To provide a method of deciding optimum welding conditions when joining a pair of resin molded bodies by welding.例文帳に追加

一対の樹脂成形体を溶着により接合する際の、好適な溶着条件を決定する方法を提供する。 - 特許庁

To provide a tubular member joining method capable of joining tubular members by welding while beads are prevented from swelling out easily under various conditions, for example under execution of piping works.例文帳に追加

配管施工の状態など様々な条件下で容易にビードの膨出を防止しながら管状部材を溶着によって接合することができる管状部材接合方法を提供する。 - 特許庁

The joining is executed preferably under the hot pressing conditions of 200 to 400°C temp. and ≥20 kg/cm2 pressure.例文帳に追加

前記接合が温度２００〜４００℃、圧力２０ｋｇ／ｃｍ^2 以上のホットプレス条件により行われることが好ましい。 - 特許庁

Besides, the conditions of treatment of the aluminum sheet in each process are changed at the time when a joining part of the aluminum sheet reaches each process.例文帳に追加

該アルミニウム板のつなぎ部が各処理工程に達したときに該アルミニウム板の該各処理工程の処理条件を変更する。 - 特許庁

To provide a highly heat resistant conductive filler by which fusion joining under lower temperature conditions (peak temperature ≥140°C) than reflow heat treatment conditions of the conventional Sn-37Pb eutectic solder is possible.例文帳に追加

従来のＳｎ—３７Ｐｂ共晶はんだのリフロー熱処理条件よりも低温条件（ピーク温度１４０℃以上）で溶融接合できる高耐熱性の導電性フィラーを提供する。 - 特許庁

To provide a filler metal which can be melt-joined at a temperature lower than that in the reflow heat treatment conditions of Sn-37Pb eutectic solder, has excellent heat resistance after joining, and also imparts satisfactory joining strength at room temperature.例文帳に追加

Ｓｎ−３７Ｐｂ共晶はんだのリフロー熱処理条件よりも低い温度で溶融接合でき、接合後は耐熱性に優れ、かつ室温で良好な接合強度を与える金属フィラーの提供。 - 特許庁

To provide a method of joining different kinds of materials, a method having extensive welding conditions and making high strength welding possible, even in aluminum/iron spot welding.例文帳に追加

アルミニウム／鉄スポット溶接においても、溶接条件が幅広く、かつ、高強度溶接が可能な異材接合方法を提供する。 - 特許庁

To provide a method for joining resin films by which film-like resin materials are joined together without the use of an appropriate mold for an object to be joined or a joint pattern and consequently, a manufacturing cost is reduced and a change in the joining conditions is flexibly dealt with.例文帳に追加

接合対象や接合パターンに対応した金型を用いることなくフィルム状の樹脂材同士を接合でき、したがってコストを低減したり、接合条件の変更に柔軟に対応することが可能な接合方法の実現。 - 特許庁