「weld toe」に関連した英語例文の一覧と使い方 - Weblio英語例文検索

To control any loss of the compressive residual stress introduced in a weld toe by the peening treatment while using a structure having a weld joint of a steel member.例文帳に追加

鋼部材の溶接継手を有する構造物の使用中に、ピーニング処理により溶接止端部に導入した圧縮残留応力が喪失することを抑制する。 - 特許庁

To provide a high-tensile strength steel weld joint having excellent resistivity to the generation of ductile cracks from a weld zone, particularly, from a weld toe, and suitably used for the field of ground structures such as bridges and buildings subjected to an earthquake load.例文帳に追加

溶接部、なかでも溶接止端部からの延性き裂発生に対する抵抗性に優れ、地震負荷を受ける橋梁や建築などの地上構造物分野に用いて好適な高張力鋼溶接継手の提供。 - 特許庁

Plastic working in excess weld metal toe part 7a on the upper face of the rail bottom in a thermit weld zone 2 of a rail 1 increases hardness, yield strength and tensile strength in the excess plastically worked weld metal toe part 7a as a result of work hardening and, imparts compressive residual stress, resulting in improved fatigue strength of the thermit weld zone.例文帳に追加

レール１のテルミット溶接部２のうち、レール底部上面の余盛止端部７ａに、塑性加工を施すことにより、この塑性加工を施された余盛止端部７ａが加工硬化によって、硬度、降伏強度、引張強さが増大し、さらに圧縮残留応力が付与されるので、テルミット溶接部の疲労強度が向上する。 - 特許庁

The fatigue characteristic is controlled by measuring Cr and Ni components in the welded metal forming the toe part of the weld.例文帳に追加

溶接止端部を形成する溶接金属のＣｒ、Ｎｉ成分を測定することにより疲労特性を管理する。 - 特許庁

To reduce stress concentration on a weld part of a round drum, particularly on its toe position, due to load when a construction machine is operated.例文帳に追加

建設機械の作動時における負荷による丸胴の溶接部、特にその止端位置への応力の集中を低減させるようにする。 - 特許庁

To provide a fillet arc welding method of a thin steel sheet, in which a weld toe shape is excellent even in the case of a welding speed of >80 to ≤150 cm/min and fatigue characteristic of a weld joint can be enhanced.例文帳に追加

溶接速度８０ｃｍ／ｍｉｎ超１５０ｃｍ／ｍｉｎ以下でも、溶接止端部形状が良好で、溶接継手の疲労特性を向上させることのできる、薄鋼板の隅肉アーク溶接方法を提供する。 - 特許庁

A peened part 20 by the ultrasonic oscillation is formed in a weld toe part 14 of each rib 12 which is Tee-welded to a base part of a steel column 10.例文帳に追加

鋼管柱１０の基部にＴ字溶接された各リブ１２の溶接止端部１４に、超音波振動によるピーニング処理部２０を形成する。 - 特許庁

In the edge face of the welded joint, plastic deformation is applied at least to weld toe parts or at least to both the edge parts in exposed roots.例文帳に追加

溶接継手の端面において、少なくとも溶接止端部或いは、少なくとも露出したルートの両端部に塑性変形を与えるものである。 - 特許庁

To provide a method for enhancing the fatigue performance of a weld joint by relieving the stress concentration at a toe and a non-welded part of the weld joint having the non-welded part, and controlling the residual stresses.例文帳に追加

本発明は、不溶着部を持つ溶接継手の止端部および不溶着部の応力集中を解放し、残留応力を制御する処理を施し、溶接継手の疲労性能を改善する方法を提供するものである。 - 特許庁

A part of a surface of a base material distant from a toe of weld is pressed normally to the surface of the base material, preferably, a part of plastically deformed zones is moved gradually to the outer side from the side in a vicinity of the toe so as to overlap each other, and subjected to plastic deformation to introduce the compressive residual stress in the toe.例文帳に追加

溶接止端部から離れた母材表面の一部を、母材表面に対して垂直に加圧、好ましくは塑性変形領域をその一部が重なるように止端部近傍側から漸次外側に移動させるように加圧して塑性変形させ、溶接止端部に圧縮の残留応力を導入する。 - 特許庁

A residual stress distribution corresponding to the welded joint form and a weld toe processing condition is extracted from the database, and the shape parameter of the member and the weld bead, a material property and a weld condition are input into the residual stress distribution, and a residual stress distribution of the plate thickness cross section 41 of the longitudinal face 21 is calculated.例文帳に追加

溶接継手形式及び溶接止端処理条件に対応する残留応力分布をデータベースから抽出し、その残留応力分布に、部材と溶接ビードの形状パラメータ、材料物性、及び溶接条件を入力し、ロンジフェイス２１の板厚断面４１の残留応力分布を算定する。 - 特許庁

In the case of the joint in which the correction is performed to the welding deformation, after completing the correction to the welding deformation, the welded metal existing in the prescribed component range is formed at the toe part of the weld as the additional bead and residual stress is reduced by utilizing deforming-expansion of the additional bead as the new toe part of the weld and then, the fatigue resistance is improved.例文帳に追加

溶接変形矯正を実施する継手の場合で、変形矯正終了後所定の成分範囲内にある溶接金属を付加ビードとして止端部に形成させ新たな溶接止端部としその付加ビードが変態膨張することを利用し残留応力を低減させることにより疲労強度を向上させる。 - 特許庁

Further, the plasma welding torch 14, while moving with the MAG welding torch 12 in the direction of the arrow A, melts the toe of the weld bead (border including the periphery between the surface of the weld bead and the surface of the first metallic plate 18 to be welded).例文帳に追加

また、プラズマ溶接トーチ１４は、ＭＡＧ溶接トーチ１２と共に矢印Ａ方向に移動しながら、溶接ビードの止端部（溶接ビードの表面と第１被溶接金属１８の表面との境界及びその周辺部分）を溶融する。 - 特許庁

To provide a base part of a steel column in which the strength in the vicinity of a weld toe of a rib is not reduced when bending moment is repeatedly applied, and a reinforcing method therefor.例文帳に追加

繰返し曲げモーメントが作用した場合においてもリブの溶接止端部付近の強度低下がない鋼管柱基部及び鋼管柱基部の強化方法を提供する。 - 特許庁

To provide a method of a laser peening treatment, which method can improve fatigue property than before under the circumstances of repeated loads by efficiently introducing compressive residual stresses into weld toe portions of a weld structure and plastically deformed regions of a formed product.例文帳に追加

溶接構造物の溶接止端部や成形加工部品の塑性変形領域に圧縮残留応力を効率的に導入し、繰り返し荷重が作用する環境で従来よりも疲労特性を向上させるためのレーザピーニング処理方法を提供する。 - 特許庁

To provide a method for the ultrasonic impact treatment improving the fatigue characteristic under the environment of the cyclic load by efficiently introducing a large residual compressive stress to a residual tensile stress generated in a weld toe of a butt weld joint.例文帳に追加

突合せ溶接継手の溶接止端部に生じた引っ張り残留応力に対して大きな圧縮残留応力を効率的に導入し、繰り返し荷重が作用する環境で従来よりも疲労特性を向上させるための超音波打撃処理法を提供する。 - 特許庁

The stress concentration at the end face and the toe is reduced by providing the plastic deformation in the end, and smoothing the shape of the surface of the weld joint 1, and the compressive residual stress is provided.例文帳に追加

また、当該端部において塑性変形を与え、溶接継手１表面の形状を平滑にして、端面および止端の応力集中を低減すると共に圧縮残留応力を与える。 - 特許庁

To prevent stress concentration from occurring at the portion where corner parts are formed at right angle to each of the bottom tip end part of a columnar base material and the toe part on the groove side face of a beam base material and where a defect such as an undercut is caused therein, in a weld toe part bead that is formed using the conventional end tab.例文帳に追加

従来型のエンドタブを用いて形成される溶接止端部ビードにおいて、柱母材底面先端部および梁母材開先側面止端部の双方に直角な隅角部が各々形成され、それらの部分にアンダカット等の欠陥が生じた場合に、その部分に応力集中が生じることを防止する。 - 特許庁

The fillet welding joint with high fatigue strength is characterized in that, in the fillet welding joint in which at least one steel sheet is 1-4 mm thick, (a) the martensitic volume % of the weld metal is 50% or above and (b) the angle of the weld toe formed on the steel sheet surface is 110-150°.例文帳に追加

少なくとも一方の鋼板の板厚が１〜４ｍｍの隅肉溶接継手において、（ａ）溶接金属中のマルテンサイトの体積率が５０％以上であり、かつ、（ｂ）上記鋼板面に形成された溶接止端部の角度が１１０〜１５０°であることを特徴とする高疲労強度隅肉溶接継手。 - 特許庁

An inverted U-shaped or inverted V-shaped rib 12 with an upper end part 14 thereof bent is Tee-type welded to the base part of the steel column 10 and a peened part 20 by the ultrasonic oscillation is formed on the weld toe of each rib 12.例文帳に追加

鋼管柱１０の基部に上端部１４が屈曲された逆Ｕ字状または逆Ｖ字状のリブ１２をＴ字溶接するとともに、各リブ１２の溶接止端部に、超音波振動によるピーニング処理部２０を形成する。 - 特許庁

Steel which restrains at least one of the initiation and progress of a fatigue crack is used as at least one of a web and a flange of an I-girder or a box girder jointed by welding in the steel structure, and reinforcement is performed against the fatigue of the toe of a weld part by toe grinding, pinning, using a low-temperature transformation hot charge, or the like.例文帳に追加

鋼構造物において、溶接による接合がなされるＩ桁または箱桁の、ウエブとフランジの少なくとも一方に、疲労亀裂の発生と進展の少なくとも一方を抑制する鋼材を用い、止端研削、ピンニング、低温変態溶材の使用等による溶接部止端の疲労に対する強化をしてなることを特徴とする。 - 特許庁

In a UOE steel tube manufacturing method in which a steel plate is successively subjected to C-forming, U-forming and O-forming, end portions of the steel plate are seam-welded to each other, and a tube is expanded, at least a seam-weld toe portion before the expansion is subjected to peening by the ultrasonic vibration.例文帳に追加

鋼板を順にＣ成形、Ｕ成形、Ｏ成形し、鋼板の端部同士をシーム溶接後、拡管するＵＯＥ鋼管の製造方法において、拡管前の少なくともシーム溶接止端部に超音波振動によるピーニング処理を施す。 - 特許庁

In a UOE steel tube manufacturing method in which a steel plate is successively subjected to C-forming, U-forming, and O-forming, end portions of the steel plate are seam-welded to each other, and a tube is expanded, at least a seam-weld toe portion after the expansion is subjected to peening by the ultrasonic vibration.例文帳に追加

鋼板を順にＣ成形、Ｕ成形、Ｏ成形し、鋼板の端部同士をシーム溶接後、拡管するＵＯＥ鋼管の製造方法において、拡管後の少なくともシーム溶接止端部に超音波振動によるピーニング処理を施す。 - 特許庁

Provided that σ_eqt is the evaluation stress, σ_top is the stress of the weld toe side metal plate surface on the shared node position, and σ_btm is the stress of the metal plate surface on the opposite side of σ_top.例文帳に追加

σ_ｅｑｔ＝（σ_ｔｏｐ＋σ_ｂｔｍ）／２＋（σ_ｔｏｐ−σ_ｂｔｍ）／４、但し、σ_ｅｑｔは評価応力でσ_ｔｏｐは共有節点位置で、溶接止端部側の金属板表面の応力、σ_ｂｔｍはσ_ｔｏｐと反対側の金属板表面の応力。 - 特許庁

To provide a fillet welded joint having high fatigue strength by improving stress concentration, without depending excessively on imposition of compressive residual stress in a weld toe part by a welding material, free from a crack, and excellent also in toughness, and a gas shielded arc welding method for obtaining the fillet welded joint.例文帳に追加

溶接材料による止端部の圧縮残留応力の付与に過度に頼らず、応力集中を改善することで高い疲労強度を有すると共に、割れがなく、靭性にも優れたすみ肉溶接継手、および、このすみ肉溶接継手を得るためのガスシールドアーク溶接方法を提供する。 - 特許庁

To provide a method for designing a joint excellent in fatigue strength, which improves fatigue crack generation property at a weld toe, and increases the fatigue life of the fillet welded joint obtained by lap fillet welding or fillet boxing welding of a sheet or a plate with a thickness of 1-20 mm.例文帳に追加

板厚１〜２０ｍｍの薄板または厚板を重ね隅肉溶接または回し隅肉溶接して得られる隅肉溶接継手の疲労寿命を長大化させるために、溶接止端部の疲労き裂発生特性を改善させた、疲労強度に優れた継ぎ手設計方法を提供する。 - 特許庁

In the ultrasonic impact treatment method in which ultrasonic vibration is imparted to a pin installed at the tip end and in which ultrasonic impact is imparted to a weld toe by means of this pin, the radius of curvature of the tip end of the pin is made <2.0 mm and desirably ≥1.0 mm and <2.0 mm.例文帳に追加

先端部に設けられたピンに超音波振動を与え、このピンにより溶接止端部に超音波衝撃を与える超音波衝撃処理方法において、前記ピンの先端部の曲率半径を２．０ｍｍ未満、好ましくは、１．０ｍｍ以上２．０ｍｍ未満とする。 - 特許庁

In this welded steel pipe, the tensile strength of the base material is ≥800 MPa, the ratio (Tsw/Tsm) between the tensile strength Tsw of the weld metal part and the tensile strength Tsm of the base material is ≥1.0, and also, the welding toe angle θ and the peaking amt.例文帳に追加

母材の引張強さが800MPa以上の溶接鋼管であって、溶接金属部の引張強さTswと母材の引張強さTsmとの比（Tsw／Tsm）が1.0以上であり、かつ鋼管外周部における溶接止端角θおよびピーキング量Ｈが、下記(1)および(2)式を満たすことを特徴とする耐破壊特性に優れたパイプライン用高強度溶接鋼管。 - 特許庁

To provide a steel sheet excellent in characteristics of stopping initiation of fatigue crack and characteristics of stopping propagation thereof which, when undergoing joint welding, provides the satisfactory shape of a toe-of-weld part in a bead cross-section and hardly initiates fatigue cracks and even if fatigue cracks is initiated, exhibits a long propagation life until the fatigue crack induces a fracture.例文帳に追加

継手溶接を行った場合に、ビード断面における止端部の形状が良好で疲労き裂が発生し難く、またたとえ疲労き裂が発生したとしても破断に到るまでの伝播寿命が長い、疲労き裂の発生阻止特性と伝播阻止特性の両者に優れた鋼材を提供する。 - 特許庁

The welded joint is formed by fastening the low-alloy iron and steel materials for structural purposes to each other by welding using welding materials in such a manner that the martensitic transformation initiation temperature of the weld metal formed by welding attains 120 to 400°C and that the coefficient Kt value of stress concentration at the toe of welding attains 1.3 to 2.8.例文帳に追加

溶接材料を用いて構造物用の低合金鉄鋼材料どうしを溶接により固着して形成した溶接継手において、溶接により生成する溶接金属のマルテンサイト変態開始温度が１２０℃以上４００℃以下であり、かつ溶接止端部において応力集中係数Ｋｔ値が、１．３以上、２．８以下となるようにした。 - 特許庁

A weld part 14 for welding the sole side wall part 12S to the head body includes a non- ridgeline wed part N passing an area 15 and extending within a range of 3 mm to 15 mm onto the sole part 4 side from a ridgeline X that partitions the crown part 3 from the side part 9 and extends from a toe to a shaft fitting part 11.例文帳に追加

ソール側壁部１２Ｓがヘッド本体部１３に溶接された溶接部１４は、クラウン部３とサイド部９とを区画しトウ５からシャフト取付部１１までのびる稜線Ｘからソール部４側へ３mm以上かつ１５mm以内で該稜線Ｘに沿ってのびる稜線下方の領域１５を通る非稜線溶接部分Ｎを含んでいる。 - 特許庁