On the other hand, by using a differential scanning calorimetry analyzer, a change in the energy in the solid-liquid coexistence region of the alloy is measured.例文帳に追加

他方、示差走査熱量分析装置を用いて、合金の固液共存域のエネルギー変化を測定する。 - 特許庁

To provide an analyzing method of a DSC curve and output temperature curve for determining the accurate freezing point from among differential scanning calorimetry result, even for a sample showing supercooling, and a temperature calibration method in cooling a differential scanning calorimetry device.例文帳に追加

過冷却を示す試料であっても、示差走査熱量測定結果から正確な凝固点を求めるＤＳＣ曲線、出力温度曲線の解析方法、および示差走査熱量測定装置の冷却時の温度較正方法を提供することを課題とする。 - 特許庁

In the expression 1, T1 represents the temperature at the endothermic highest peak in differential scanning calorimetry of the 10-30C aliphatic monovalent alcohol; and T2 represents the temperature at the endothermic highest peak in differential scanning calorimetry of the ester compound for the electrophotographic toner.例文帳に追加

１０℃＜Ｔ２−Ｔ１＜５０℃ 式１Ｔ１＝炭素数１０〜３０の１価の脂肪族アルコールの示差走査熱量測定における吸熱の最高ピーク温度Ｔ２＝電子写真用トナー用エステル化合物の示差走査熱量測定における吸熱の最高ピーク温度 - 特許庁

(a) a crystal melting enthalpy of 0 to 70 J/g measured at a heating rate of 10°C/min in differential scanning calorimetry; (b) a crystal melting peak temperature of at least 100°C and a crystal melting of 5 to 70 J/g measured at a heating rate of 10°C/min in differential scanning calorimetry.例文帳に追加

（ａ）示差走査熱量測定における加熱速度１０℃／分で測定される結晶融解熱量が０〜７０Ｊ／ｇ （ｂ）示差走査熱量測定における加熱速度１０℃／分で測定される結晶融解ピーク温度が１００℃以上であり、かつ、結晶融解熱量が５〜７０Ｊ／ｇ - 特許庁

In the positive electrode active material for the nonaqueous electrolyte secondary battery composed of at least lithium transition metal complex oxide of a spinel structure, a heat generation starting temperature by a differential scanning calorimetry of the lithium transition metal complex oxide is 220°C or more, a calorific value by the differential scanning calorimetry of the lithium transition metal complex oxide is 700 to 900 mJ/mg.例文帳に追加

非水電解液二次電池用正極活物質を、少なくともスピネル構造のリチウム遷移金属複合酸化物からなる非水電解液二次電池用正極活物質において、前記リチウム遷移金属複合酸化物の示差走査熱量測定による発熱開始温度は、２２０℃以上であり、前記リチウム遷移金属複合酸化物の示差走査熱量測定による発熱量は、７００〜９００ｍＪ／ｍｇである構成とする。 - 特許庁

To provide a differential scanning calorimeter capable of preventing heat escape from a sample container presser mechanism occurring as before, and measuring up to the temperature equal to ordinary measurement without temperature limitation, when differential scanning calorimetry is executed, while an electromagnetic wave beam line in the horizontal direction is transmitted through a sample.例文帳に追加

水平方向の電磁波ビームラインを試料透過させながら示差走査熱量測定を行なう際、従来の様な試料容器押さえ機構からの熱の逃げを防ぐと共に、温度制限も無く通常の測定と同等の温度まで測定できる示差走査熱量計を提供すること。 - 特許庁

The fiber sheet includes a whole aromatic polyamide fiber and a polyester resin wherein two or more melting peaks are drawn on a DSC curve drawn by the measurement of the polyester resin by differential scanning calorimetry.例文帳に追加

本発明の繊維シートは、全芳香族ポリアミド繊維とポリエステル樹脂とを含み、前記ポリエステル樹脂を示差走査熱量測定して描いたＤＳＣ曲線に、融解ピークが２ヶ所以上描かれる。 - 特許庁

This mat is made of an ethylenic copolymer resin in which the peak of the DSC curve in a temperature rise in differential scanning calorimetry ranges between 50°C and 70°C.例文帳に追加

示差走査熱量測定法における昇温時のＤＳＣ曲線のピークが５０〜７０℃にあるエチレン系共重合体樹脂製のマットである。 - 特許庁

The high density polytetrafluoroethylene tape is characterized in that the crystal fusion curve obtained by a differential scanning calorimetry shows peaks in near 330°C, near 345°C, and near 380°C.例文帳に追加

本発明に係る高密度ポリテトラフルオロエチレンテープは、示差走査熱量測定で得られる結晶融解曲線が３３０℃付近、３４５℃付近及び３８０℃付近にピークを示す。 - 特許庁

The binder contains polytetrafluoroethylene wherein a molecular weight is in the range of 1.0×107-1.0×108, and crystallization heat measured by differential scanning calorimetry is in the range of -20 to 0 J/g.例文帳に追加

バインダーは、分子量が１．０×１０^7〜１．０×１０^8の範囲内であり且つ示差走査熱量測定で測定した結晶化熱が−２０（Ｊ／ｇ）〜０（Ｊ／ｇ）の範囲内であるポリテトラフルオロエチレンを含む。 - 特許庁

The absolute value of the difference between the heat generation starting temperature and the heat generation termination temperature by the differential scanning calorimetry of the lithium transition metal complex oxide is preferably 13°C or more.例文帳に追加

前記リチウム遷移金属複合酸化物の示差走査熱量測定による発熱開始温度と発熱終了温度の差の絶対値は、１３℃以上であることが好ましい。 - 特許庁

The crystallinity is calculated by differential scanning calorimetry and is found by ((the heat of crystallization of the amorphous alloy - the heat of crystallization of the object to be measured)/(the heat of crystallization of the amorphous alloy)) × 100.例文帳に追加

結晶化度は、示差走査熱量測定により算出され、（（アモルファス合金の結晶化熱−測定物の結晶化熱）／（アモルファス合金の結晶化熱））×１００で求められる。 - 特許庁

This silicone wax is characterized by having ≥45°C melting point, and ≤7°C half width of the endothermic peak in the differential scanning calorimetry measurement.例文帳に追加

融点が４５℃以上であると共に、示差走査熱量測定における吸熱メインピークの半値幅が７℃以下であることを特徴とするシリコーンワックス。 - 特許庁

Namely, if the fully charged negative electrode 22 is subjected to differential scanning calorimetry under the condition that an electrolytic solution is removed, an endothermic peak due to fusion of lithium metal can be obtained.例文帳に追加

つまり、完全充電状態の負極２２について電解液を除去した状態で示差走査熱量測定を行うと、リチウム金属の融解に起因する吸熱ピークが得られる。 - 特許庁

Starch whose heat absorption completion temperature measured by differential scanning calorimetry is at least 95°C is mixed in the food raw materials, and the mixture is dried by a drum dryer to be powdered.例文帳に追加

食品原料に、示差走査熱量測定法により測定された吸熱終了温度が９５℃以上である澱粉を混合し、当該混合物をドラムドライヤー乾燥機で乾燥して、粉末化する。 - 特許庁

The amorphous compound is shown by formula (1), wherein the temperature showing an endothermic peak by differential scanning calorimetry (DSC) is 40 to 80°C, and the solution rate into n-hexane is 1.5 mg/sec or more.例文帳に追加

式（１）で示され、示差走査熱量測定（ＤＳＣ）による吸熱ピークを示す温度が４０〜８０℃であり、ｎ−ヘキサンに対する溶解速度が１．５ｍｇ／ｓｅｃ以上である非晶質化合物。 - 特許庁

This purified stannous di(2-ethylhexanoate) of the formula (I) is characterized as the melting peak top temperature determined by differential scanning calorimetry(DSC) is -3.0°C.例文帳に追加

示差走査熱量測定（ＤＳＣ）による融解ピークトップ温度が−３．０℃であることを特徴とする式Ｉの精製ジ（２−エチルヘキサン酸）錫（ＩＩ）。 - 特許庁

Alternatively, in the range of discharge depth of 50-90%, differential scanning calorimetry does not exhibit a heat absorption-heat radiation peak of not less than 10 J/g in the range of 20-80°C.例文帳に追加

あるいは、放電深度５０％〜９０％の範囲内において、示差走査熱量測定で２０℃〜８０℃の範囲に１０Ｊ／ｇ以上の吸熱−放熱ピークを示さない。 - 特許庁

Therein, Tc(T) represents the crystallization temperature during cooling measured in conditions of melting at the maximum temperature T°C by using a differential scanning calorimetry (DSC).例文帳に追加

Ｔｃ（２７０）−Ｔｃ（３００）≧２０・・・・ａＴｃ（３００）≦１９０・・・・ｂここでＴｃ（Ｔ）は、示差走査熱分析（ＤＳＣ）により最高温度Ｔ℃で溶融する条件で測定した降温結晶化温度を示す。 - 特許庁

The hemihydrate of the compound shown by an X-ray powder diffraction diagram includes a melting point of Tm.p.=120±5°C (measured by differential scanning calorimetry; evaluation by the peak maximum; and heating rate: 10°C/min).例文帳に追加

Ｔm.p.＝１２０±５℃の融点（示差走査熱量測定法により測定；ピーク最大により評価；加熱速度：１０℃／分）でＸ線粉末回折図で示される半水化物。 - 特許庁

(a) The amorphous ethylene-propylene-1-butene copolymer has neither a peak having a heat quantity of fusion of 1 J/g or more based on crystal fusion nor a peak having a heat quantity of crystallization of 1 J/g or more based on crystallization measured by differential scanning calorimetry.例文帳に追加

（ａ）示差走査熱量測定で測定される結晶融解に基づく融解熱量が１Ｊ／ｇ以上のピーク及び結晶化に基づく結晶化熱量が１Ｊ／ｇ以上であるピークのいずれも有しない。 - 特許庁

The propylene resin is characterized by (a) an MFR (230°C, 21.2 N load) of 50-5,000 g/10 min and (b) a melting peak temperature (Tm)of 110-150°C measured by a DSC (differential scanning calorimetry) method.例文帳に追加

ａ）ＭＦＲ（温度２３０℃・荷重２１．２Ｎ）が５０〜５，０００ｇ／１０ｍｉｎであるｂ）ＤＳＣ（示差走査熱量計測定）法により測定される融解ピーク温度（Ｔｍ）が１１０〜１５０℃である - 特許庁

In the conjugated fiber that has a strength of more than 10 cN/dtex and comprises (A) the molten liquid crystal forming polyester and (B) the bendable thermoplastic resin, the crystallization temperature peak can be observed by using the differential scanning calorimetry (DSC).例文帳に追加

強度１０ｃＮ／ｄｔｅｘ以上、かつ溶融液晶形成性ポリエステル（Ａ）と屈曲性熱可塑性樹脂（Ｂ）の複合繊維において示差走査熱量（ＤＳＣ）測定で結晶化温度ピークが観察されることを特徴とする高強度複合繊維。 - 特許庁

In the manufacturing method for the resin particle (X), heat of fusion of the obtained resin particle (X) obtained by measurement by differential scanning calorimetry (DSC) satisfies following relationship equation (1): 0≤H2/H1≤0.9 (1).例文帳に追加

０≦Ｈ２／Ｈ１≦０．９ (１)［関係式（１）中、Ｈ１はＤＳＣ測定による初回昇温時の融解熱（Ｊ／ｇ）；Ｈ２はＤＳＣ測定による２回目昇温時の融解熱（Ｊ／ｇ）の測定値を表す。 - 特許庁

Calorific value by a differential scanning calorimetry when charging the negative active material layer 12 is 500 J/g or less and preferably 400 J/g or less in a range of 230°C or more and 370°C or less.例文帳に追加

この負極活物質層１２の充電時における示差走査熱量測定による発熱量は、２３０℃以上３７０℃以下の範囲内において、５００Ｊ／ｇ以下、好ましくは４００Ｊ／ｇ以下である。 - 特許庁

This resin composition generates in the reducing temperature process of a differential scanning calorimetry(DSC) an exothermal peek derived from crystallization of not less than 10 J/g equivalent of a polylactic acid resin at a reducing temperature rate of not less than 20°C/min.例文帳に追加

示差走査型熱量（ＤＳＣ）測定の降温過程においてポリ乳酸樹脂換算で１０Ｊ／ｇ以上の結晶化由来発熱ピークが降温速度２０℃／ｍｉｎ以上で発生する樹脂組成物。 - 特許庁

A part of or all of the sealing material 3 is a cured material formed by curing a curing composition containing at least a photosetting resin and the curing reaction percentage of the photosetting resin measured by a light differential scanning calorimetry is ≥90%.例文帳に追加

シール材３の一部または全部は、少なくとも光硬化性樹脂を含む硬化性組成物が硬化した硬化物であり、光示差走査熱量測定による前記光硬化性樹脂の硬化反応率が９０％以上である。 - 特許庁

This stabilizer for polymers includes an amorphous compound expressed by formula (1), wherein the temperature showing an endothermic peak by differential scanning calorimetry (DSC) is 40 to 80°C, and the rate of dissolution into n-hexane is 1.5 mg/sec or more.例文帳に追加

式（１）で示され、示差走査熱量測定（ＤＳＣ）による吸熱ピークを示す温度が４０〜８０℃であり、ｎ−ヘキサンに対する溶解速度が１．５ｍｇ／ｓｅｃ以上である非晶質化合物を含有することを特徴とするポリマー安定剤。 - 特許庁

The coating composition for drying by heating essentially comprises the emulsion having ≤50°C glass transition temperature and fine particles having ≤15 μm average particle diameter and has ≥65°C melting temperature by differential scanning calorimetry.例文帳に追加

ガラス転移温度が５０℃以下のエマルションと、平均粒径が１５μｍ以下の微粒子とを必須としてなる加熱乾燥用塗料組成物、好ましくは、上記微粒子は、示差走査熱量測定による融解温度が６５℃以上である上記加熱乾燥用塗料組成物。 - 特許庁

The lubricating oil composition contains a boron modified polybutenyl mono- or di-imido succinate compound and an aromatic amine compound into a base oil, and has ≥6.0 point in a hot tube test at ≥290°C for ≥65 min oxidation derivative time in a pressure differential scanning calorimetry (PDSC).例文帳に追加

基油にホウ素変性したポリブテニルコハク酸モノおよび／またはジイミド化合物と芳香族アミン化合物を含有する、ＰＤＳＣ（加圧示差走査熱量計）による酸化誘導時間が６５分以上かつ２９０℃におけるホットチューブ試験の評点が６．０点以上の潤滑油組成物。 - 特許庁

This crosslinked polyolefinic resin foamed article is formed by crosslinking and foaming a foamable resin composition obtained by blending a crosslinking agent and a foaming agent with a polyolefinic resin comprising a block copolymer having a melting point of 118-122°C measured by differential scanning calorimetry and a Shore A hardness of 59-86, and kneading the mixture.例文帳に追加

示差操作熱量分析により測定された融点が１１８〜１２２℃、ショアＡ硬度が５９〜８６のブロックコポリマーからなるポリオレフィン系樹脂に、架橋剤と発泡剤を配合して混練した発泡性樹脂組成物を架橋及び発泡させて架橋ポリオレフィン系樹脂発泡体を形成した。 - 特許庁

The aliphatic polyester-based resin foam molding has an open cell ratio of 50% or more, and heat of fusion of 15-60 J/g in a DSC curve obtained when a temperature is raised from 0 to 200°C by 10°C/min in differential scanning calorimetry.例文帳に追加

連続気泡率が５０％以上であり、示差走査熱量測定において０℃から２００℃まで１０℃／ｍｉｎで昇温した際に得られるＤＳＣ曲線において、融解熱量が１５Ｊ／ｇ以上６０Ｊ／ｇ以下である脂肪族ポリエステル系樹脂発泡成形体。 - 特許庁

The pedestal for flower arrangement is formed of aliphatic polyester-based resin, wherein a continuous air bubble rate is ≥50%, and melting calorie is 15-60J/g in a DSC curve obtained when raising temperature from 0°C to 200°C by 10°C/min in differential scanning calorimetry.例文帳に追加

脂肪族ポリエステル系樹脂からなり、連続気泡率が５０％以上であり、示差走査熱量測定において０℃から２００℃まで１０℃／ｍｉｎで昇温した際に得られるＤＳＣ曲線において、融解熱量が１５Ｊ／ｇ以上６０Ｊ／ｇ以下であるフラワーアレンジメント用台座。 - 特許庁

The electrically conductive filler comprises metal grains having a metastable alloy phase observed as a heat generation peak by differential scanning calorimetry (DSC) by at least one between 250°C and 285°C, and having melting points observed as heat absorption peaks in the two parts of 50 to 95°C and 400 to 475°C at least one by one, respectively.例文帳に追加

示差走査熱量測定（ＤＳＣ）で発熱ピークとして観測される準安定合金相を２５０〜２８５℃に少なくとも１つと、吸熱ピークとして観測される融点を５０〜９５℃と４００〜４７５℃の２箇所に少なくとも１つずつ有している金属粒子からなることを特徴とする導電性フィラー。 - 特許庁

The microporous polyolefin membrane contains a polyethylene having 50x10^3-1,000x10^3 of viscosity average molecular weight and a polypropylene and exhibits two peaks of melting point in 125-140°C and 140-155°C belonging to the polyethylene observed in differential scanning calorimetry.例文帳に追加

粘度平均分子量が５万以上から１００万以下であるポリエチレンと、ポリプロピレンとを含有し、示差走査熱量計で観察したときに、ポリエチレンに帰属する二つの融点ピークが、１２５℃以上から１４０℃未満と１４０℃以上から１５５℃以下に現れることを特徴とするポリオレフィン微多孔膜。 - 特許庁

The reinforced cord of a carcass ply is set to nylon 66 having a melting point of 250° or higher measured by DSC(Differential Scanning Calorimetry) so as to provide firm adhesion with a rubber member at a high temperature, and when the run-flat tire becomes hot in traveling, this constitution can suppress the peeling between the reinforced cord and the rubber.例文帳に追加

カーカスプライの補強コードを、ＤＳＣで測定した融点が２５０°Ｃ以上のナイロン６６としたので、高温においてもゴム部材との強固な接着が得られ、ランフラット走行時にタイヤ温度が高温となっても補強コードとゴムとの剥離を抑制することができる。 - 特許庁

In this method, it is found that the sample can specify a range showing the state of a constant state at the freezing temperature, by latent heat from the differential scanning calorimetry result in the cooling process, and the freezing point of the sample is determined, based on the data in this range.例文帳に追加

冷却過程の示差走査熱量測定結果から試料が潜熱により凝固温度で一定温度の状態を示す範囲を特定することが可能であることを発見し、この範囲のデータから試料の凝固点を求める方法を示した。 - 特許庁

The near IR absorbing film has a base material and a near IR ray absorbing layer containing a diimmonium compound which shows the endothermic peak at ≥200°C by differential scanning calorimetry (DSC) at 10°C/minutes temperature rising rate.例文帳に追加

基材と、昇温速度１０℃／分での示差走査熱量測定（ＤＳＣ測定）において温度２２０℃以上に吸熱ピークを有するジイモニウム系化合物を含有する近赤外線吸収層と、を有することを特徴とする近赤外線吸収フィルムである。 - 特許庁

This aluminum alloy sheet excellent in coating/baking hardenability and workability is characterized by having the total heating value in the range of 150 to 250°C in all heat generating parts of ≥0.1 cal/g by differential scanning calorimetry at a temperature rising rate of 20°C/min, and a producing method of the same is provided.例文帳に追加

昇温速度２０℃／ｍｉｎの示差走査熱量測定において、１５０〜２５０℃の範囲がすべて発熱部で、１５０〜２５０℃の合計の発熱量が０．１ｃａｌ／ｇ以上であることを特徴とする塗装焼付け硬化性および加工性に優れるアルミニウム合金板およびその製造方法。 - 特許庁

Hereby, when the differential scanning calorimetry is executed, while the electromagnetic wave beam line in the horizontal direction is transmitted through the sample, such effects are obtained that the heat escape from the sample container presser mechanism occurring as before can be prevented and that measurement can be executed up to the temperature equal to ordinary measurement without temperature limitation.例文帳に追加

これにより、水平方向の電磁波ビームラインを試料透過させながら示差走査熱量測定を行なう際、従来の様な試料容器押さえ機構からの熱の逃げを防ぐと共に、温度制限も無く通常の測定と同等の温度まで測定できる効果が得られた。 - 特許庁

The metallic soap package comprises the metallic soap heat-seal packaged with the polyethylene-based film, which has a density of 0.922 to 0.944 g/cm^2 (measured by the JIS K6760-1981 method) and a melting point of 110 to 130°C (measured by differential scanning calorimetry (DSC)).例文帳に追加

金属石鹸をポリエチレン系フィルムでヒートシール包装した金属石鹸包装物において、ポリエチレン系フィルムが、密度０．９２２〜０．９４４ｇ／cm^2（ＪＩＳ Ｋ６７６０−１９８１法）、かつ融点（ＤＳＣ法）１１０〜１３０℃であることを特徴とする金属石鹸包装物。 - 特許庁

A small piece of a laminated packing material for the retort product is analyzed by differential scanning calorimetry, and the retorting temperature of the retort product is estimated by a following general equation, based on an endothermic peak temperature T1 found from the endothermic peak appearing in a temperature region of the melting point or less of polyolefin resin used for the laminated packing material.例文帳に追加

レトルト製品の積層包材の小片を示差走査熱量測定により分析し、積層包材に用いたポリオレフィン樹脂の融点以下の温度領域に出現する吸熱ピークから求めた吸熱ピ−ク温度（Ｔ_１）を基に、下記一般式で、該レトルト製品のレトルト処理温度を推定する。 - 特許庁

Differential scanning calorimetry is performed on a horny layer sample to perform evaluation, on the basis of a heat absorption peak caused by the destruction of a structure of intercellular lipids of stratum corneum and/or the peak strength of heat absorption peak caused by alteration of keratin proteins and/or a peak temperature.例文帳に追加

角層試料を示差走査熱量測定し、角層細胞間脂質構造の破壊に由来する吸熱ピーク、及び／又は、ケラチンタンパク質の変性に由来する吸熱ピークのピーク強度及び／又はピーク温度に基づいて評価を行なう。 - 特許庁

The OA equipment exterior parts are obtained by injection molding of a polylactic acid (A component) at a mold temperature within a range of 80-130°C, wherein the polylactic acid has ≥70% ratio of ≥195°C melting peaks in melting peaks in the temperature rising step in (A) differential scanning calorimetry (DSC) measurement.例文帳に追加

（Ａ）示差走査熱量計（ＤＳＣ）測定において、昇温過程における融解ピークのうち、１９５℃以上の融解ピークの割合が７０％以上であるポリ乳酸（Ａ成分）を、金型温度８０〜１３０℃の範囲で射出成形して得られるＯＡ機器外装部品。 - 特許庁

The electric/electronic components are obtained by injection molding of a polylactic acid (A component) at a mold temperature within a range of 80-130°C, wherein the polylactic acid has ≥70% ratio of ≥195°C melting peaks in melting peaks in the temperature rising step in (A) differential scanning calorimetry (DSC) measurement.例文帳に追加

（Ａ）示差走査熱量計（ＤＳＣ）測定において、昇温過程における融解ピークのうち、１９５℃以上の融解ピークの割合が７０％以上であるポリ乳酸（Ａ成分）を、金型温度８０〜１３０℃の範囲で射出成形して得られる電気・電子部品。 - 特許庁