「Powder diffraction」に関連した英語例文の一覧と使い方(3ページ目) - Weblio英語例文検索

A part of a lightweight cellular concrete panel to be diagnosed is sampled and a repairing method is determined depending on a degree of carbonation or a degradation level determined by powder X-ray diffraction method, surface finish and a desired use years of the lightweight cellular concrete panel.例文帳に追加

診断する軽量気泡コンクリートパネルの一部を採取して、炭酸化度あるいは粉末Ｘ線回折法により得た劣化レベル、該軽量気泡コンクリートパネルの表面仕上げ、および希望使用年数に応じて、補修・改修方法を決定する。 - 特許庁

This is an electrode material for lithium secondary battery which consists of a powder containing Si as a main component and of which the surface interval in (111) face of Si by X-ray diffraction is in a range 3.15 Å or more and 3.20 Å or less.例文帳に追加

Ｓｉを主成分として含有する粉末からなり、Ｘ線回折によるＳｉの（１１１）面の面間隔が３．１５Å以上３．２０Å以下の範囲であることを特徴とするリチウム二次電池用電極材料を採用する。 - 特許庁

The solid crystalline atorvastatin hemi-calcium or the solvate thereof is characterized in that an atorvastatin hemi-calcium form V is collected from the mixture with water and 1-butanol and has a powder X-ray diffraction pattern which has peaks in 9.3 and 9.5±0.2 degrees 2θ.例文帳に追加

アトルバスタチンヘミカルシウム形態Ｖを、１−ブタノールとの水の混合物から回収した、９．３および９．５±０．２度２θにピークを有する粉末Ｘ線回折パターンによって特徴付けられる固体結晶アトルバスタチンヘミカルシウム又はその溶媒和物。 - 特許庁

The high-modulus carbon fiber has ≥1,000Å spread La in the a-axis direction of a graphite crystal obtained from a powder X-ray diffraction spectrum, >104 ton/mm^2 tensile modulus and ≥15 μm fiber diameter.例文帳に追加

粉末Ｘ線スペクトルから求めた、黒鉛結晶のａ軸方向の広がりＬａが１０００Å以上であって、引張弾性率が１０４ｔｏｎ／mm^２より大きく繊維径が、１５μｍ以上であることを特徴とする高弾性率炭素繊維。 - 特許庁

The powder X-ray diffraction diagram is measured by using an X'Celerator detector and a PANalytical X' Pert Pro diffracting device and the diagram is represented by items of ray position, ray height, ray range, ray width in half height and face-to-face dimension.例文帳に追加

Ｘ’Ｃｅｌｅｒａｔｏｒ検出器とともにＰＡＮａｌｙｔｉｃａｌ Ｘ’Ｐｅｒｔ Ｐｒｏ回折装置を用いて測定され、光線位置、光線高、光線範囲、半分の高さにおける光線幅および面間距離の項目で表される。 - 特許庁

This readily water-soluble and stable pharmaceutical composition containing conivaptane hydrochloride crystal as the active ingredient is characterized by having the most intense peak near the interplanar spacing 7.82 in the powder X-ray diffraction spectrum thereof given by the use of Cu-Kα rays.例文帳に追加

Ｃｕ−Ｋα線を使用して得られる粉末Ｘ線回折スペクトルにおいて格子間隔７．８２付近に最も強いピークを有することを特徴とする塩酸コニバプタンの結晶を有効成分とする水易溶性且つ安定性医薬組成物。 - 特許庁

The medicine comprises a crystal of a 1-methyl carbapenem compound represented by formula (I) or its pharmaceutically permissible salt as an active ingredient exhibits a specific main peak in a powder X-ray diffraction obtained by irradiation with copper K_α ray.例文帳に追加

銅のＫ_α線の照射で得られる粉末Ｘ線回折において、特定の主ピークを示すことを特徴とする式（Ｉ）で表される１−メチルカルバペネム化合物又はその薬理上許容される塩の結晶を有効成分として含有する医薬。 - 特許庁

A hydrated crystal form of (±)-cis-FTC (that is, racemic cis-FTC) which is distinguishable from other form of FTC by its powder X-ray diffraction pattern, heat characteristic and production methods in a similar way, and a dehydrated form of the hydrate are also provided.例文帳に追加

同様にＸ線粉末回折パターン、熱特性、および製造の方法によって、ＦＴＣの他の型と区別することができる、（±）−シス−ＦＴＣの水和した結晶型（すなわちラセミ体のシス−ＦＴＣ）、およびこの水和物の脱水された型も提供する。 - 特許庁

The surface of particles of nickel hydroxide powder is coated with the β-type cobalt hydroxide wherein the half-width obtained from the face (101) by X-ray diffraction is not less than 0.229° and not more than 0.851° or in which the crystallite diameter is not less than 100 Å and not more than 450 Å.例文帳に追加

Ｘ線回折において（１０１）面より求めた半価幅が０．２２９°以上０．８５１°以下、あるいは結晶子径が１００Å以上４５０Å以下であるβ型水酸化コバルトにより、水酸化ニッケル粉末の粒子の表面を被覆する。 - 特許庁

The production method for a crystal polymorphism A (Fig.1: X-ray powder diffraction pattern) of a pitavastatin hemicalcium salt (formula) comprises allowing a sodium salt of pitavastatin to react with CaCl_2 in an aqueous reaction medium, separating a formed crystal, and drying it so that the water content is adjusted to 3-12%.例文帳に追加

ピタバスタチンのナトリウム塩とＣａＣｌ_2とを水性反応媒体中で反応させ、生成した結晶を分離し、乾燥して含水量を３〜１２％に調節する、ピタバスタチンヘミカルシウム塩（下式）の結晶多形Ａ（図１：Ｘ線粉末回折図形）の製造方法。 - 特許庁

A solid phase of amorphous (-)-FTC and (-)-cis-FTC called II and III(-)-cis-FTC which is distinguishable from I(-)-cis-FTC by its powder X-ray diffraction pattern, heat characteristic and production methods is provided.例文帳に追加

Ｘ線粉末回折パターン、熱特性、および製造の方法によってＩ型（−）−シス−ＦＴＣと区別することができ、ここでは非晶質（−）−ＦＴＣおよびＩＩおよびＩＩＩ型（−）−シス−ＦＴＣ）と呼ばれる（−）−シス−ＦＴＣの固相を提供する。 - 特許庁

A β type crystal and a γ type crystal of 4-amino-5-chloro-2-ethoxy-N-[[4-(4-fluorobenzyl)-2-morpholinyl]methyl]benzamide-citrate which are characterized by a powder x-ray diffraction pattern and/or a differential scanning calorimetric analysis thermogram, and are stable at the room temperature are disclosed.例文帳に追加

粉末Ｘ線回折パターン及び／又は示差走査熱量分析サーモグラムで特徴付けられ、室温で安定な、４−アミノ−５−クロロ−２−エトキシ−Ｎ−［［４−（４−フルオロベンジル）−２−モルホリニル］メチル］ベンズアミド・クエン酸のβ型結晶及びγ型結晶。 - 特許庁

The gallium oxide powder having a (D90-D10)/D50 value of 1.00-1.50 is provided in D10, D50 and D90 by volume standard particle size distribution obtained by measuring by a laser diffraction scattering-type particle-size distribution measuring method.例文帳に追加

レーザー回折散乱式粒度分布測定法により測定して得られる体積基準粒度分布によるＤ１０、Ｄ５０及びＤ９０において、（Ｄ９０−Ｄ１０）／Ｄ５０の値が１．００〜１．５０であることを特徴とする酸化ガリウム粉末を提案する。 - 特許庁

The binder for a glass chopped strand mat comprises a polyester resin powder (A) having a volume-average particle diameter Dv of 280-350 μm and a coefficient Cv of variation of volume-based particle diameter distribution of 10-35% as measured by the laser diffraction scattering method.例文帳に追加

レーザー回折散乱法による体積平均粒子径Ｄｖが２８０〜３５０μｍであり、体積基準の粒子径分布の変動係数Ｃｖが１０〜３５％であるポリエステル樹脂粉末（Ａ）を含有してなることを特徴とするガラスチョップドストランドマット用バインダー。 - 特許庁

The TMPB substance of the present invention is a crystal of 2-methyl-2-triazolylmethylpenam-3-carboxylic acid 1,1dioxidodiphenylmethyl ester having peaks in lattice face intervals in X-ray diffraction pattern of powder obtained with copper radioactive ray of λ=1.5418 angstrom passed through a monochromater.例文帳に追加

本発明のＴＡＺＢ結晶は、モノクロメーターを通したλ＝１．５４１８Åの銅放射線で得られるＸ線粉末回折パターンで格子面間隔にピークを有する２−メチル−２−トリアゾリルメチルペナム−３−カルボン酸１，１−ジオキシドジフェニルメチルエステルの結晶である。 - 特許庁

The product proves to be a crystal by powder X-ray diffraction and gives a maximum endothermic peak at a temperature of 180°C or higher by DST to prove to be a uniform crystalline α-lipoic acid lysine salt in its chemical composition and crystalline shape.例文帳に追加

生成物は粉末Ｘ線回折により結晶であることを示し、ＤＳＴにおいて１８０℃以上の温度において最大吸熱ピークを示し、化学組成および結晶形態において均一な結晶性α−リポ酸リジン塩であることが証明された。 - 特許庁

The TMPB substance of the present invention is a crystal of 2-methyl-2-triazolylmethylpenam-3-carboxylic acid diphenylmethyl ester having peaks in lattice face intervals in X-ray diffraction pattern of powder obtained with copper radioactive ray of λ=1.5418 angstrom passed through a monochromater.例文帳に追加

本発明のＴＭＰＢ結晶は、モノクロメーターを通したλ＝１．５４１８Åの銅放射線で得られるＸ線粉末回折パターンで格子面間隔にピークを有する２−メチル−２−トリアゾリルメチルペナム−３−カルボン酸ジフェニルメチルエステルの結晶である。 - 特許庁

Moreover, the compositions having a powder X-ray diffraction pattern comprising at least three peaks with 2θ angles selected from about 18.2, 28.5, 29.5, 33.7, 41.2, 47.4, and 56.2 and a solid state ^23Na MAS NMR spectra peak at about 18 ppm.例文帳に追加

約１８．２、２８．５、２９．５、３３．７、４１．２、４７．４、および５６．２から選択される２θ角を有する少なくとも三つのピークを含有する粉末Ｘ線回折パターンおよび約１８ｐｐｍにおいて固体状態^２３Ｎａ ＭＡＳ ＮＭＲスペクトルピークを有する。 - 特許庁

The photosensitive silver paste is a photosensitive electrically conductive resin paste comprising an alkali-soluble resin, a crosslinkable monomer having an unsaturated double bond, a photopolymerization initiator, silver powder, glass frit, calcium carbonate having 0.01-1 μm average particle diameter measured by a laser diffraction method and an organic solvent.例文帳に追加

アルカリ可溶性樹脂、不飽和二重結合を有する架橋性モノマー、光重合開始剤、銀粉、ガラスフリット、平均粒径がレーザー回折法による測定で０．０１〜１μｍである炭酸カルシウム、有機溶剤からなる感光性の導電性樹脂ペーストである。 - 特許庁

Requirement (1): Carbon powder obtained by subjecting the binder (B), which can be graphitized, to graphitization treatment has a spacing (d002) on the 002 face by the X-ray wide-angle diffraction method of 0.3357 nm or greater and 0.34 nm or less, and an Lc (004) of 10 nm or greater and 500 nm or less.例文帳に追加

条件（１）：黒鉛化可能なバインダー（Ｂ）を黒鉛化処理して得られた炭素粉末のＸ線広角回折法による００２面の面間隔（ｄ００２）が０．３３５７ｎｍ以上０．３４ｎｍ以下、且つＬｃ（００４）が１０ｎｍ以上５００ｎｍ以下である。 - 特許庁

To provide a method for early determining whether there is a risk of occurrence of the delayed formation of ettringite after service by powder X-ray diffraction, in a cured article using a cement composition such as concrete or mortar receiving high-temperature ageing at the initial stage of hydration.例文帳に追加

水和初期に高温養生を受けたコンクリート、モルタル等のセメント組成物を用いた硬化物において、供用後生じる恐れがあるエトリンガイトの遅延生成の発生有無を粉末Ｘ線回折によって早期に判定する方法を提供する。 - 特許庁

In an iron-nitride magnetic powder which consists of particles that are mainly composed of a Fe_16N_2 phase and whose average particle size is 20 nm or smaller, TAP density is 0.75 g/cm^3 or below and a nitriding rate calculated from an X-ray diffraction pattern is 70 to 100%.例文帳に追加

Ｆｅ_16Ｎ_2相主体の粒子からなる平均粒子径２０ｎｍ以下の粉末において、ＴＡＰ密度が０.７５ｇ／ｃｍ^3以下、かつＸ線回折パターンから算出される窒化率が７０〜１００％であることを特徴とする窒化鉄系磁性粉末。 - 特許庁

By a powder X-ray diffraction analysis, FeYO_3 and/or AlYO_3 are identified as the perovskite type oxide, and at least a species selected from among Y_3Al_5O_12, Al_2Fe_3Y_3O_12, and Al_3Fe_2Y_3O_12 is identified.例文帳に追加

粉末Ｘ線回折分析により、上記ペロブスカイト型酸化物として、ＦｅＹＯ_３及び／又はＡｌＹＯ_３が同定され、上記ガーネット型酸化物として、Ｙ_３Ａｌ_５Ｏ_１２、Ａｌ_２Ｆｅ_３Ｙ_３Ｏ_１２及びＡｌ_３Ｆｅ_２Ｙ_３Ｏ_１２から選ばれる少なくとも１種が同定される。 - 特許庁

The agrochemical composition comprises a crystal of 1-(N,N-dimethylsulfamoyl)-3-[2-methyl-3-bromo-6-fluoroindol-1-yl]sulfonyl-1,2,4-triazole having peaks at 2θ=8.08, 14.68, 16.20, 18.74, 21.06, 24.76 and 26.44 in powder X-ray diffraction.例文帳に追加

粉末Ｘ線回折において２θ＝８．０８、１４．６８、１６．２０、１８．７４、２１．０６、２４．７６および２６．４４にピ−クを有する1−（Ｎ，Ｎ−ジメチルスルファモイル）−3−〔2−メチル−3−ブロム−6−フルオロインド−ル−1−イル〕スルホニル−1，2，4−トリアゾ−ルの結晶を含有する農薬組成物。 - 特許庁

There are provided type II crystals and type I crystals of (±)2-(dimethylamino)-1-{[O-(m-methoxyphenetyl)phenoxy]methyl}ethyl hydrogen succinate hydrochloride characterized by at least one physicochemical property selected from a specific diffraction peak in X-ray powder diffraction spectrum, a specific endothermic peak in differential scanning calorimetry, a specific peak in solid ^13C-NMR spectrum, and a specific peak in infrared absorption spectrum.例文帳に追加

粉末Ｘ線回折スペクトルにおける特定の回折ピーク、示差走査熱量測定における特定の吸熱ピーク、固体^１３Ｃ−ＮＭＲスペクトルにおける特定のピーク及び赤外吸収スペクトルにおける特定のピークから選ばれる少なくとも１種の物理化学的性質により特徴付けられる、（±）２−（ジメチルアミノ）−１−{〔Ｏ−（ｍ−メトキシフェネチル）フェノキシ〕メチル}エチル水素サクシナート塩酸塩のII形結晶及びI形結晶。 - 特許庁

The toner includes toner particles consisting of a binder resin and a colorant and fine powder of magnesium oxide, in which the fine powder exhibits an absorption moisture content of a specific range at relative humidity 95% in an adsorption process of its moisture adsorption/desorption isothermal line and has a peak in specific Bragg angle in its CuKα characteristic X-ray diffraction and the half width of the peak is below the specific value.例文帳に追加

結着樹脂および着色剤からなるトナー粒子と酸化マグネシウム微粉末とを含むトナーにおいて、該微粉末が、その水分吸・脱着等温線の吸着過程における相対湿度９５％で特定の範囲の吸収水分量を示し、かつそのＣｕＫα特性Ｘ線回折における特定のブラッグ角でピークを有し、該ピークの半値幅が特定の値以下である。 - 特許庁

The dielectric powder containing titanium, having a crystal structure of a perovskite, and having an average particle size of not greater than 1 μm has a ratio c/a of a c-axis lattice parameter to an a-axis lattice parameter by X-ray diffraction of not less than 1.009, and particularly includes a group 2a element of the periodic table.例文帳に追加

チタンを含有し、結晶構造がペロブスカイトからなり、平均結晶粒子径が１μｍ以下の誘電体粉末において、Ｘ線回折によるｃ軸の格子定数とａ軸の格子定数の比ｃ／ａが１．００９以上であり、特に、周期律表第２ａ族元素を含む。 - 特許庁

The low magnetic black pigment powder is a mixed-phase crystalline, having a rutile-type TiO2 phase as a base, wherein the base is characterized by a particle structure covered with Fe2TiO4 phase, and having a peak of Fe2TiO4 with the rutile-type TiO2 as a main peak in X-ray diffraction.例文帳に追加

本発明に関わる低磁性黒色顔料粉末は、ルチル型ＴｉＯ_2相を基体とし、該基体がＦｅ_2ＴｉＯ_4相で被覆された粒子構造を特徴とし、Ｘ線回折においてルチル型ＴｉＯ_2をメインピ−クとして、Ｆｅ_2ＴｉＯ_4のピ−クを含む混合相結晶である。 - 特許庁

This aripiprazole anhydrous crystal exhibits the same ^1H-NMR spectrum as that shown in, e.g. Fig. 9, the same powder X-ray diffraction spectrum as that shown in Fig. 10 and the same IR (KBr) spectrum as that shown in Fig. 11.例文帳に追加

本発明のアリピプラゾール無水物結晶は、例えば図９に示される^1Ｈ−ＮＭＲスペクトルと同じ^1Ｈ−ＮＭＲスペクトル、図１０に示される粉末Ｘ線回析スペクトルと同じ粉末Ｘ線回析スペクトル、図１１に示されるＩＲ（ＫＢｒ）スペクトルと同じＩＲスペクトルを示す。 - 特許庁

This aripiprazole anhydrous crystal exhibits the same 1H-NMR spectrum as that shown in, e.g. Fig. 2 (refer to the specification), the same powder X-ray diffraction spectrum as that shown in Fig. 3 (refer to the specification) and the same IR (KBr) spectrum as that shown in Fig. 4 (refer to the specification).例文帳に追加

本発明のアリピプラゾール無水物結晶は、例えば図２に示される１Ｈ−ＮＭＲスペクトルと同じ１Ｈ−ＮＭＲスペクトル、図３に示される粉末Ｘ線回析スペクトルと同じ粉末Ｘ線回析スペクトル、図４に示されるＩＲ（ＫＢｒ）スペクトルと同じＩＲスペクトルを示す。 - 特許庁

The invention relates to an ε-type crystal of N-benzyl-N-ethyl-2-(7-methyl-8-oxo-2-phenyl-7, 8-dihydro-9H-purin-9-yl) acetamide identified by powder X-ray diffraction pattern and/or differential scan calorimetric analysis thermogram, and having an excellent heat stability, etc.例文帳に追加

粉末Ｘ線回折パターンおよび／または示差走査熱量分析サーモグラムで特定され、優れた熱安定性などの性質を有する、Ｎ−ベンジル−Ｎ−エチル−２−（７−メチル−８−オキソ−２−フェニル−７,８−ジヒドロ−９Ｈ−プリン−９−イル）アセトアミドのε型結晶。 - 特許庁

An area other than the crystal grain of a measuring object is coated thinly with an amorphous liquid material, an amorphous powder of high X-ray absorptivity is further applied thereto to be fixed, and only the crystal information about a specified crystal is thereby acquired by X-ray diffraction.例文帳に追加

測定対象である結晶粒以外の領域を非晶質の液状材料で薄く塗布して覆い、さらにＸ線吸収率が高い非晶質粉末を塗布して固着させて特定の結晶についての結晶情報のみをＸ線回折によって得る。 - 特許庁

The spherical alumina powder is characterized in that the ratio of the δ-phase peak intensity detected at 2θ=45.6° to the θ-phase peak intensity detected at 2θ=44.8°, (δ-phase peak intensity/θ-phase peak intensity), is ≥1.0 in X-ray diffraction, the average sphericity is ≥0.90, and the average particle diameter is ≤100 μm.例文帳に追加

Ｘ線回折において２θ＝４５．６°に検出されるδ相ピーク強度と２θ＝４４．８°に検出されるθ相ピーク強度の比、（δ相ピーク強度／θ相ピーク強度）が１．０以上である、平均球形度が０．９０以上、平均粒子径１００μｍ以下の球状アルミナ粉末。 - 特許庁

The powder for nanocarbon production for producing nanocarbon by plasma contains carbon and a metal and/or a metal compound and has, in a particle size distribution on a volume basis measured by a laser diffraction/scattering type particle size measurement method, a mode diameter of ≤10 μm.例文帳に追加

プラズマによりナノカーボンを製造するためのナノカーボン製造用粉末であって、炭素と、金属及び／又は金属化合物とを含み、且つ、レーザー回折散乱式粒子径測定法で測定した体積基準の粒度分布において、モード径が１０μｍ以下であることを特徴とする。 - 特許庁

The above object can be attained by preparing the silver powder for conductive paste having flaky particle shape, 3-8 μm laser diffraction 50% particle size, (0.4 to 1.1)/cm^3 apparent density and (1.5 to 4.0) m^2/g value of specific surface area by the BET method.例文帳に追加

上記の課題は、フレーク状の粒径を有し、レーザー回折法５０％粒径が３〜８μｍであり、見掛密度が０．４〜１．１／ｃｍ^3 であり、ＢＥＴ法比表面積値が１．５〜４．０ｍ^2 ／ｇであることを特徴とする導体ペースト用銀粉を調製することによって解決できる。 - 特許庁

The powder has a ratio of 20-micron or larger particles of lower than 5 wt.%, an average particle size of ≤5 microns and a degree of crystallinity, measured by X-ray diffraction, of ≤10 wt.% and comprises ellipsoidal particles of a length/breadth ratio of ≤3.例文帳に追加

２０ミクロン以上の粒子の割合が５重量％未満であり、平均粒径が５ミクロン以下で、かつ粒子の長径／短径比が３以下の楕円状粒子であり、Ｘ線回折による結晶化度が１０重量％以下であることを特徴とする非晶質セルロース微粉体を得ること。 - 特許庁

The α-crystalline form of strontium ranelate of formula (I) is characterized by its powder X-ray diffraction diagram and by a water content of from 22 to 24%, wherein the diagram is expressed by items of a ray position, a ray quantity, a ray range, a ray width in a half height, and a distance between faces.例文帳に追加

光線位置、光線高、光線範囲、半分の高さにおける光線幅および面間距離の項目で表わされる、粉末Ｘ線回析ダイヤグラムおよび２２〜２４％の水分含有量により特徴付けられる、式（Ｉ）：のストロンチウムラネレートのα−結晶形。 - 特許庁

The electroconductive resin paste contains, as essential components, a thermosetting resin (A) being liquid at room temperature and a silver powder (B) having a half width of a peak of X-ray diffraction of not greater than 0.26, where the total content of silver in the components is 68-94 wt.%, the semiconductor device is manufactured therewith.例文帳に追加

（Ａ）常温で液状である熱硬化性樹脂、（Ｂ）Ｘ線回折におけるピークの半価幅が0.26以下である銀粉を必須成分として、該成分中全銀含有率が６８〜９４重量％である導電性樹脂ペーストであり、それを用いて製造した半導体装置である。 - 特許庁

As for particularly a dihydrochloride hydrate of the compound, a pharmaceutical comprising the crystal exhibiting main peaks at spacings of 17, 7.1, 4.9, 4.3, 3.9 and 3.5 Å in a powder X-ray diffraction pattern obtained by exposure to Kα radiation of copper as the active ingredient is preferable.例文帳に追加

特に、該化合物の二塩酸塩水和物では、銅のＫα線の照射で得られる粉末Ｘ線回折図において、面間隔が１７、７．１、４．９、４．３、３．９、および、３．５オングストロームに主要なピークを示す結晶を有効成分として含有する医薬が好ましい。 - 特許庁

The sprayed coating is formed by thermal spraying of mixed powder of Cr_3C_2 and NiCr wherein the ratio of the peak area of the plane indices (012) of Cr_2O_3 to the peak area of the plane indices (121) of Cr_3C_2 in an X-ray diffraction chart is 2% or more and 16% or less.例文帳に追加

Ｃｒ_３Ｃ_２とＮｉＣｒとの混合粉末の溶射によって形成された溶射皮膜を、Ｘ線回折チャートにおける、Ｃｒ_３Ｃ_２の面指数（１２１）のピーク面積に対するＣｒ_２Ｏ_３の面指数（０１２）のピーク面積の割合が２％以上１６％以下となるようにする。 - 特許庁

The negative electrode material for a nonaqueous secondary battery includes a nitrogen-containing carbon compound containing 1 mass% or more and 20 mass% or less of nitrogen and having a graphite structure where a spacing on the d002 face measured by means of a powder X-ray diffraction method is 3.40 Å or more and 4.00 Å or less.例文帳に追加

１質量％以上２０質量％以下の窒素を含有し、粉末Ｘ線回折法により測定されるｄ００２面の間隔が３．４０Å以上４．００Å以下であるグラファイト構造を有する含窒素炭素化合物を含む非水系二次電池用負極材料とする。 - 特許庁

This invention relates to: novel salt forms of [R-(R^*,R^*)]-2-(4-fluorophenyl)-β,δ-dihydroxy-5-(1-methylethyl)-3-phenyl-4-[(phenylamino)carbonyl]-1H-pyrrole-1-heptanoic acid characterized by their X-ray powder diffraction pattern and solid-state NMR spectra; and methods for the preparation and pharmaceutical composition of the same.例文帳に追加

Ｘ線粉末回析パターンおよび固体ＮＭＲスペクトルにより特徴付けられる［Ｒ−（Ｒ^*，Ｒ^*）］−２−（４−フルオロフェニル）−β，δ−ジヒドロキシ−５−（１−メチルエチル）−３−フェニル−４−［（フェニルアミノ）カルボニル］−１Ｈ−ピロール−１−ヘプタン酸の新規な塩形態、ならびに、それらの製造方法および医薬組成物。 - 特許庁

Novel crystalline forms of [R-(R*,R*)]-2-(4-fluorophenyl)-β, Δ-dihydroxy-5-(1-methylethyl)-3-phenyl-4-[(phenylamino)carbonyl]-1H-pyrrole-1-heptanoic acid hemi calcium salt (atorvastatin) designed form X or form XII are characterized by their X-ray powder diffraction, solid-state NMR, and/or Raman spectroscopy.例文帳に追加

Ｘ型、またはXII型として示される、[R−(R^*,R^*)]−２−(４−フルオロフェニル)−β,Δ−ジヒドロキシ−５−(１−メチルエチル)−３−フェニル−４−[(フェニルアミノ)カルボニル]−１Ｈ−ピロール−１−ヘプタン酸ヘミカルシウム塩（アトロバスタチン）の新規結晶型が提供され、そのＸ線粉末回折、固体NMR、および／またはラマン分光法により特徴付けられた。 - 特許庁

A molding obtained by compressively molding rare-earth alloy powder or its sintered compact is equally divided into odd number of pieces, and X-ray diffraction processes are applied on the divided pieces of the center section and the outermost section, and then orientation degrees of respective divided pieces are calculated by using a Lotgering method, thereby evaluating variations in the orientation degrees.例文帳に追加

希土類合金粉末が圧縮成形された成形体またはその焼結体を奇数個に等分割し、中央部分の分割片と最外部の分割片についてＸ線回折を行った後、ロットゲーリング法により各分割片の配向度を算出して配向度のばらつきを評価する。 - 特許庁

The method for producing the fine barium titanate powder comprises the steps of mixing a barium compound which forms barium oxide by thermolysis with a titanium dioxide having a rutile content determined by X-ray diffraction of 30% or more and a specific surface area of 30 m^2/g or more and calcining the resulting mixture.例文帳に追加

加熱分解により酸化バリウムを生成するバリウム化合物と、Ｘ線回折法により求められるルチル化率が３０％以上、比表面積が３０ｍ^２／ｇ以上である二酸化チタンとを混合し、仮焼する工程を具備するチタン酸バリウム粉末の製法であることを特徴とする。 - 特許庁