The aliphatic polyester resin molded product is composed of a resin composition mainly composed of an aliphatic polyester and has a Charpy impact strength of 15-230 kJ/m^2 and a flexural modulus of elasticity of 3,000-20,000 MPa each at 25°C.例文帳に追加

脂肪族ポリエステルを主成分とした樹脂組成物からなり、２５℃におけるシャルピー衝撃強度が１５〜２３０ｋＪ／ｍ^2、曲げ弾性率が３，０００〜２０，０００ＭＰａであることを特徴とする脂肪族ポリエステル樹脂成形体。 - 特許庁

To obtain an optical filter using a resin material whose cost is lower than that of polyimide, whose transmittance in the visible light range is higher than that of polyimide, whose glass transition temperature is higher than that of norbornane-based resin material, whose flexural modulus is high and whose amount of outgases is scarce as a base material.例文帳に追加

基材にポリイミドより安価で可視光域の透過率が高く、ノルボルネン系樹脂材料よりガラス転移温度が高く、曲げ弾性率も高く、アウトガス量が少ない樹脂材料を利用した光学フィルタを得る。 - 特許庁

This laminated rubber stopper for the medical vial is so formed that a thermoplastic resin having the flexural modulus of elasticity of 600 MPa or less and dynamic friction coefficient of 0.4 or less is laminated on the whole bottom surface or the whole bottom face and a part of the upper face of the rubber stopper.例文帳に追加

曲げ弾性率が６００ＭＰａ以下で、且つ動摩擦係数が０．４以下である熱可塑性プラスチックを、ゴム栓の下面全面又は下面全面及び上面の一部に積層してなる、医薬バイアル用ラミネートゴム栓。 - 特許庁

Preferably, the cellular density of this foam is 10^9-10^15 pcs./cm^3, the specific gravity is less than 1.0 g/cm^3, the tensile strength is 700 MPa or more, and the flexural modulus is 800 MPa or more.例文帳に追加

好ましくは、この発泡体の気泡密度は１０^９〜１０^１５個／ｃｍ^３であり、比重は１．０ｇ／ｃｍ^３以下であり、引張強度は７００ＭＰａ以上であり、曲げ弾性率は８００ＭＰａ以上である。 - 特許庁

The resin composition contains a highly elastic polyamide resin having a flexural modulus of 700 MPa or higher and 5,000 MPa or lower, a metal-neutralized product of ethylene-(meth)acrylic acid copolymer, and a resin having a polar functional group.例文帳に追加

この樹脂組成物は、７００ＭＰａ以上５０００ＭＰａ以下である曲げ弾性率を有する高弾性ポリアミド樹脂、金属イオンで中和されたエチレン−（メタ）アクリル酸共重合体及び極性官能基を有する樹脂を含む。 - 特許庁

Besides, a resin material (PC, PAR, PPS) of which the rate of change of the flexural modulus in the range of working temperature -20-80°C is small is used for the shaft rotation support member 20 and this is fitted to the shaft member 10 with integral molding by a mold.例文帳に追加

また、軸回動支持部材２０を使用温度（−２０〜８０℃）内での曲げ弾性率の変化の割合が小さい樹脂材料（ＰＣ、ＰＡＲ、ＰＰＳ）を用いて、軸部材１０に対してモ−ルドにより一体成形で組み付ける。 - 特許庁

A laminated body is provided which has, between its paper layers 1a and 1b, a polyolefin resin layer 2 with a flexural modulus of 10,000 kg/cm^2 or more being extruded for lamination, and wherein a sealant layer 3 is laminated outside of the paper layer 1b for bonding with a container.例文帳に追加

紙層１ａと１ｂとの間に、曲げ弾性率が１００００ｋｇ／ｃｍ^2以上のポリオレフィン系樹脂層２を押し出しラミネートし、紙層１ｂの外側に容器に接着させるためのシーラント層３を積層した積層体とする。 - 特許庁

To provide a resin composition which uses an ethylene-vinyl ester based copolymer saponification product, has impact resistance which is excellent in all of a flexural modulus, tensile strength, and a tensile elongation nature, and has hardness and ductility, and to provide a multilayer structure using the same.例文帳に追加

エチレン−ビニルエステル系共重合体ケン化物を用い、かつ、曲げ弾性率、引張強さ、引張伸び性の全てに優れる耐衝撃性を有し、硬さと粘り強さを有する樹脂組成物およびそれを用いた多層構造体を提供する。 - 特許庁

To provide a rubber-modified styrenic resin composition that is excellent in mechanical properties such as flexural modulus and impact strength, is excellent in oil resistance and chemical resistance and can be suitably used mainly in food containers or packaging materials that directly contact oil.例文帳に追加

曲げ弾性率及び衝撃強度などの機械的特性に優れ、かつ耐油性、耐薬品性に優れ、主に油に直接接する食品容器や包装材料に好適に使用することができるゴム変性スチレン系樹脂組成物を提供する。 - 特許庁

To provide a fiber-reinforced polyamide resin composition that uses a silane coupling agent with a specific ratio in a resin composition comprising a polyamide resin, a fibrous clay mineral, and a fibrous reinforcing material, and that is excellent in tensile strength, flexural modulus, and surface smoothness.例文帳に追加

ポリアミド樹脂、繊維状粘土鉱物、および繊維状強化材とからなる樹脂組成物において、シランカップリング剤を特定比率で用いた、引張強度、曲げ弾性率、および表面平滑性に優れる繊維強化ポリアミド樹脂組成物の提供。 - 特許庁

The polypropylene composition has not only excellent impact resistance and flexural modulus but also excellent transparency, and is suitable for producing refrigerating containers, freezing containers, food-packing containers, extrusion-molded articles, hollow molding articles, films, sheets and bottle stoppers.例文帳に追加

本発明のポリプロピレン組成物は、耐衝撃性および曲げ弾性率のみならず透明性にも優れており、冷蔵容器、冷凍容器、食品包装容器、押出成形物、中空成形物、フィルム、シートおよび瓶栓などの製造に適している。 - 特許庁

To provide a method for producing a carbon fiber-reinforced polyamide resin composite material, avoiding a problem in that mechanical strength is insufficient in the carbon fiber-reinforced polyamide resin composite material, and improving mechanical characteristics such as bending strength, flexural modulus, etc.例文帳に追加

炭素繊維強化ポリアミド樹脂複合材における、機械的強度が不充分である問題を回避し、曲げ強度や曲げ弾性率等の機械的特性の向上した炭素繊維強化ポリアミド樹脂複合材の製造方法を提供する。 - 特許庁

The cover 8 includes (A) a highly elastic polyamide resin with a flexural modulus of 700 MPa or greater and 5000 MPa or less, (B) an ethylene-(meth)acrylic acid copolymer that is neutralized with a metal ion, and (C) a resin having a polar functional group.例文帳に追加

カバー８は、（Ａ）７００ＭＰａ以上５０００ＭＰａ以下である曲げ弾性率を有する高弾性ポリアミド樹脂、（Ｂ）金属イオンで中和されたエチレン−（メタ）アクリル酸共重合体、及び（Ｃ）極性官能基を有する樹脂を含む。 - 特許庁

To provide a granular talc-compounded thermoplastic resin composition which gives molded articles having excellent appearances or has excellent talc dispersibility and extrusion-processability (productivity, workability), improved mechanical properties such as flexural modulus and impact strength, and improved hue.例文帳に追加

成形品の外観又はタルクの分散性及び押出加工性（生産性、作業性）に優れ、曲げ弾性率や衝撃強度等の機械的性質及び色調の改善された、顆粒状タルク配合の熱可塑性樹脂組成物を提供する。 - 特許庁

The styrene resin composition is caused to have a flexural modulus of at least 1,800 MPa, an unnotched Charpy impact strength of at least 12 kJ/m^2 and a saturated water absorption ratio of at most 0.4% at a temperature of 60°C and a relative humidity of 90%.例文帳に追加

また、スチレン系樹脂組成物の、曲げ弾性率を１８００ＭＰａ以上とし、ノッチなし試験片のシャルピー衝撃強さを１２ｋＪ／ｍ^２以上とし、温度６０℃、相対湿度９０％での飽和吸水率を０．４％以下とする。 - 特許庁

The plastic sheet 2 has a pencil scratch value measured by the method of the JIS K 5400 tester within the range of B to 3B and ≤1,000 MPa flexural modulus of elasticity of the flexible PBT copolymer alone measured by ASTM D790.例文帳に追加

プラスチックシート状材２は、ＪＩＳ Ｋ ５４００試験機法で測定した鉛筆引っ掻き値がＢ〜３Ｂの範囲で、前記軟質ＰＢＴ系共重合体単独での、ＡＳＴＭ Ｄ７９０で測定した曲げ弾性率が１０００ＭＰａ以下である。 - 特許庁

To provide a resin composition for an exterior trim part of automobiles having excellent moldability and balanced physical properties such as flexural modulus, impact resistance, hardness and brittle temperature, free from flow mark and weld mark on the surface of the molded article and usable without painting.例文帳に追加

成形加工性が優れ、曲げ弾性率、耐衝撃性、硬度及び脆化温度などの物性バランスも良好で、しかも成形品表面にフローマークやウエルドマークが目立たない、無塗装化に対応可能な自動車外装用樹脂組成物を提供する。 - 特許庁

The film is formed by injection-molding a raw material in a molten state and the flexural modulus along the injection flow direction of the film is 6 GPa or above and 20 times or below with respect to the flexural modulus along the surface of the film orthogonally crossing the injection flow direction.例文帳に追加

光路を開閉するための細長い本発明による遮光羽根１３〜２１は、溶融状態の原料を射出成形してなるフィルムから製造され、その射出流動方向に沿った曲げ弾性率が６GＰa以上であり、射出流動方向に沿った曲げ弾性率がこの射出流動方向と直交するフィルム面に沿った方向の曲げ弾性率に対して２０倍以下に設定され、そりが少なく、流動方向に裂け難く、高強度かつ軽量であって安定した品質のものを安価に提供することができる。 - 特許庁

This polypropylene composition for the trim part of the automobile has (a) ≥1,500 MPa flexural modulus, (b) ≥20 kJ/m2 izod impact strength (at 23°C), (c) ≥7 melt index (at 230°C at 2.16 kg load) and ≥200 g weight for scratching and whitening.例文帳に追加

自動車内装部品用ポリプロピレン系組成物は、（ａ）曲げ弾性率が１５００ＭＰａ以上、（ｂ）アイゾッド衝撃強度（２３℃）が２０ｋＪ／ｍ^^^2 以上、（ｃ）メルトインデックス（２３０℃、荷重２．１６ｋｇ）が７以上、及び（ｄ）傷付白化荷重が２００ｇ以上である。 - 特許庁

To provide a flame-retardant polyester resin composition that exhibits excellent flame retardancy, especially a self-extinguishing property without containing a halogen atom-containing flame retardant and also is excellent in mechanical performance, such as elastic modulus, flexural strength, and impact strength, and a method for producing the same.例文帳に追加

ハロゲン原子含有難燃剤を含有しなくとも優れた難燃性、特に自己消火性を示し、しかも弾性率、曲げ強度および衝撃強度等の機械的性能に優れた難燃性ポリエステル樹脂組成物およびその製造方法を提供すること。 - 特許庁

The car seat member is produced by using a polyolefin resin composition which contains 0.3-5 mass parts of titanium dioxide and 0.03-2 mass parts of black pigment based on 100 mass parts of polyolefin and has a flexural modulus of at least 900 MPa.例文帳に追加

ポリオレフィン樹脂１００質量部に対して０．３〜５質量部の二酸化チタン及び０．０３〜２質量部の黒色顔料を含んでなり、曲げ弾性率が９００ＭＰａ以上である、ポリオレフィン樹脂組成物を用いて自動車シート部材を製造する。 - 特許庁

A tray 10 made of a plastic whose flexural modulus is 100 to 600 MPa is fitted into the storage recess 5 to come into contact with the foams 8 and 9, and an end 11 of the tray 10 is engaged with and held by a recessed groove 12 at a peripheral end on a side of opening of the recess 5.例文帳に追加

収納リセス５内に、曲げ弾性率が１００〜６００ＭＰａのプラスチック製のトレイ１０を発泡体８、９に接するように嵌め込み、かつそのトレイ１０の端部１１を収納リセス５の開口側周端部の凹溝１２に噛み込み保持する。 - 特許庁

This glass ceramic has 95×10-7 to 140×10-7/°C coefficient of thermal expansion at-20 to 70°C, preferably ≥85 GPa Young's modulus, ≥10 kg/mm2 flexural strength in a board material of 10 mm thickness, ≥60% light transmittance at 95-1,600 nm wavelength.例文帳に追加

−２０〜＋７０℃における熱膨張係数が９５×１０^-7〜１４０×１０^-7／℃であり、好ましくはヤング率が８５ＧＰａ以上，曲げ強度が１０ｋｇ／ｍｍ^2以上，９５０〜１６００ｎｍの波長の光線透過率が６０％以上のガラスセラミックス。 - 特許庁

This hollow molded product is characterized in that the hollow molded product is formed out of a polyamide resin composition comprising 90-50 wt.% polyamide and 10-50 wt.% inorganic filler, and having ≥5.0 GPa flexural modulus measured according to ASTM D-790, and has ≥0.90 circularity of the cross section shape at the hollow part.例文帳に追加

ポリアミド90〜50質量％と無機強化材10〜50質量％とからなりASTM D−790による曲げ弾性率が5.0ＧＰａ以上であるポリアミド樹脂組成物から形成され、中空部の断面形状の真円度が0.90以上であることを特徴とする中空成形品。 - 特許庁

To provide a polylactic acid-containing resin composition providing a molded article having excellent flexural modulus and impact strength, hardly causing delamination of the surface at injection molding, and exhibiting excellent ability for inhibiting the generation of aldehydes of volatile materials.例文帳に追加

優れた曲げ弾性率と衝撃強度を持つ成形体を形成することができ、しかも射出成形時に表面が剥離せず、揮発性物質であるアルデヒド類に対する優れた発生抑止性能を示すポリ乳酸含有樹脂組成物を提供する。 - 特許庁

(°C) in the DSC curve of the crystalline resin with the flexural modulus of elasticity of 9,000 kg/cm2 or more at 23°C].例文帳に追加

ただし、Ａは２３℃での曲げ弾性率が９０００Ｋｇ／ｃｍ^2以上の結晶性樹脂のＤＳＣ曲線における結晶化ピーク温度（℃）、Ｂは２３℃における曲げ弾性率が９０００Ｋｇ／ｃｍ^2以上の結晶性樹脂のＤＳＣ曲線における融解ピーク温度（℃）である。 - 特許庁

To provide an inexpensive polyphenylene ether composition excellent in heat resistance, flexural modulus, flame retardance, etc. and applicable to injection moldings, blow moldings, tubes, pipes, bottles, automobile external plate members, housing materials, electric/electronic parts, automobile parts, films, sheets, etc.例文帳に追加

安価な樹脂組成物で、耐熱性、曲げ弾性率、難燃性などに優れしかも射出成形体、ブロー成形体、チューブ、パイプ、ボトル、自動車外板部材、ハウジング材、電気・電子部品、自動車部品、フィルム、シートなどに適用可能なポリフェニレンエーテル組成物を提供する。 - 特許庁

The polypropylene cap is made of a resin composition including 70 to 95 wt.% of a homopolypropylene and 5 to 30 wt.% of a modifier composed of a polyolefine-based elastomer, and has a flexural modulus of 800 to 2,000.例文帳に追加

ホモポリプロピレンを７０乃至９５重量％、及びポリオレフィン系エラストマーから成る改質材を５乃至３０重量％の量で含有する樹脂組成物から成り、曲げ弾性率が８００乃至２０００の範囲にあることを特徴とするポリプロピレン製キャップ。 - 特許庁

The chopsticks are made of a plastic material having a flexural modulus of 1 GPa or more and a deflection temperature under load of 190°C or more, e.g., a syndiotactic polystyrene resin, and have a minimum diameter of 1.0 to 3.8 mm in the range of 1 to 10 mm from the tip end.例文帳に追加

曲げ弾性率が１ＧＰａ以上、荷重たわみ温度が１９０℃以上のプラスチック素材、例えばシンジオタクチック・ポリスチレン樹脂を用いて、箸先端からの距離１〜１０ｍｍの範囲における最小径が１.０〜３.８ｍｍとなる形状に成形してなる箸。 - 特許庁

The outer periphery surface region of a neutral axis X parallel to the flat region 10a of the top rod 10 has a reinforcing part 20 having a flexural modulus higher than that of the superelastic alloy or the superelastic resin and oriented in the longitudinal direction.例文帳に追加

そして、穂先竿１０の平面部領域１０ａと平行な中立軸Ｘの外周面領域に、超弾性合金又は超弾性樹脂よりも曲げ剛性の大きい長さ方向に指向した補強部２０が設けられていることを特徴とする。 - 特許庁

To obtain a polyamide resin from which a molding having excellent molding processability and precision, remarkably excellent chemical resistance (oil resistance), flexural modulus, impact resistance, abrasion resistance, durability, sliding properties, etc., a polyamide resin molding using the same and to provide a method for producing the molding.例文帳に追加

成形加工性や精度にも優れ，耐薬品性（耐油性）、曲げ弾性率、耐衝撃性、耐摩耗性、耐久性、摺動性などが顕著に優れた成形品が得られるポリアミド樹脂と、それを用いたポリアミド樹脂成形品、および、該成形品の製造方法を提供すること。 - 特許庁

The chamber member 6 comprises materials having 500 MPa flexural modulus or less, therefore, collapse load tolerance upon pedestrian collision becomes 2 kN or less, and impact absorbing performance of an absorber 5 (reaction force upon pedestrian collision is 6-8 kN) provided in a bumper 2 is not adversely affected.例文帳に追加

チャンバ部材６は、曲げ弾性率が５００ＭＰａ以下である材料からなるので、歩行者衝突時の許容潰れ荷重が２ｋＮ以下となり、バンパ２内に設けられるアブソーバ５（歩行者衝突時の反力が６〜８ｋＮ）の衝撃吸収性能を阻害することがない。 - 特許庁

This thermoplastic polyester elastomer is characterized by <1,000 MPa flexural modulus, >50% retention of breaking elongation after a heat aging test, >50% retention of breaking elongation after a water-resisting aging test, and <-15°C temperature exhibiting the maximum value of loss tangent (tan δ).例文帳に追加

曲げ弾性率＜１０００ＭＰａであり、耐熱老化テスト後の切断時伸び保持率＞５０％、耐水老化テスト後の切断時伸び保持率＞５０％であり、かつ、損失正接ｔａｎδが最大値を示す温度が＜−１５℃であることを特徴とする熱可塑性ポリエステルエラストマー。 - 特許庁

This thermoplastic polyester elastomer is characterized in that the flexural modulus is <1,000 MPa and elongation-retaining ratio in breakage after heat aging test is >50% and a temperature at which the loss tangent tan δ exhibits maximum value is <-15°C.例文帳に追加

曲げ弾性率＜１０００ＭＰａであり、耐熱老化テスト後の切断時伸び保持率＞５０％、耐水老化テスト後の切断時伸び保持率＞５０％であり、かつ、損失正接ｔａｎδが最大値を示す温度が＜−１５℃であることを特徴とする熱可塑性ポリエステルエラストマー。 - 特許庁

This case for portable electronic equipment has at least a part consisting of a thermoplastic elastomer composition obtained by dispersing a rubber at least a part of which is vulcanized, in a thermoplastic resin, and having ≥25,000 kg/cm2 flexural modulus and ≥20 kg.cm/cm izod impact strength.例文帳に追加

熱可塑性樹脂中に、少なくとも一部が加硫されたゴムが分散してなり、曲げ弾性率が２５０００［ｋｇ／ｃｍ^2 ］以上、かつ、アイゾット衝撃強度が２０［ｋｇ・ｃｍ／ｃｍ］以上である熱可塑性エラストマー組成物より少なくとも一部がなる携帯電子機器筐体。 - 特許庁

In this hose for civil engineering work having a fiber reinforcement layer 3 between an inner layer 2 and an outer layer 4 made out of a resin and/or rubber, a thermoplastic resin of flexural modulus of 300-5000 MPa is used in the resin layer configurating the inner layer 2 or the outer layer 4.例文帳に追加

樹脂及び／又はゴムからなる内面層２と外面層４との間に、繊維補強層３を介在させた土木工事用ホースであって、内面層２又は外面層４を構成する樹脂層に、曲げ弾性率３００〜５０００ＭＰａの熱可塑性樹脂を使用する。 - 特許庁

The soft polymer consists of a rubber-modified polymer (C) which is obtained by polymerizing a vinyl monomer (B) containing a (meth)acrylate in the presence of a rubbery polymer (A) having a Mooney viscosity (ASTM D1646, ML(1+4)121°C) of ≤8 and which has a flexural modulus (ISO) of ≤700 MPa.例文帳に追加

ムーニー粘度（ＡＳＴＭ Ｄ１６４６，ＭＬ（１＋４）１２１℃）が８以下であるゴム状重合体（Ａ）の存在下に（メタ）アクリル酸エステルを含むビニル系単量体（Ｂ）を重合して得られ、曲げモジュラス（ＩＳＯ）が７００ＭＰａ以下であるゴム変性重合体（Ｃ）からなる軟質性重合体。 - 特許庁

Since a stress acting on the recording head based on the rigidity of the first ink supply member 11 can be absorbed by the second ink supply member 13 composed of a rubber material having a low flexural modulus, the stress acting on the recording head can be reduced.例文帳に追加

したがって、第１のインク供給部材１１の剛性に基づいて記録ヘッドに作用する応力を、曲げ弾性率が低いゴム材料により形成された第２のインク供給部材１３により吸収することができ、記録ヘッドに作用する応力を低減させることができる。 - 特許庁

To provide a method of manufacturing a polyethylene porous product is used in fixing or moving an article by suction and having an arithmetic average roughness (Ra) of the surface of ≤1 μm at least at its one side, an air flow resistance of 300-1,500 mmAq, and a flexural modulus of 500-7,000 kg/cm2.例文帳に追加

吸引により固定乃至は移動する際に使用する多孔質体の少なくとも片面の表面粗さが算術平均粗さ（Ｒa）で１μｍ以下、通気抵抗を３００〜１５００mmAq、曲げ弾性率が５００〜７０００kg/cm^2のポリエチレン製多孔質体の製造方法を提供する。 - 特許庁

The cylindrical body made of the fiber-reinforced plastic is characterized by the matrix of the fiber-reinforced plastic, comprising an epoxy resin-cured product containing fullerenes having ≤10 μm maximum particle diameter, and ≥0.9 retention of 90° flexural modulus of the fiber-reinforced plastic.例文帳に追加

繊維強化プラスチック製円筒体であって、繊維強化プラスチックのマトリックスは、最大粒径が１０μｍ以下のフラーレン類を含むエポキシ樹脂硬化物であり、かつ、繊維強化プラスチックは、その９０度曲げ剛性保持率が０．９以上であることを特徴とする繊維強化プラスチック製円筒体。 - 特許庁

The composition obtained by adding 30-100 mass part of an olefin-based resin whose flexural modulus is ≤1,000 MPa and 70 mass part or less of an ethylene-α-olefin-based resin to 100 mass part of a styrene-based elastomer, allows to form the flexible medical tube excellent in the folding resistance and transparency.例文帳に追加

スチレン系エラストマー１００質量部に、曲げ弾性率１０００ＭＰａ以下のオレフィン系樹脂３０〜１００質量部、エチレン−α−オレフィン系樹脂７０質量部以下を添加してなる組成物は、柔軟かつ耐折曲性の良好な、そして透明性に優れた医療用チューブを与える。 - 特許庁

To provide a polylactic acid-containing polypropylene resin composition for extrusion molding which has an excellent flexural modulus, excellent heat resistance and impact resistance and an excellent melt tension and can easily form an extrusion molded product such as a blow molded product, a method for producing the same, and an extrusion molded product comprising the same.例文帳に追加

優れた曲げ弾性率、耐熱性及び耐衝撃性と、優れた溶融張力を持ちブロー成形体などの押出成形体を容易に形成することができる押出成形用ポリ乳酸含有ポリプロピレン樹脂組成物、その製造方法及びそれからなる押出成形体を提供する。 - 特許庁

This laminated body at least has the resin layer (A) including a propylene resin (a), a resin layer (B) including an acrylic resin (b) having a flexural modulus of 100 MPa or more to 1,500 MPa or less and a resin layer (C) including an acrylic resin (c) in the order of the resin layers (A), (B) and (C).例文帳に追加

プロピレン系樹脂（ａ）を含む樹脂層（Ａ）、１００ＭＰａ以上１５００ＭＰａ以下の曲げ弾性率を有するアクリル系樹脂（ｂ）を含む樹脂層（Ｂ）、及びアクリル系樹脂（ｃ）を含む樹脂層（Ｃ）を少なくとも有し、該樹脂層（Ａ）、（Ｂ）及び（Ｃ）がこの順序で積層されている積層体。 - 特許庁

The resinous hinged cap element has 300-1,000 MPa flexural modulus, comprises (A) polyacetal resin and (B) thermoplastic elastomer polyacetal resin composition having ≤60°C glass transition temperature, has both of hinge properties and molded product surface coatability and comprises a cap part 1 and a hinge part 2.例文帳に追加

曲げ弾性率が３００〜１０００ＭＰａの範囲である、（Ａ）ポリアセタール樹脂と（Ｂ）ガラス転移温度が６０℃以下の熱可塑性エラストマーポリアセタール樹脂組成物からなり、ヒンジ特性と成形品表面の塗装性を併せもつ、キャップ部１及びヒンジ部２を有する樹脂製ヒンジ付きキャップ部品。 - 特許庁

The resin hinge comprises a movable side cam element comprising a thermoplastic resin (A) having 0.05-0.3 friction factor and a fixed side cam element comprising a thermoplastic resin (B), wherein the ratio of flexural modulus (ASTM, D790) of the thermoplastic resin (A) and the thermoplastic resin (B), (A)/(B), is 0.1-1.例文帳に追加

摩擦係数が０．０５〜０．３である熱可塑性樹脂（Ａ）よりなる可動側カム部品と、熱可塑性樹脂（Ｂ）よりなる固定側カム部品を有し、該熱可塑性樹脂（Ａ）と該熱可塑性樹脂（Ｂ）の曲げ弾性率（ＡＳＴＭ、Ｄ７９０）の比（Ａ）／（Ｂ）が０．１〜１である樹脂ヒンジ。 - 特許庁