分割練り混ぜ工法においてトルク試験を行うことなく一次水量を決定する。例文帳に追加

To determine a primary water amount without performing a torque test in a dividing kneading and mixing method. - 特許庁

計量して練り混ぜる直前の骨材に直接蒸気を吹き込み、効率よく熱交換をするため温度制御の応答性が良い。例文帳に追加

Steam is introduced directly into the aggregate immediately before the aggregate is weighed and kneaded, and heat exchange is carried out efficiently, to well respond to temperature control. - 特許庁

予め練り混ぜられた硬練りのベースコンクリートに、該ベースコンクリート中のセメント１００質量部当たり、収縮低減用流動化剤を０．１〜８．０質量部の割合となるよう添加して混合した。例文帳に追加

The preparation method for the low shrinkage AE concrete comprises a step of adding 0.1-8.0 pts.mass of a low shrinkage reduction fluidizing agent per 100 pts.mass of cement in the base concrete to stiff-consistency base concrete that has been kneaded and mixed in advance. - 特許庁

含水率５％以下の人工軽量骨材を使用して、空練り工程Ｓ４０、混練工程Ｓ５０を経て軽量コンクリートを製造する場合に、補正水と練り混ぜ水とを、混練工程Ｓ５０で一括投入することにより、水供給の手間を低減する。例文帳に追加

When lightweight concrete is manufactured through a dry mixing process S40 and a kneading process S50 by using artificial lightweight aggregate with a water content of 5% or below, correction water and kneading/mixing water are collectively charged in the kneading process S50 to reduce supply labor of water. - 特許庁

また、このチーズ粕みそ漬けの製造方法は、酒粕の所望量と、白みその所望量とを練り混ぜ、これを所望量のクリームチーズの周りに塗布し、低温状態で所定期間漬け込むことを特徴とする。例文帳に追加

A method for producing the cheese preserved in the sake lees and miso includes: kneading a desired amount of the sake less with a desired amount of the white miso; coating the periphery of a desired amount of the cream cheese therewith; and carrying out preserving of the resultant material therein in a low-temperature state for a prescribed period of time. - 特許庁

セメントモルタル用骨材として超軽量骨材を用いた場合でも、材料分離を生じさせることなく、かつ、１分以内の短時間で均一に練り混ぜることが可能な、セメント系高流動軽量モルタルを提供する。例文帳に追加

To provide cement based high fluidity lightweight mortar without causing material separation even when super lightweight aggregate is used as aggregate for cement mortar and capable of being uniformly kneaded for a short time within 1 min. - 特許庁

水１１、セメント１２及び骨材１３，１４を含むコンクリート材料の練り混ぜ後に、ブリーディング水に相当する量の水１１ａを拘束する増粘剤１５と適量の流動化剤１６を添加する。例文帳に追加

This method involves the procedures to knead a concrete material including water 11, cement 12 and aggregates 13 and 14 and add a thickening agent 15 which restrains the equivalent amount of water 11a to the bleeding water and an appropriate amount of fluidizing agent 16. - 特許庁

セメントに超軽量骨材と補強繊維と微粒球形粉体とを配合し、さらに水を添加して練り混ぜる超軽量コンクリートの製造方法。例文帳に追加

This super lightweight concrete production process comprises: mixing super lightweight aggregate, reinforcing fiber and a fine-spherical- granular powder with cement to obtain a mixture; further adding water to the mixture; and mixing the resulting mix. - 特許庁

練り混ぜによる連行空気量の経時的な増加を抑えて高強度の硬化体を与える水硬性セメント組成物用空気量安定化剤及び水硬性セメント組成物を提供する。例文帳に追加

To obtain an air content stabilizer for a hydraulic cement composition which suppresses the increase of the quantity of air entrained by kneading with time and gives a high strength hardened body, and to obtain a hydraulic cement composition. - 特許庁

そして、この混合物に微小中空骨材を徐々に加えていきながら練り混ぜを行うことによって、水結合材比が小さい場合でも微粒子状の微小中空骨材を多量に混練することが可能となる。例文帳に追加

While microhollow aggregate is gradually added to the mixture, the mixture is mixed so that the mixing of the microhollow aggregate in the particulate form in a large amount is made possible even if the mixing ratio of the water to the binder is small. - 特許庁

吹き付けコンクリートの粗骨材を取り除いたモルタルの配合に関し、細骨材の一部を微粉末に置換すると共に微粉末の含有量を順次変化させて配合して練り混ぜして複数種類のモルタルを製造する。例文帳に追加

With regard to the blending of mortar excluding the coarse aggregate of the shotcrete, a plurality of kinds of mortar are produced by replacing part of the fine aggregate with the fine powder, changing the content of the fine powder in turn, blending, and kneading. - 特許庁

ごく当り前の米の飯を炊いて作り、これに暖かい内に重量比で千分の１から十分の１まで程度の食塩を混ぜ、擂り鉢や臼と擂り粉木や杵により搗きまた練り合わせなどして均一な組成のねばねばした物体を得る。例文帳に追加

Ordinary rice is boiled, mixed with salts at a weight ratio of 1000:1 to 10:1 while hot, and pounded or kneaded using a mortar and a pestle to obtain a sticky material with a uniform composition. - 特許庁

これらを一定の水量のもとで練り混ぜ、この混練した材料を球状成形型加圧装置により所定の球状に成形し、一定期間（２８日）養生後、高温１１１５〜１１６０℃で５〜１８０分間焼成する。例文帳に追加

These are kneaded under a specific amount of water, and the kneaded material is shaped into a predetermined globular shape by a globular shaping mold pressurizing apparatus and fired at a high temperature of 1,115-1,160°C for 5-180 minutes after being cured for a definite period (28 days). - 特許庁

また、本発明の混練物は、水硬性成分と、土砂成分とを含有し、前記土砂成分の総量に対する粒径１．５ｍｍ以下の土砂成分の重量割合が、９５重量％以上である硬化性シロアリ防除組成物と、ポリマーを含有している液体とを練り混ぜることにより得られる。例文帳に追加

The kneaded product is obtained by kneading the curable termite-controlling composition containing the hydraulic component and the soil component wherein the weight ratio of the soil component having the particle diameter of 1.5 mm or smaller is 95 wt.% or more based on the total amount of the soil component and a liquid containing a polymer together. - 特許庁

本製法による硬化樹脂の比重は０．３〜０．６と軽量であるにもかかわらず圧縮強度に優れ、低吸収性であることから練り混ぜ後の圧送性にも優れ、さらに断熱性にも優れることを特徴とするコンクリート用軽量骨材。例文帳に追加

The lightweight aggregate for concrete according to the present production method has excellent compressive strength although the cured resin is lightweight with a specific gravity of 0.3-0.6, has excellent pumpability after mixing because it has a low water absorption properties, and has excellent heat insulation. - 特許庁

簡素な検知センサーを貯蔵ビン容器内で一回の練り混ぜに必要な細骨材の貯蔵領域に設置し、連続的に細骨材の表面水量を確実に測定でき、正確なコンクリートが製造できる細骨材の表面水量検知方法と検知装置を提供する。例文帳に追加

To provide a method for sensing the amount of the surface water of fine aggregate which can continuously and surely measure the amount of the surface water of the fine aggregate by installing a simple sensing sensor in the storage region of the fine aggregate necessary to one time knead and mix in a storage bottle container and which can manufacture an accurate concrete, and an apparatus therefor. - 特許庁

所定量のモルタルまたはコンクリートが投入されたミキサー１中に切断された有機または無機の補強繊維４を連続的に投入しつつ、該ミキサーによってモルタルまたはコンクリートを練り混ぜることにより、前記切断繊維４をモルタルまたはコンクリート中に混合分散させる例文帳に追加

The cut organic or inorganic reinforcing fibers 4 are mixed and dispersed in the mortar or the concrete by kneading the mortar or the concrete with the help of a mixer l while continuously charging the cut fibers 4 into the mixer l filled with a specified amount of the charged mortar or concrete. - 特許庁

メッキ廃液より生成したメッキスラッジをフェライト化させてなるフェライト化メッキスラッジをＭＤＦセメントに、重量比で７０〜９２％混ぜて練り、これを温度１００〜１５０℃、圧力１００〜１５０ｋｇｆ／ｃｍ^２で高温加圧してタイル化する。例文帳に追加

A ferrite-plating sludge constituted by making the plating sludge produced from a plating liquid waste as the ferrite is mixed with an MDF cement by 70 to 92 wt.% and is kneaded to make the ferrite tile at temperature 100 to 150°C and pressure 100 to 150 kgf/cm2. - 特許庁

低熱ポルトランドセメントと、セメント分散剤とを併用し、かつ低熱ポルトランドセメント組成物のクリンカ鉱物組成および石膏の量をそれぞれ調整することにより、コンクリートの練り混ぜ後のこわばりの発生が抑制されるとともに、コンクリートの経時的な流動性の変化も小さくすることができる。例文帳に追加

Development of stiffness after kneading of concrete is restrained and the change of fluidity of the concrete with time can be reduced by using both a low heat Portland cement and a cement dispersant, and regulating the composition of clinker mineral and the quantity of gypsum in the low heat Portland cement composition. - 特許庁

専用の攪拌装置や注入容器を使用せずに少量のセメントを手軽に且つ簡単に水等と練り混ぜ、得られた結合剤をそのまま注入し得る効率的な水等との攪拌混合と注入作業が期待できるコンクリート建造物用結合剤の混合・注入方法及びその装置を提供する。例文帳に追加

To provide a method and a device for mixing and injecting a binder for a concrete building, which can bring about efficient work for agitation/mixing with water, etc., and injection, wherein a small amount of cement is readily and easily mixed with the water, etc., without using an exclusive agitation device and an exclusive injection container and wherein the obtained binder can be injected as it is. - 特許庁

モルタルやコンクリート組成物中の水の使用量を少なくしてもその流動性を高めることができ、スランプ保持効果を有し、かつ低温時におけるモルタルやコンクリートの練り混ぜ直後の流動性不良を抑制し、さらにモルタルやコンクリートの強度を向上させ、かつモルタルやコンクリートの凝結遅延の少ない新たなセメント用添加剤を提供する。例文帳に追加

To provide a new cement additive which enables enhancement of flowability of mortar or a concrete composition even when the amount of water used is reduced, and has a slump retention effect on concrete and is capable of inhibiting defective flowability of mortar or concrete immediately after mixing it at a low temperature from being caused, improving strength of such mortar or concrete and also reducing setting retardation of it. - 特許庁

細骨材、粗骨材、水、ＰＦＢＣ灰及び高炉スラグ微粉末を含み、セメントを含まない材料からなるコンクリート二次製品は、材料の計量工程Ｓ１０、練り混ぜ工程Ｓ２０、打ち込み工程Ｓ３０、締め固め工程Ｓ４０、蒸気養生工程Ｓ５０、及び脱型工程Ｓ６０を実施することにより製造される。例文帳に追加

The concrete secondary product comprising materials containing a fine aggregate, a coarse aggregate, water, PFBC ash and fine blast furnace slag powders and not containing cement is manufactured by performing a step S10 of weighing materials, a step S20 of kneading, a step S30 of placing, a step S40 of compacting, a step S50 of steam curing and a step S60 of demolding. - 特許庁

本発明によるコンクリートの製造方法は、セメントと水とで生成したブリージング水もしくはブリージング水と同等の水和生成物Ｃａ（ＯＨ）_2、ＮａＯＨ、ＫＯＨ、Ｍｇ（ＯＨ）_2等を含有する人工水を、セメント、フライアッシュ等の可溶性けい酸を含む混和材、細骨材及び粗骨材の練り混ぜ水として用いることを特徴としており、フライアッシュ等の可溶性けい酸を含む混和材の使用を増量して強度発現のさらなる早期化と水和熱の徹底した抑制を図って温度ひび割れの防止が出来る効果を奏している。例文帳に追加

The bleeding water formed from cement and water or the artificial water containing the hydration products Ca(OH)2, NaOH, KOH, Mg(OH)2, etc., equal to the bleeding water is used as the water for kneading and mixing the intimate mixture containing the soluble silicic acid, such as fly ash and blast furnace slag, fine aggregate and coarse aggregate. - 特許庁