「recrystallization」に関連した英語例文の一覧と使い方(2ページ目) - Weblio英語例文検索

The recrystallization refinement experiments conducted by the Chemicals Evaluation and Research Institute, Japan (CERI), have confirmed that a single recrystallization refinement can reduce HCB by around 65% (with a TCPA yield of 70-80%) and that three repeated recrystallization refinements can reduce HCB by around 95% (with a TCPA yield of 50-60%). 例文帳に追加

財団法人化学物質評価研究機構で行ったこれらの再結晶精製実験では、１回の再結晶精製で 65％程度のＨＣＢ削減（ＴＣＰＡの歩留まりは 70～80％）、また、３回の再結晶精製で 95％程度のＨＣＢ削減（ＴＣＰＡの歩留まりは 50～60％）を確認している。 - 経済産業省

In its production method, after hot rolling accompanied by recrystallization, different peripheral speed rolling is performed at a draft of ≥30% in the nonrecrystallization temperature region of 170 to 350°C, and thereafter, solution treatment accompanied by recrystallization is performed.例文帳に追加

その製法として、再結晶を伴なう熱間圧延後、１７０〜３５０℃の非再結晶温度域で３０％以上の圧下率で異周速圧延を行なった後、再結晶を伴なう溶体化処理を施す。 - 特許庁

This refining process comprises reusing, as a recrystallization solvent for acrylamidoalkanesulfonic acid, a filtrate generated by the recrystallization of the subject acid using a lower alcohol as a solvent.例文帳に追加

低級アルコールを溶媒とするアクリルアミドアルカンスルホン酸の再結晶において生じたろ液を、アクリルアミドアルカンスルホン酸の再結晶溶媒として再使用することを特徴とするアクリルアミドアルカンスルホン酸の精製方法。 - 特許庁

To make clear the cause of the unstabilizing of secondary recrystallization in the case of increasing the heating rate in decarburizing annealing and controlling primary recrystallization in the method for producing a grain oriented silicon steel sheet, and to provide stable production conditions.例文帳に追加

方向性電磁鋼板の製造方法において、脱炭焼鈍の加熱速度を高めて一次再結晶を制御する場合の二次再結晶が不安定になる原因を解明し、安定製造条件を提示する。 - 特許庁

To solve the problem of concentration change of the brine of high concentration and troubles in a tank and a supply conduit caused by recrystallization of the dissolved salts by preventing recrystallization of dissolved salts during storing and feeding of the brine of high concentration.例文帳に追加

高濃度塩水の貯留中や供給中に、溶解している塩類の再結晶化を防止して、塩類の再結晶化に起因する高濃度塩水の濃度変化、タンクや供給管路でのトラブルを解消する。 - 特許庁

Furthermore, one company reported that refinement using this solvent can reduce HCB concentration by 80% with a single recrystallization, with HCB concentration reduced to some 200ppm in the first recrystallization, to some 80ppm in the second and to some 40ppm in the third. 例文帳に追加

また、ある社からの情報によれば、この溶媒での再結晶は１回でＨＣＢの 80％の削減が可能であり、１回目で約 200ppmまで、２回目で約 80ppmまで、３回目で約 40ppmまで低減されるとされている。 - 経済産業省

METHOD FOR MANUFACTURING COLD-ROLLED STEEL SHEET SUPERIOR IN RECRYSTALLIZATION SOFTENING RESISTANCE, AND COLD-ROLLED STEEL SHEET FOR AUTOMATIC TRANSMISSION例文帳に追加

耐再結晶軟化特性に優れた冷延鋼板の製造方法およびオートマチック・トランスミッション用冷延鋼板 - 特許庁

Because the SOI substrate was under stress during the recrystallization process, the final semiconductor layer will be under stress as well.例文帳に追加

再結晶化プロセスの間、ＳＯＩ基板は応力を受けたので、最終的な半導体層も、応力を受ける。 - 特許庁

Moreover, a melting time is extended by spraying a nitrogen gas and radiating a microwave, and the recrystallization is effectively carried out.例文帳に追加

また窒素ガスとマイクロ波を照射により溶融時間を長くし、再単結晶化をより効果的に行う。 - 特許庁

To provide an anti-freeze protein having high nonfreezing activities such as temperature hysteresis activity, ice recrystallization inhibitory activity, etc.例文帳に追加

温度ヒステリシス活性、氷の再結晶阻害活性等の不凍活性の高い不凍タンパク質を提供する。 - 特許庁

To provide an aqueous cosmetic which inhibits the recrystallization of paraben.例文帳に追加

本発明は、パラベンの再結晶化が抑制された水性化粧料を提供することを主目的とするものである。 - 特許庁

At least one or more among Fe oxide, Mo oxide, Mn oxide, Sn oxide, W oxide, Ga oxide, Ge oxide, Cu oxide, Cr oxide and Sb oxide are applied to a steel sheet into linear and/or dotted-line shape after primary recrystallization annealing and before secondary recrystallization annealing, or after secondary recrystallization annealing and before purification annealing.例文帳に追加

一次再結晶焼鈍後二次再結晶焼鈍前に、もしくは二次再結晶焼鈍後純化焼鈍前に、Ｆｅ酸化物、Ｍｏ酸化物、Ｍｎ酸化物、Ｓｎ酸化物、Ｗ酸化物、Ｇａ酸化物、Ｇｅ酸化物、Ｃｕ酸化物、Ｃｒ酸化物、Ｓｂ酸化物のうちの少なくとも１種以上を、鋼板に線状および／または点列状に塗布する。 - 特許庁

To stably secure higher grade magnetic characteristics by making a primary recrystallization texture adequate or enhancing the texture thereby sharpening (upgrading) Goss-orientation integration degree in a secondary recrystallization texture in a method of producing a complete solid solution nitrided type grain oriented magnetic steel sheet.例文帳に追加

完全固溶窒化型の製造方法において、一次再結晶集合組織を適正化又は改善して、二次再結晶集合組織におけるGoss方位集積度を先鋭（高度）にし、より高位の磁気特性を安定的に確保する。 - 特許庁

The manufacturing method includes heating the sheet to a recrystallization temperature after a final cold rolling, forming the linear or discontinuously linear grooves in the approximately transverse direction against the rolling direction by machining, and then annealing it for the purpose of secondary recrystallization.例文帳に追加

また、最終冷延後、再結晶温度まで加熱した後、圧延方向とほぼ直角方向に線状あるいは不連続な線状の溝を機械加工によって形成した後、二次再結晶を目的とする焼鈍を行う。 - 特許庁

In this way, by the mechanical recrystallization, a fine crystal part 21 where the crystal grains are locally refined is formed.例文帳に追加

このように機械的再結晶によって、局部的に結晶粒が微細化された微細結晶部２１が形成される。 - 特許庁

Further, a laser beam is irradiated to the single-crystal semiconductor layer of the semiconductor substrate so as to melt for recrystallization.例文帳に追加

さらに、この半導体基板の単結晶半導体層にレーザ光を照射して、溶融させ、再結晶化させる。 - 特許庁

The annealing step anneals the metal layer at a temperature higher than a recrystallization temperature of the metal that forms the metal layer.例文帳に追加

焼き鈍し段階は、金属層を形成する金属の再結晶温度よりも高い温度で金属層を焼き鈍しする。 - 特許庁

To secure interchangeability between mediums having different recrystallization speed and speed dependency in phase transition type recording mediums.例文帳に追加

相変化型記録媒体について、再結晶化速度及び速度依存性が異なる媒体間の互換性を確保する。 - 特許庁

To provide a bi-directional silicon steel sheet where the degree of accumulation in the {100}<001> orientation is improved with secondary recrystallization.例文帳に追加

二次再結晶により｛１００｝＜００１＞方位集積度を向上させた二方向性電磁鋼板を提供する。 - 特許庁

To prevent a grain oriented silicon steel sheet using no inhibitors from deteriorating in magnetic characteristics in a secondary recrystallization annealing.例文帳に追加

インヒビターを使用しない方向性電磁鋼板において、二次再結晶焼鈍における磁気特性の劣化を防止する。 - 特許庁

To perform an online separate measurement on a rate of recrystallization and the aspect ratio of crystal grains of an object to be measured hot online.例文帳に追加

熱間オンラインで測定対象物についての再結晶率と結晶粒アスペクト比とを分離測定すること。 - 特許庁

The thickness of a recrystallization layer 2 on the surface of an extruded material 1 of an aluminum alloy to be welded is 50 μm or smaller.例文帳に追加

被溶接材であるアルミニウム合金押出材１の表面の再結晶層２の厚さを５０μｍ以下にする。 - 特許庁

To control the position of a crystal grain at a high degree in a crystalline thin film obtained by scanning type melting recrystallization.例文帳に追加

走査型溶融再結晶によって得られる結晶性薄膜において、結晶粒位置を高度に制御する。 - 特許庁

This method for producing the α-SiC crystal comprises growing the α-SiC crystal on a substrate by a sublimation recrystallization method of an SiC powder.例文帳に追加

ＳｉＣ粉末の昇華再結晶法により、基板上にα−ＳｉＣ結晶を成長させる方法である。 - 特許庁

In concentration distribution in the depth direction of the single-crystal semiconductor layer after the recrystallization, a carbon concentration has the local maximum.例文帳に追加

再結晶化後の単結晶半導体層は深さ方向の濃度分布において、炭素濃度が極大を有する。 - 特許庁

The nano-size particle can have a melting point ranging from approximately 50°C to approximately 140°C and a recrystallization point ranging from approximately 30°C to approximately 80°C.例文帳に追加

このナノサイズ粒子は、約５０℃〜約１４０℃の融点と約３０℃〜約８０℃の再結晶点とを有し得る。 - 特許庁

Since it partially has the portions becoming the recrystallization grain structures, strength and yield stress of the portion are made high, whereas the portions (non-reinforcement treatment parts 212, 222, 312, 322) not becoming the recrystallization grain structures become the portions having relatively low strength.例文帳に追加

再結晶粒組織となっている部位を部分的に有するため、当該部位の強度、降伏応力が高くなる一方で、再結晶粒組織となっていない部位（非強化処理部２１２，２２２，３１２，３２２）は、相対的に強度の低い部位となる。 - 特許庁

Further, in a method of manufacturing the oxide dispersion strengthened ferritic steel where yttrium oxide is dispersed in a metallic base phase composed essentially of Fe-Cr, which is provided with a step of recrystallization heat treatment, cold rolling of 5-50% is performed after recrystallization treatment.例文帳に追加

また、再結晶熱処理工程を備えた、酸化イットリウムをＦｅ−Ｃｒを主体とする金属母相内に分散させた酸化物分散強化型フェライト鋼の製造方法において、再結晶化処理後に、５〜５０％の冷間加工を行う。 - 特許庁

To provide a seamless pipe made of molybdenum, which has a higher recrystallization temperature, higher radial crushing strength each before and after recrystallization, and a more excellent high-temperature resistance (hanging down resistance) in a horizontal-position than the seamless pipe made of pure molybdenum has, and to provide a manufacturing method therefor.例文帳に追加

純モリブデン製シームレスパイプに比べ、再結晶温度並びに再結晶前後の圧環強さが夫々高く、且つ水平姿勢における耐高温特性（耐垂下性）に優れるモリブデン製シームレスパイプおよびその製造方法を提供すること。 - 特許庁

To provide an adhesive composition which is extremely easy to control freely a recrystallization rate (or the finish time of recrystallization) of a polymer contained as a crystallization component and is capable of increasing effectively the easiness of peeling and the clean peelability.例文帳に追加

結晶性成分として含まれるポリマーの再結晶化速度（または、再結晶化完了時間）を自由に制御することが極めて容易であり、剥離容易性や剥離清浄性を効果的に高めることができる、接着剤組成物を提供する。 - 特許庁

To provide a grain oriented electromagnetic steel plate having excellent magnetic properties free from variation, in the case secondary recrystallization is caused, so as to be the grain oriented electromagnetic steel sheet without the incorporation of inhibitors, by allowing the secondary recrystallization to stably appear.例文帳に追加

インヒビターを含有させずに二次再結晶を生じさせて方向性電磁鋼板とする場合に、安定して二次再結晶を発現させることにより、ばらつきのない優れた磁気特性を有する方向性電磁鋼板を提供する。 - 特許庁

To provide an information recording medium which generates less recrystallization rings during information recording and also enables a good high speed information erasure.例文帳に追加

情報記録時に再結晶化リングが発生しにくく、かつ良好な高速記録消去が可能な情報記録媒体を得る。 - 特許庁

The nano crystal is melt by irradiation with laser to generate compressive stress within the nano crystal by recrystallization thereafter.例文帳に追加

該ナノ結晶をレーザ照射により融解させ、その後の再結晶化によりナノ結晶内に圧縮応力を発生させる。 - 特許庁

Such the crystal is obtained by recrystallization under a condition of holding for ≥1 hr within a temperature range of 50-70°C.例文帳に追加

このような結晶は、５０〜７０℃の温度範囲で１時間以上保持する条件で再結晶化することによって得られる。 - 特許庁

To manufacture a birefringent crystal from a saturated aqueous solution of a polarizer material by recrystallization method.例文帳に追加

本発明は、複屈折性結晶を偏光子物質の飽和水溶液からの再結晶法により製造することを目的とする。 - 特許庁

To provide a semiconductor device with a high dielectric-constant gate insulating film in which a recrystallization is inhibited, and to provide its manufacturing method.例文帳に追加

再結晶化が抑制された高誘電率ゲート絶縁膜を有する半導体装置及びその製造方法を提供する。 - 特許庁

(a) TCPA Yield and HCB Reduction Rate (n=3 average) by Recrystallization using Sample with HCB Concentration of 461ppm 例文帳に追加

①ＨＣＢ濃度 461ppmのサンプルを使用した場合の再結晶によるＴＣＰＡの歩留まり及びＨＣＢ削減率（ｎ＝３の平均値） - 経済産業省

The single recrystallization refinement produced a TCPA yield of around 70-80% and a HCB reduction rate of around 65% (or the reduction by around two-thirds). 例文帳に追加

１回の再結晶精製でＴＣＰＡの歩留まりは 70～80％程度、ＨＣＢ削減率は 65％程度（2/3程度）となった。 - 経済産業省

To provide an industrially advantageous molybdenum material which is capable of secondary recrystallization at a temperature lower than that of a conventional molybdenum material and which can be converted through the secondary recrystallization into a material that has a structure comprising very large grains with reduced grain boundaries and thus exhibits excellent creep resistance.例文帳に追加

従来よりも低い温度で二次再結晶を引き起すことが可能で、且つ二次再結晶後の組織が粒界の少ない巨大な結晶粒からなり耐クリープ特性に優れるようにすることが可能な工業的に優位性のあるモリブデン材を提供する。 - 特許庁

The method for producing the imidazolium salt includes purifying the imidazolium salt by recrystallization using a solvent containing alcohols.例文帳に追加

本発明はアルコール類を含む溶媒を用いて、再結晶により精製することを特徴とするイミダゾリウム塩の製造方法である。 - 特許庁

Furthermore, the rolling until the temperature in the fillet part becomes not higher than the recrystallization temperature of austenite is performed only by the rolling mill on the upstream side.例文帳に追加

さらには、フィレット部温度がオーステナイトの再結晶温度以下になるまでの圧延を上流側の圧延機のみで行なう。 - 特許庁

A method for industrial production of aloin is also provided, wherein recrystallization is carried out in the presence of 0.5-5 wt.% water based on the total weight of the medium.例文帳に追加

再結晶化が、媒質総重量に対して０．５〜５重量％の水の存在下で行われる、アロインの工業生産方法。 - 特許庁

According to the method, the yield is nearly 100% and the method is economically advantageous without requiring purification such as recrystallization.例文帳に追加

またこの方法によれば収率もほぼ１００％であり、再結晶等の精製を必要としない経済的に有利な方法である。 - 特許庁

This manufacturing process is conducted at a temperature of lower than 1200 °C and the time to inhibit recrystallization of a highly-fine structure in the alloy MA956.例文帳に追加

この製法は、合金MA956中の非常に細かい構造の再結晶化を阻止するための１２００℃未満の温度および時間で行う。 - 特許庁

To provide a brass material excellent in ductility, in particlar in forgeability at a temperature in which strain recovery and recrystallization occurs.例文帳に追加

回復または再結晶を起こす温度での延性、好適には鍛造性に優れた黄銅材を提供することを主目的とする。 - 特許庁