This copper powder for the conductive paste, with excellent resistance to the oxidation containing 5 wt.% or less of Si, substantially all the Si is coated on surface of copper particles as SiO_2 gel-coating film.例文帳に追加

５重量％以下のＳｉを含有した銅粉であって，そのＳｉの実質上全てがＳｉＯ_2系ゲルコーティング膜として銅粒子表面に被着していることを特徴とする耐酸化性に優れた導電ペースト用銅粉である。 - 特許庁

To provide a colored film-forming coating solution prepared by dissolving a silicon(Si) alkoxide and metal salts in a solvent, and to provide a method of forming a colored film having a surface resistance of high resistivity on a surface of glass plate through a sol-gel process.例文帳に追加

Ｓｉアルコキシドと金属塩を溶媒中に溶解させた塗布液を用いて、ゾルゲル法で表面抵抗が高抵抗な着色膜をガラス板表面に得る。 - 特許庁

The copper powder, which is used as a conductive filler for a conductive paste and excellent in oxidation resistance and sinterability, is characterized in that it contains 5 wt.% or lower Si, that substantially all the Si is adhered, as an SiO_2-based gel coating film, to the surfaces of copper particles, and that the SiO_2-based gel coating film contains at least one glass-forming component.例文帳に追加

導電ペーストの導電フイラーに用いる銅粉において，５重量％以下のＳｉを含有し，そのＳｉの実質上全てがＳｉＯ_２系ゲルコーティング膜として銅粒子表面に被着しており，このＳｉＯ_２系ゲルコーティング膜に少なくとも１種のガラス形成性成分が含まれていることを特徴とする耐酸化性および焼結性に優れた導電ペースト用銅粉である。 - 特許庁

Regarding the copper powder used for an electrically conductive filler in electrically conductive paste having excellent oxidation resistance and sinterability, Si is comprised by ≤5 wt.%, substantially all the Si is deposited on the surfaces of copper particles as an SiO_2-based gel coating film, and at least one of glass formable component is comprised in the SiO_2-based gel coating film.例文帳に追加

導電ペーストの導電フィラーに用いる銅粉において，５重量％以下のＳｉを含有し，そのＳｉの実質上全てがＳｉＯ_2系ゲルコーティング膜として銅粒子表面に被着しており，このＳｉＯ_2系ゲルコーティング膜に少なくとも１種のガラス形成性成分が含まれていることを特徴とする耐酸化性および焼結性に優れた導電ペースト用銅粉である。 - 特許庁

A sol composition obtained by dispersing and/or dissolving a compound containing a metal and/or Si as a cation in a solvent is dried to make a gel composition and the gel composition is dispersed into a matrix composed of a polymeric material to obtain the flame-retardant polymeric composite material.例文帳に追加

金属及び／又はＳｉをカチオンとする化合物を溶媒中に分散及び／又は溶解させたゾル状組成物を乾燥させてゲル状組成物となし、そのゲル状組成物を高分子材料からなる基質中に分散させて難燃性高分子複合材料を得る。 - 特許庁

Bubbles 61 left in an Si(silicon) gel (sealing material) 60 on the rear surface side of the upper one 50 of two circuit boards 20 and 50 housed in a case 10 get away of the gel 60, namely, to the atmosphere through vent holes 55 bored through the board 50 before the bubbles 61 grow larger.例文帳に追加

ケース１０に収容された２枚の回路基板２０，５０のうち上側の回路基板５０の裏面側のＳi ゲル（封止材）６０中に残留された気泡６１は、大きく成長する前に上側の回路基板５０に穿設された抜き穴５５を通ってＳi ゲル６０の外、即ち、大気中に抜ける。 - 特許庁

A sol composition wherein a compound containing a metal element and/or Si is dispersed and/or dissolved in a solvent is mixed with carrier material particles, and the mixed sol composition is dried to yield a gel composition to obtain the flame retardance- imparting composite composition wherein the gel composition is compounded with the carrier material particles.例文帳に追加

金属元素及び／又はＳｉの化合物を溶媒中に分散及び／又は溶解させたゾル状組成物を担持材料粒子と混合し、混合したゾル状組成物を乾燥させてゲル状組成物となし、担持材料粒子にゲル状組成物が複合化した難燃性付与用複合組成物を得る。 - 特許庁

This composite composition for giving flame retardance is obtained as a gel composition compounded on a support material particle by mixing a sol composition which is prepared by dispersing and/or mixing zinc nitrate (containing water or crystallization) and an Si alkoxide in a solvent, with a support material particle, then drying the mixed sol composition to a gel composition.例文帳に追加

硝酸亜鉛（結晶水を含む）及びＳｉアルコキシドを溶媒中に分散及び／又は溶解させたゾル状組成物を担持材料粒子と混合し、混合したゾル状組成物を乾燥させてゲル状組成物となし、担持材料粒子にゲル状組成物が複合化した難燃性付与用複合組成物を得る。 - 特許庁