a MORとは 意味・読み方・使い方

(1) A film MOR-c value is ≥1.05 and ≤5.0; (2) a molecular-chain principal-axis orientation angle is -30° to 30° against an MD direction; and (3) a difference between the maximum and the minimum values of the film MOR-c is 1.0 or below.例文帳に追加

（１）フィルムのＭＯＲ−ｃ値が１．０５以上５．０以下、（２）分子鎖主軸配向角がＭＤ方向に対して−３０から３０度、（３）フィルムＭＯＲ−ｃ値の最大値と最小値の差が１．０以下 - 特許庁

The film shows: (1) a haze of 4% or less; (2) a MOR (maximum oriented ratio) value of 1.80 to 2.10; and (3) a change amount in the orientation angle of 3.0° to 5.0° per 500 mm.例文帳に追加

（１）ヘイズが４％以下、（２）ＭＯＲ値が１．８０〜２．１０、（３）配向角の変化量が５００ｍｍ当り３．０°〜５．０° - 特許庁

To provide a new MOR type metalloaluminosilicate with a metal introduced into a skeleton, and a method for producing the same, which is easily and industrially applicable.例文帳に追加

本発明は、骨格に金属を導入した新規なＭＯＲ型メタロアルミノシリケート、及び簡便且つ工業的に適用可能なその製造方法を提供するものである。 - 特許庁

The optical polyester film is characterized in that the thickness of the film is 1-12 μm, the film haze is 8.0% or less and the MOR-C value measured by a micro-wave system molecule orientation meter is 3.0 or less.例文帳に追加

フィルムの厚さが１〜１２μｍであり、フィルムヘーズが８．０％以下であり、マイクロ波方式分子配向計で測定したＭＯＲ＿Ｃ値が３．０以下であることを特徴とする光学用ポリエステルフィルム。 - 特許庁

A perfluoro compound having three or more carbons and having no double bond is removed by adsorption with the perfluoro compound adsorbent comprising any zeolite among LSX type zeolite, X type zeolite, MOR type zeolite and MFI type zeolite.例文帳に追加

二重結合を有しない炭素数３以上のパーフルオロ化合物をＬＳＸ型、Ｘ型、ＭＯＲ型及びＭＦＩ型のいずれかのゼオライトを含んでなるパーフルオロ化合物の吸着剤で吸着除去する。 - 特許庁

The polyester film for a base material-less double-sided adhesive sheet is a release film which has a silicone-based release layer containing 0.5 to 5.0 wt.% of a transition metal catalyst of at least one kind, with the MOR value of the release film being 1.5 to 3.0.例文帳に追加

少なくとも１種類以上の遷移金属系触媒を０．５〜５．０重量％含有するシリコーン系離型層を有する離型フィルムであり、当該離型フィルムのＭＯＲ値が１．５〜３．０であることを特徴とする基材レス両面粘着シート用ポリエステルフィルム。 - 特許庁

The film is composed of a crystalline polyester and has a difference ΔTcg of 60°C or less between a crystallization peak temperature (Tc) and a glass transition temperature (Tg) in a second run in a differential scanning calorimetry (DSC), an MOR of at least 3 in the surface of the film measured by a molecular orientation meter, and a deviation of an orientation angle within ±2°.例文帳に追加

結晶性ポリエステルからなり、示差走査熱量測定（ＤＳＣ）による２ｎｄＲｕｎにおける、結晶化ピーク温度（Ｔｃ）とガラス転移点温度（Ｔｇ）との差ΔＴｃｇが６０℃以下、かつ、分子配向計にて測定されたフィルム面内におけるＭＯＲが３以上であり、配向角度の偏差が±２°以内であることを特徴とするフィルムとする。 - 特許庁