「continuous casting method」に関連した英語例文の一覧と使い方(19ページ目) - Weblio英語例文検索

To provide a continuous casting method capable of manufacturing a cast bloom having an excellent internal quality by stabilizing the internal segregation state of a cast bloom by improving control accuracy of a casting speed.例文帳に追加

鋳造速度の制御精度を向上させることにより、鋳片の内部偏析性状を安定化させ、内部品質の良好なブルーム鋳片を製造できる連続鋳造方法を提供する。 - 特許庁

To provide a method for controlling a short side taper in a mold for continuous casting, with which the surface quality of a cast slab can be secured and casting to surely prevent a breakout is made possible, by ensuring a suitable shell thickness not only to the short side, but also to the long side corner part.例文帳に追加

短辺側はもとより長辺コーナー部に対しても適正なシェル厚を確保することにより、鋳片表面品質の確保およびブレークアウトを確実に防止する鋳造を可能とする。 - 特許庁

To provide a continuous casting method with which a good internal quality cast slab having little center segregation and V segregation even at the end part thereof can be obtd. without development of the leakage of steel in the final stage of the casting.例文帳に追加

鋳造末期において漏鋼を発生させず、鋳片の末端部でも中心偏析やＶ偏析の少ない内部品質の良好な鋳片を得ることができる連続鋳造方法の提供。 - 特許庁

To provide a method for predicting a restrictive breakout with which the predicting accuracy in the prediction of the breakout, is improved and the lowering of productivity in continuous casting is restrained.例文帳に追加

ブレークアウト予知における予知精度を高め、連続鋳造の生産性低下を抑止する拘束性ブレークアウト予知方法を提供する。 - 特許庁

To provide a controlling method and a controlling apparatus with which the control for molten metal surface level variation can safely be performed at high precision, in a continuous casting using slag.例文帳に追加

スラグを使用した連続鋳造にあって、安全かつ高精度に湯面制御が可能な制御方法及び制御装置を提供する - 特許庁

To provide a continuous casting method of steel by which steel containing REM is continuously cast without causing any blockage of a nozzle with inclusions.例文帳に追加

介在物によるノズルの閉塞を生じることなくＲＥＭを含有する鋼の連続鋳造が可能な連続鋳造方法を提供する。 - 特許庁

To provide a continuous casting method of high-titanium-containing steel which makes a cast steel slab free from any surface defect and enables the high-titanium-containing steel slab to be rolled without care.例文帳に追加

鋳片の表面欠陥を防止し、無手入れで圧延することが可能な高Ｔｉ含有鋼の連続鋳造方法を提供する。 - 特許庁

To provide a continuous steel casting method which prevents mold powder inclusion, and which is able to prevent P or Ni in surface layer of cast pieces from segregation.例文帳に追加

モールドパウダーの巻き込みを防止し、かつ鋳片の表面層におけるPやNiの偏析防止できる鋼の連続鋳造方法を提案する。 - 特許庁

To provide a controlling method and a controlling apparatus with which the control for molten metal surface can safely be performed at high precision, in a continuous casting using slag.例文帳に追加

スラグを使用した連続鋳造にあって、安全かつ高精度に湯面制御が可能な制御方法及び制御装置を提供する。 - 特許庁

To provide a continuous steel casting method capable of producing a cast slag excellent in inner quality without generating segregation such as center segregation or V segregation.例文帳に追加

中心偏析やＶ偏析などの偏析を発生せず、内部品質の良好な鋳片を製造できる鋼の連続鋳造方法の提供。 - 特許庁

(3) In the method for continuous casting, the wire or the rod contains one or more kinds selected from Mg, Bi, Ca, Te, Yb, Tl, and lead.例文帳に追加

(3）ワイヤーまたはロッドがＭｇ、Ｂｉ、Ｃａ、Ｔｅ、Ｙｂ、Ｔｌおよび鉛から選ばれた１種以上を含むものである連続鋳造方法。 - 特許庁

To provide a continuous-cast steel piece having little center segregation in the whole width and length of the piece, and a method for casting the piece.例文帳に追加

鋳片の全幅および全長にわたって、中心偏析の少ない鋼の連続鋳造鋳片およびその鋳片の鋳造方法の提供。 - 特許庁

To provide a method of casting a cover layer about a golf ball core utilizing a single cavity mold that moves on a continuous conveyor.例文帳に追加

連続したコンベアにおいて移動する単一キャビティ金型を利用してゴルフボールコアのまわりにカバー層を注型する方法を提供する。 - 特許庁

To provide a continuous casting method of steel with which a sound cast slab having no internal crack near the short side part and little in center segregation can be obtd.例文帳に追加

短辺部近傍の内部割れがなく中心偏析の少ない健全な鋳片を得ることが可能な鋼の連続鋳造方法の提供。 - 特許庁

To provide a continuous casting operation method which produces steel products having excellent slab surface cleanability and excellent in cleanability within slabs as well.例文帳に追加

本発明は、鋳片表面清浄性に優れ、かつ、鋳片内部の清浄性にも優れた鋼材を製造する連鋳操業方法を提供する。 - 特許庁

To provide a continuous steel casting method to obtain sound billets with less center segregation and V segregation without generating internal cracks.例文帳に追加

内部割れを発生させることなく、中心偏析やＶ偏析の少ない健全な鋳片を得ることが可能な鋼の連続鋳造方法の提供。 - 特許庁

To provide a continuous casting method, which prevents blockage in a nozzle due to adhesion of oxides of rare earth elements onto the inner surface of the immersion nozzle.例文帳に追加

希土類元素の酸化物の浸漬ノズル内面への付着に起因するノズルの閉塞を防止し得る連続鋳造方法を提供する。 - 特許庁

To provide a continuous casting tundish capable of removing oxides effectively, etc., and a method for removing oxides, etc., using the tundish.例文帳に追加

酸化物等の高い除去効果を得ることができる連続鋳造用タンディッシュ、およびそれを用いる酸化物等の除去方法を提供する。 - 特許庁

To provide a continuous casting method for molten steel capable of performing stable operation by preventing the defect due to hydrogen in the molten steel and heat extraction defect.例文帳に追加

溶鋼中の水素による欠陥及び抜熱不良を防止し、安定した操業ができる溶鋼の連続鋳造方法を提供する。 - 特許庁

To provide a continuous casting method for obtaining a magnesium alloy cast slab of a high yield and high quality without using any protective gas or flux.例文帳に追加

保護ガスおよびフラックスを必要とせず、高歩留りおよび高品質のマグネシウム合金鋳片を得ることのできる連続鋳造方法の提供。 - 特許庁

To provide a vertical type continuous casting method of a large section cast slab having ≥380 mm thickness of the cast slab while restraining the surface crack.例文帳に追加

鋳片厚みが380mm以上の厚鋼板用大断面鋳片を、表面割れを抑制しながら垂直型連続鋳造する方法を提供する。 - 特許庁

The clad material production apparatus A includes: a continuous casting device 1 of forming a metal substrate X2 to form into a base material by a continuous casting method; and a powder rolling device 7 of press-joining powders P1, P2 functioning as brazing filler metals to one side or both the sides of the metal substrate X2 formed by the continuous casting device 1 to form a clad material X4.例文帳に追加

クラッド材製造装置Ａは、基材となる金属基板Ｘ２を連続鋳造法によって形成する連続鋳造装置１と、前記連続鋳造装置１にて形成された前記金属基板Ｘ２の片面或いは両面にロウ材として機能する粉末Ｐ１，Ｐ２を圧着させてクラッド材Ｘ４を形成する粉末圧延装置７とを備える。 - 特許庁

The continuous casting method of molten metal is characterized in that a temperature of molten metal 2 at a central part of a depth beneath the surface of molten metal in the continuous casting mold 1 is made higher by 5°C or more than a liquid-phase line temperature and a forced fluidity of molten metal 2 along a solid-liquid interface is provided in the continuous casting mold.例文帳に追加

溶融金属の連続鋳造方法であって、連続鋳造鋳型１内の溶融金属表面直下の厚み中央部における溶融金属２の温度を液相線温度＋５℃以上とし、連続鋳造鋳型内において固液界面に沿った溶融金属２の強制流動を起こさせることを特徴とする溶融金属の連続鋳造方法。 - 特許庁

To provide a forcibly opening method of a tundish nozzle for continuous casting in which the forcible opening of a tundish nozzle clogging part formed at the start of the continuous casting can be surely performed without causing the excessive oxidation of molten steel and without generating damages to a refractory, and to provide a device.例文帳に追加

連続鋳造開始時に発生するタンディッシュノズル閉塞部の強制開口を溶鋼の過度の酸化を招かず、耐火物の損傷を生ぜずに確実に行い得る連続鋳造用タンディッシュノズルの強制開口方法及び装置を提案する。 - 特許庁

To provide a sealing method for molten steel in continuous casting where an N_2 gas and an Ar gas are used at a suitable mixing ratio in a seal gas to molten steel within a passage of molten steel from a ladle to a tundish and within the tundish in continuous casting equipment for steel, thus the using amount of expensive Ar is reduced while securing sealability.例文帳に追加

鋼の連続鋳造設備における取鍋からタンディッシュへの溶鋼の通路、タンディッシュ内の溶鋼に対するシールガスにＮ_2ガスとＡｒガスを適切な混合比で使用することでシール性を確保しながら高価なＡｒの使用量を減らす。 - 特許庁

To provide a nozzle for continuous casting in which the flow rate of gas to be blown from the inner wall is reduced to a degree to prevent the defect of bubbles or the like, and the sticking of inclusions in molten steel to the inner wall can be securely prevented, and to provide a continuous casting method.例文帳に追加

気泡系欠陥を防止できる程度までノズル内壁からのガス吹き込み流量を低減した上で、溶鋼中介在物のノズル内壁への付着を確実に防止できる連続鋳造用ノズルと連続鋳造方法を提供すること。 - 特許庁

(1) In this continuous casting method of steel for performing the rolling reduction by using a pair of rolling reduction rolls after bulging a cast slab including a non-solidified portion, a lower roll of the pair of rolling reduction rolls is protruded from a lower side pass line of the cast slab to roll down the cast slab in a continuous casting machine.例文帳に追加

（１）未凝固部を含む鋳片をバルジングさせた後に、圧下ロール対を用いて圧下する連続鋳造方法であって、連続鋳造機内において、圧下ロール対の下部ロールを鋳片の下側パスラインよりも突出させて圧下する鋼の連続鋳造方法。 - 特許庁

To provide a method for producing a thinned fin material composed of an Al-Ni-Fe alloy with a high strength and highly thermal conductivity by a continuous casting and rolling method.例文帳に追加

高強度、高熱伝導材料の合金であるＡｌ−Ｎｉ−Ｆｅ系合金からなる薄肉化フィン材の連続鋳造圧延法による製造方法を提供する。 - 特許庁

To provide a method for preventing erroneous detection of breakout in a method for predicting the breakout, specifically the restrained breakout which can be caused in continuous casting of molten metal.例文帳に追加

溶融金属の連続鋳造において発生しうるブレークアウト、特に拘束性ブレークアウトを予知する方法において、ブレークアウト誤検出を防止する方法を提供する。 - 特許庁

To provide a continuous casting method for a steel by which a cast slab having good surface quality can be obtained without developing the clogging of an immersion nozzle, and a production method for a steel strip.例文帳に追加

浸漬ノズルに詰まりが発生することもなく、表面品質の良好な鋳片を得ることができる鋼の連続鋳造方法および鋼帯の製造方法の提供。 - 特許庁

A method for casting an ingot for a bonding wire by slowly cooling a crucible from the lower part thereof or by a continuous casting method is disclosed, wherein molten metal is solidified by setting a relative shifting speed at the interface between the molten metal and the solidified portion to ≥20 mm/min.例文帳に追加

ルツボ下部から徐冷してインゴットを鋳造する方法、ないしは、連続鋳造法によりインゴットを鋳造する方法において、溶湯と凝固部分の界面の相対移動速度を２０ｍｍ／分以上として凝固させる。 - 特許庁

To realize a control method capable of suppressing the variation of a molten metal level in a mold more effectively as compared with a conventional method even when errors exist in a numerical model of a continuous casting machine or the frequency characteristic of the casting machine is unknown.例文帳に追加

連続鋳造機の数式モデルに誤差が存在しても、また連続鋳造機の周波数特性が未知であっても、従来よりも効果的にモールド内湯面レベルの変動を抑制することができる制御方法。 - 特許庁

To provide a method for giving resiliency with electromagnetic force and repulsion in the soft contacting state for preventing the stickiness of metal particularly to side weirs of a twin roll type continuous casting, etc., related to the casting method of a metallic strip.例文帳に追加

本発明は、金属ストリップ鋳造方法に関し、特に双ロール式連続鋳造等のサイド堰への地金の付着を防止するために、電磁力による反発力および軟接触状態での斥力を付与する方法を提供する。 - 特許庁

In the casting starting method in the continuous casting machine, a molten steel flowing rate at the molten steel surface in the mold in a vicinity of the short wall sides of the mold is controlled to 20 cm/second or less till the length of the cast slab to be cast reaches at least 2.0 m at the start of casting in continuously casting the cast slab.例文帳に追加

本発明に係る連続鋳造機での鋳造開始方法は、スラブ鋳片を連続鋳造するにあたり、鋳造開始時、少なくとも鋳造された鋳片の長さが２．０ｍに達するまでは、鋳型短辺近傍の鋳型内溶鋼湯面の溶鋼流速を２０ｃｍ／秒以下に制御することを特徴とする。 - 特許庁

To provide an immersion nozzle having a shape capable of stably casting a slab, which is less in defects in nonmetallic inclusions caused by mold powder, and also less in surface microcracks caused by the remelting of a solidified shell in a continuous casting, and to provide a casting method therefor.例文帳に追加

連続鋳造において、モールドパウダーに起因する非金属介在物の欠陥が少なく、凝固シェルの再溶解による表面微小割れの少ない鋳片を安定して鋳造可能とする形状の浸漬ノズルおよびその鋳造方法を提供する。 - 特許庁

To provide a continuous casting method of metal in which stable casting can be carried out and cast pieces with high quality can produced, without big fluctuation of a thrust applied to molten metal in a casting mold by variation in a thickness of a mold plate.例文帳に追加

モールド板の厚みのバラツキによって鋳型内の溶融金属に付与される推力が大きく変動することなく、安定した鋳造を実施することができ、高品質な鋳造鋳片を製出することが可能な金属の連続鋳造方法を提供する。 - 特許庁

(2) The continuous casting method is performed, by which the thickness of the cast slab is increased step by step to the casting direction by increasing step by step to the roll gap in the range of ≤(8.5 mm/one roll segment) in each roll segment having substantially the same roll gap in the casting direction.例文帳に追加

(2)鋳造方向に実質的に同一のロールキャビティを有するロールセグメントごとに、ロールキャビティを（８．５ｍｍ／１ロールセグメント）以下の範囲で段階的に増加させ、鋳片の厚さを鋳造方向に対して段階的に増加させる連続鋳造方法。 - 特許庁

To provide a continuous casting method for steel which allows the easy precipitation of crystal phases into mold powder and ensures effective slow cooling by the mold powder.例文帳に追加

モールドパウダー中に結晶相が析出しやすく、モールドパウダーにより緩冷却を有効に行なうことができる鋼の連続鋳造方法を提供する。 - 特許庁

To provide the continuous casting method for a cast slab capable of reducing center porosity without causing any surface crack when reducing the cast slab.例文帳に追加

鋳片を圧下するに際し、表面ひび割れを発生させることなく、中心ポロシティを低減することができる、鋳片の連続鋳造方法を提供する。 - 特許庁

To provide an immersion nozzle with which the sticking of alumina on the inner surface of the nozzle is prevented and development of surface defect is prevented, and a continuous casting method.例文帳に追加

ノズル内面にアルミナが付着するのを防止し、製品の表面欠陥の発生を防止する浸漬ノズルおよび連続鋳造方法を提供する。 - 特許庁

To provide a method for preventing degradation of cleanability of steel caused by inclusions in a tundish in changing a ladle during the continuous casting.例文帳に追加

連続鋳造における取鍋交換の際に生じるタンディッシュ内の介在物の巻き込みによる鋼の清浄度の悪化を防ぐ方法を提供する。 - 特許庁

METHOD FOR CHANGING WIDTH OF CAST SLAB DURING CONTINUOUS CASTING, SYSTEM FOR CHANGING WIDTH OF CAST SLAB, UNIT FOR MAKING POSITIONAL PATTERN TABLE OF SHORT SIDES IN MOLD AND COMPUTER PROGRAM AND RECORDING MEDIUM例文帳に追加

連続鋳造中の鋳片幅変更方法、鋳片幅変更システム、鋳型短辺の位置パターン表生成装置、コンピュータプログラム、及び記録媒体 - 特許庁

To provide a continuous casting method of a pipe material with a screwed center hole, with which the pipe materials with screwed center holes can be mass-produced and the manufacturing cost can drastically be reduced.例文帳に追加

ねじ孔管材を大量生産することができ、製作コストを大幅に低減することができるねじ孔管材の連続鋳造法を提供する。 - 特許庁

To provide a method for subjecting a slab of high internal quality having reduced center segregation and center porosities to soft reduction continuous casting only by the addition of a simple apparatus.例文帳に追加

簡単な装置の追加だけで中心偏析やセンターポロシティの少ない内部品質の良好な鋳片を軽圧下連続鋳造する方法を提案する。 - 特許庁

To provide a continuous casting method for steel which can continuously cast steel such as a molten steel at high speed without causing the occurrence of crack defects or the like.例文帳に追加

割れ欠陥の発生等を招くことなく溶鋼などの鋼を高速で連続鋳造することのできる鋼の連続鋳造方法を提供する。 - 特許庁