「powder lubricant」に関連した英語例文の一覧と使い方(2ページ目) - Weblio英語例文検索

A solid lubricant powder 1 is dispersed and embedded on and under the surface of the fishing line guide projected stripe G.例文帳に追加

釣糸案内突条Ｇの表面に固体潤滑粉１が分散、埋設されている。 - 特許庁

This iron-base powdery mixture is prepared by mixing, for an iron-base powder, a free lubricant powder containing 0.02-1 mass % antistatic agent in an amount of 0.1-0.5 mass % based on the total amount of the powder mixture or further mixing an alloying powder and/or a machinability-improving powder.例文帳に追加

鉄基粉に、混合粉全量に対し0.1 〜0.5 質量％の、帯電防止剤を0.02〜１質量％含有する遊離潤滑剤粉と、あるいはさらに合金用粉および／または切削性改善粉を混合し、鉄基混合粉とする。 - 特許庁

The lubricant includes a lubrication liquid and an aluminum powder, and is formed into a paste by mixing the lubrication liquid with the aluminum powder.例文帳に追加

潤滑剤は、潤滑液と、アルミニウム粉末とからなり、潤滑液とアルミニウム粉末を混合してペースト状に形成した。 - 特許庁

A powder of a metal soap such as barium stearate or lithium stearate is used as the insulating powder lubricant.例文帳に追加

絶縁性粉末潤滑剤として、ステアリン酸バリウム又はステアリン酸リチウムなどの金属石鹸粉末を使用する。 - 特許庁

To provide a powder slurry composition uniformly mixing a fluorine lubricant with a lubricant such as a hydrocarbon oil and a silicone oil without reducing water and oil repellency which are characteristics of the fluorine lubricant.例文帳に追加

フッ素系油剤の特性である撥水撥油性を低下することなく、フッ素系油剤と、炭化水素油、シリコーン油等の油剤とを均一に混合した粉体スラリー組成物を提供すること。 - 特許庁

This lubricant for cable insertion is characterized in that the lubricant is used in inserting the cable into the protecting tube and the lubricant is composed of a water-absorbing resin powder (A).例文帳に追加

ケーブルを保護管内に挿通する際に用いられる潤滑剤であって、該潤滑剤が吸水性樹脂粉末（Ａ）からなることを特徴とするケーブル挿通用潤滑剤。 - 特許庁

There are used a lubricant application blade to spread a lubricant and an elastic rotational body such as a melamine roller or a sponge roller as a supply roller which is pressed on an image bearing member to apply the powder lubricant.例文帳に追加

潤滑剤を伸展させる潤滑剤塗付ブレードと、像担持体に押圧されて前記粉体潤滑剤を塗布する供給ローラとしてメラミンローラやスポンジローラ等の弾性回転体を用いる。 - 特許庁

Lubricant powder 310 generated by rotating the lubricant roller 31 in such a state that the lubricant roller 31 and the cutting member 32 are in press-contact with each other is supplied to the surface of the image carrier 8.例文帳に追加

潤滑剤ローラ３１と切削部材３２が互いに圧接した状態で潤滑剤ローラ３１を回転させることによって生じる潤滑剤粉３１０を像担持体８の表面へ供給するように構成した。 - 特許庁

To provide a compacting composition in which residues are not left at the time of removing a lubricant from a compact by a thermal means and having sufficient lubricity and powder fluidity with respect to a mixed compacting composition composed of metal powder or ceramic powder and a lubricant, which is the starting material for a powder metallurgical or ceramic product.例文帳に追加

粉末冶金またはセラミック製品の出発材料である、金属粉末またはセラミック粉末と潤滑剤との混合成形組成物において、熱的手段による成形体からの潤滑剤除去に際して残留物が残らず、十分な潤滑性と粉末流動性を有する成形組成物。 - 特許庁

In the iron-base powdery mixture mixing the iron-base powder, powder for alloy, powder for improving the machinability and further, lubricant, as the powder for improving the machinability, manganese sulfide powder and further, calcium phosphate powder and/or hydroxyapatite powder are added.例文帳に追加

鉄基粉末に、合金用粉末と、切削性改善用粉末と、さらに潤滑剤と、を混合した鉄基混合粉で、切削性改善用粉末を、硫化マンガン粉とさらに加えてリン酸カルシウム粉および／またはヒドロキシアパタイト粉とする。 - 特許庁

Moreover, preferably, organosiloxane has phenyl group, the lubricant melted and fixed to the iron base powder is composed of a co-melted material of calcium soap and rithium soap or a co-melted material of calcium soap and an amide lubricant, the freed lubricant is composed of a powdery mixture of an amide lubricant and polymethyl methacrylate powder or rithium soap powder.例文帳に追加

なお、オルガノシロキサンがフェニル基を有し、鉄基粉末に溶融・固着した潤滑剤がカルシウム石鹸とリチウム石鹸の共溶融物またはカルシウム石鹸とアミド系潤滑剤の共溶融物であり、遊離した潤滑剤がアミド系潤滑剤とポリメタクリル酸メチル粉末との混合粉末またはリチウム石鹸粉末とするのが好ましい。 - 特許庁

Prior to the operation, the lubricant powder 102 is applied on the surface of a transfer roller 15, a recess 101 formed of the foam 100 on the surface of foam urethane constituting the transfer roller 15 is filled up with the lubricant powder 102.例文帳に追加

使用前の転写ローラ１５の表面に潤滑性粉体１０２を塗布し、転写ローラ１５を構成する発泡ウレタン等の表面において発泡体１００が形成する凹部１０１を潤滑性粉体１０２によって埋めておく。 - 特許庁

During operation of a generator 10, metal abrasion powder 44 is formed by abrasion between the tooth parts 22 and the tooth parts 24, and this abrasion powder 44 is mixed with the lubricant 40 in a chamber 42 for the lubricant.例文帳に追加

ジェネレータ１０の動作時には、歯部２２と歯部２４とが摩耗することにより金属摩耗粉４４が形成され、この摩耗粉４４は、潤滑油用チャンバ４２において潤滑油４０と混合される。 - 特許庁

The lower punch 12 has a liquid-reservoir groove 24 to be charged with molding lubricant formed by dispersing solid lubricant powder having a maximum particle diameter of 20 μm or less for each powder particle into a liquid solvent.例文帳に追加

下パンチ12は、最大粒径:20μm以下の固体潤滑剤の粉末を液媒に分散させた金型用潤滑剤を充填する液溜め溝24を具える。 - 特許庁

To provide a blowing control method for a powder die parting agent/ lubricant to evenly and uniformly coat on the face to be coated with a powder die parting agent/lubricant.例文帳に追加

粉体離型剤・潤滑剤を塗布すべき面に万遍なく均一に塗布する粉体離型剤・潤滑剤の吹き付け制御方法とその装置の提供。 - 特許庁

To provide a rolling bearing which retains abrasive powder or lubricant within the bearing over a long period and hardly releases the abrasive powder or lubricant within the bearing outside the bearing over a long period.例文帳に追加

摩耗粉や潤滑剤を軸受内に長期に亘って保持することができて、軸受内の摩耗粉や潤滑剤を軸受外に長期に亘って放出しにくい転がり軸受を提供すること。 - 特許庁

On powder compression, by the operation of the three way valve 80, powder 34 in a cavity 27 is degassed, and the lubricant 68 in the lubricant feed path 74 is recovered to the recovery tank 82.例文帳に追加

粉末圧縮時には、三方バルブ８０の動作によって、キャビティ２７内の粉末３４が脱気され、潤滑剤供給路７４内の潤滑剤６８が回収タンク８２に回収される。 - 特許庁

A method for supplying the lubricant comprises converting the lubricant to be applied onto a die 14 into a misty state, naturally or forcefully attaching and applying the lubricant supplied from a charging line 4 onto an inner wall of the die 14, and discharging a surplus misty lubricant (b) before charging powder (a).例文帳に追加

潤滑剤の供給方法としては、ダイス１４に塗布される潤滑剤を霧状にして供給配管４よりダイス１４内壁に自然又は強制的に付着、塗布して、粉末体ａ充填前に余剰の霧状潤滑剤ｂを排出する構成とする。 - 特許庁

The wire drawing dry lubricant recycling machine for recycling a dry lubricant used between dies of a wire drawing machine and the wire rod is equipped with a hopper section 1 in which the lubricant A to be recycled is charged, a filter section 2, an iron powder removing section 3 and a recycled lubricant recovering section 4.例文帳に追加

この伸線乾式潤滑剤再生機は、伸線機のダイスと線材との間に用いられる乾式の潤滑剤を再生する装置であって、再生する潤滑剤Ａを入れるホッパ部１と、フィルタ部２と、鉄粉除去部３と、再生潤滑剤回収部４とを備える。 - 特許庁

The lubricant application device 31 is provided with application mechanisms 33 and 35 of applying the lubricant from a solid lubricant 34 on the surface of a photoreceptor 20 being an image carrier carrying toner, and silicon-based powder or silicon-based fine particles are used as the lubricant.例文帳に追加

潤滑材塗布装置３１は、トナーを担持する像担持体である感光体２０の表面に固形潤滑材３４から潤滑材を塗布する塗布機構３３，３５を具備し、潤滑材としてシリコン系粉末又はシリコン系粉体を使用している。 - 特許庁

The characteristic of this lubricant is to have a lubricant A comprising ≤50 wt.% graphite powder, an organic and/or inorganic water-soluble binder and water and boron carbide powder in an amount of ≤20 wt.% based on the lubricant A and to form dried film after applying it to a sliding part.例文帳に追加

黒鉛粉末５０重量％以下、有機系およびまたは無機系の水溶性バインダおよび他を水とする潤滑剤Ａと、この潤滑剤Ａに対して２０重量％以下の炭化ホウ素粉末とを有し、摺動部への塗布後に乾燥被膜を形成することを特徴とする。 - 特許庁

To allow a lubricant to be added to the powder in such an amount that can secure the coagulation preventing effect of powder to a die, furthermore to prevent the remaining of the components of the lubricant in a molded body after a delubricant stage and to suppress the oxidation and componental fluctuation of a sintered body caused by the lubricant.例文帳に追加

型に対する粉末の凝着防止効果を十分に確保できるだけの潤滑剤をその粉末に添加できるようにするとともに、脱潤滑剤工程後に潤滑剤の成分が成形体に残留しないようにして、潤滑剤に起因した焼結体の酸化や成分変動を抑制する。 - 特許庁

A lubricant discharge aperture is provided in the nut 11 or a seal cap 15 and the oil content, and the iron powder concentration of the lubricant discharged outside the nut 11 from this lubricant discharge aperture are measured with an oil content meter 26 and an iron powder densitometer 27.例文帳に追加

ナット１１またはシールキャップ１５に潤滑剤排出孔を設け、この潤滑剤排出孔からナット１１の外部に排出された潤滑剤の油分率や鉄粉濃度を油分率計２６及び鉄粉濃度計２７で計測するようにした。 - 特許庁

The iron-based powdery mixture contains iron-based powder whose surface is stuck with graphite powder as powder for alloying and the fluoride of alkaline earth metals as powder for improving machinability and a free lubricant.例文帳に追加

鉄基粉末表面に、合金用粉末としての黒鉛粉と、切削性改善用粉末としてのアルカリ土類金属のフッ化物とを固着した鉄基粉末と、遊離潤滑剤とを含む鉄基混合粉とする。 - 特許庁

To provide a powder applying device capable of supplying/applying powder (powder lubricant) to an image carrier such as a photoreceptor or an intermediate transfer member while regulating the amount of the powder.例文帳に追加

粉体(粉体状潤滑剤)を感光体、中間転写体等の像担持体に量を規制して供給・塗布することができる粉体塗布装置を提供する。 - 特許庁

A powder mixture which contains a soft magnetic powder and an insulating powder lubricant in an amount of 0.1% by mass or more relative to the soft magnetic powder, is compaction-molded at a molding pressure of 800 MPa or less, thereby obtaining a powder compact that has a space factor of the soft magnetic powder of 93% or more.例文帳に追加

軟磁性粉末に対して０．１質量％以上の絶縁性粉末潤滑剤を添加した粉末混合物に、８００ＭＰａ以下の成形圧力を加えて、軟磁性粉末の占積率が９３％以上の圧粉体に圧縮成形する。 - 特許庁

This iron-based powdery mixture is composed of iron-based powder the surface of which is stuck with powder for an alloy or further with machinability improving powder by a binder and a free lubricant, the iron-based powder is composed of 60 to 90 mass% atomized iron powder and 40 to 10 mass% reduced iron powder.例文帳に追加

表面に合金用粉末あるいはさらに切削性改善粉末が結合材により固着された鉄基粉末と、さらに遊離潤滑剤とからなる鉄基混合粉とし、鉄基粉末を、60〜90質量％のアトマイズ鉄粉と、40〜10質量％の還元鉄粉とする。 - 特許庁

Dust core powder is composed of ferromagnetic powder, an insulating material containing silicone resin or phenolic resin, and a lubricant, where the lubricant contains aluminum stearate, and the dust core is formed of the dust core powder.例文帳に追加

強磁性粉末と、シリコーン樹脂又はフェノール樹脂を含む絶縁材と、潤滑剤とを含む圧粉磁芯用粉末であって、潤滑剤がステアリン酸アルミニウムを含有する圧粉磁芯用粉末であり、この圧粉磁芯用粉末を用いる圧粉磁芯である。 - 特許庁

This powder molding method comprises a stage where a die lubricant 21 is jetted and the die lubricant 21 is stuck to the inside wall 3 of a heated mold device 1 and a stage where the molding is molded by filling the molding powder in the mold device 1 and pressing and molding the molding powder.例文帳に追加

粉末成形方法は、金型潤滑剤２１を噴出し、金型潤滑剤２１を加熱された金型装置１の内壁３に付着させる工程と、金型装置１に成形用粉末を充填し、成形用粉末を加圧成形することによって成形体を形成する工程とを備える。 - 特許庁

The powder molding method comprises a process of injecting a die lubricant 21 to allow the die lubricant 21 to adhere to a heated inner wall 3 of a die apparatus 1 and a process of forming the molding body by packing powder for molding into the die apparatus 1 and press molding the powder for molding.例文帳に追加

粉末成形方法は、金型潤滑剤２１を噴出し、金型潤滑剤２１を加熱された金型装置１の内壁３に付着させる工程と、金型装置１に成形用粉末を充填し、成形用粉末を加圧成形することによって成形体を形成する工程とを備える。 - 特許庁

Since the solid lubricant 86 is in a solid state, irregular charge when the material powder 34 is charged into the cavity C is significantly suppressed as compared with a conventional powder-molding device in which a liquid lubricant is applied to the side face of the through-hole, in the powder-molding apparatus 10.例文帳に追加

この固体潤滑剤８６は固体状であるため、本発明に係る粉末成形装置１０においては、液体状の潤滑剤を貫通孔側面に塗布する従来の粉末成形装置に比べて、原料粉末３４をキャビティＣ内に充填したときの充填ムラが有意に抑制される。 - 特許庁

The powdery in-mold lubricant for powder metallurgy, having an average particle diameter of 0.05-80 μm and containing, as an essential component, an amorphous polymer powder based on a polymer which is a (meth) acrylate-base polymer and has a glass transition temperature of ≥50°C, and a powder metallurgy method using the lubricant are disclosed.例文帳に追加

（メタ）アクリレート系ポリマーであって、ガラス転移温度が５０℃以上のポリマーをベースとし、平均粒径が０．０５〜８０μｍである非晶質ポリマー粉末を必須成分として含む粉末冶金用粉状型内潤滑剤と、該潤滑剤を用いた粉末冶金法を開示する。 - 特許庁

The solid lubricant (50) is used in lubricating the surface of an image carrier (1) in an elecrophotographic image-forming apparatus, and the solid lubricant surface is scraped off by a brush roll (51) of a lubricant feed member, and the scraped solid lubricant is fed to the image carrier (1), and the solid lubricant comprises zinc stearate as the major component and a fine powder material.例文帳に追加

電子写真画像形成装置における像担持体（１）表面の潤滑のために使用される固形潤滑剤（５０）であって、その表面が潤滑剤供給部材であるブラシロール（５１）によって掻き取られ、この掻き取られたものが像担持体（１）に供給されるものであり、主成分としてのステアリン酸亜鉛と、微粉末材料とを含有してなる。 - 特許庁

A blowing control method for a powder die parting agent/ lubricant is constituted so that plural nozzles 12 are arranged in a die 11, the discharging of the powder die parting agent/lubricant of respective nozzles 12 and the evacuation of a die cavity 17 are arbitrarily switched, the flow of the air and powder dir parting agent/lubricant is controlled.例文帳に追加

（１）金型１１内に複数のノズル１２を設けておき、各ノズル１２の粉体離型剤・潤滑剤の吐出と金型キャビティ１７減圧とを任意に切替え、金型キャビティ１７内の空気および粉体離型剤・潤滑剤の流れを制御する粉体離型剤・潤滑剤の吹き付け制御方法。 - 特許庁

In the powder molding method by which powder is packed into a cavity and is subjected to compression molding into a compact, and the compact is taken out from the cavity, before the powder is packed, the molding face of the cavity is electrostatically coated with a microcapsule lubricant obtained by coating a liquid lubricant with a solid film formation substance so as to provide a film of the microcapsule lubricant.例文帳に追加

キャビティに粉末を充填して圧粉体に圧縮成形した後に圧粉体をキャビティから取り出す粉末成形方法であり、粉末を充填する前に、液状潤滑剤を固体成膜物質で被覆したマイクロカプセル潤滑剤をキャビティの成形面に静電塗布してマイクロカプセル潤滑剤の被膜を設ける。 - 特許庁

This method for manufacturing the sintered metallic compact comprises compressing metal powder comprising iron powder as a main component, and copper-plated metal powder which includes 20-80 mass% of plated copper, or lubricant powder such as carbon powder, while pressurizing it, machining the obtained compact, and then sintering it.例文帳に追加

メッキされた銅を２０〜８０質量％含有する銅メッキ金属粉末、又は炭素粉末などの潤滑剤粉末の添加された鉄粉からなる金属紛末を加圧しながら圧縮し、得た成形体を機械加工したのち焼結して焼結金属体とする。 - 特許庁

The lubricating film is formed of the mixed powder of molybdenum disulfide powder and titanium powder as a solid lubricant which are jetted at a jetting speed of 80 m/sec or higher or a jetting pressure of 0.3 MPa or higher.例文帳に追加

この潤滑被膜は、固体潤滑剤である二硫化モリブデンの粉末とチタン粉末との混合粉末を、噴射速度８０ｍ／ｓ以上又は噴射圧力０．３ＭＰａ以上で噴射することにより形成されたものである。 - 特許庁

A lubricant fine powder 5, for example, silicon powder, polyamide resin powder, molybdenum disulfide, fatty acid amide or the like is dispersed and included in the body part 40 of the glass run 4 consisting of EPDM rubber or TPO.例文帳に追加

ＥＰＤＭゴムまたはＴＰＯからなるガラスラン４の本体部４０に、滑剤の微粉末５、例えばシリコンパウダ、ポリアミド樹脂パウダ、二硫化モリブデン、脂肪酸アミドを分散含有せしめる。 - 特許庁

The powder magnetic core 10 is pressed out of what is obtained by adding a binder resin and a lubricant to soft magnetic powder having electric resistance making it possible to suppress eddy current among soft magnetic powder particles.例文帳に追加

圧粉磁心１０は、軟磁性粉末粒子間における渦電流を抑制し得る電気抵抗を有する軟磁性粉末にバインダー樹脂および潤滑剤を加えて加圧成形される。 - 特許庁

In the iron based powdery mixture obtained by adding graphite powder and a lubricant to iron powder, as the iron powder, the one in which the hardness at the central part is ≤75 by micro Vickers hardness Hv is used.例文帳に追加

鉄粉に、黒鉛粉および潤滑剤を添加した鉄基粉末混合物において、鉄粉として、中心部の硬さがマイクロビッカース硬さＨv で75以下である鉄粉を用いる。 - 特許庁

An aqueous solution L of the lubricant is atomized from an atomization part 12 to a molding part 6 formed at a die 2, thereafter, raw material powder M is filled into the molding part 6, and the filled raw material powder M is compressed to mold the powder molding 101.例文帳に追加

ダイ２に形成した成形部６に噴霧部12から潤滑剤の水溶液Ｌを噴霧した後、原料粉末Ｍを成形部６に充填し、充填した原料粉末Ｍを圧縮して粉末成形体101を成形する。 - 特許庁

Powder prepd. by blending org. matter, such as binder and lubricant, of several bulk to several tens bulk % with fine metallic powder of 5 to 44 μm in grain size is pressurized under low-temp. heating, by which the powder is molded to a shape approximate to a desired shape 9.例文帳に追加

粒径５乃至４４μｍの金属細粉に数嵩％〜数十嵩％の結合剤、潤滑剤等の有機物をブレンドした粉末を低温加熱しながら加圧することによって目的形状に近似した形状に成形する。 - 特許庁

The powder molding method is further provided with a stage where powder for molding is filled into the die apparatus with the die lubricant stuck thereto, and the powder for molding is subjected to pressure molding to form a molding.例文帳に追加

粉末成形方法は、金型潤滑剤が付着された金型装置に成形用粉末を充填し、成形用粉末を加圧成形することによって成形体を形成する工程をさらに備える。 - 特許庁

A mixture of polytetrafluoroethylene fine powder with a liquid lubricant is molded in the form of a sheet extending in a predetermined direction, this sheet-like molding containing the liquid lubricant is stretched in a width direction, and the liquid lubricant is removed from the sheet-like molding.例文帳に追加

ポリテトラフルオロエチレン微粉末に液状潤滑剤を加えた混合物を所定方向に延びるシート状に成形し、このシート状成形体を液状潤滑剤を含んだ状態で幅方向に延伸した後に、当該シート状成形体から液状潤滑剤を除去する。 - 特許庁

The soft magnetic powder core having a soft magnetic material and low melting point lubricant is manufactured by: adding the low melting point lubricant to the insulation-treated soft magnetic material; carrying out warm forming of the soft magnetic material to which the low melting point lubricant is added; and heat processing the soft magnetic material being formed.例文帳に追加

絶縁処理された軟磁性材料に低融点潤滑剤を添加し、低融点潤滑剤が添加された軟磁性材料を温間成形し、成形された軟磁性材料を熱処理することで、軟磁性材料および低融点潤滑剤を含む軟磁性圧粉磁芯を製造する。 - 特許庁