「PRIMARY SINTERING」に関連した英語例文の一覧と使い方 - Weblio英語例文検索

It is preferable to manufacture the alloy material by kneading and molding raw material powders and successively passing the resultant green body through a primary sintering stage, a repressing/forging stage where repressing by press or squeezing by roll forging is done, and a secondary sintering stage.例文帳に追加

原料粉を混練、成形したのち、１次焼結工程と、プレスで再圧しまたは回転鍛造で鍛圧する再圧／鍛造工程と、ついで２次焼結工程を経て製造されるのが好適である。 - 特許庁

In this method of manufacturing a tape-like high-temperature superconductive wire formed by arranging a plurality of core wires, the number of core wires is increased in accordance with a desired n value, and a primary sintering time is adjusted so that primary sintering is prevented from excessively advancing to increase Ic.例文帳に追加

複数の芯線が配置されて構成されているテープ状高温超電導線の製造方法であって、所望のｎ値に対応して、芯線の数を増加させると共に、過剰な一次焼結の進行を防止してＩｃを増加させるように、一次焼結時間を調整する。 - 特許庁

A system 1 of manufacturing a sliding member 2 first forms a sintered alloy layer 4 laminated on a back metal 3 during a primary sintering process.例文帳に追加

摺動部材２の製造システム１は、先ず１次焼結工程において裏金３上に焼結合金層４を積層させて形成する。 - 特許庁

The transition layer is applied to the component as slurry comprising at least an organic solvent, the primary transition material and at least one slurry sintering aid, and wherein a reaction between the slurry sintering aid and the primary transition material results in the transition layer comprising porosity of 0 to about 15 vol.% of the transition layer.例文帳に追加

この遷移層は、少なくとも有機溶剤、主要遷移材料及び少なくとも１つのスラリー焼結助剤からなるスラリーとして部品に塗布され、スラリー焼結助剤と主要遷移材料の間の反応によって、その０％〜約１５容量％の多孔率を有する遷移層が形成される。 - 特許庁

In the ceramic member for the ESD protection containing a sintering composition formed from a base material and a resistivity regulator, the base material contains a primary component and a secondary component, and the primary component contains Al_2O_3 and the secondary component contains a tetragonal ZrO_2.例文帳に追加

基材と抵抗率調節剤から形成される焼結組成物を含むＥＳＤ保護用セラミック部材であり、該基材は一次成分と二次成分を含み、一次成分はＡｌ_2Ｏ_3を含み、二次成分は正方晶ＺｒＯ_2を含む。 - 特許庁

The compact is sintered into a porous sintered body (a primary sintering stage S2), and, after that, a catalyst-containing solution is impregnated into the porous sintered body (an impregnating stage S2).例文帳に追加

該成形体を焼結して多孔質焼結体とした後（一次焼結工程Ｓ２）、この多孔質焼結体の内部に触媒含有溶液を含浸する（含浸工程Ｓ３）。 - 特許庁

To provide a multi-component based metal particle slurry containing primary particle of nm-order showing good particle dispersion property and sufficient low temperature sintering property.例文帳に追加

良好な粒子分散性を示すｎｍオーダーの１次粒子径を含み、十分な低温焼結特性を示す多成分系金属粒子スラリーの提供を目的とする。 - 特許庁

To provide ITO (indium tin oxide) powder consisting of fine primary particles in which aggregation with each other is relatively weak, and which are excellent in sintering property so as to give a high density ITO sintered compact.例文帳に追加

微細な一次粒子からなり、一次粒子同士の凝集が比較的弱く、高密度のＩＴＯ焼結体を与える焼結性に優れたＩＴＯ粉末を提供する。 - 特許庁

The copper-based sintered sliding material is manufactured by scattering a powder of Cu or Cu alloy on a steel plate, followed by a primary sintering process, a primary rolling process with pressure, and secondary sintering process, and then a secondary rolling process at a pressure drop rate of 10%, and finally a heating process at a temperature over the Cu/Cu alloy recrystallization starting temperature but under the recrystallization starting temperature of the steel backing strip.例文帳に追加

鋼板上にＣｕまたはＣｕ合金の粉末を散布し、一次焼結、一次圧延および二次焼結を順次行った後、圧下率１０％以上で二次圧延を行い、続いて、ＣｕまたはＣｕ合金の再結晶開始温度以上で鋼裏金の再結晶開始温度未満の温度で加熱処理を行い、銅系焼結摺動材料を製造する。 - 特許庁

Accordingly, the sintering properties of mutual ceramic primary grains are improved and the reduction of a ceramic layer is controlled uniformly, thus reducing the dispersion of varistor voltage and electrostatic capacity.例文帳に追加

これによりセラミック１次粒子どうしの焼結性を向上しセラミック層の還元を均一に制御するものであり、これにより、バリスタ電圧や静電容量のバラツキを低減することができる。 - 特許庁

In a production process comprising, for example, shaping a zirconia powder containing 6 to 15 mol% of yttria and 3 to 20 mol% of titania, and carrying out hot isostatic press (HIP) processing of the primary sintered body obtained by normal primary sintering of the shaped product, the sintered body is produced so as to have an average grain diameter less than 30 μm.例文帳に追加

当該焼結体は、例えば、イットリアを６〜１５ｍｏｌ％、チタニアを３〜２０ｍｏｌ％含有するジルコニア粉末を成形後、常圧で一次焼結して得られる一次焼結体を熱間静水圧プレス（ＨＩＰ）処理する製造方法において、平均粒径が３０μｍ未満の焼結体とすることによって得られる。 - 特許庁

This non-aqueous electrolyte secondary battery contains positive electrode active material secondary particles which are made by sintering in mutual contacted state the primary particles A composed of at least one kind of compounds selected from a group of lithium cobaltate and lithium nickelate, and the primary particles B composed of lithium manganate.例文帳に追加

コバルト酸リチウム及びニッケル酸リチウムからなる群から選ばれる少なくとも一種の化合物からなる一次粒子Ａと、マンガン酸リチウムからなる一次粒子Ｂとが、互いに接触した状態で焼結されてなる正極活物質二次粒子を含むことを特徴とする非水電解質二次電池。 - 特許庁

Further, the method of producing the photocatalyst membrane comprises adding a binder to primary particles of TiO2 having an average particle size of ≤100 nm, being a raw material, to obtain a slurry, then coating the slurry onto a substrate by a slip casting method and sintering the coated film.例文帳に追加

さらに原料に平均粒径１００ｍｍ以下のＴｉＯ_２一次粒子を用い、バインダを添加してスラリーとし、スラリーを基板上にスリップキャスト法により塗布した後、焼結する光触媒膜の製造方法。 - 特許庁

Slurry compositions for making an environmental barrier coating comprises about 9-81 wt.% water, about 3-72 wt.% primary material; and about 0.1-18 wt.% slurry sintering aid.例文帳に追加

耐環境コーティングを製造するためのスラリー組成物は、約９ｗｔ％〜約８１ｗｔ％の水、約３ｗｔ％〜約７２ｗｔ％の主要材料、及び約０．１ｗｔ％〜約１８ｗｔ％のスラリー焼結助剤からなる。 - 特許庁

An insulating film composed of at least one of fullerene or chemically modified fullerene is formed on a boundary surface of magnetic powder containing rare earth, molding or density growth is performed on the magnetic powder in a magnetic field to obtain a primary compact, sintering or plastic working is performed on the primary compact to obtain a secondary compact, and then heat treatment is performed on the secondary compact.例文帳に追加

希土類含有磁性粉末の界面にフラーレンまたは化学修飾フラーレンのうちの少なくとも１つからなる絶縁被膜を形成し、該磁性粉末を磁場中成形または高密度化させて一次成形体を得、該一次成形体を焼結または塑性加工して二次成形体を得、最後に二次成形体を熱処理する。 - 特許庁

The method for manufacturing the composite material composed of tourmaline and silicon oxide comprises hydrolysing tetraethoxysilane with a basic catalyst, obtaining a polymeric primary condensation product by sol-gel reaction, mixing the primary condensation product with a fine powder of tourmaline, granulating, drying, and thereafter sintering at a temperature of 250-650°C.例文帳に追加

本発明の電気石と酸化ケイ素とからなる複合体の製造方法は、テトラエトキシシランを塩基性触媒の存在下に加水分解すると共に、ゾル−ゲル反応により高分子初期縮合物を得、該初期縮合物に電気石の微粉末を混合し、造粒し、乾燥した後、２５０℃から６５０℃までの温度で焼結することを特徴とする。 - 特許庁

The resin composition is produced by dispersing an inorganic filler into a matrix resin component, wherein the inorganic filler contains secondary sintering particles composed of primary particles of scale-like boron nitride having a mean long diameter of more than 0.1 μm and 5 μm or less and the secondary sintering particles have a porosity of 40% or less and a modulus of 40 MPa or more.例文帳に追加

無機充填材をマトリックス樹脂成分中に分散してなる樹脂組成物であって、 前記無機充填材は、０．１μｍ超過５μｍ以下の平均長径を有する鱗片状窒化ホウ素の一次粒子から構成される二次焼結粒子を含み、且つ前記二次焼結粒子は、４０％以下の気孔率及び４０ＭＰａ以上の弾性率を有することを特徴とする樹脂組成物とする。 - 特許庁

This heating treatment contains a primary stage (to the time T6) for removing the binder and a secondary stage (on and after the time T6) for sintering the metallic material powder, and, in the secondary stage, rapid heating is executed at the time of T6 to T7 at a temp. rising rate of ≥8°C/min.例文帳に追加

この加熱処理はバインダーの除去のための第１段階（時刻Ｔ_6 まで）と金属材料粉末の燒結のための第２段階（時刻Ｔ_6 以降）とを含んでおり、第２段階では時刻Ｔ_6 〜Ｔ_7 において８℃／分以上の昇温速度での急速加熱がなされる。 - 特許庁

A method for molding a ceramic powder comprises the steps of primary-molding a cylindrical molded body by extrusion molding a raw material before molding obtained by adding a sintering additive and a resin binder to the ceramic powder, secondary molding the cylindrical molded body by charging the body in a heated mold while being compressed and gradually cooled and then burning it.例文帳に追加

セラミックス粉末に焼結助剤と樹脂バインダーを添加した成形前原料を押出成形にて円筒成形体とした１次成形と、該円筒成形体を加熱した金型に装填し、圧縮しながら徐冷して２次成形を行った後、焼成することを特徴とするセラミックス粉末の成形方法を用いる。 - 特許庁

This method for manufacturing a ceramic substrate characteristically comprises forming an electric conductor on a surface or an inside of the substrate form, making the molded form containing ceramic powders into a primary sintered compact by sintering and then annealing the compact at 1,400-1,800°C.例文帳に追加

その表面または内部に導電体が形成されてなるセラミック基板の製造方法であって、セラミック粉末を含む成形体の焼成を行って一次焼結体を製造した後、上記一次焼結体に１４００〜１８００℃の温度範囲でアニーリング処理を施すことを特徴とするセラミック基板の製造方法。 - 特許庁

This semiconductor ceramic obtained by sintering a semiconductor material comprising a lanthanum oxide or compound, and a cobalt oxide is characterized by ≥3 m2/g specific surface area, ≤2.0 μm average particle diameter of primary particles and ≤10 μm average particle diameter of secondary particles of the semiconductor material.例文帳に追加

ランタン酸化物または化合物と、コバルト酸化物とを含む半導体材料を焼結させてなる半導体セラミックであって、前記半導体材料の比表面積が３ｍ^2／ｇ以上であり、一次粒子の平均粒径が２．０μｍ以下、かつ二次粒子の平均粒径が１０μｍ以下であることを特徴とする。 - 特許庁

In a gas thermal decomposition device comprising a thermal decomposition part 10 in which an electric resistance heat generating body heated in atmosphere insulated from oxygen to effect thermal decomposition of primary treatment gas, and a combustion part 40 to burn thermal decomposition gas generated by the thermal decomposition part 10, an electric resistance heat generating body is a non-sintering type.例文帳に追加

一次処理ガスを熱分解するために酸素を遮断した雰囲気で加熱する電気抵抗発熱体が配置された熱分解部と、該熱分解部で生成した熱分解ガスを燃焼する燃焼部とからなるガス熱分解装置において、該電気抵抗発熱体は非焼結型であることを特徴とする。 - 特許庁

The sputtering target is obtained by molding and sintering a conductive inorganic oxide powder having an average primary particle diameter of 3-40 nm, which is provided with conductivity by being doped with one or more components selected from aluminum, gallium and indium in an amount of 0.1-20.0 wt.% in terms of oxides.例文帳に追加

この目的を達成するため、アルミニウム、ガリウム及びインジウムから選択される１種又は２種以上の成分を酸化物換算で０．１ｗｔ％〜２０．０ｗｔ％ドーピングして導電性を付与した、平均１次粒子径が３ｎｍ〜４０ｎｍの導電性無機酸化物粉を成形して焼結したスパッタリングターゲットとする。 - 特許庁

The manufacturing method of rare earth sintered magnet comprises the steps of inputting particles formed of a primary alloy particles of the predetermined composition and an organic solution, obtaining a molding body by impressing a magnetic field to the particles for pressure molding, and sintering the molding body.例文帳に追加

本発明の希土類焼結磁石の製造方法は、所定組成の一次合金粒子と有機液体で構成された顆粒を金型キャビティに投入する工程と、顆粒に磁場を印加し、かつ加圧成形することにより成形体を得る工程と、成形体を焼結する工程と、を備えることを特徴としている。 - 特許庁

The translucent alumina sintered compact having ≥60% all light transmittance in 600 nm measuring wavelength using a 1 mm thick sample is obtained by compacting alumina powder having ≥99.9% purity, 16-25 m^2/g specific surface area and 40-80% (based on number standard) primary particle having ≤0.1 μm particle diameter, primarily sintering and after that, hot-isostatic-press (HIP)-treating.例文帳に追加

純度９９．９％以上、比表面積が１６〜２５ｍ^２／ｇ、粒子径０．１μｍ以下の一次粒子が４０〜８０％（個数基準）のアルミナ粉末を、成型、一次焼結した後に熱間静水圧プレス（ＨＩＰ）処理することにより、測定波長６００ｎｍ、試料厚さ１ｍｍにおける全光線透過率が６０％以上の透光性アルミナ焼結体を得る。 - 特許庁