compounding conditionとは 意味・読み方・使い方

To provide a wax composition for rubber compounding which, when it is used for a vibration proof rubber product, can not only keep a coefficient of friction at a normal temperature condition lower but also does not cause large difference in the coefficient of friction even when it is exposed for many hours in a condition of such a high temperature as 120°C.例文帳に追加

防振ゴム製品に使用したときに、通常の温度条件下での摩擦係数を低く抑えることができるだけで無く、１２０℃という高温条件下に長時間曝されても、摩擦係数の大きな変動を生じない、ゴム配合用ワックス組成物の提供。 - 特許庁

The rubber grip for a golf club is manufactured, in a compounding process for manufacturing the rubber grip for the golf club from raw rubber, by mixing the natural vegetable aromatic component of 0.05-10 wt.% with respect to the raw rubber of 100 wt.% by external rate together with various compounding agents, which stabilizes the mental condition, gives the relaxation effect, concentrates attentions, and raises concentration.例文帳に追加

生ゴムからゴルフクラブ用ゴムグリップを製造する配合工程において、生ゴム１００重量％に対して、外割として、精神状態を安定させると共に、リラックス効果を与えて、神経を集中させ、集中力を高めることができる植物性天然芳香成分０．０５〜１０重量％を、各種配合剤と共に混合してゴルフクラブ用ゴムグリップを製造する。 - 特許庁

To provide a base oil for a four-cycle engine oil having a characteristic of stably retaining an oil film under a severe condition for a long time without compounding an additive, and showing extreme excellence in rocker arm pad scuffing prevention performance, a camshaft abrasion prevention performance and a camshaft pitching prevention performance.例文帳に追加

添加剤を配合しなくても、長時間過酷な条件で安定な油膜保持性を有し、ロッカーアームパッドスカッフィング防止性能、カムシャフト摩耗の防止性能及びカムシャフトピッチングの防止性能に極めて優れた４サイクルエンジン油基油を提供する。 - 特許庁

To provide a method for making paper, by which the paper can be made at a low cost in a high yield, even when a paper-making raw material containing mechanical pulp and waste paper at increased compounding rates is used to make the paper, especially even when newspaper or medium quality paper is used in an acidic condition to make the paper.例文帳に追加

機械パルプや古紙の配合比率が増加した製紙原料を用いて抄造する場合、また特に酸性において新聞用紙あるいは中質紙原料を抄造する場合でも低コストで高い歩留率を発現する製紙方法を提供する。 - 特許庁

Especially, the rubber kneading method is preferably used in the rough kneading of a raw material rubber, the compounding amount of a peptizer is controlled on the basis of a viscosity value obtained by measuring Mooney viscosity prescribed in JIS K6300 under a condition that a temperature is 60°C and the (L-type) number of rotations of a rotor is 6 rmp before rough kneading.例文帳に追加

特に、原料ゴムの素練りにおいて、該素練り前にＪＩＳ Ｋ６３００に規定するムーニー粘度を温度６０℃、ローター（Ｌ型）回転数６ｒｐｍの条件で実測した粘度値に基づき、上記嚼解剤（ペプタイザー）の配合量を制御するゴムの混練方法に好適に適用される。 - 特許庁

After a rubber compd. formed by compounding a synthetic rubber polymer with a carbon black and a vulcanizing agent is heated in a rubber mold and is molded under semi-vulcanization condition, it is inserted into an injection molding mold and after an ultrahigh mol.wt. polyethylene is injected into the above described mold to perform compression molding, it is taken out of the above described mold and is vulcanized under vulcanization condition.例文帳に追加

合成ゴムのポリマーにカーボンブラックと加硫剤とを配合して形成したゴムパウンドを、ゴム金型内で加熱して半加硫状態で成形したのち、射出成形金型内にインサートし、超高分子量ポリエチレンを前記金型内に射出して圧縮成形後、前記金型から取り出して加硫状態に加温する。 - 特許庁

An apparatus for synthesizing emulsion fuel emulsifies fuel oil and water using cavitation generated by a shear flow occurred by jetting the fuel oil of an amount necessary for combustion and the water of a definite ratio from a compound nozzle, and combusts instantly, and, in addition, reduces a fuel cost and purifies exhaust gas by adjusting a compounding ratio of the fuel and the water according to a condition of combustion.例文帳に追加

燃焼に必要な量の燃料油と、一定比率の水を、複合ノズルから噴出するせん断流によって生じるキャビテーションを利用して、燃料油と水をエマルジョン化し、これを即時に燃焼させる、併せて、燃焼状態に応じて燃料油と水の配合比を調節する、ことで燃料費を低減し、排気ガスを浄化する、エマルジョン燃料合成装置。 - 特許庁

A thermoplastic elastomer composition is obtained by dynamically crosslinking a mixture under the condition of being melted, wherein the mixture contains a specific compounding ratio of an addition-polymerized block copolymer (I), specific functionalized addition-polymerized block copolymer (II), thermoplastic polyamide polymer (III), crosslinking agent (IV) and softener for a rubber (V).例文帳に追加

熱可塑性エラストマー組成物は、特定の付加重合系ブロック共重合体（Ｉ）、特定の官能化付加重合系ブロック共重合体（II）、熱可塑性ポリアミド系重合体（III）、架橋剤（IV）及びゴム用軟化剤（Ｖ）を特定の配合比で含有する混合物を、溶融条件下で動的に架橋処理してなるものである。 - 特許庁