「Liquidus」に関連した英語例文の一覧と使い方(2ページ目) - Weblio英語例文検索

To be concrete, the temperature at the portion R1 which starts to come into contact with the molten metal M, of one side of the rotational molding member 11 is set to [melting point or liquidus temperature of the metal]×0.35 or more, and the other side of the rotational molding member 10 is cooled.例文帳に追加

具体的には、一部の回転モールド部材11の溶湯Ｍと接触し始める部分Ｒ１の温度を、〔前記金属の融点または液相線温度〕×０．３５以上に設定する一方、他の回転モールド部材10を冷却する。 - 特許庁

To achieve continuous casting for an Fe base alloy and an Ni base alloy having a low liquidus temperature of 1,330 to 1,420°C, while reducing occurrence of surface defects, improving a grinding yield, and reducing a production cost.例文帳に追加

液相線温度が1330〜1420℃と低いFe基合金およびNi基合金の連続鋳造を可能にすると共に、表面欠陥の発生が少なく、研削歩留まりが向上し、製造コスト低減をもたらす。 - 特許庁

The molten metal can rapidly be cooled to not higher than the liquidus temperature within such short time as about 1-10 sec after pouring the molten metal, and many crystal nucleus can uniformly be generated over the whole range.例文帳に追加

溶融金属の注湯後の１秒以上１０秒以下程度の短い時間内に溶融金属を液相線温度以下に急速に冷却でき、多数の結晶核を全領域にわたって均一に生成できる。 - 特許庁

It is confirmed that the wet-spreading property of the solder is improved both in the industrial applications and in the test, if the temperature of the molten solder alloy is set to the liquidus temperature of the solder alloy +10 to +30°C.例文帳に追加

半田合金溶湯の温度を当該半田合金液相線温度の＋１０〜＋３０℃に保持すると、工業的にも試験的にも半田の濡れ広がり性が改善されることが確認されている。 - 特許庁

The temporal stop of the formation is performed so that the stored semi-solid material becomes the perfect melting state by rising the temperature of a heating holding cylinder to the temperature of a liquidus temperature or higher.例文帳に追加

成形の一時休止は、加熱保持筒の温度を液相線温度以上の温度に昇温して、蓄積されているセミソリッド材料を完全溶融状態にして行う。 - 特許庁

The lead-free solder alloy is the one of which the main component is Sn, which contains 1.5-8 wt% of Cu, 0.01-2 wt% of Co, and occasionally 0.01-1 wt% of Ni, and of which the liquidus temperature is lower than 420°C.例文帳に追加

主成分がSnであって、Cuを 1.5〜8 質量％、Coを0.01〜2 質量％、場合によりNiを0.01〜１質量％含有する、液相線温度が420 ℃以下の鉛フリーはんだ合金。 - 特許庁

It is confirmed that the wet-spreading property of the solder is improved both in the industrial applications and in the test, if the atomization temperature (the dripping temperature) of the molten solder alloy is set to the liquidus temperature of the solder alloy +10 to +30°C.例文帳に追加

半田合金溶湯のアトマイズ温度（滴下温度）を当該半田合金液相線温度の＋１０〜＋３０℃に設定すると、工業的にも試験的にも半田の濡れ広がり性が改善されることが確認されている。 - 特許庁

In this invention, since the Al eutectic alloy whose liquidus line temperature (melting point) is lower than 660°C is used, a holding temperature of the melt can be set at a temperature lower than a holding temperature (670-800°C) of conventional molten Al.例文帳に追加

本発明では、その液相線温度（融点）が６６０℃より低いＡｌ共晶系合金を使用するので、その溶融物の保持温度を従来の溶融Ａｌの保持温度（６７０〜８００℃）よりも低い温度に設定できる。 - 特許庁

The molten metal can rapidly be cooled to not higher than the liquidus temperature within such short period of time as about 1-10 sec after pouring the molten metal, and many crystal nucleus can uniformly be generated over the whole range.例文帳に追加

溶融金属の注湯後の１秒以上１０秒以下程度の短い時間内に溶融金属を液相線温度以下に急速に冷却でき、多数の結晶核を全領域にわたって均一に生成できる。 - 特許庁

An aspect 3 is a method for manufacturing an aluminum-based casting alloy, which includes applying an ultrasonic vibration to a molten aluminum-based casting alloy in such a temperature range as to astride a liquidus line of the molten alloy.例文帳に追加

発明３は、アルミニウム系鋳造合金の製造方法であって、アルミニウム系鋳造合金の溶湯の液相線温度をまたいで超音波振動を付与する。 - 特許庁

By the adoption of the above compositions, even in the case Sn is used as the main, and the content of Pb is remarkably reduced, the liquidus temperature of the solder can be set to the one suitable for soldering at a lower temperature.例文帳に追加

このような組成の採用により、Ｓｎを主体としつつＰｂの含有量を大幅に削減しても、はんだ合金の液相線温度をより低温でのはんだ付けに好適なものに設定できる。 - 特許庁

To accelerate recrystallization in subsequent rolling or forging of a steel having a steel composition showing austenitic phase at liquidus temperature by refining the solidification structure of the steel and to reduce manufacturing cost by reducing reduction ratio and forging ratio, lowering recrystallization temperature, and shortening recrystallization time.例文帳に追加

鋼の組成が液相線温度においてオーステナイト相を呈する鋼について、凝固組織を微細化することにより、その後の圧延または鍛造における再結晶を促進し、圧減比や鍛造比の節減、および再結晶温度の低温化、再結晶時間の短時間化による製造コスト削減を図る。 - 特許庁

A manganin plate 14 is directly joined to the ceramic substrate 12 by mounting the ceramic substrate 12 on a bottom board 10, then directly arranging the manganin plate on the substrate 12, and heating to a temperature not lower than the solidus and not higher than the liquidus of the alloy under atmosphere or in an inert atmospheric gas.例文帳に追加

敷板１０上にセラミックス基板１２を載せ、その上面にマンガニン板１４を直接配置し、大気中または不活性雰囲気ガス中において合金の固相線以上且つ液相線以下の温度に加熱することにより、マンガニン板１４をセラミックス基板１２に直接接合する。 - 特許庁

To provide solder in which liquidus temperature can be controlled to about 70 to 205°C as the content of Pb is suppressed to ≤1.0 wt.%, and further, strength or oxidation resistance is improved more than that of the conventional lead-free solder.例文帳に追加

Ｐｂの含有量を１．０重量％以下に留めながら、液相線温度がＳｎ−Ｐｂ共晶系はんだ合金に近い１７０〜２０５℃程度とでき、さらに従来の無鉛はんだよりも強度あるいは耐酸化性が改善されたはんだ合金を提供する。 - 特許庁

In the solder powder manufacturing method, a raw solder alloy is melted, the temperature of a molten solder alloy is adjusted to the liquidus temperature of the solder alloy +10 to +30°C, and the molten solder alloy is atomized after the temperature is maintained.例文帳に追加

半田合金原料を溶解し、半田合金溶湯の温度を当該半田合金の液相線温度の＋１０〜＋３０℃に調整し、当該温度を保持した後、半田合金溶湯をアトマイズすることを特徴とする半田粉の製造方法を提案する。 - 特許庁

To provide at low price, a high-temperature lead-free solder material which contains no lead, gold or the like, prevents deterioration with time resulting from oxidation or corrosion corresponding to high-temperature soldering needing a liquidus temperature of about 250 to 400°C, and has high reliability.例文帳に追加

本発明の課題は、前記事情に鑑み、鉛や金等を含有することなく、液相線温度が２５０℃〜４００℃程度必要となる高温はんだに対応した酸化や腐食に起因する経時劣化を防止し、高信頼性を有する高温鉛フリーはんだ材料を低価格で提供することである。 - 特許庁

The die-bonding solder material 30 has a solidus temperature of 243°C and the mounting solder material 70 has a liquidus temperature of approximately 215 to 220°C, so the die-bonding solder material 30 is not molten even at a heating temperature (equal to or lower than 240°C) of a reflow furnace.例文帳に追加

ダイボンド用はんだ材料３０の固相線温度は２４３℃であり、実装用はんだ材料７０の液相線温度は２１５〜２２０℃程度であるので、リフロー炉の加熱温度（２４０℃以下）によってもダイボンド用はんだ材料３０は溶解しない。 - 特許庁

In the coated electrode for arc welding having a core wire made of mild steel or low-alloy steel coated with a coating agent, the coating agent contains 1.3-9.0 mass% of a Cu alloy whose liquidus temperature is 1,150-1,400°C and average particle diameter is 40-160 μm.例文帳に追加

軟鋼または低合金鋼からなる心線に被覆剤が塗装されている被覆アーク溶接棒において、液相線温度が１１５０〜１４００℃、かつ平均粒径が４０〜１６０μｍのＣｕ合金を被覆剤中に１．３〜９．０質量％含有させる。 - 特許庁

The joined product 10 is equipped with a first ceramic member 11, a second ceramic member 12 and a joining layer 13 that contains a flexible metal and joins the first ceramic member 11 and the second ceramic member 12 through the thermocompression bonding at a joining temperature lower than the liquidus of the flexible metal.例文帳に追加

接合体１０は、第１のセラミックス部材１１と、第２のセラミックス部材１２と、軟質金属を含み、その軟質金属の液相線未満の接合温度において熱圧接することにより、第１のセラミックス部材１１及び第２のセラミックス部材１２を接合する接合層１３とを備える。 - 特許庁

To provide an induction heater which can reliably raise the temperature of a center part of a steel member to the temperature immediately below the liquidus, maintain a surface layer part in a non-molten condition, and feed the steel member to the next hot working in a most favorable condition.例文帳に追加

鋼材中心部を液相線直下の温度まで確実に昇温すると共に、表層部は非溶融状態を維持することができ、最も好適な状態で鋼材を次の熱間加工へ供給することができる高周波誘導加熱装置を提供すること。 - 特許庁

The addition of low-quantity Ga allows the liquidus temperatures of both Au and Sn to be fairly lowered for the purpose of lowering a melting point (lowering it by 10°C or more, by approximately 27°C under normal conditions, in comparison with Au-Sn eutectic solder) and reinforcing the temperature sensitivity of the creep resistance of the solder.例文帳に追加

少量のＧａを添加することで、ＡｕおよびＳｎ双方の液相線温度を相当に下げ、したがって融点を下げる（共晶Ａｕ—Ｓｎはんだよりも少なくとも１０℃、通常約２７℃下がる）とともに、はんだの耐クリープ性の温度敏感性も強化する。 - 特許庁

The method for manufacturing the alloy product having an average grain size of 1 to 3 μm comprises the steps of: casting a molten metal having a composition which satisfies the above expression; quenching it at a cooling rate of 270°C/minute or higher while the metal is in between a liquidus curve temperature and 600°C, to produce an ingot; and then repeating rolling and annealing each several times.例文帳に追加

また、本合金の製造にあたっては上述の式を満たす組成の溶湯を鋳造し、液相線温度から６００℃までの間を２７０℃／分以上の冷却速度で急冷して鋳塊とし、その後圧延、焼鈍をそれぞれ複数回繰り返して平均結晶粒径１μｍ〜３μｍの製品を得る。 - 特許庁

The molten metal of an aluminum alloy comprising, by mass, 15 to 20% Si, 1 to 4% Fe, 0.004 to 0.02% P, 0.15 to 0.4% Ti, 0.15 to 0.55% Cr and 0.4 to 2.4% Mn, and the balance Al with inevitable impurities is irradiated with ultrasonic vibration at a liquidus temperature or above.例文帳に追加

Si：15〜20質量％，Fe：1〜4質量％、P：0.004〜0.02質量％、Ti：0.15〜0.4質量％、Cr：0.15〜0.55質量％、Mn：0.4〜2.4質量％を含み、残部がAlと不可避的不純物からなるアルミニウム合金溶湯に、液相線温度以上で超音波振動を照射する。 - 特許庁

And by making the brazing filler sheet the skin material, using the same plate continuous casting machine, bringing into contact with the aluminum alloy molten metal having the higher solid line temperature than the liquidus line temperature of the brazing filler, and conducting making the brazing sheet and the core material into a clad together with the solidification of the core material molten metal, the brazing material is manufactured.例文帳に追加

また、上記ろう材シートを皮材として同じく板連続鋳造機を用い、ろう材の液相線温度より高い固相線温度を有するアルミニウム合金芯材溶湯と接触させ芯材溶湯の凝固とともにろう材シートと芯材のクラッド化を行ないブレージングシートを製造する。 - 特許庁

To provide a lead-free solder alloy which accommodates high-temperature soldering which needs a liquidus-line temperature of about 250-400°C without containing lead, gold or the like, and secure high reliability of a solder joint portion, and to provide a solder joint which is soldered using the lead-free solder alloy at a low price.例文帳に追加

鉛や金等を含有することなく、液相線温度が２５０℃〜４００℃程度必要となる高温はんだ付けに対応し、はんだ接合部の高信頼性を確保した鉛フリーはんだ合金及び当該鉛フリーはんだ合金を用いてはんだ付けを行ったはんだ継手を低価格で提供することである。 - 特許庁

To provide a nickel based brazing filler metal which is completely free from boron (B) or phosphorus (P) that is likely to form a hard and brittle compound in the brazed layer part, and in which the liquidus is lowered below 1,100°C by adding a small amount of silicon (Si) and which is abundant in ductility, heat resistance and corrosion resistance.例文帳に追加

ろう層部に硬くて脆い化合物を形成しやすいボロン（Ｂ）と燐（Ｐ）を全く含有せず、また、少量のシリコン（Ｓｉ）を添加して液相線が１１００℃より低く、延性と耐熱性及び耐食性に富むニッケル基ろう材を提供すること。 - 特許庁

The alkali-free glass substantially free from alkali metal oxides has: a strain point of higher than 680°C; a mean thermal expansion coefficient of 40×10^-7 to 55×10^-7/°C within a temperature range of 30 to 380°C; and a liquidus temperature of lower than 1,200°C.例文帳に追加

本発明の無アルカリガラスは、実質的にアルカリ金属酸化物を含有せず、歪点が６８０℃より高く、３０〜３８０℃の温度範囲における平均熱膨張係数が４０〜５５×１０^−７／℃であり、液相温度が１２００℃より低いことを特徴とする。 - 特許庁

Its wear resistance or the like can be improved because of the incorporation of 14 to 20% Cu and 8.5 to 15% Zn in this way, and the fluidity of molten metal can be improved, and further, its liquidus temperature can be reduced by the blending of 5 to 8% Si therein.例文帳に追加

このようにＣｕを１４〜２０重量％およびＺｎを８．５〜１５重量％含むため耐摩耗性などを向上させることができ、これにＳｉを５〜８重量％配合することによって溶湯の流動性を向上させるとともに液相線温度を下げることができる。 - 特許庁

In a continuous casting method for casting an aluminum-killed steel into a mold from a ladle through a tundish, related to the heat insulating agent for adding onto the molten steel surface in the tundish, a high clean aluminum-killed steel is produced by changing the necessary charging quantity according to the liquidus temperature of this heat insulating agent.例文帳に追加

取鍋からタンディッシュを経由してモールドに、アルミキルド鋼を鋳造する連続鋳造法において、タンディッシュ内溶鋼表面に添加する保温剤について、その保温剤の液相線温度に応じて必要投入量を変化させることにより、高清浄のアルミキルド鋼を製造する。 - 特許庁

The casting method forms a casting by pouring a molten active metal alloy 20 into an interior space 2 formed in a casting mold 1 and solidifying the molten active metal alloy 20 in the interior space 2, and uses the casting mold 1 formed from a high melting point pure metal which has a melting point higher than the liquidus line temperature of the active metal alloy and consists of one metal element among metal elements contained in the active metal alloy.例文帳に追加

鋳型１に形成された内部空間２に活性金属合金の溶湯２０を注湯し、内部空間２において溶湯２０を固化させて鋳造品を形成する鋳造方法であって、活性金属合金の液相線温度よりも融点が高く、かつ、活性金属合金が含有する金属元素のうち一の金属元素からなる高融点純金属で形成された鋳型１を用いることを特徴とする。 - 特許庁

An independent face is formed on the stream of the first alloy, the stream of the second alloy is first contacted with the independent face at a place in which the temperature of the independent face is lower than the solidus temperature of the first alloy, and next, the boundary between the two alloys is reheated to a temperature between a liquidus temperature and a solidus temperature between the two alloys so as to form a composite ingot.例文帳に追加

第１合金のストリームの上に自立面を生成させ、自立面の温度が第１合金の固相線温度よりも低い場所で第２合金のストリームを自立面に最初に接触させ、次いで２つの合金の間の界面を液相線温度と固相線温度との間の温度まで再加熱することにより、複合インゴットを形成する。 - 特許庁

By weight, 9.5 to 12% aluminum, 0.65 to 1.75% zinc, 0.5 to 1.5% calcium and 0.17 to 0.4% manganese are incorporated into a magnesium alloy molded into a prescribed shape by using an injection molding machine 10 in a state of being heated and melted to a temperature higher than a liquidus line.例文帳に追加

液相線以上の温度に加熱溶解された状態で射出成形機１０によって所定の形状に成形されるマグネシウム合金に、アルミニウム９．５〜１２重量％、亜鉛０．６５〜１．７５重量％、カルシウム０．５〜１．５重量％およびマンガン０．１７〜０．４重量％を含有させた。 - 特許庁

The Al-Si aluminum alloy billet having a structure including an eutectic phase and an α-Al phase, which has been grown to be lumps after dividing the billet, is reheated up to a temperature between the eutectic temperature and the liquidus line of the Al-Si aluminum alloy by means of a ceramic infra-red heating source.例文帳に追加

共晶相と、分断して塊状に成長させたα−Ａｌ相を有する組織としたＡｌ−Ｓｉ系アルミニウム合金ビレットを、セラミックス赤外線加熱源により当該Ａｌ−Ｓｉ系アルミニウム合金の共晶温度から液相線の間の温度に再加熱して前記Ａｌ−Ｓｉ系アルミニウム合金ビレットを半溶融状態した後に、所定の加圧成形を施す。 - 特許庁

Disclosed is a leadless bronze casting alloy in which the intrusion of low Pb is allowable, and at least comprising Bi and high concentration P, where Ni is comprised, so as to increase liquidus temperature by the interaction between P and Ni, and excessive Massesy solidification is relaxed, so as to be a leadless bronze casting alloy in which the soundness of a casting is secured.例文帳に追加

本発明は、低Ｐｂが混入することを許容し、少なくともＢｉと高濃度のＰを含有する青銅鋳物合金において、Ｎｉを含有させてＰとＮｉとの交互作用により固相線温度を上げ、過度のマッシー型凝固を緩和することで鋳物の健全性を確保した鉛レス青銅鋳物合金である。 - 特許庁

When the permanent magnet 40 is rotated by the rotary motor 46, and molten metal is supplied into the vessel 12 at a fixed superheat degree from a liquidus temperature, magnetic force of the permanent magnet 40 acts, the whole of the molten metal in the vessel 12 is stirred, and metal slurry in a solid-liquid coexistent state can be homogeneously and efficiently obtained.例文帳に追加

前記回転モータ４６によって永久磁石４０を回転させておき、前記容器１２に、溶湯を液層線温度より一定の過熱度で注湯すると、永久磁石４０の磁力が作用し、前記容器１２内の溶湯の全体が攪拌され、固液共存状態の金属スラリーを均質に効率良く得ることができる。 - 特許庁

Further, in this casting system (3), the refined liquid metal source (1) obtained by removing the oxide and the sulfide from the metal by refining, a solid metal particle adding system (200) for adding the solid metal particles on the surface of the liquidus portion in the casting, and the nucleation casting system (2) for forming the casting, are provided.例文帳に追加

鋳造システム（３）は、精錬により金属から酸化物および硫化物を除去した精錬された液体金属のソース（１）と、鋳造物の液相線部分の表面に固体金属粒子を添加する固体金属粒子添加システム（２００）と、鋳造物を形成する核生成鋳造システム（２）とを備える。 - 特許庁