「diffraction ray」に関連した英語例文の一覧と使い方(17ページ目) - Weblio英語例文検索

The above diffraction peak strength is determined under the following conditions: X-ray source is Cuk α; tube bulb voltage is 40 kV; tube bulb current is 20 mA; filter is Ni-filter; divergent slit is 1°, scattering slit is 1°; and light receiving slit is 0.3 mm.例文帳に追加

但し、上記の回折ピーク強度とは、ＣｕＫαをＸ線源、管球電圧を４０ｋＶ、管球電流を２０ｍＡとし、Ｎｉフィルターを用い、発散スリットに１°、散乱スリットに１°、受光スリットに０．３ｍｍを使用した場合のピーク強度をいう。 - 特許庁

The surface of particles of nickel hydroxide powder is coated with the β-type cobalt hydroxide wherein the half-width obtained from the face (101) by X-ray diffraction is not less than 0.229° and not more than 0.851° or in which the crystallite diameter is not less than 100 Å and not more than 450 Å.例文帳に追加

Ｘ線回折において（１０１）面より求めた半価幅が０．２２９°以上０．８５１°以下、あるいは結晶子径が１００Å以上４５０Å以下であるβ型水酸化コバルトにより、水酸化ニッケル粉末の粒子の表面を被覆する。 - 特許庁

It is also desirable that the peak intensity P1 at an Si peak point appearing around 2θ=28° and the base intensity P2 at the peak point assumed by using the average gradient in the vicinity of the Si peak point satisfy (P1-P2)/P2≤0.2 in a graph obtained by X-ray diffraction.例文帳に追加

また、Ｘ線回折により得られたグラフにおいて、２θ＝２８°付近に発生するＳｉピーク点におけるピーク強度Ｐ１と、ピーク点前後の平均勾配から想定したピーク点におけるベース強度Ｐ２が、（Ｐ１−Ｐ２）／Ｐ２≦０．２を満足することが望ましい。 - 特許庁

The production method for a crystal polymorphism A (Fig.1: X-ray powder diffraction pattern) of a pitavastatin hemicalcium salt (formula) comprises allowing a sodium salt of pitavastatin to react with CaCl_2 in an aqueous reaction medium, separating a formed crystal, and drying it so that the water content is adjusted to 3-12%.例文帳に追加

ピタバスタチンのナトリウム塩とＣａＣｌ_2とを水性反応媒体中で反応させ、生成した結晶を分離し、乾燥して含水量を３〜１２％に調節する、ピタバスタチンヘミカルシウム塩（下式）の結晶多形Ａ（図１：Ｘ線粉末回折図形）の製造方法。 - 特許庁

The sputtering target comprises a zinc oxide sintered body, wherein a crystalline orientation degree I_002/(I_002+I_110) calculated by peak intensities in the X-ray diffraction measurement on the major face 11a to be exposed to a sputtering atmosphere, is 0.2 to <0.58.例文帳に追加

酸化亜鉛焼結体からなり、スパッタリング雰囲気にさらされる主面１１ａのＸ線回折測定のピーク強度により算出される結晶配向度Ｉ_００２／（Ｉ_００２+Ｉ_１１０）が０．２以上、０．５８未満であることを特徴とするスパッタリングターゲット。 - 特許庁

This slide fastener includes a lock pin and/or a spring composed of molecularly oriented polyethylene terephthalate-based resin having a half value width of azimuthal distribution of an X-ray diffraction strength of 30° or less in a crystal surface 100 (spacing of approximately 3.40Å).例文帳に追加

結晶面（１００）（面間隔約３．４０Å）について、Ｘ線回折強度の方位角分布の半値幅が３０°以下である分子配向したポリエチレンテレフタレート系樹脂からなるロックピンおよび／またはスプリングを含むことを特徴とするスライドファスナーである。 - 特許庁

A solid phase of amorphous (-)-FTC and (-)-cis-FTC called II and III(-)-cis-FTC which is distinguishable from I(-)-cis-FTC by its powder X-ray diffraction pattern, heat characteristic and production methods is provided.例文帳に追加

Ｘ線粉末回折パターン、熱特性、および製造の方法によってＩ型（−）−シス−ＦＴＣと区別することができ、ここでは非晶質（−）−ＦＴＣおよびＩＩおよびＩＩＩ型（−）−シス−ＦＴＣ）と呼ばれる（−）−シス−ＦＴＣの固相を提供する。 - 特許庁

To provide a structural analysis method of a crystal for easily deciding whether the spread shape of a peak to be measured is determined, by reflecting the nonuniform distribution of the composition in the crystal, when evaluating the structure of the crystal by X-ray diffraction.例文帳に追加

Ｘ線回折により結晶構造評価を行う際、測定されるピークの拡がり形状が、結晶中の組成が不均一に分布していることを反映して決まっているか否かを、簡便に判定できる、結晶の構造解析方法を提供する。 - 特許庁

The magnetic material has an X-ray diffraction peak corresponding to the crystal structure of ε-Fe_2O_3 and is composed of a crystal of ε-Ga_xFe_2-xO_3, formed by replacing a part of Ga^3+ ion site in the ε-Fe_2O_3 crystal with Ga^3+ ion, wherein 0<X<1.例文帳に追加

ε−Ｆｅ_2Ｏ_3の結晶構造に対応するＸ線回折ピークを有し、ε−Ｆｅ_2Ｏ_3結晶のＧａ^3+イオンサイトの一部がＧａ^3+イオンで置換されたε−Ｇａ_xＦｅ_2-xＯ_3〔ただし０＜Ｘ＜１である〕の結晶からなる磁性材料である。 - 特許庁

Alternatively, a nonmagnetic part for magnetically separating the magnetic recording pattern part is formed by partially implanting atoms into a deposited Co-containing magnetic layer, and setting Co (002) or Co(110) peak strength of X-ray diffraction of the magnetic layer of a relevant part to 1/2 or less.例文帳に追加

または、磁気記録パターン部を磁気的に分離する非磁性部を、すでに成膜されたＣｏ含有磁性層に部分的に原子を注入し、該箇所の磁性層のＸ線回折によるＣｏ（００２）またはＣｏ（１１０）ピーク強度を１／２以下にして形成する。 - 特許庁

A β type crystal and a γ type crystal of 4-amino-5-chloro-2-ethoxy-N-[[4-(4-fluorobenzyl)-2-morpholinyl]methyl]benzamide-citrate which are characterized by a powder x-ray diffraction pattern and/or a differential scanning calorimetric analysis thermogram, and are stable at the room temperature are disclosed.例文帳に追加

粉末Ｘ線回折パターン及び／又は示差走査熱量分析サーモグラムで特徴付けられ、室温で安定な、４−アミノ−５−クロロ−２−エトキシ−Ｎ−［［４−（４−フルオロベンジル）−２−モルホリニル］メチル］ベンズアミド・クエン酸のβ型結晶及びγ型結晶。 - 特許庁

To evade the lowering of measuring precision caused by a cross error in biaxial lines, simplify structure of a diffractometer, and shorten a measuring time, by omitting rotation corresponding to one axis out of biaxial rotations conducted conventionally in micro X-ray diffraction measurement.例文帳に追加

微小部Ｘ線回折測定において従来行われていた２軸回転のうちの１軸分を省略することにより、２軸線の交差誤差に起因する測定精度の低下を回避し、装置の構造を簡単にし、さらに測定時間を短縮する。 - 特許庁

The SiC dummy wafer being obtained by forming an SiC film on the surface of a basic material by CVD and then removing the basic material comprises an SiC shaped body having such properties as the half peak width of SiC (111) face measured by X-ray diffraction is 0.2° or less and the warp is 0.5 mm or less.例文帳に追加

ＣＶＤ法により基材面にＳｉＣ膜を成膜した後基材を除去して得られ、Ｘ線回折により測定されるＳｉＣ（１１１）面の半値幅が０．２°以下、反りが０．５mm以下の性状を備えたＳｉＣ成形体からなるＳｉＣダミーウエハ。 - 特許庁

It is desirable for the sintered body to contain MgO in addition, and if it contains MgAl_2O_4 and MgO, it is preferred that the peak intensity of MgO (200) plane in an X-ray diffraction pattern is in the range from 0.5 to 50, provided that the peak intensity of MgAl_2O_4 (311) plane is 100.例文帳に追加

この焼結体は、ＭｇＯをさらに含むことが好ましく、ＭｇＡｌ_２Ｏ_４及びＭｇＯを含む場合、Ｘ線回折によるＭｇＡｌ_２Ｏ_４（３１１）面のピーク強度を１００としたときのＭｇＯ（２００）面のピーク強度が０．５〜５０であること好ましい。 - 特許庁

In each TiO_2 film of the optical multilayer film formed by alternately stacking TiO_2 films and SiO_2 films, the X-ray diffraction peak intensity ratio (anatase structure/rutile structure) of anatase structure to rutile structure is within a range of 70/30 to 100/0.例文帳に追加

ＴｉＯ_２膜とＳｉＯ_２膜とを交互に積層してなる光学多層膜において、ＴｉＯ_２膜中におけるアナターゼ構造とルチル構造のＸ線回折ピーク強度比（アナターゼ構造：ルチル構造）が７０：３０〜１００：０の範囲内であることを特徴としている。 - 特許庁

The cellulose nanofiber has an average polymerization degree of not less than 600 and not more than 30,000, an aspect ratio of 20-10,000, and an average diameter of 1-800 nm, and has an X-ray diffraction pattern having a Iβ type crystal peak.例文帳に追加

本発明のセルロースナノファイバーは、平均重合度が６００以上３００００以下であり、アスペクト比が２０〜１００００であり、平均直径が１〜８００ｎｍであり、Ｘ線回折パターンにおいて、Ｉβ型の結晶ピークを有することを特徴とする。 - 特許庁

The product proves to be a crystal by powder X-ray diffraction and gives a maximum endothermic peak at a temperature of 180°C or higher by DST to prove to be a uniform crystalline α-lipoic acid lysine salt in its chemical composition and crystalline shape.例文帳に追加

生成物は粉末Ｘ線回折により結晶であることを示し、ＤＳＴにおいて１８０℃以上の温度において最大吸熱ピークを示し、化学組成および結晶形態において均一な結晶性α−リポ酸リジン塩であることが証明された。 - 特許庁

According to this method, the dendrite structure of the casting 1 composed of coarse crystal grains can be fined at the surface layer part 2, so that an X-ray diffraction phenomenon can be well generated to stably obtain the correct residual stress.例文帳に追加

この方法によれば、粗大な結晶粒からなる鋳物１の樹枝状晶組織を、その表層部２で微細化することができるため、Ｘ線の回折現象を良好に生じさせることができ、正しい残留応力を安定して求めることができ得る。 - 特許庁

The metal partitioning material for the image display unit is the Fe-Ni alloy or the Fe-Ni-Cr alloy including, by wt.% 38-52% Ni, and the residual stress is controlled to 0.2-0.7 degrees by half-width of a X-ray diffraction peak for the face (311).例文帳に追加

重量％でＮｉを３８〜５２％含むＦｅ−Ｎｉ系合金またはＦｅ−Ｎｉ−Ｃｒ系合金であって、残留応力が（３１１）面Ｘ線回折ピークの半価幅で０．２〜０．７度に制御した画像表示装置用金属隔壁材とする。 - 特許庁

A crystal sample holder which is set on a sample stage of an X-ray diffraction system, is provided with a holder main body 2; a plurality of sample mount sections 3 formed on the holder main body 2; and a sample rotating mechanism which rotates each sample mount section 3 along a prescribed direction.例文帳に追加

Ｘ線回折装置の試料ステージに装着される結晶試料ホルダであって、ホルダ本体２と、このホルダ本体２に設けられた複数の試料マウント部３と、各試料マウント部３を所定の方向に回転させる試料回転機構とを備える。 - 特許庁

The manganese dioxide in which a content molar ratio (H_2O/MnO_2) of a structural water is larger than 0.20 and a ratio of peak strength for (110)/(021) of X-ray diffraction is 0.50-0.80 can stably exhibits an alkaline electric potential of 350-400 mV.例文帳に追加

構造水の含有モル比（Ｈ_２Ｏ／ＭｎＯ_２）が０．２０より大きく、Ｘ線回折の（１１０）／（０２１）のピーク強度比が０．５０以上０．８０以下の二酸化マンガンは、アルカリ電位が３５０ｍＶ以上４００ｍＶ以下を安定的に発揮することができる。 - 特許庁

This ceramic substrate for the semiconductor manufacture/ detector is composed by disposing a conductor to the ceramic substrate containing both of carbon for which a peak can not be detected or is at or below a detection limit on an X-ray diffraction chart and the carbon for which the peak can be detected.例文帳に追加

Ｘ線回折チャート上ではピークが検出できないか検出限界以下であるカーボンと、ピークが検出できるカーボンとの両方を含有するセラミック基板に、導電体を配設してなることを特徴とする半導体製造・検査装置用セラミック基板。 - 特許庁

The engine additive comprises a BN powder having an average particle diameter of above 1.0 to 3.0 μm, a maximum particle diameter of at most 15 μm, a graphitization index (GI) of 4.0 or below as measured by a powder X-ray diffraction method, and a boron oxide content of 0.5-5 mass %.例文帳に追加

平均粒径１．０μｍ超３．０μｍ以下、最大粒径１５μｍ以下、粉末Ｘ線回折法による黒鉛化指数（ＧＩ）４．０以下、酸化ほう素含有率０．５〜５質量％のＢＮ粉末からなることを特徴とするエンジンオイル添加剤。 - 特許庁

Moreover, the compositions having a powder X-ray diffraction pattern comprising at least three peaks with 2θ angles selected from about 18.2, 28.5, 29.5, 33.7, 41.2, 47.4, and 56.2 and a solid state ^23Na MAS NMR spectra peak at about 18 ppm.例文帳に追加

約１８．２、２８．５、２９．５、３３．７、４１．２、４７．４、および５６．２から選択される２θ角を有する少なくとも三つのピークを含有する粉末Ｘ線回折パターンおよび約１８ｐｐｍにおいて固体状態^２３Ｎａ ＭＡＳ ＮＭＲスペクトルピークを有する。 - 特許庁

The lithium secondary battery is formed of the negative electrode carbon material, which is formed of carbon material of which a graphitization degree P_1 obtained from 11 diffraction line intensity measured by using a CuKα ray is 0.3≤P_1≤0.8.例文帳に追加

炭素材料で構成されている負極炭素材であって、ＣｕＫα線を用いて測定される１１回折線強度から求められる黒鉛化度Ｐ_１が、０．３≦Ｐ_１≦０．８である炭素材料で構成された負極炭素材でリチウム二次電池を構成する。 - 特許庁

ranging from 5 to 15° and 20 to 30° in CuKα characteristic X-ray diffraction and (B) is a vinyl polymer containing a hydrophobic structure unit (a) and a hydrophilic structure unit (c).例文帳に追加

Ａ：ＣｕＫα特性Ｘ線回折におけるブラッグ角（２θ±０．２°）が５〜１５°及び２０〜３０°に特徴的なＸ線回折ピークを１個以上有する下記式等で表されるアゾ顔料、Ｂ：疎水性構造単位（ａ）と、親水性構造単位（ｃ）とを含むビニルポリマー。 - 特許庁

The control of the density of the dislocation is carried out by suppressing the width of a half value in the X-ray diffraction of a base powder to low, or by the method of not applying a pressure of >100 kgf/cm2 in the steps before obtaining the sintered compact, or by sintering with nitrifying reaction of Si powder.例文帳に追加

転位密度の制御は、原料粉末のＸ線回折における半価幅を低く抑えるか、焼結体を得るまでの工程で１００ｋｇｆ／ｃｍ^2を越える圧力を加えない方法、又はＳｉ粉末の窒化反応焼結による。 - 特許庁

An Ag particle where a BET value and half-value width in an X-ray diffraction peak are controlled is contained into the conductive paste, thus allowing the contraction behavior of the conductive paste after the completion of degreasing in a burning process to coincide with that of the ceramic green sheet.例文帳に追加

導電性ペーストに、ＢＥＴ値、Ｘ線回析ピークの半値幅を規制したＡｇ粒子を含有させることにより、焼成過程の脱脂終了後の導電性ペーストの収縮挙動を、セラミックグリーンシートの収縮挙動に合わせることができる。 - 特許庁

This fiber-reinforced resin composition comprises a thermoplastic resin and a polyethylene naphthalate fiber and has a crystal volume obtained by an X-ray wide-angle diffraction of a fiber of 550 to 1,200 nm^3 and a crystallinity of 30 to 60%.例文帳に追加

熱可塑性樹脂とポリエチレンナフタレート繊維からなる繊維補強樹脂組成物であって、繊維のＸ線広角回折より得られる結晶体積が５５０〜１２００ｎｍ^３であり、結晶化度が３０〜６０％であることを特徴とする繊維補強樹脂組成物。 - 特許庁

The inorganic material is composed of a multiple oxide containing at least cerium and niobium having the maximum peak height originating from niobium oxide which is ≤1/10 of the maximum peak height originating cerium oxide in the X-ray diffraction using CuKα line.例文帳に追加

少なくともセリウムとニオブとを含有する複合酸化物からなり、ＣｕＫα線を用いたＸ線回折分析による酸化ニオブ由来の最高ピーク高さが、酸化セリウム由来の最高ピーク高さの１０分の１以下であることを特徴とする無機材料である。 - 特許庁

The invention provides a fine carbon fiber having a layer spacing d_002 of 0.337 nm measured by X-ray diffraction method, a fiber diameter of ≤1,000 nm and a compact specific resistance of ≤0.02 Ω.cm and a fine carbon fiber having a metal content of ≤500 mass ppm.例文帳に追加

Ｘ線回折法で求めた層面間隔ｄ_002が０．３３７ｎｍを超え、繊維径１０００ｎｍ以下、圧密比抵抗が０．０２Ω・ｃｍ以下の微細な炭素繊維及び金属含有量が５００質量ｐｐｍ以下である微細な炭素繊維である。 - 特許庁

The third carbonizing step is separated to the primary treatment and the secondary treatment, and the specific resistance value, the specific gravity, the N/C, the single fiber elongation and the crystal size by a wide angle x-ray measurement (at 26° diffraction angle) of the fiber, and the temperature and the draw ratio are regulated in each treatment.例文帳に追加

第三炭素化工程では、一次処理と二次処理とに分け、それぞれの処理における繊維の比抵抗値、比重、Ｎ／Ｃ、単繊維伸度、並びに、広角Ｘ線測定(回折角２６°)での結晶子サイズと、温度と、延伸倍率とを制御する。 - 特許庁

Requirement (1): Carbon powder obtained by subjecting the binder (B), which can be graphitized, to graphitization treatment has a spacing (d002) on the 002 face by the X-ray wide-angle diffraction method of 0.3357 nm or greater and 0.34 nm or less, and an Lc (004) of 10 nm or greater and 500 nm or less.例文帳に追加

条件（１）：黒鉛化可能なバインダー（Ｂ）を黒鉛化処理して得られた炭素粉末のＸ線広角回折法による００２面の面間隔（ｄ００２）が０．３３５７ｎｍ以上０．３４ｎｍ以下、且つＬｃ（００４）が１０ｎｍ以上５００ｎｍ以下である。 - 特許庁

To provide a method for early determining whether there is a risk of occurrence of the delayed formation of ettringite after service by powder X-ray diffraction, in a cured article using a cement composition such as concrete or mortar receiving high-temperature ageing at the initial stage of hydration.例文帳に追加

水和初期に高温養生を受けたコンクリート、モルタル等のセメント組成物を用いた硬化物において、供用後生じる恐れがあるエトリンガイトの遅延生成の発生有無を粉末Ｘ線回折によって早期に判定する方法を提供する。 - 特許庁

To develop a protein-removing treatment method using squid tendons as a raw material and not accompanying a deacetylating reaction, and provide a starting substance containing βbased-chitin (relative degree of crystallization of 10 to 80% by X-ray diffraction) such asβ-chitin and amorphous chitin and used for new uses.例文帳に追加

イカの腱を原料とした、脱アセチル化反応を伴わない脱タンパク処理方法を開発し、βキチン及びアモルフアスキチンなどのβ性キチン（X線回折による相対結晶化度１０〜８０％）を含む新しい用途への出発物質を提供する。 - 特許庁

In an iron-nitride magnetic powder which consists of particles that are mainly composed of a Fe_16N_2 phase and whose average particle size is 20 nm or smaller, TAP density is 0.75 g/cm^3 or below and a nitriding rate calculated from an X-ray diffraction pattern is 70 to 100%.例文帳に追加

Ｆｅ_16Ｎ_2相主体の粒子からなる平均粒子径２０ｎｍ以下の粉末において、ＴＡＰ密度が０.７５ｇ／ｃｍ^3以下、かつＸ線回折パターンから算出される窒化率が７０〜１００％であることを特徴とする窒化鉄系磁性粉末。 - 特許庁

By a powder X-ray diffraction analysis, FeYO_3 and/or AlYO_3 are identified as the perovskite type oxide, and at least a species selected from among Y_3Al_5O_12, Al_2Fe_3Y_3O_12, and Al_3Fe_2Y_3O_12 is identified.例文帳に追加

粉末Ｘ線回折分析により、上記ペロブスカイト型酸化物として、ＦｅＹＯ_３及び／又はＡｌＹＯ_３が同定され、上記ガーネット型酸化物として、Ｙ_３Ａｌ_５Ｏ_１２、Ａｌ_２Ｆｅ_３Ｙ_３Ｏ_１２及びＡｌ_３Ｆｅ_２Ｙ_３Ｏ_１２から選ばれる少なくとも１種が同定される。 - 特許庁

After removing the respective portions of the growth layers 32-34 in the object region to be measured 41, the lattice constants of the semiconductor substrate 23 and growth layers 24-31 in the object region to be measured 41 are obtained, by using X-ray diffraction method.例文帳に追加

このように測定対象領域内４１で、前記成長層３２〜３４の各一部が除去された後、Ｘ線回折法によって、前記測定対象領域４１内の半導体基板２３および成長層２４〜３１の格子定数が求められる。 - 特許庁

The agrochemical composition comprises a crystal of 1-(N,N-dimethylsulfamoyl)-3-[2-methyl-3-bromo-6-fluoroindol-1-yl]sulfonyl-1,2,4-triazole having peaks at 2θ=8.08, 14.68, 16.20, 18.74, 21.06, 24.76 and 26.44 in powder X-ray diffraction.例文帳に追加

粉末Ｘ線回折において２θ＝８．０８、１４．６８、１６．２０、１８．７４、２１．０６、２４．７６および２６．４４にピ−クを有する1−（Ｎ，Ｎ−ジメチルスルファモイル）−3−〔2−メチル−3−ブロム−6−フルオロインド−ル−1−イル〕スルホニル−1，2，4−トリアゾ−ルの結晶を含有する農薬組成物。 - 特許庁

In the electrophotographic photoreceptor having an intermediate layer and a charge generation layer on a conductive support, the charge generation layer contains a moisture agent and the titanylphthalocyanine pigment having the maximum peak when the Bragg angle 2θ of X-ray diffraction spectrum using Cu-Kα characteristic X-ray (wavelength 1.541A) is 27.2±0.2°, and also the intermediate layer contains titanium oxide particles.例文帳に追加

導電性支持体上に中間層、電荷発生層を有する電子写真感光体において、該電荷発生層がＣｕ−Ｋα特性Ｘ線（波長１．５４１Ａ）を用いたＸ線回折スペクトルのブラッグ角２θが２７．２±０．２°に、最大ピークを有するチタニルフタロシアニン顔料と保湿剤を含有し、且つ中間層が酸化チタン粒子を含有することを特徴とする電子写真感光体。 - 特許庁

The phosphor has a specific chemical composition and a crystal phase, for example, the phosphor has the crystal phase of an alkaline earth metal silicates comprising one or more elements selected from a group comprising Ba, Sr, Ca and Mg, wherein the crystal phase satisfies specific requirements in X ray diffraction measurement using CuKα X-ray source.例文帳に追加

特定の化学組成を有する結晶相を有する蛍光体、例えば、Ｂａ、Ｓｒ、Ｃａ及びＭｇからなる群から選ばれる一種以上の元素を含むアルカリ土類金属珪酸塩の結晶相を有する蛍光体であって、該結晶相がＣｕＫαのＸ線源を用いたＸ線回折測定において特定の条件を満足する結晶相である蛍光体。 - 特許庁

A biaxially oriented polyester film comprises a polyester (A) and a polyether imide (B) and has a single glass transition temperature, wherein the diffraction peak of the crystal face in the main chain direction of the biaxially oriented polyester has a half-width in the range of 55-85 degrees in the circumference direction when the film is rotated about its normal line in crystal orientation analysis by diffractometry of wide angle X-ray diffraction.例文帳に追加

ポリエステル（Ａ）とポリエーテルイミド（Ｂ）とを含んでなる単一のガラス転移温度を有する二軸配向ポリエステルフィルムであって、広角Ｘ線回折のディフラクトメータ法による結晶配向解析で該フィルムをその法線を軸として回転した時に得られる該二軸配向ポリエステル主鎖方向の結晶面の回折ピークの円周方向の半値幅が５５〜８５度の範囲であることを特徴とする二軸配向ポリエステルフィルム。 - 特許庁

There are provided type II crystals and type I crystals of (±)2-(dimethylamino)-1-{[O-(m-methoxyphenetyl)phenoxy]methyl}ethyl hydrogen succinate hydrochloride characterized by at least one physicochemical property selected from a specific diffraction peak in X-ray powder diffraction spectrum, a specific endothermic peak in differential scanning calorimetry, a specific peak in solid ^13C-NMR spectrum, and a specific peak in infrared absorption spectrum.例文帳に追加

粉末Ｘ線回折スペクトルにおける特定の回折ピーク、示差走査熱量測定における特定の吸熱ピーク、固体^１３Ｃ−ＮＭＲスペクトルにおける特定のピーク及び赤外吸収スペクトルにおける特定のピークから選ばれる少なくとも１種の物理化学的性質により特徴付けられる、（±）２−（ジメチルアミノ）−１−{〔Ｏ−（ｍ−メトキシフェネチル）フェノキシ〕メチル}エチル水素サクシナート塩酸塩のII形結晶及びI形結晶。 - 特許庁

The electrophotographic photoreceptor having a layer containing a titanyl phthalocyanine pigment on an electrically conductive support, is characterized in that the titanyl phthalocyanine pigment has the maximum diffraction peak at 26.3° Bragg angle (2θ±0.2°) in its X-ray diffraction spectrum with Cu-Ka characteristic X-rays and a 2-12C alkylenediol is contained in the layer containing the titanyl phthalocyanine pigment.例文帳に追加

導電性支持体上にチタニルフタロシアニン顔料を含有する層を有する感光体において、前記チタニルフタロシアニン顔料が、Ｃｕ−Ｋα特性Ｘ線によるＸ線回折スペクトルにおいて、ブラッグ角（２θ±０．２°）２６．３°に最大回折ピークを有するチタニルフタロシアニン顔料であり、チタニルフタロシアニン顔料を含有する層に、炭素数２〜１２のアルキレンジオールを含有していることを特徴とする電子写真感光体。 - 特許庁

In the multi-layered plastic container including a resin layer mainly comprising a xylylene radical containing polyamide, a heat generation peak with crystallization measured by a differential scanning calorimeter(DSC) on the resin layer of at least a barrel is 10 J/g or less, and a half width of the maximum of a diffraction profile at 2θ=0 to 100 degrees measured by X-ray diffraction is 10 degrees or less.例文帳に追加

キシリレン基含有ポリアミドを主体とする樹脂層を備えた多層プラスチック容器において、少なくとも胴部の前記樹脂層について、示差走査熱量計（ＤＳＣ）で測定した結晶化に伴う発熱ピークが １０Ｊ／ｇ以下であり且つＸ線回折で測定した２θ＝０乃至１００度における回折プロファイルの最大値の半値幅が１０度以下であることを特徴とする多層プラスチック容器。 - 特許庁