To provide a process for producing a sheet for bone prosthesis which positively accomplished the bonding of particles consisting of calcium phosphate, or the like, to a bone and does not scatter into the body, and the sheet for bone prosthesis produced by such process.例文帳に追加

リン酸カルシウム等からなる粒子の骨との結合を積極的に図り、体内に散在しない骨補填用シートの製造方法およびかかる方法により製造される骨補填用シートを提供する。 - 特許庁

The method of manufacturing the sintered compact shown in Figure 1 has a process step [S1] of obtaining a composition containing a calcium phosphate compound, a process step [S2] of obtaining a molding by molding the composition, a process step [S3] of calcining the molding and a process step [S4] of firing (normal firing) the calcined molding.例文帳に追加

図１に示す焼結体の製造方法は、リン酸カルシウム系化合物を含む組成物を得る工程[Ｓ１]と、組成物を成形し成形体を得る工程[Ｓ２]と、成形体を仮焼成する工程[Ｓ３]と、仮焼成した成形体（仮焼成体）を焼成(本焼成)する工程[Ｓ４]とを有している。 - 特許庁

To provide a method of manufacturing an electrode material, capable of efficiently recovering Li salt formed in a manufacturing process of LiFePO_4 as high-purity lithium phosphate, with low manufacturing cost and capable of reducing an environmental load, and to provide a recovery method of lithium phosphate.例文帳に追加

ＬｉＦｅＰＯ_４の製造過程で生成するＬｉ塩を高純度のリン酸リチウムとして効率的に回収することができ、製造コストが低く、環境負荷も低減可能な電極材料の製造方法及びリン酸リチウムの回収方法を提供する。 - 特許庁

To provide a method for recovering and reusing phosphate chemical processing liquid, in which the accumulation of unnecessary components in a chemical processing vessel is prevented and a concentrating process is smoothly performed.例文帳に追加

化成処理槽中の不要成分の蓄積を防ぎ、且つ濃縮工程を円滑に行うりん酸塩化成処理液の回収再利用方法方法を提供する。 - 特許庁

This method for producing the retort shrimp comprises retort-treating raw material shrimp after a process of serially soaking in transglutaminase solution, salt water of ≥10 wt.% or salt powder, and phosphate solution.例文帳に追加

原料エビをトランスグルタミナーゼ溶液、１０重量％以上の食塩水又は食塩粉末、リン酸塩溶液に順次浸漬する工程を経た後にレトルト処理する。 - 特許庁

This proton conductive material is constituted using a crystalline metal phosphate as a major component of which the proton conductivity has been improved using a mechanical milling process.例文帳に追加

結晶性リン酸金属塩をメカニカルミリングにより処理することによって、そのプロトン伝導性を向上させ、それを主成分としてプロトン伝導性材料を構成する。 - 特許庁

To provide a method of manufacturing drum cans capable of enhancing production efficiency and reducing manufacturing cost, by substituting a conventional metal surface conversion treatment process carried out by two treatments, that is, zinc phosphate conversion treatment and iron phosphate conversion treatment with a metal surface conversion treatment process superior in both of corrosion resistance and chemical resistance, also excellent in coated film adhesion and low in cost.例文帳に追加

優れた耐食性・耐薬品性と優れた塗膜密着性が両立した、コストが安い金属表面化成処理工程で、従来のリン酸亜鉛化成処理とリン酸鉄化成処理の２本立てであった金属表面化成処理工程を置き換えて、生産効率を向上させ、製造コストが低減できるドラム缶製造方法を提供すること。 - 特許庁

The low thermally expandable filler comprises a hexagonal zirconium phosphate synthesized by a wet process or a hydrothermal process using zirconium oxychloride as a raw material, and has a purity of 99 wt.% or more.例文帳に追加

本発明は、オキシ塩化ジルコニウムを原料とする湿式法または水熱法により合成した六方晶リン酸ジルコニウムからなり、純度が９９重量％以上であることを特徴とする低熱膨張性フィラーである。 - 特許庁

The process cheese is produced by selecting as a raw material natural cheese having specifically high CPP (casein phosphopeptide) content, and if necessary, adding CPP-ACP (amorphous calcium phosphate) and/or CPP as a food material so as to bring CPP content to ≥1.8 times of ordinary process cheese on the market.例文帳に追加

特異的にCPP含量が高いナチュラルチーズを原料として選別し、必要に応じて食品素材としてのCPP-ACP及びまたはCPPを加えることで、CPP含量が通常の市販プロセスチーズの1.8倍以上のプロセスチーズを製造する。 - 特許庁

The manufacturing method of the active material includes a process of forming an intermediate by heating a phosphate source, a vanadium source, a water-soluble organic compound and water for 1 to 12 hours, and a process of heating the intermediate, lithium salt and water.例文帳に追加

本発明に係る活物質の製造方法は、リン酸源、バナジウム源、水溶性の有機化合物及び水を１〜１２時間加熱して、中間体を形成する工程と、中間体、リチウム塩及び水を加熱する工程と、を備える。 - 特許庁

There are provided a food extract having food-quality improving effect on food, which is made to contain a chelating agent to inhibit generation of insoluble phosphate or made to solubilize the insoluble phosphate, and a method for producing the food extract characterized by addition of the chelating agent to the food extract in its production process.例文帳に追加

食用エキスにキレート剤を存在させ、不溶性リン酸塩の生成抑制または可溶化してなる食品の品質改良効果を奏する食用エキス、および食用エキスの製造に際し、キレート剤を添加することを特徴とする当該食用エキスの製造法。 - 特許庁

The method of removing the metal ion substituted with the Ca in the calcium phosphate base compound comprises: a contact process for bringing the calcium phosphate base compound contact with a remover solution containing at least a kind of heterocyclic compound containing at least two Ns and its derivative as a principal ingredient; and a removing process for removing the remover solution, after the contact with the calcium phosphate base compound.例文帳に追加

本発明の金属イオンの除去方法は、リン酸カルシウム系化合物が有するＣａに置換した金属イオンを除去する金属イオンの除去方法であり、前記リン酸カルシウム系化合物と、少なくとも２つのＮを含むヘテロ環化合物およびその誘導体のうちの少なくとも１種を主成分とする除去剤を含む除去液とを接触させる接触工程と、前記リン酸カルシウム系化合物に接触させた後の前記除去液を除去する除去工程とを有する。 - 特許庁

To provide a treatment and recovery method capable of again reutilizing washing water discharged from a phosphate chemical conversion treatment process as a chemical conversion treatment liquid and washing water at a low cost with high efficiency.例文帳に追加

りん酸塩化成処理工程から排出された水洗水を、再び化成処理液及び水洗水に、低コストで高効率で再利用することができる処理回収方法の提供。 - 特許庁

The photocatalyst comprises coating the substrate side with titanium dioxide and the surface thereof with an amorphous denseness calcium phosphate thin film on the surface of the substrate using a sputtering process.例文帳に追加

基材表面上にスパッタリング法を用いて、基材側に二酸化チタン、その表面にアモルファス緻密リン酸カルシウム薄膜がコーティングされていることを特徴とする光触媒。 - 特許庁

To provide a treatment method for sewage sludge, capable of attaining a decrease in the water content ratio of dehydrated cake and suppressing generation of magnesium ammonium phosphate scale in a dewatering process of sewage digested sludge.例文帳に追加

下水消化汚泥の脱水処理において、脱水ケーキの含水率の低下を実現すると共に、燐酸マグネシウムアンモニウムスケールの生成を低減できる下水汚泥の処理方法の提供。 - 特許庁

This manufacturing method includes: a process of putting 5 to 15g of sodium chloride in hot water having a temperature ranging from 30 to 40 degrees, and dissolving 50 to 70g of diammonium phosphate in the above solution; and a process of putting 50 to 70g of ammonium bicarbonate in the above solution to be dissolved.例文帳に追加

本発明の製造方法は、３０度から４０度のお湯に塩化ナトリウムを５ｇから１５ｇ入れ、リン酸二アンモニウムを５０ｇから７０ｇ入れて溶解する工程と、重炭酸アンモニウムを５０ｇから７０ｇ入れて溶解する工程とを備える。 - 特許庁

The method of treating washing waste water after phosphate chemical conversion treatment is characterized by being composed of a process in which the waste washing water is neutralized to have a pH of ≥6 and of a process in which electrolytic treatment is executed so as to have a pH of ≥7.例文帳に追加

リン酸塩化成処理後の洗浄廃水の処理方法であって、上記洗浄廃水をｐＨ６以上に中和する工程、及び、ｐＨ７以上になるように電気分解処理を行う工程からなることを特徴とする洗浄廃水の処理方法。 - 特許庁

This method for producing collagens comprises at least a process for culturing collagen-producing cells on a fibrous sheet containing calcium phosphate as a substrate for culturing the cells and a process for thermally sterilizing (autoclave) the cultured cells together with the fibrous sheet.例文帳に追加

リン酸カルシウム類を含有する繊維状シートを細胞培養用基材に用いてコラーゲン産生細胞の培養を行った後、前記繊維状シートごと加熱滅菌（オートクレーブ）処理を行う手順を少なくとも含むコラーゲン類生産方法を提供する。 - 特許庁

To provide a manufacturing method of synthetic fluorite which can be suitably used for removing fluorine from a gas containing fluorine such as an exhaust gas generated in a process for manufacturing tricalcium phosphate by thermal decomposition of rock phosphate and also for producing a product (synthetic fluorite) high in the content of calcium fluoride from the above fluorine.例文帳に追加

リン鉱石の熱分解により第三リン酸カルシウムを製造するプロセスで発生するフッ素を含む排ガス等のようなフッ素を含むガスからフッ素を除去すると共にこのフッ素からフッ化カルシウム含有率が高い生成物（合成蛍石）を生成することができる合成蛍石の製造方法を提供する。 - 特許庁

The hydrating process of the cadmium oxide of an electrode plate is conducted in a hydrated solution added with a phosphate and/or a silicate to a potassium hydroxide aqueous solution with the specific gravity of 1.25 or below at 25°C.例文帳に追加

電極板の酸化カドミウムの水和処理を、２５℃における比重が１.２５以下の水酸化カリウム水溶液に燐酸塩及び／又は珪酸塩を添加して調製された水和液の中で行なう。 - 特許庁

To provide a phosphorus removal apparatus which can carry out a crystallization process without using phosphate ore or the like as a seed crystal by generating fine particles of apatite working as a seed crystal from wastewater.例文帳に追加

種結晶となるアパタイトの微粒子を排水中から生成させることにより、種結晶としてリン鉱石等を使用せずに晶析法を実施することができる脱リン装置を提供する。 - 特許庁

The manufacturing apparatus of fertilizer raw material has a preparation/disinfection process 18 of preparing the crystal grains of ammonium magnesium phosphate by adding a magnesium compound to phosphorus and ammonia-containing waste water and, at the same time, disinfecting the crystal grains and a recovery process 14 of recovering the crystal grains.例文帳に追加

リンおよびアンモニア含有汚水にマグネシウム化合物を添加して、リン酸マグネシウムアンモニウムの結晶粒子を生成させると同時に前記結晶粒子を消毒する生成・消毒工程１８と、前記結晶粒子を回収する回収工程１４とを備えている。 - 特許庁

This method of treating acidic waste water including phosphate ions comprises a process of neutralizing the acidic waste water to ≥pH 6 with a basic substance containing calcium and a process of performing electrolysis in such a manner that the pH of the acidic waste water becomes ≥7.例文帳に追加

リン酸イオンを含有する酸性廃水の処理方法であって、上記酸性廃水をカルシウムを含有する塩基性物質でｐＨ６以上に中和する工程、および、ｐＨ７以上になるように電気分解を行う工程からなることを特徴とする酸性廃水の処理方法である。 - 特許庁

This treatment method of organic waste water incorporates a process (1) in which phosphor and nitrogen in the waste water is made to a form of ammonium magnesium phosphate and taken out the same outside the system and, therein, is characterized in that a vacuum treatment process (2) in which the waste water which contains phosphor and nitrogen is subjected to vacuum treatment prior to the process (1).例文帳に追加

有機性排水を処理する方法であって、該排水中のリン及び窒素をリン酸マグネシウムアンモニウムの形態にして系外に取り出す工程（１）を組み入れている処理方法において、前記工程（１）の前にリン及び窒素を含有する該排水を減圧処理する減圧処理工程（２）を組み込むことを特徴とする有機性排水の処理方法。 - 特許庁

To provide a multilayer coating film deposition method including a substrate rust prevention process capable of exhibiting rust preventing property, adhesion and coating film appearance equal to or above those in a conventional chemical conversion treatment process, and suitable for electrodeposition coating excellent in economic efficiency and environmental conservation by eliminating the conventional complicated and expensive rust preventing chemical conversion treatment process (for example, zinc phosphate treatment process).例文帳に追加

従来の煩雑かつ高コストの防錆化成処理工程（例えば、リン酸亜鉛処理工程など）を省略し、なおかつ、その代替として、従来の化成処理工程と同等もしくはそれ以上の優れた防錆性、密着性ならびに優れた塗膜外観を発現させることができ、さらに、経済性および環境保全性に優れた、電着塗装に適した下地防錆工程を含む複層塗膜形成方法の提供。 - 特許庁

In the process for producing processed cheese, a mono-phosphate salt or carboxylate salt is used in the thermal emulsification so that the pH of the emulsion may become ≥6.0 immediately after the thermal emulsification, then the objective processed cheese is produced from the pH-adjusted emulsion.例文帳に追加

プロセスチーズの製造工程において、加熱乳化時にモノリン酸塩又はカルボン酸塩を用い、加熱乳化直後の乳化物のｐＨが６．０以上となるように調整して、プロセスチーズを製造する。 - 特許庁

The method includes a process for contacting the blood product containing viruses with a solvent of di- or trialkylphosphate and a non-ionic detergent, wherein the protein yield of the blood product is at least 90%.例文帳に追加

本方法は、ウイルスを含んでいる血液製品を、ジ−（di-）またはトリ−アルキル・ホスフェート（tri-alkyl phosphate）の溶媒および非イオン性の洗剤に接触させる処理を含み、血液製品タンパク質の収率が少なくとも９０％である。 - 特許庁

At the time of coating the steel material and the Al alloy material in the same treating process after phosphating, the coating is performed with the coating material containing no lead based pigment but containing calcium phosphate.例文帳に追加

鋼材とアルミニウム合金材とを、同じ処理工程にて、リン酸塩処理した後に塗装するに際し、該塗装を、防錆顔料として、鉛系顔料を含まずに、リン酸カルシウムを含む塗料により行うことである。 - 特許庁

The manufacturing method of the electron conductive ionic conductive material contains a process for polymerizing one or more kinds of monomers containing a phosphate group in a solution containing at least nonionic conductive copolymer resin.例文帳に追加

少なくとも非イオン伝導性共重合樹脂を含む液中で、リン酸基を有する１種類以上のモノマーを重合する工程を有することを特徴とする電子伝導イオン伝導物質の製造方法。 - 特許庁

In the preparation process for covered particles with the surface covered with a calcium phosphate layer, resin particles comprising a biodegradable resin or the like and having an average particle size of 0.01μm to 1,000 μm are dispersed or dipped in an aqueous solution containing calcium ions and phosphate ions at 30°C or higher for at least 12 hr.例文帳に追加

平均粒子径が０．０１μｍ以上１，０００μｍ以下である生分解性樹脂などからなる樹脂粒子を、カルシウムイオンおよび燐酸イオンを含む水溶液中に、３０℃以上の温度で１２時間以上分散または浸漬することを特徴とする、表面を燐酸カルシウムからなる層で被覆した被覆粒子の製造方法。 - 特許庁

This process for producing a protein with reduction of an acidic sugar chain includes: controlling a gene participating in the addition of mannose phosphate to a sugar chain of a glycoprotein originating in a yeast belonging to the genus Pichia; and producing a protein with reduction of the acidic sugar chain by using the gene-controlled yeast strain belonging to the genus Pichia.例文帳に追加

ピキア属酵母に由来する糖蛋白質の糖鎖へのマンノースリン酸付加に携わる遺伝子を制御し、該遺伝子が制御されたピキア属酵母株を用いて酸性糖鎖減少蛋白質を製造する方法。 - 特許庁

The method comprises a process for culturing the stromal cells from the adipose tissue in β-glycerophosphate and ascorbic acid and/or ascorbate-2-phosphate for a time sufficient to allow differentiation of the cells into osteoblasts.例文帳に追加

本方法は、脂肪組織からの間質細胞を、上記細胞を骨芽細胞に分化させるのに十分な時間、βグルセロリン酸およびアスコルビン酸またはアスコルビン酸２リン酸、あるいはそれらの両方中で培養する工程を含む。 - 特許庁

This has a coprecipitation process wherein a mixed aqueous solution is prepared by mixing a water-soluble organic reducer with a phosphoric acid aqueous solution containing lithium salts and iron salts, and wherein an alkaline solution is mixed with the mixed aqueous solution to form a coprecipitate of complex phosphate with lithium and iron, and has a calcination process to calcine the coprecipitate.例文帳に追加

リチウム塩と鉄塩とを含有するリン酸水溶液に水溶性有機還元剤を混合して混合水溶液を調製し、当該混合水溶液にアルカリ溶液を混合してリチウムと鉄との複合リン酸化物の共沈体を生成させる共沈工程と、上記共沈体を焼成する焼成工程とを有する。 - 特許庁

The manufacturing method of the active material includes a process of forming an intermediate containing phosphorus and vanadium with a specific surface area of 0.1 m^2/g or more and less than 25 m^2/g by heating a phosphate source, a vanadium source and water, and a process of heating the intermediate, water-soluble lithium salt and water.例文帳に追加

本発明に係る活物質の製造方法は、リン酸源、バナジウム源及び水を加熱して、リン及びバナジウムを含み、比表面積が０．１ｍ^２／ｇ以上であり２５ｍ^２／ｇ未満である中間体を形成する工程と、中間体、水溶性のリチウム塩及び水を加熱する工程と、を備える。 - 特許庁

The process for recovering unreacted ammonia from a reactor effluent liquid obtained from a reaction zone used for generating acrylonitrile or methacrylonitrile comprises a step for quenching the effluent liquid from the reactor with an aqueous solution of ammonium phosphate, where the ratio of an ammonium ion to a phosphate ion in the solution is between approximately 0.7 to approximately 1.3, preferably approximately 0.9 to 1.2.例文帳に追加

アクリロニトリルまたはメタクリロニトリルを生成するために使用される反応ゾーンから得た反応器流出液から未反応アンモニアを回収するためのプロセスであって、この反応器流出液をリン酸アンモニウム水溶液でクエンチする工程を包含し、ここでこの溶液中のアンモニウムイオンとリン酸イオンとの比が約0.7から約1.3の間、好ましくは約0.9から1.2の間である、プロセスが提供される。 - 特許庁

The manufacturing method of the active material includes a hydrothermal synthesis process where a mixture composed of a lithium source, a pentavalent vanadium source, a phosphate source, water and a citric acid is heated to 200°C or more under pressure thereby LiVOPO_4 having a β type crystal structure is obtained.例文帳に追加

リチウム源と、５価のバナジウム源と、リン酸源と、水と、クエン酸とを含む混合物を、加圧下で２００℃以上に加熱することにより、β型結晶構造のＬｉＶＯＰＯ_４を得る水熱合成工程を備える活物質の製造方法。 - 特許庁

To provide a method for coating a metal material forming a treatment film capable of obtaining corrosion resistance corresponding to chromate treatment or zinc phosphate treatment and also very excellent in the adhesiveness with a coating film formed by a coating process after the treatment.例文帳に追加

クロム酸塩処理やリン酸亜鉛処理に匹敵する耐食性が得られる処理皮膜を形成し、さらに処理後の塗装工程によって形成される塗膜との付着性にも非常に優れた金属材料の塗装方法を提供する。 - 特許庁

To enable prevention of damage due to MAP (magnesium ammonium phosphate) scale deposition in a digestion tank or a digested sludge transfer pipe, and improvement of phosphorus recovery rate in the subsequent phosphorus recovery process by controlling a pH value during digestion treatment.例文帳に追加

消化処理におけるｐＨ値を制御することによって、消化槽あるいは消化汚泥移送管のＭＡＰスケール析出による被害をこうむることなく、また、後段のりん回収工程におけるりん回収率を向上させることができる。 - 特許庁

The process for preparing an anthraquinone-based dye represented by the formula (wherein R is -CH2CH2OSO3M or -CH=CH2; and M is hydrogen or an alkali metal) comprises reacting bromamine acid or its alkali metal salt with 4-(β-sulfatoethylsulfonyl) aniline or its alkali metal salt in an aqueous medium in the presence of a phosphate buffering agent and a copper catalyst.例文帳に追加

ブロマミン酸又はそのアルカリ金属塩と４−（β−スルファートエチルスルホニル）アニリン又はそのアルカリ金属塩を、水性媒体中、燐酸塩緩衝剤と銅触媒の存在下に反応させることを特徴とする下式（Ｉ） - 特許庁

The method for examining a bacterium belonging to the genus Legionella, with which a bacterium belonging to the genus Legionella in water is detected by a culture method by a flat plate medium comprises an acid treatment process for treating an object sample to be examined with an acidic phosphate buffer solution.例文帳に追加

水中のレジオネラ属菌を平板培地による培養法によって検出するレジオネラ属菌の検査方法であって、検査対象サンプルを酸性リン酸緩衝液で処理する酸処理工程を有するレジオネラ属菌の検査方法。 - 特許庁

The scale generation prevention method which inhibits the separation of magnesium ammonium phosphate (MAP) crystals in the process for treating the aqueous liquid containing three components, phosphorus, ammonia, and magnesium by adjusting the pH of the aqueous liquid to acidic.例文帳に追加

リン、アンモニア、マグネシウムの三成分を含む水性液を扱う工程において、当該水性液のｐＨを酸性に調整することにより、リン酸マグネシウムアンモニウム（ＭＡＰ）結晶の析出を抑制することを特徴とするスケール生成防止方法。 - 特許庁

An anodic oxidation treatment method for a piston made of the aluminum alloy consists of a process for forming the anodically oxidized film 16 on the aluminum alloy 10 containing Si 12, 13, 14 with an electrolyte mixed with phosphate and fluoride, a process for impregnating the micropores 18 of the anodically oxidized film 16 with a photosetting resin and a process for curing the photosetting resin by casting light thereto.例文帳に追加

アルミニウム合金製ピストンの陽極酸化処理方法は、りん酸塩並びにふっ化物を混合した電解液でＳｉ１２，１３，１４を含むアルミニウム合金１０に陽極酸化皮膜１６を生成する工程と、陽極酸化皮膜１６の微細な孔１８…に液状の光硬化性樹脂２０を含浸する工程と、この光硬化性樹脂２０に光を当てて硬化する工程とからなる。 - 特許庁

To provide a method for producing raw material for fertilizer with which a large quantity of slag produced in a hot metal pretreatment process can be utilized as the raw material for fertilizer, such that the raw material for phosphate fertilizer can be obtained from dephosphorized slag without adding a special process and the raw material for potassium silicate fertilizer can be obtained from desiliconized slag, and so on.例文帳に追加

特別な工程を付加することなく脱燐スラグから燐酸質肥料用原料を得ることができ且つ脱珪スラグからも珪酸質カリ肥料用原料を得るなど、溶銑予備処理工程で発生する大量のスラグを肥料用原料として利材化することができる肥料用原料の製造方法を提供する。 - 特許庁

The manufacture process for calcium phosphate moldings includes the gel composite generation step S1 to form a gel ceramic composite by blending calcium phosphate particles, a solvent and a gelatinizer; the molding step S2 to mold a gel ceramic composite generated at the gel composite generation step S1; and the sintering step S3 to sinter the ceramic composite molded at the molding step S2.例文帳に追加

リン酸カルシウム粒子と、溶媒と、ゲル化剤とを混合してゲル状のセラミックス複合体を生成するゲル複合体生成ステップＳ１と、該ゲル複合体生成ステップＳ１において生成されたゲル状のセラミックス複合体を成形する成形ステップＳ２と、該成形ステップにおいて成形されたセラミックス複合体を焼成する焼成ステップＳ３とを含むリン酸カルシウム成形体の製造方法を提供する。 - 特許庁

The processing method for the radioactive waste liquid containing phosphate ester includes an oxidative decomposition processing process of adding a solution containing copper salt capable of producing copper ions or copper ions produced from copper salt and hydrogen peroxide to the radioactive waste liquid, and oxidatively decomposing the phosphate ester within a temperature range of 20-60°C in the presence of the copper ions produced from the copper salt.例文帳に追加

本発明の放射性廃液の処理方法は、リン酸エステルを含む放射性廃液の処理方法であって、前記放射性廃液に、銅イオンを生成し得る銅塩または銅塩から生成した銅イオンを含む溶液と過酸化水素とを添加し、前記銅塩から生成した銅イオンの存在下、２０〜６０℃の温度範囲で、前記リン酸エステルを酸化分解する酸化分解処理工程を含むことを特徴とする。 - 特許庁