 特許庁

The electrical porcelain 1, supported by a support member 330 with the barrel part 72 abutted on an edge part of an upper end 331, is heated in a glost firing part 315 of a furnace 310 of an electric furnace 300 by the radiation heat emitted from a heater unit 320 with an arch cross-section provided to its right and left side faces.例文帳に追加

胴部７２が上端３３１の縁部分に当接することで支持部材３３０に支持された絶縁碍子１は、電気炉３００の窯３１０の釉焼部３１５内にて、その左右側面に設けられた断面弓状のヒータユニット３２０から放射される放射熱によって加熱される。 - 特許庁

The container body is provided with a small shrine body 2 (the basic container body) which has a housing space 12 inside, an insulation member 4 housed in the housing space 12 of the small shrine body 2, and the statue of Buddha 6 insulated by the insulation member 4, while the statue of Buddha 6 is formed of china of glost firing on which gold is coated.例文帳に追加

内部に収容空間１２を有する祠本体２（容器本体）と、この祠本体２の収容空間１２に収容された断熱部材４と、断熱部材４により断熱された仏像６と、を具備し、仏像６が金絵付けされた本焼きの陶磁器から形成されている。 - 特許庁

Thereafter, the bodies W are oxidatively fired wile driving a vacuum pump 31 for exhausting the inside of the casing 10, and further after stopping the vacuum pump 31, the bodies W are subjected to reductive firing for glost firing the bodies W.例文帳に追加

電気炉２０に通電して素地Ｗ、Ｗを脱水し、ケーシング１０内を排気する真空ポンプ３１を運転して素地Ｗ、Ｗを酸化焼成し、真空ポンプ３１を停止させて素地Ｗ、Ｗを還元焼成することにより、素地Ｗ、Ｗを本焼きすることができる。 - 特許庁

To provide a method of manufacturing an oxide superconducting thin film, enabling manufacture of the oxide superconducting thin film having uniform-crystal-orientation high Ic by stacking calcined films produced in a MOD method to produce a thick calcined film and then applying glost firing heat treatment thereto.例文帳に追加

ＭＯＤ法を用いて作製された仮焼膜を積層して厚膜の仮焼膜とした後、本焼熱処理を行って酸化物超電導薄膜を作製するに際して、結晶配向性が揃った高いＩｃを有する酸化物超電導薄膜を作製することができる酸化物超電導薄膜の製造方法を提供する。 - 特許庁

To obtain minimum risk and cost by realizing the sure baking up of leaves during the process of a glost firing at an arbitrary position in an arbitrary color with neither dissolving nor drifting away of the leaves.例文帳に追加

従来、木の葉を陶磁器に本焼きする場合、焼き付け面に特定の自然の葉をただ置くだけなので、その素材に含まれる水分や成分の固有の特性のために、位置と色は限定されるばかりか、窯の中の熱でちぢれて丸くなったり、対流で離脱移動してしまい、意図的に焼きつけることが極めて困難であり、完品の歩留まりが悪く、非常にコスト高となる。 - 特許庁