To securely prevent the generation of the defects of coating caused by the entrainment of air at the time of dipping a balcony frame into an electrodeposition coating material and executing electrodeposition.例文帳に追加

バルコニーフレームを電着塗料に浸漬して電着する際、空気の巻き込みによる塗装不良の発生を確実に防止する。 - 特許庁

In performing electrodeposition coating while moving a material to be coated in an electrodeposition tank, the film thickness of the electrodeposition coating film on the surface of the material to be coated is predicted by measuring the potential on the surface of the moving material to be coated with lapse of time during electrodeposition coating.例文帳に追加

電着槽中において、被塗物を移動させながら電着塗装するに際して、移動中の被塗物の外表面の電位を、電着塗装中に経時的に測定することによって被塗物表面の電着塗膜の膜厚を予測する。 - 特許庁

To provide a measuring device and a measuring method capable of measuring an electrodeposition paint characteristic simply in a short time, and contributing to management of the electrodeposition paint characteristic.例文帳に追加

電着塗料特性を簡易的で短時間に測定できる測定装置、測定方法を見出し、電着塗料特性の管理に寄与すること。 - 特許庁

To provide an electrodeposition coating composition being hardenable at low temperatures in electrodeposition coating for one-time coating finish and having excellent corrosion and weather resistance.例文帳に追加

１回塗装仕上げ用電着塗装において、低温硬化が可能で、かつ耐食性と耐候性にすぐれる電着塗料組成物を得ること。 - 特許庁

To provide an electrodeposition vessel and electrodeposition apparatus capable of suppressing the generation of powder and film pieces, etc., in an electrodeposition bath and uniformly forming evenly oxidized films free from the occurrence of unevenness by preventing the deposition of oxides in a piping system connected to the electrodeposition vessel and the piping system arranged within the electrodeposition vessel at the time of forming the oxidized films on a substrate.例文帳に追加

基板上に酸化膜を作成するに際し、電析槽に繋がる配管系や、電析槽内に配置された配管系に酸化物が堆積するのを防止して、浴中に粉や膜片等が発生するのを抑制でき、ムラの発生しない一様な酸化膜を均一に作成できる電析槽、および電析装置を提供する。 - 特許庁

In the evaluation method of the electrodeposition paint characteristic, the electrodeposition characteristic measuring device is dipped into the electrodeposition paint, and the film thickness (μm) to an applied voltage V at the electrodeposition painting time of the electrodeposition paint is calculated from a resonance frequency and/or a resonance resistance value acquired from the quartz oscillator (a).例文帳に追加

上記電着特性測定装置を電着塗料中に浸漬し、水晶振動子（ａ）から得られる共振周波数及び／又は共振抵抗値から、電着塗料の電着塗装時における印加電圧（Ｖ）に対する膜厚（μｍ）を算出する電着塗料特性の評価方法が提供される。 - 特許庁

A light-transmissive protective film 5 for protecting the reflection film 4 is formed on the reflection film 4 at the time of electrodeposition and a transparent conductive layer 6 for electrodeposition is formed on the protective film 5 and the color filter 7 is formed on the transparent conductive layer 6 for electrodeposition by an electrodeposition method.例文帳に追加

反射膜４の上に、電着に際して反射膜４を保護するための透光性の保護膜５を形成し、保護膜５の上に電着用透明導電層６を形成し、電着用透明導電層６の上にカラーフィルタ７を電着法にて形成する。 - 特許庁

To provide a manufacturing method of an electrodeposition type display panel by which the display panel having high reliability can be efficiently manufactured for a short time and to provide the electrodeposition type display panel and an electrodeposition type display device.例文帳に追加

短時間で効率的に、しかも信頼性の高い表示パネルの製造を可能とするエレクトロデポジション型表示パネルの製造方法、並びに、エレクトロデポジション型表示パネルおよびエレクトロデポジション型表示装置を提供する。 - 特許庁

This electrodeposition coating method includes: sequentially submerging and immersing the plurality of articles (M) to be coated into the electrodeposition paint bath liquid (L), while transporting the articles, and raising up each of the article (M) to be coated from the electrodeposition paint bath liquid (L) after having immersed each of the article (M) for an individually predetermined period of time.例文帳に追加

複数の被塗物Ｍを搬送しつつ電着塗料浴液Ｌ中に順次沈めて浸漬し、予め個々に設定した浸漬時間が経過した時に各被塗物Ｍを電着塗料浴液Ｌから引き上げる。 - 特許庁

The stage for forming the colored electrodeposition film is preferably the form of the stage for forming the colored electrodeposition film by depositing the electrodeposition material selectively to photoirradiated parts by irradiating the substrate with light or the stage of forming the colored electrodeposition film on the conductive film by driving the active element and utilizing the voltage at the time of driving.例文帳に追加

着色電着膜を形成する工程が、基板を光照射し、該光照射部に選択的に電着材料を析出させて着色電着膜を形成する工程、又は前記能動素子を駆動し、該駆動時の電圧を利用して導電膜上に着色電着膜を形成する工程である態様が好ましい。 - 特許庁

To provide an electrodeposition method using a lead-free cation electrodeposition coating material not forming pinholes and craters in the coating film even when using a zinc steel plate as the material to be coated, excellent in economical efficiency because of a small amount of the electrodeposition coating material used, having slight influence on the environment, enabling short-time electrodeposition.例文帳に追加

被塗物として亜鉛鋼鈑を用いる場合でも塗膜にピンホールやクレーターが生じ難く、また、電着塗料自体の使用量も少なくて済むために経済性に優れ、さらに環境に与える影響が少ない短時間電着可能な高つきまわり性の無鉛性カチオン電着塗料の塗装方法を提供すること。 - 特許庁

To obtain a high adhesion property to an electrodeposition film by a short-time treatment to a titanium base metal surface and to develop the pretreatment liquid having excellent stability with lapse of time.例文帳に追加

チタン素地面への短時間の処理で電着皮膜に対する高い密着性を得るとともに、経時安定性に優れた前処理液を開発する。 - 特許庁

To provide an electrodeposition grindstone capable of precluding preventing clogging caused by heat emission or polishing waste generated at the time of grinding.例文帳に追加

研削時に発生する発熱や研磨カスによる目詰まりを防止することが可能な電着砥石を提供する。 - 特許庁

To provide an electrodeposition grinding wheel having the long service life by restraining mesh-clogging of the grinding wheel by chips of a machined material at grinding time.例文帳に追加

研削時の被削材の切り粉による砥石の目詰まりが抑制され、耐用命数が長い電着砥石を提供する。 - 特許庁

At the time of electrodepositing a balcony frame 1, the balcony frame 1 is dipped into an electrodeposition coating material C in a state of being tilted at a fixed angle.例文帳に追加

バルコニーフレーム１を電着する際、バルコニーフレーム１を一定角度傾斜した状態で電着塗料Ｃに浸漬する。 - 特許庁

At the time when electrodeposition coating is applied to a roller with electroconductivity imparted or an electroconductive roller, interelectrode energizing in a constant current amount is performed in a filler-containing electrodeposition coating liquid preferably while rotating the roller.例文帳に追加

導電性を付与したあるいは導電性のローラに電着塗装を行うに際し、フィラーを含有する電着塗装液中で好ましくはローラを回転させながら定電流量の電極間加電を行う。 - 特許庁

An automotive body W is guided by a conveyer into the tank, immersed in the electrodeposition paint for a predetermined period, and raised after a lapse of the predetermined time.例文帳に追加

コンベアによって自動車ボディＷが案内され、電着塗料中に所定時間浸漬され、所定時間経過後、引き上げられる。 - 特許庁

To obtain a cationic electrodeposition coating composition which restrains the activity of a curing catalyst while being stored for a long time or when used as an electrodeposition coating material and which restrains such disadvantageous conditions as the lowering of the reactivity of unsaturated double bonds introduced into the resin and the polymerization during the storage or at the time of use.例文帳に追加

長期貯蔵時又は電着塗料としての使用時における硬化触媒の活性を抑制し、樹脂に導入された不飽和二重結合の反応性の低下や、貯蔵時や使用時に重合してしまうことによる不具合が抑制されたカチオン電着塗料組成物を提供する。 - 特許庁

The color of an electrodeposition coating film to be applied at the 2nd time in a double coat electrodeposition coating is made to be the same chromatic color in the hue of Muncell system as the color of a top coating film consisting of three layers to be applied next or white color.例文帳に追加

ダブルコート電着塗装において2回目に塗装される電着塗膜の塗色が、次に塗装される３層からなる上塗り塗膜の塗色と、マンセル表示の色相で同系色有彩色、又は白の塗色とすること。 - 特許庁

To provide an electrodeposition coating apparatus by which a desired film thickness on the outside surface of a material to be coated and a desired film thickness of the inside surface thereof are simultaneously obtained in the same treating time and an electrodeposition coating method using the apparatus.例文帳に追加

被塗物の外面の所望の塗装膜厚と被塗物の内面の所望の塗装膜厚とを同一の処理時間で得られるようにした電着塗装装置およびその装置を用いた電着塗装方法を提供すること。 - 特許庁

To provide an electrodeposition type display device having a structure for shortening the time required for writing in and erasing and to provide a method for driving the same.例文帳に追加

書き込みや消去に要する時間を短時間に出来る構造のエレクトロデポジション型表示装置とその駆動方法を提供することを目的とする。 - 特許庁

The electrodeposition process employed uses current waveforms that apply a low current density initially, and after a predetermined period of time, the current density is changed to a high current density.例文帳に追加

用いる電着プロセスには、最初に低電流密度を加え、所定の時間後に電流密度を高電流密度に変える電流波形が用いられる。 - 特許庁

To provide an anionic electrodeposition coating which generates a reduced amount of formaldehyde from a coating film at the time of baking and is excellent in chemical resistance and low-temperature curability.例文帳に追加

焼付け時に塗膜から発生するホルムアルデヒドを低減し、耐薬品性及び低温硬化性に優れるアニオン電着塗料を提供すること。 - 特許庁

To perform the starting and stopping of deposition, the setup of various data, the completion of deposition preparations and the check of deposition elapsed time at a separate position from an electrodeposition device.例文帳に追加

融着の開始・停止、各種のデータの設定、融着準備の完了や融着経過時間の確認を、電気融着装置から離れた位置において行なう。 - 特許庁

To provide an electrodeposition display device with which problems such as fading after long-time use do not occur, and black density is maintained at a high value.例文帳に追加

長時間使用した場合でも褪色なども問題が発生せず黒色濃度も高い値に維持することが可能なエレクトロデポジション表示装置を提供する。 - 特許庁

To provide an anion electrodeposition coating material which generates less formaldehyde from a coating film at the time of baking and is excellent in curability, chemical resistance, and die mark hiding effect.例文帳に追加

焼付け時に塗膜からホルムアルデヒドの発生が少なく、硬化性、耐薬品性及びダイスマーク隠蔽性に優れるアニオン電着塗料を提供すること。 - 特許庁

To obtain a cationic electrodeposition coating composition which restrains the side reactions between activated oxygen, free radicals, and the like in a prolonged storage or at the time of use as an electrodeposition coating material and which has the restrained inconveniences, ones caused due to the lowering of the reactivity of unsaturated double bonds introduced into the resin and due to the polymerization during the storage or at the time of use.例文帳に追加

長期貯蔵時又は電着塗料としての使用時における活性酸素やラジカル等との副反応を抑制し、樹脂に導入された不飽和二重結合の反応性の低下や、貯蔵時や使用時に重合してしまうことによる不具合が抑制されたカチオン電着塗料組成物を提供する。 - 特許庁

The electrodeposition coating is excellent in stability and shows no changes in the characteristic features such as coating and anticorrosion properties due to the incorporation of a specific polyether compound of a molecular weight of ≤1,000, even after the use as an electrodeposition coating in a coating line for a long period of time.例文帳に追加

分子量が１，０００以下の特定のポリエーテル化合物を配合することにより、安定性に優れ、長期間塗装ラインにおいて電着塗料として使用した後でも塗装性や防食性などの特性が変化することがない電着塗料。 - 特許庁

To provide a process for coating an electric wire, which provides an insulation wire having superior breakdown voltage through immersing an article to be coated into an electrodeposition tank for a comparatively short period of time.例文帳に追加

被塗物を電着槽に比較的短時間浸漬することにより、絶縁破壊電圧に優れる絶縁電線を得ることができる電線の塗装方法を提供する。 - 特許庁

In electrodeposition coating with a cationic electrodeposition coating material, the maximum value (I) of current density appears within 5 sec from the start of energizing, and the time in which the current density (0.51), i.e., 1/2 of the maximum value (I) of current density appers is ≤5 sec.例文帳に追加

カチオン電着塗料の電着塗装において、電流密度の最高値（Ｉ）が通電開始から５秒間以内に発現し、かつ電流密度の最高値（Ｉ）の１／２の電流密度（０．５Ｉ）以上を有する時間が５秒間以内であることを特徴とする隙間部における塗膜形成方法 - 特許庁

To provide a resin film laminated steel panel excellent in shape retention at the time of stamping especially becoming a problem in a high tensile strength steel panel and, if necessary, also excellent in electrodeposition coating properties.例文帳に追加

高張力鋼板において特に問題となるプレス加工時の形状凍結性に優れ、必要によって電着塗装性にも優れた樹脂膜積層鋼板を提供する。 - 特許庁

To provide a composition for a positive type photosensitive anionic electrodeposition coating material, which is good in stability with the lapse of time in a liquid state and exhibits good circuit formation performances such as developability or etching resistance.例文帳に追加

液経時安定性が良好であり、且つ現像性、耐エッチング性等の回路形成能が良好なポジ型感光性アニオン電着塗料用組成物を提供すること。 - 特許庁

To provide a dash panel structure of a vehicle capable of easily discharging the air in good performance at the time of electrodeposition coating without requiring much labor and expense and of accomplishing a good waterproofness.例文帳に追加

手間と費用を掛けることなく容易に電着塗装時のエア抜きを良好に行うことができると同時に、良好な防水性を実現できる車両用ダッシュパネル構造の提供。 - 特許庁

To promote the flow of electric current flowing to a substrate by utilizing the current conduction capacity of a deposited metal and to provide an electrodeposition device by which the electrodepositing time is shortened.例文帳に追加

堆積された金属の電流伝導容量を利用することによって基板へ流れる電流の流れを促進させ、電着時間を短くすることができる電着装置を提供すること。 - 特許庁

To provide a composition for a UV curable type cationic electrodeposition paint having satisfactory liquid stability with passage of time, high sensitivity and satisfactory scratch resistance, surface curing properties and adhesiveness.例文帳に追加

液経時安定性が良好であり、高感度で、且つ、耐傷つき性、表面硬化性、付着性が良好な紫外線硬化型カチオン電着塗料用組成物を提供すること。 - 特許庁

To shorten time required for formation of an abrasive grain layer, and facilitate adjustment of concentration degree of abrasive grains in manufacturing an electrodeposition tool for forming a multilayer structure of abrasive grain layers.例文帳に追加

多層構造の砥粒層を形成させる電着工具の製造において、砥粒層形成に要する時間を短縮し、さらに砥粒の集中度の調整を容易にする。 - 特許庁

The electrodeposition coating method can easily make an electrodeposition coating condition in the upper part of the article to be coated differ from that in the lower part, by immersing the lower part of the article to be coated for a longer period of time than the upper part, and can form the paint film with desired thicknesses respectively on the upper part and the lower part.例文帳に追加

本発明の電着塗装方法を用いれば、被塗物の上方部分より下方部分を長く浸漬することにより、電着塗装の条件を被塗物の上方部分と下方部分とで容易に異ならせることができ、上方部分および下方部分につきそれぞれ所望の厚さの塗膜を形成できる。 - 特許庁

To provide an electrodeposition apparatus which improves the arrangement of an anode to shorten the required time for the maintenance, and prevents the liquid from entering inside a cable, and the corrosion of the cable.例文帳に追加

アノードの取り回しを向上させてメンテナンスの所要時間を短縮することができ、ケーブル内部への浴の浸入を防止して、ケーブルの腐蝕を防止することができる電析装置を提供する。 - 特許庁

Electrodeposition coating is started at the initial voltage of 20-100 V in this electrodeposition coating method, the voltage is increased to a first maximum current value from the initial voltage at a rate of 20-200 V/s in a short time, and then the voltage is gradually increased to a set voltage at a rate of 2-20 V/s and kept at the set voltage for a fixed time.例文帳に追加

２０〜１００Ｖの初期電圧で電着塗装を開始し、前記初期電圧から第１電流極大値になるまでは２０〜２００Ｖ／ｓの上昇速度で短時間で電圧を昇圧し、その後は２〜２０Ｖ／ｓの上昇速度に切り替えて徐々に設定電圧に昇圧させ、一定時間設定電圧に保持する電着塗装方法およびこの方法を実施するための電着塗装装置。 - 特許庁

To provide a device for attaching and detaching a masking holder for electrodeposition coating, which can attach and detach magnetic-force-type masking holders of the same number as that of many bolt holes at one time, even if many bolt holes are formed in a cover member.例文帳に追加

カバー部材に多数のボルト孔が形成された場合においても、多数のボルト孔と同数の磁力式マスキング治具を一度に着脱することができる電着塗装用マスキング治具の着脱装置を提供する。 - 特許庁

To provide a single particle film excellent in light transmission properties and antiglare properties, an aqueous resin composition for manufacturing the same and an electrodeposition coating method for manufacturing a large amount of the single particle film in a short time using the same.例文帳に追加

優れた光透過性と防眩性を有する単粒子膜、それを作製するための水性樹脂組成物、およびそれを用いて短時間で大量に単粒子膜を作製する電着塗装法を提供する。 - 特許庁

To provide a washing system for an electrodeposition coated material by which generation of air bubbles accumulated on the bottom of a washing chamber can be prevented even for a long time washing and the closed system of the washing chamber can be achieved.例文帳に追加

水洗を長時間行った場合でも水洗室底部に蓄積する気泡の量が増大せず、電着塗装物水洗システムのクローズド系を保つことができる、電着塗装物の水洗システムを提供すること。 - 特許庁

At that time, the coating film re-adhering to the surface of the electrodeposition coating device 16 can be perfectly removed by the synergistic effect of the chemical peeling force of the spraying peeling liquid and the physical peeling force by spraying.例文帳に追加

このとき、噴射用剥離液の化学的な剥離力と、噴射による物理的な剥離力との相乗効果により、電着塗装治具１６の表面に再付着した塗膜を完全に除去することができる。 - 特許庁

To provide a display element whose white color tone variation at the time of repetitive driving is reduced in the display element of an ED (electrodeposition) system which can be driven with a simple member constitution at a low voltage and has high display contrast and white display reflectance.例文帳に追加

簡便な部材構成、低電圧で駆動可能で、表示コントラスト、白表示反射率が高いＥＤ方式表示素子において、繰り返し駆動時の白の色調変動が低減された表示素子を提供する。 - 特許庁

To prolong the duration period of an edge strip by improving the adhesion of a cathode plate to the edge strip by preventing the infiltration of an electrolyte to an inner side of the edge strip and the electrodeposition of copper onto the side face portion of the cathode plate for a long period of time.例文帳に追加

カソード板とエッジストリップの密着性を向上させ、エッジストリップ内側への電解液の侵入、およびカソード板側面部への銅の電着を長期的に防ぐことで、エッジストリップの使用期間を延長させることである。 - 特許庁