「NON-OXIDATIVE」に関連した英語例文の一覧と使い方(2ページ目) - Weblio英語例文検索

The rare earth oxide coating film is obtained by heating and melting organic complex of rare earth elements having the non-degradable melting point such as 8-quinolinol, β-diketones and aromatic carboxylic acid as ligand under the atmosphere substantially not containing any steam or substantially not containing any oxygen, a coating film is formed of the molten liquid, and the coating film is heated and subjected to the oxidative decomposition.例文帳に追加

配位子として、８−キノリノール、β−ジケトン類、芳香族カルボン酸などの、非分解の融点を持つ希土類元素の有機錯体を、実質的に水蒸気を含まないかあるいは実質的に酸素を含まない雰囲気下で加熱溶融し、その融液によって皮膜を形成し、これを加熱して酸化分解することによって希土類酸化物皮膜を得る。 - 特許庁

The semiconductor film 3 formed on the substrate 2 is irradiated with laser light 21 in a non-oxidative processing atmosphere containing hydrogen gas 31 and while a temperature of the substrate 2 is held not higher than a fusion point, the semiconductor film 3 is heated to not lower than 1,000°C to be fused, and then solidified to crystallize the semiconductor film 3.例文帳に追加

水素ガス３１を含み且つ非酸化性の処理雰囲気中で基板２上に形成された半導体膜３にレーザ光１を照射し、基板２の温度を融点以下に保持したまま、半導体膜３を１０００℃以上に加熱して溶融させその後凝固させることにより、半導体膜３を結晶化させる。 - 特許庁

This method for recovering the CF in the CFRP is provided by pressurizing and heating a mixture of the CFRP and tetralin or decalin, further more preferably of the CFRP with tetralin and incorporated with a catalyst such as Na_2CO_3, CaCO_3, etc., as necessary under a non-oxidative gas atmosphere to decompose and remove the resin in the CFRP.例文帳に追加

ＣＦＲＰと、テトラリン又はデカリンとの混合物を、更に好ましくはＣＦＲＰと、テトラリンとの混合物を、また、必要に応じてＮａ_２ＣＯ_３、ＣａＣＯ_３等の触媒を追加した混合物を、非酸化性ガス雰囲気下、加圧・加熱してＣＦＲＰ中の樹脂を分解・除去するＣＦＲＰ中のＣＦの回収方法。 - 特許庁

Silicon carbide powder and water easily dispersible carbon black are dispersed in water, and a slurry of liquid dispersoid controlled at pH 6-11 is cast into a molding block and to burn the dried molded product in a silicon-intervened state in vacuum or in a non-oxidative atmosphere at ≥2,000°C.例文帳に追加

炭化珪素粉末と易水分散性カーボンブラックとを水中に分散させ、分散液のｐＨを６〜１１に調整したスラリーを成形型に注入して鋳込み成形し離型、乾燥した成形体を、珪素を介在させた状態で真空中あるいは非酸化性ガス雰囲気中２０００℃以上の温度で焼成する。 - 特許庁

The negative electrode for a lithium secondary battery is obtained by arranging a conductive middle layer 2 including a second binder 2b and conductive particles 2a, between a mixture layer 3 including an activator particle 3a including silicon and/or a silicon alloy and a first binder 3b, and a metal foil current collector 1, and baking it in the above state under a non-oxidative atmosphere.例文帳に追加

ケイ素及び／またはケイ素合金を含む活物質粒子３ａと第１のバインダー３ｂとを含む合剤層３と、金属箔集電体１との間に、第２のバインダー２ｂと導電性粒子２ａとを含む導電性中間層２を配置し、この状態で非酸化性雰囲気下に焼結して得られることを特徴とするリチウム二次電池用負極。 - 特許庁

The method for producing the bonded material comprises laminating a metal foil to a soldering alloy foil with an organic adhesive, sticking the outer surface of the laminated soldering alloy foil to at least one side of a ceramic substrate with an organic adhesive to give a laminate, and subjecting the laminate to a heat treatment step in a non-oxidative atmosphere with an oxygen concentration of 50 ppm or lower.例文帳に追加

金属箔とロウ材合金箔とを有機系接着剤を用いて張り合わせ、そのロウ材合金箔面をセラミックス基板の片面又は両面に有機接着剤を用いて張り合わせられてなる積層体を、酸素濃度５０ｐｐｍ以下の非酸化性雰囲気下で熱処理工程を経由させることを特徴とする接合体の製造方法である。 - 特許庁

The pollutants are subjected to oxidative chemical treatment to be converted into non hazardous substances in an in situ environment including at least one soil zone of an unsaturated zone and saturated zone by preparing a mixed aqueous solution containing ferrous sulfate, sodium citrate, and hydrogen peroxide, and having a pH range of 4-7 in a treatment vessel provided on the ground, and feeding the mixed aqueous solution into the in situ environment.例文帳に追加

地上に用意した処理槽内で、硫酸第一鉄、クエン酸ナトリウムおよび過酸化水素を含みｐＨ４〜７の範囲に混合水溶液を調製し、混合水溶液を原位置環境へ提供して、不飽和帯ないし飽和帯の少なくとも１つの地盤を含む原位置環境で汚染物質を無害な物質に化学酸化処理する。 - 特許庁

After a convex part is selectively formed on a flat plate by a convex part material in which disappearing fine particle polymer is further added to a flat plate material by using a mixture in which graphite powder and fibrous carbon are made to be homogeneously dispersed and compounded into a liquid composition of a thermoset resin as a material of a flat plate, it is baked in an inert atmosphere, non-oxidative atmosphere, or vacuum.例文帳に追加

熱硬化性樹脂の液状組成物に黒鉛粉末及び繊維状炭素を均一に分散複合させた混合物を平板の材料として、平板材料にさらに消失性微粒子ポリマーを加えた凸部材料により平板の上に選択的に凸部を形成した後、不活性雰囲気中、非酸化性雰囲気中、又は真空中で焼成する。 - 特許庁

The method for manufacturing the steel having the ultrafine grains comprises the steps of: adding an appropriate amount of a bonding agent to an iron powder having a nanocrystal structure; compacting the mixture to produce a cold compact having a predetermined shape; heating it to a warm or hot temperature, specifically, to 700°C or lower in a non-oxidative atmosphere in the state; and then immediately extruding it.例文帳に追加

ナノ結晶組織を付与された鉄鋼粉末に適量の結合剤を添加して所定形状に成形した冷間成形体を作製し、これをそのまま非酸化性雰囲気で温間あるいは熱間の温度、具体的には７００℃以下の温度に加熱した後、直ちに押し出し加工を施すことにより固化成形することを特徴とする。 - 特許庁

The mold for molding quartz glass comprises a glassy carbon material and is obtained by molding a thermosetting resin material into a predetermined shape at a temperature lower than the thermosetting temperature of the resin material, thermosetting the molded resin material, and baking the thermally set resin material at 1,300-2,200°C in a non-oxidative atmosphere.例文帳に追加

ガラス状カーボン材からなることを特徴とする石英ガラス成形用型を用い、また、その石英ガラス成形用型は、熱硬化性を有する樹脂材料を用いて、該樹脂材料の熱硬化温度よりも低温で、所定の形状の型を形成した後、熱硬化させ、次いで、非酸化性雰囲気中で、１３００℃以上２２００℃以下で焼成することにより得られる。 - 特許庁

The method for manufacturing an optical element includes: a heat treating process (A) for heating a bismuth-based optical material, while floating it by non-oxidative gas flow, to thereby evaporate and remove bismuth contained in the optical material; and a molding process (B) for press-molding the heat-treated bismuth-based optical material to have a prescribed shape by using a mold.例文帳に追加

光学素子の製造方法は、ビスマス系光学素材を非酸化性ガス流により浮上させつつ加熱して、光学素材に含まれるビスマスを揮発除去する熱処理工程（Ａ）と、熱処理したビスマス系光学素材を成形型を用いて所定の形状にプレス成形する成形工程（Ｂ）とを含む。 - 特許庁