To provide a steel for a machine structure which has excellent cold workability, in which, adjustment such as the limitation of components is not difficult, and further, the deposition of cementite is suppressed, to provide a method for producing the same, and to provide a method for producing a worked component using the steel for a machine structure.例文帳に追加

成分の制限等の調整が難しくなく、また、セメンタイトの析出を抑制して、冷間加工性に優れた機械構造用鋼、その製造方法、並びに、機械構造用鋼を用いた加工部品製造方法を提供する。 - 特許庁

To provide a brazing filler metal which has an excellent cold workability, a melting point which is similar to that of Cu brazing filler metal or lower, excellent corrosion resistance and oxidation resistance, in particular, the excellent oxidation resistance in a hot and humid environment, and to provide a clad material and a brazed structural body.例文帳に追加

優れた冷間加工性を備え、Ｃｕろう程度あるいはそれ以下の融点を有し、耐食性および耐酸化性、特に高温湿潤雰囲気での耐酸化性に優れたろう材、その他にクラッド材、ろう接構造物を提供する。 - 特許庁

To provide a heat insulation cover for a meter unit providing very easy attachment and detachment to the meter unit, realizing low costs and superior workability which can be positively carried out, and capable of positively preventing trouble due to freezing of water in a cold district or the like.例文帳に追加

メータユニットへの取付け・取外しが極めて簡単で、且つ、確実に行い得る優れた作業性並びに低コストを実現し、しかも、寒冷地等における水凍結によるトラブルを確実に防止し得るメータユニット用保温カバーを提供する。 - 特許庁

To provide a ferritic stainless steel slab with which the solidified structure is made to fine equiaxed crystal and the workability to the steel sheet can drastically be improved while preventing the closure of a tundish nozzle and the development of the surface flaw on a continuous casting slab and cold-rolled sheet.例文帳に追加

タンディッシュノズルの閉塞および連鋳スラブや冷延板での表面疵発生を防止しながら、凝固組織を微細等軸晶化し、鋼板にける加工性を顕著に改善することのできるフェライト系ステンレス鋼スラブを提供する。 - 特許庁

To provide a cold insulation container in which vegetables having upper portions wider than lower portions can be stored in standing positions and which effectively prevents toppling of the vegetables at the start of packing the vegetables and has a degree of freedom of shape and size to improve workability in storage work.例文帳に追加

上部が下部より拡がった形の野菜を立てて収納する保冷容器において、詰め始めの際の転倒を効果的に防止でき、形状や大きさ等に対する自由度もあり、収納時の作業性を向上できるようにする。 - 特許庁

To obtain a low-odor resin composition which is excellent in cold-setting property, surface-drying property and workability and, after drying, yields a coating film excellent in physical properties, surface appearance and adhesion and assembly adhesion properties to concrete, asphalt, wood, or the like.例文帳に追加

本発明の課題は、低臭気性、常温硬化性、表面乾燥性、作業性、乾燥後の塗膜の物性、表面の外観ならびにコンクリート、アスファルト、木材等に対する接着性、二次接着性に優れる樹脂組成物を提供することである。 - 特許庁

To provide a steel wire rod provided with sufficient deformability by the reduction of deformation resistance in low-medium carbon steel and low-medium carbon low alloy steel as hot-rolled and excellent in cold workability even if spheroidizing annealing treatment is simplified or omitted.例文帳に追加

熱間圧延ままの低中炭素鋼や低中炭素低合金鋼における変形抵抗を低減して十分な変形能を与え、球状化焼鈍処理を簡略化若しくは省略しても冷間加工性に優れた鋼線材を提供する。 - 特許庁

To provide superclean steel which is intended to be used for valve springs, suspension springs, fine steel wire or the like and exhibits performance exceeding that of the conventional material in cold workability and fatigue properties by controlling oxide inclusions in the steel.例文帳に追加

弁ばねや懸架ばね、極細鋼線などを対象とし、鋼中の酸化物系介在物を制御することにより、冷間加工性や疲労特性において従来材を凌駕する性能を発揮する高清浄度鋼を提供すること。 - 特許庁

The clad plate having excellent cold workability is characterized in that the surfaces on both the sides of a magnesium alloy plate comprising, by mass, 5.5 to 11.0% lithium, and the balance magnesium with impurities are held with aluminum plates or aluminum alloy plates.例文帳に追加

質量％で５．５％から１１．０％までのリチウムを含有し、残部がマグネシウムおよび不純物であるマグネシウム合金板の両側表面を、アルミニウム板またはアルミニウム合金板で挟んだことを特徴とする冷間加工性に優れたクラッド板。 - 特許庁

To provide a cold rolled steel sheet for enameling treatment having excellent enameling properties and workability, and having satisfactory adhesion of an oxide coating film to be formed on a non-glazed face in firing treatment after glazing, and to provide a method for producing an enameling worked product.例文帳に追加

ほうろう特性及び加工性が優れると共に、施釉後の焼成処理において非施釉面に形成される酸化皮膜の密着性が良好なほうろう処理用冷延鋼板及びほうろう加工品の製造方法を提供する。 - 特許庁

To provide a method for producing cold offset printing paper, particularly acid-free newsprint paper, excellent in ink impressionability under cold offset printing, slight in piling with suppressed paper dust emission, and having excellent printability and printing workability, through accomplishing high performance development of a surface coating agent such as uniform coating surface and resistance to water absorption in applying the surface coating agent by a spray coating system.例文帳に追加

スプレー塗工方式による表面塗工剤の塗工において、均一な塗工面、吸水抵抗性など表面塗工剤の高い性能発現を得ることで、コールドオフセット印刷時のインキ着肉性に優れ、また紙粉が抑えられてパイリングの少ない、優れた印刷適性、印刷作業性を持つコールドオフセット印刷用紙、特に中性新聞用紙の製造方法を提供する。 - 特許庁

To provide a high strength cold rolled steel sheet which has high strength and excellent workability, wherein the maximum tensile strength is ≥900 MPa and the mechanical cutting property is excellent and a method for producing the same, and to provide a high strength galvanized steel sheet and a method for producing the same.例文帳に追加

高強度であるとともに加工性に優れ、機械切断特性に優れた引張最大強度９００ＭＰａ以上の高強度冷延鋼板及びその製造方法、並びに、高強度亜鉛めっき鋼板及びその製造方法を提供する。 - 特許庁

To provide an extremely lightweight magnesium-lithium alloy which has corrosion resistance and cold workability compatibly in a high level, has tensile strength to some extent, and is reduced in surface electric resistance value, to provide a rolled material thereof, to provide a formed article, and to provide a process for producing them.例文帳に追加

耐食性と冷間での加工性とを高レベルで両立させ、ある程度の引張強度を有するとともに、表面電気抵抗値を低くした、非常に軽量なマグネシウム−リチウム合金、その圧延材および成型品と、その製造方法とを提供する。 - 特許庁

To provide an aqueous adhesive composition for wet laminate, relating mainly with the wet lamination such as adhesion or the like between paper and aluminum foil, which is excellent in environmental fitness and workability, and which can improve water resistance, heat resistance, freezing resistance, cold resistance, oil resistance and corrosion resistance of a laminate article.例文帳に追加

主として紙とアルミニウム箔との接着等のウエットラミネーションに関し、環境適性と作業性に優れ、ラミネート物の耐水性、耐熱性、耐冷凍性、耐寒性、耐油性、耐蝕性を向上しうるウエットラミネート用水性接着剤組成物を提供する。 - 特許庁

To provide a rolled sheet tempered material which consists of an Al-Mg alloy, and has a heat treatment degree of H32 to 36, particularly, which stably has excellent bending workability as a thick sheet of about 0.8 mm by a process where process annealing during cold rolling is obviated.例文帳に追加

Ａｌ−Ｍｇ系合金からなる調質度Ｈ３２〜Ｈ３６の圧延板調質材、特に０．８ｍｍ程度以上の厚い板として、冷間圧延中途の中間焼鈍を省略したプロセスで、曲げ加工性が安定して優れたものを提供する。 - 特許庁

In the method for producing the steel tube having excellent workability, the draft in cold rolling is controlled to 25 to <60%, and the steel is annealed at the average heating rate of 4 to 200°C/hr so as to control the maximum arrival tempearture in the range of 600 to 800°C, and is made into a tube.例文帳に追加

冷間圧延の圧下率を２５〜６０％未満とし、平均加熱速度４〜２００℃／時間で加熱し、最高到達温度を６００〜８００℃とする焼鈍を行ったのち、造管することを特徴とする加工性に優れた鋼管の製造方法。 - 特許庁

To provide a hot-forged part in which good cold-workability is imparted to a flange part and also, high fatigue strength is imparted to a boundary part between the flange part and a shaft part, when the shaft part having the flange part is manufactured by hot-forging using a steel blank.例文帳に追加

鋼素材を用いて、フランジ部を有する軸部品を熱間鍛造により製造するに当り、フランジ部に良好な冷間加工性を付与するとともに、フランジ部と軸部との境界部に高い疲労強度を付与した、熱間鍛造部品を提供する。 - 特許庁

To provide a rolled sheet tempered material which consists of an Al-Mg alloy, and has a heat treatment degree of H32 to 36, particularly, which has stably excellent bending workability as a thick sheet of about ≥0.8 mm by a process where process annealing during cold rolling is obviated.例文帳に追加

Ａｌ−Ｍｇ系合金からなる調質度Ｈ３２〜Ｈ３６の圧延板調質材、特に０．８ｍｍ程度以上の厚い板として、冷間圧延中途の中間焼鈍を省略したプロセスで、曲げ加工性が安定して優れたものを提供する。 - 特許庁

As to this steel, by precipitating C in the steel as VC carbides at a temp. higher than the cementite forming temp., the content of solid solution C in the steel is substantially reduced, the amt. of pro-eutectoid ferrite is remarkably increased, and its cold workability is remarkably improved.例文帳に追加

鋼中のＣをセメンタイト生成温度よりも高温でＶＣ炭化物として析出させることにより、鋼中の固溶Ｃ量を実質的に低減させ、初析フェライト量を大幅に増加させ、冷間加工性を著しく向上させたものである。 - 特許庁

To provide an insulating oil cover which is more improved in oil resistance, thermal resistance, cold temperature resistance, impermeability to gases, flexibility, flexing characteristics, processability during processing, and workability in a fixing operation than a conventional one formed of synthetic rubber laminated cloth as components.例文帳に追加

従来の合成ゴム積層布を構成材とするものに比し、耐油性、耐熱性、耐寒性及びガス不透過性に富み、柔軟性があって屈曲特性が優れ、更に、加工時の作業を向上させると共に取り付け時の作業をも容易にしたことにある。 - 特許庁

To provide a 6000 series aluminum alloy sheet whose press formability and bending workability are improved even if the sheet thickness is improved or impurity elements are increased, and further, even in the case annealing is not performed after hot rolling and also before cold rolling, and to provide a production method therefor.例文帳に追加

板厚の増加や不純物元素の増加に伴っても、更に、熱延後で冷間圧延前の焼鈍を施こさない場合でも、プレス成形性や曲げ加工性を向上させた6000系アルミニウム合金板と、その製造方法を提供することを目的とする。 - 特許庁

To provide an iron-based material for machine structural use from which a machine component which is provided with both cold workability and final component strength and which is also excellent in strength properties in a high temperature use environment can be obtained without necessarily containing high concentration of C and an alloy element in steel.例文帳に追加

鋼中に高濃度のＣおよび合金元素を必ずしも含有させることなく、冷間加工性と最終部品強度を兼備し、更には高温使用環境における強度特性にも優れた機械部品が得られる機械構造用鉄系材料の提供。 - 特許庁

To provide a high strength cold rolled steel sheet which has excellent workability and strength, wherein surface defects are suppressed and fatigue durability is excellent, and the maximum tensile strength is ≥900 MPa, and a method for producing the same, and to provide a high strength galvanized steel sheet and a method for producing the same.例文帳に追加

優れた加工性及び強度を有し、表面欠陥が抑制されるとともに疲労耐久性に優れた引張最大強度９００ＭＰａ以上の高強度冷延鋼板及びその製造方法、並びに、高強度亜鉛めっき鋼板及びその製造方法を提供する。 - 特許庁

To provide a magnesium alloy which is suitable for the manufacture of a thin sheet, a filler rod, an extruded molding and/or a die-cast molding and a die-cast component, specifically, a magnesium alloy which has excellent workability, high corrosion resistance, improved weldability, a high yielding point and excellent cold formability.例文帳に追加

薄板、溶接棒、押出成形品及び／又はダイカスト成形品及びダイカスト構成部材の製造に適するマグネシウム合金、即ち良好な加工性、高い耐蝕性、改善された溶接性、高い降伏点並びに良好な冷間成形性を有するマグネシウム合金を提供する。 - 特許庁

To provide a lubricant for metal plastic working such as for use in film-forming cold forging processes for carbon steel, alloy steel, etc., excellent in workability, causing no deterioration of objects such as phosphorus infiltration, being friendly to the environment with low waste liquid levels, and leading to the reduction in plant and equipment investment cost and also in operating cost.例文帳に追加

炭素鋼、合金鋼などの皮膜形成型冷間鍛造加工において、加工性に優れ、浸リン等の変質を起こさず、廃液量が少なく環境に対する負荷が低く、そして設備投資や操業費用の低減に繋がる、金属塑性加工用潤滑剤を提供すること。 - 特許庁

To provide a high carbon hot rolled steel sheet to which B is added, and, even if, upon hardening, long time heating is performed in an atmosphere in which air is mixed and carbon potential is controlled, which can stably obtain excellent hardenability, also, has the total elongation El of ≥37%, and has excellent cold workability, and to provide a method for producing the same.例文帳に追加

Bが添加されており、焼入れ処理時に空気を混合してカーボンポテンシャルを制御した雰囲気中で長時間加熱しても安定して優れた焼入れ性が得られ、かつ全伸びElが37%以上で優れた冷間加工性を有する高炭素熱延鋼板およびその製法を提供する。 - 特許庁

To provide a thermosetting type adhesive composition having excellent workability capable of curing in a relatively short time, showing good adhesiveness to metallic materials, etc., and having cold weather resistance in addition to heat resistance and the above-mentioned properties, and adhesive sheet therewith.例文帳に追加

比較的短時間で硬化しうる優れた作業性を有し、かつ金属材料等に対しても良好な接着性を示し、更には耐熱性、また前記性能に加えて、耐寒性をも併せ有する熱硬化型接着剤組成物およびその接着シートを提供すること。 - 特許庁

To provide a method for producing a fine diameter wire made of titanium or a titanium alloy having a beautiful surface, excellent in secondary cold workability, and in which the time required for mirror polishing of about 1 μm by R max is short as possible in surface polishing for the wire rod executed after heat treatment, i.e., excellent in polishability.例文帳に追加

表面が美麗で、２次冷間加工性に優れ、熱処理後におこなう線材の表面研磨において、Ｒmax で１μｍ程度の鏡面研磨に要する時間が可及的に短い、いわゆる研磨性に優れたチタンまたはチタン合金製の細径線材の製造方法を提供する。 - 特許庁

To produce steel excellent in cold workability after spheroidizing annealing and induction hardenability having graded grains without grain coarsening even if induction hardening is executed under the conditions of high temp. and long time, to provide parts for machine structure using it as a base material and to provide a method for producing the same.例文帳に追加

球状化焼鈍後の冷間加工性と高周波焼入れ性に優れ、従来よりも高温且つ長時間の条件で高周波焼入れしても粗粒化せず整細粒を呈する鋼と、それを母材とする機械構造用部品及びその製造方法を提供する。 - 特許庁

To provide a structural member for use in an eyeglass which has a super elastic property and a shape memory property while retaining an excellent biocompatibility in spite of the fact that it is Ni-free, and which also has an excellent cold workability; an eyeglass frame comprising the structural member; and a process for producing the structural member or eyeglass frame.例文帳に追加

本発明は、Ｎｉフリーで、生体親和性に優れているにも拘らず超弾性特性及び形状記憶特性を有し、しかも優れた冷間加工性を有する眼鏡用部材及びこれを含む眼鏡用フレーム並びにこれらの製造方法を提供することである。 - 特許庁

To provide a steel for a carburized component, to a component produced through a spheroidizing annealing, cold forging, and a carburizing, quenching and tempering stage, while having excellent workability, in which the coarsening of crystal grains even in the subsequent carburizing is suppressed, and having excellent impact resistance and impact fatigue resistance.例文帳に追加

球状化焼鈍後、冷間鍛造を行い、浸炭焼入焼戻し工程で製造される部品に対し、優れた加工性を有しながら、その後の浸炭でも結晶粒の粗大化を抑制し、優れた耐衝撃特性、耐衝撃疲労特性を有する浸炭部品用鋼を提供する。 - 特許庁

To provide a 6000 type high-strength aluminum alloy wire and rod material which is excellent in softening resistance, maintains high mechanical characteristics even when being exposed to a high temperature for a long time and is excellent in both of cold workability and corrosion resistance, and to provide a method of manufacturing the high-strength aluminum alloy wire and rod material.例文帳に追加

長時間高温に曝された場合にも、耐軟化性が優れて高い機械的諸特性を保持でき、冷間加工性や耐食性も合わせて優れた、６０００系高強度アルミニウム合金線棒材およびその製造方法を提供することを目的とする。 - 特許庁

To produce a steel wire rod in which deformation resistance in low- medium carbon steel and low-medium carbon low alloy steel as-hot rolled is reduced to impart sufficient deformability and exhibiting excellent cold workability even if spheroidizing annealing treatment is obviated and to provide a method useful for producing such steel wire rod.例文帳に追加

熱間圧延ままの低中炭素鋼や低中炭素低合金鋼における変形抵抗を低減して十分な変形能を与え、球状化焼鈍処理を省略しても優れた冷間加工性を示す鋼線材、およびその様な鋼線材を製造する為の有用な方法を提供する。 - 特許庁

To provide a stainless steel material as the material having excellent plastic workability and corrosion resistance and also having a hydrogen embrittlement resisting function, and particularly suitable as the one for heading or molding in cold and warm conditions, a stainless steel wire, and a stainless steel formed part obtained by subjecting them to plastic working.例文帳に追加

塑性加工性とともに耐食性にすぐれ、かつ耐水素脆性機能を兼備する好適材料として、特に冷間や温間状態での圧造加工用、成形加工用として好適するステンレス鋼材料、ステンレス鋼線並びにこれらを塑性加工してなるステンレス鋼成形品の提供を目的とする。 - 特許庁

To provide a method for manufacturing a clad material, which manufactures a clad plate by covering the surface of a magnesium-lithium-based alloy plate with an aluminum or aluminum alloy plate and imparts excellent strength, lightness, cold workability, and corrosion resistance to the clad material, and which manufactures it at more advantageous cost than conventional joining techniques of rolling, and to provide a clad material.例文帳に追加

マグネシウム−リチウム系合金板の表面にアルミニウムまたはその合金板を被覆したクラッド板であって、強さや軽さや冷間加工性に加えて耐食性にも優れ、しかも前記従来の圧延接合技術に比べてコスト的に有利なクラッド材の製造方法およびクラッド材を提供する。 - 特許庁

To obtain a cold-setting composition that has practically good workability without trouble on the viscosity of the composition, gives flexible hardened products and bears hydrolyzable silicon groups that causes no contamination around sealed areas, when the composition is used as a sealing agent and no contamination of a coating material, when the coating material is applied to the surface of the sealing agent.例文帳に追加

組成物の粘度が実用上問題なく作業性良好であって、その硬化物が柔軟性を有し、かつ、シーリング剤等に使用した場合にシーリング目地周辺の汚染や、シーリング剤表面に塗料が塗られた場合に塗料汚染がない加水分解性ケイ素基を有する室温硬化性組成物を提供する。 - 特許庁

To provide a reactive hot-melt adhesive for bookbinding, excellent in adhesive strength, high-speed workability, openability of book pages, cold and hot resistant tough coating, bookbinding processing and the like, composed to conventional adhesives for bookbinding such as thermoplastic resin-based adhesives or urethane-based reactive adhesives.例文帳に追加

従来の熱可塑樹脂系ホットメルト接着剤やウレタン系反応性接着剤を使用した製本用の接着剤よりも接着強度、高速作業性、本の見開き性、耐寒・耐熱性の強靭な被膜性、製本加工性などに優れた製本用の反応性ホットメルト接着剤を提供すること。 - 特許庁

To provide a case hardening steel which can secure bending fatigue strength and pitching strength equal to or above those in the case SNCM220H and SCM420H are used as stock steel even in the case N and Mo are not comprised as possible, in which componential cost is low, and which has satisfactory workability upon hot and cold rolling and forging as well.例文帳に追加

Ni、Moを極力含有しない場合でも、SNCM220H及びSCM420Hを素材鋼とする場合と同程度又はそれを上回る曲げ疲労強度とピッチング強度を確保させることができるとともに成分コストが低く、しかも、熱間および冷間での圧延や鍛造の際の良好な加工性も具備する肌焼鋼を提供する。 - 特許庁

To provide an inexpensive cold rolled steel sheet for a gasket material which has excellent gas seal ability while reconciling bead workability with spring properties, to provide its production method, and to provide an inexpensive gasket material which has excellent sealing performance, and is suitably used for opening parts such as an opening for cooling water, an opening for lubricating oil and a bolthole.例文帳に追加

安価で、ビード加工性とばね性との調和をとりながら、すぐれたガスシール性を有するガスケット材用冷延鋼板およびその製造法を提供し、冷却水用開口、潤滑油用開口およびボルト孔等の開口部について好適に用いられるシール性能が優れた安価なガスケット材を提供する。 - 特許庁

And the method for manufacturing the ferrite system stainless steel wire rod, bar steel and steel tube excellent in cold workability characterized by the feature that in the above method, reduction of area at the time of bloom-rolling is 60% or more and reduction of area at the time of slant-rolling 40% or more, and the wire rod, bar steel and steel tube manufactured by the method.例文帳に追加

上記において、分塊圧延時の減面率を６０％以上とすること、さらに、傾斜圧延時の減面率を４０％以上とする冷間加工性に優れたフェライト系ステンレス鋼線材、棒鋼および鋼管の製造方法並びにその方法により製造された線材、棒鋼および鋼管。 - 特許庁

To provide an Ni-based alloy material having excellent cold strength and workability, and having excellent high temperature creep properties equal to or above those of the conventional Ni-based alloy material, and to provide a method for inexpensively producing the Ni-based alloy material by a continuous casting process without undergoing a hot forging stage.例文帳に追加

常温での強度と加工性とに優れると共に、従来Ｎｉ基合金材料以上の高温クリープ特性に優れるＮｉ基合金材料を提供すること、およびそのＮｉ基合金材料を、熱間鍛造工程を経ることなく連続鋳造法によって安価に製造する方法を提案すること。 - 特許庁

To provide a polyolefinic resin laminated foam self-adhesive tape having a property reducing deterioration by ultraviolet ray in addition to foam body characteristics such as a heat-retaining property, a cold insulation property, heat insulation property, a shock absorbing property, and a cushioning property, and further having characteristics such as damage prevention, workability, a designing property based on a regular rugged pattern.例文帳に追加

保温性、保冷性、断熱性、緩衝性、クッション性等の発泡体特性に加え紫外線劣化を軽減する特性を有し、更に規則的凹凸模様により傷防止、施工性、意匠性等の特性が付与されたポリオレフィン系樹脂積層発泡体粘着テープを提供することにある。 - 特許庁

To provide a steel for vacuum carburizing or a steel for vacuum carbonitriding, in which even in the case Ni and Mo are not comprised as possible, which can secure bending fatigue strength and pitting strength equal to or above those in the case SCM822H is used as a material steel, further has a low componential cost, and further has satisfactory workability upon hot and cold rolling and forging.例文帳に追加

Ni、Moを極力含有しない場合でも、SCM822Hを素材鋼とする場合と同程度又はそれを上回る曲げ疲労強度とピッチング強度を確保させることができるとともに成分コストが低く、熱間および冷間での圧延や鍛造の際の良好な加工性も具備する真空浸炭用鋼あるいは真空浸炭窒化用鋼の提供。 - 特許庁

To provide a hot-melt adhesive useful for bookbinding, etc., which shows an excellent initial bond strength, environmental shelf stability such as heat resistance and cold resistance and high-speed workability when bonding book blocks and covers at bookbinding and yields a book showing an excellent spreadability and recyclability compared to the conventional adhesives such as thermoplastic resin adhesives, reactive urethane adhesives, etc.例文帳に追加

従来の熱可塑性樹脂、あるいは反応型のウレタン系接着剤などの接着剤よりも、製本時の中本と表紙との接着において、優れた初期接着力、本の見開き性、耐熱・耐寒性の環境保存安定性、高速作業性および本のリサイクル性に優れた製本用などに有用なホットメルト接着剤の提供。 - 特許庁

To provide a low-cost cold rolled steel sheet which has superior gas sealing property while balancing workability and spring characteristic and is used for a gasket material having excellent spring characteristic and a manufacturing method thereof and to provide a low-cost gasket material excellent in spring characteristic, having superior sealing property and suitably used for openings for cooling water, openings for lubricating oil and openings such as bolt holes.例文帳に追加

安価で、加工性とばね性との調和をとりながら、すぐれたガスシール性を有するばね性に優れたガスケット材用冷延鋼板およびその製造法を提供し、冷却水用開口、潤滑油用開口およびボルト孔等の開口部について好適に用いられるシール性能が優れた安価なばね性に優れたガスケット材を提供する。 - 特許庁