Specifically, a vacuum annealing treatment is carried out after the TaXN thin film is formed into a film, and a protecting film is fabricated on it, thereby determining an optimum annealing condition while observing a change of Ta-N coupling by the X-ray diffraction method.例文帳に追加

具体的には、ＴａＸＮを成膜してその上に保護膜を製作した後、真空アニール処理を行い、Ｘ線回折法によりＴａーＮ結合の変化を観察しながら、最適なアニール条件を決める方法がある。 - 特許庁

To provide a catalyst for heterogeneously catalyzed reaction, containing an active component and a catalyst carrier containing δ-Al2O3 of the amount detectable by an X-ray diffraction method, particularly a catalyst for oxychlorination of ethylene to 1,2-dichloroethane.例文帳に追加

活性成分と、Ｘ線回折法で検出可能な量のδ−Ａｌ_２Ｏ_３を含む触媒担体を含む不均一触媒反応用触媒、特にエチレンから１，２−ジクロロエタンへのオキシ塩素化のための触媒を提供する。 - 特許庁

This highly precise diffraction method of the present invention is invented by executing a simulation based on the principle to conduct verification, and by limiting the x-ray size incident into the test piece by a slit or a condenser.例文帳に追加

この原理に基づいてシミュレーションを行い検証し、このシミュレーションに基づき、試験片に入射するＸ線サイズを、スリット又は集光器により制限することにより、高い精度が得られる回折方法を発明した。 - 特許庁

To obtain a transparent activated alumina having an amorphous structure in terms of X-ray diffraction study, useful for a resin compounding agent, an adsorbent for a photocatalyst, a carrier, etc., and to provide a method for producing the alumina.例文帳に追加

透明でしかもＸ線回折学的に非晶質構造を有する透明活性アルミナで、樹脂配合剤、光触媒用吸着剤、及び担体等の用途に有用な透明活性アルミナ及びその製造法を提供する。 - 特許庁

The plastic structuring the container has a crystallinity measured by an X-ray diffraction method from 10 to 80%, and also has transparency capable of checking an amount of methanol inside the container.例文帳に追加

この容器は、容器を構成するプラスチックが、Ｘ線回折法によって測定された結晶化度が１０〜８０％であると共に容器内部のメタノールの量を確認できる透明性を有するプラスチックである点に特徴を有する。 - 特許庁

In the graphitized fiber, the spacing d(002) between graphitized layers according to an X-ray diffraction method is within the range of ≥0.3354 to ≤0.3366 nm; and the crystallite size Lc(002) of graphite crystals is ≥60 nm.例文帳に追加

この黒鉛化繊維によれば、Ｘ線回折法による黒鉛化層間の面間隔ｄ（００２）が０．３３５４ｎｍ以上０．３３６６ｎｍ以下の範囲であり、かつ黒鉛結晶の結晶子サイズＬｃ（００２）が６０ｎｍ以上である。 - 特許庁

In a measuring method of an X-ray diffraction pattern of the translin crystal, the translin crystal obtained using sodium formate as a precipitant is frozen in crystallizing solution containing polyalcohol, and X-ray diffraction data is collected in a frozen state.例文帳に追加

トランスリン結晶のＸ線回折像の測定方法、該結晶のＸ線回折像より得られる３次元構造座標、該構造座標を含むデータベース若しくは記録媒体、該構造座標を用いるトランスリンの機能を調節する能力を有する化合物の同定方法、該３次元構造座標を用いるトランスリンに潜在的に結合しうる化合物からなる化合物群の調製方法、及び、該３次元構造座標を用いるトランスリンの変異体の作製方法。 - 特許庁

The tissue structure has the structural characteristic in which the crystal structure substantially exclusive of a graphite structure does not substantially exist, the diffraction lines belonging to the metal Si and Si compound by the pattern analysis using an X-ray diffraction method are not detected and the granular structure is not identifiable by the observation of a transmission type electronmicroscope(TEM).例文帳に追加

その組織構造は、実質的に黒鉛構造以外の結晶構造が存在せず、Ｘ線回折法によるパターン解析により金属Ｓｉ及びＳｉ化合物に帰属する回折線が検出されず、透過型電子顕微鏡(TEM) の観察によって粒状組織が識別できない組織性状を備えている。 - 特許庁

The method for producing the metal oxide-containing titanium oxide compound comprises the steps of: mixing a raw material of titanium oxide, which has ≤1.40° half-value width of a diffraction peak of the (101) plane when measured by X-ray diffraction analysis, with an oxide of a metal other than titanium; and firing the obtained mixture at 300-600°C.例文帳に追加

Ｘ線回折分析による（１０１）面の回折ピークの半値幅が１．４０°以下である原料酸化チタンと、チタン以外の金属の酸化物とを混合し、得られた混合物を３００℃〜６００℃で焼成することを特徴とする金属酸化物含有酸化チタン化合物の製造方法である。 - 特許庁

The Si dispersed vitreous carbon material is provided with structural performance that a crystalline structure except graphite structure does not exist practically in the structure, the diffraction line attributed to metal Si or an Si compound is not detected in an X-ray diffraction method and granular structure is not discriminated by the observation by a transmission electron microscope(TEM).例文帳に追加

また、その組織中には実質的に黒鉛構造以外の結晶構造が存在せず、Ｘ線回折法により金属ＳｉおよびＳｉ化合物に帰属する回折線が検出されず、透過型電子顕微鏡（ＴＥＭ）の観察によって粒状組織が識別できない組織性状を備えている。 - 特許庁

This is the non-aqueous electrolyte secondary battery which is equipped with a cathode 1 that contains a cathode active material having reflecting angles 2θ of peak positions of diffraction pattern by X-ray diffraction method at least at 40±2°, 47±2°, and 68±2°, a cathode 2 that contains a material that stores and releases lithium ions, and a non-aqueous electrolyte 5.例文帳に追加

この非水電解質二次電池は、Ｘ線回折法による回折パターンのピーク位置の反射角２θを、少なくとも、４０±２度と、４７±２度と、６８±２度とに有する正極活物質を含む正極１と、リチウムイオンを吸蔵および放出する材料を含む負極２と、非水電解質５とを備えている。 - 特許庁

The SiC formed material is formed by a CVD method and has crystallite diameters of 36 to 54 nm, measured by X-ray diffraction, half- value width of (111) face in the range of 0.155 to 0.224° and a electrical resistivity of 1 to 106 Ωm.例文帳に追加

ＣＶＤ法により形成され、Ｘ線回折によって測定した結晶子径が３６〜５４nmであって、（１１１）面の半価幅が０．１５５〜０．２２４°の範囲にあり、電気抵抗率が１〜１０^6 Ωm であることを特徴とするＳｉＣ成形体。 - 特許庁

It is preferable that the ratio (I_2/I_1) of the maximum peak value (I_1) of the Fe_3O_4 and the maximum peak value (I_2) of the metal iron is 0.05 to 0.70 by powder X-ray diffraction method from a standpoint for further improving the mechanical strength of the sintered particle.例文帳に追加

ここで、焼結粒子の機械的強度を一層向上させる観点からは、粉末Ｘ線回折によるＦｅ_３Ｏ_４の最大ピーク値（Ｉ_１）と金属鉄の最大ピーク値（Ｉ_２）の比（Ｉ_２／Ｉ_１）を０．０５〜０．７０の範囲とするのが好ましい。 - 特許庁

Main components of this polyester film comprise ethylene terephthalate unit and ethylene naphthalene dicarboxylate unit, and crystal size of this polyethylene terephthalate is 10-50 Å, when the polyester film is measured by X-ray diffraction method.例文帳に追加

ポリエステルの主たる成分がエチレンテレフタレート単位とエチレンナフタレンジカルボキシレート単位であるポリエステルフィルムであり、かつ、ポリエステルフィルムをＸ線回折法で測定したときのポリエチレンテレフタレートの結晶サイズが１０〜５０オングストロームであるポリエステルフィルムである。 - 特許庁

To provide an evaluating method capable of easily detecting, even in multiple phases, the microscopic area of a bismuth layered structural ferroelectric material which is difficult to detect by normal XRD(x-ray diffraction), and also capable of quantitatively determining its multiple phases.例文帳に追加

通常のＸＲＤでは困難なビスマス層状構造強誘電体材料の、簡便に、短時間に、微小領域を，多相でも検出することができ、しかもその多相の定量化も可能である評価方法を提供すること。 - 特許庁

The method for preparing crystalline forms of tegaserod maleate having X-ray diffraction patterns with peaks at 2θ of about 5.4, 6.0, 6.6 and 10.8±0.2 degree comprises spray drying a solution of tegaserod maleate in a solvent selected from the group consisting of an amine, an amide, a ketone and their mixtures with a 1-8C alcohol or water.例文帳に追加

約５．４、６．０、６．６及び１０．８±０．２度２θにおいてピークを有するX線回折パターンを特徴とする結晶質マレイン酸テガセロドを調製する方法であって、マレイン酸テガセロドの溶液を、アミン、アミド、ケトン及びそれらのC1-C8アルコール又は水との混合物からなる群から選択される溶媒中で噴霧乾燥する。 - 特許庁

A sample containing the hydroxyapatite is taken out and is formed into a shape with at least a detection surface 3 by such method as compression molding, then a forming body 1 is burned, and a substance existing on the detection surface 3 of an obtained sintered body 2 is analyzed, for example, by the X-ray diffraction method.例文帳に追加

ハイドロキシアパタイトを含む試料を取り出し、該試料を圧縮成形等の方法により少なくとも検出面３を有する形状に成形し、次いで、該成形体１を焼成し、得られた焼結体２の検出面３に存在する物質を例えばＸ線回折法により解析する。 - 特許庁

A base film is provided on a substrate and a perpendicular magnetic film having an easily-magnetized axis oriented principally perpendicularly to the substrate is formed on the base layer and a locking curve 21 of the perpendicular magnetic film obtained by using a θ-2θ scanning method in the X-ray diffraction method has plural maximum points 22 and 23.例文帳に追加

基板上に下地膜が設けられ、その上に磁化容易軸が基板に対し主に垂直に配向した垂直磁性膜が設けられ、この垂直磁性膜は、Ｘ線回折法によるθ−２θスキャン法を用いて得たロッキングカーブ２１が複数の極大点２２、２３を有するものである。 - 特許庁

This method for producing the cyclopentanol is characterized by using a protonic zeolite having ≥10 ratio of (SiO2)/(Al2O3) and regulated in x-ray diffraction pattern substantially to the pattern represented by the table 1 as a catalyst in the method for producing the cyclopentanol by hydrating the cyclopentene in the presence of the catalyst.例文帳に追加

触媒の存在下でシクロペンテンを水和してシクロペンタノールを製造する方法において、ＳｉＯ_2/Ａｌ_2Ｏ_3比が１０以上であり、且つＸ線回折パターンが実質的に第１表のパターンで規定されるプロトン型ゼオライトを触媒として使用することを特徴とするシクロペンタノールの製造方法。 - 特許庁

The conductive substrate has an ITO film formed thereon, in which the integrated intensity ratio A/C of the integrated intensity A of 2θ peak corresponding to (222) plane and the integrated intensity of 2θ peak corresponding to (440) plane by the X-ray diffraction method is not less than 5.0.例文帳に追加

Ｘ線回折法による（２２２）面に相当する２θピークの積分強度Ａと（４４０）面に相当する２θピークの積分強度Ｃとの積分強度比Ａ／Ｃが５．０以上であるＩＴＯ膜が形成されていることを特徴とする、導電性基板。 - 特許庁

To provide a structural analysis method of a crystal for easily deciding whether spread shape of a peak to be measured is measured, by reflecting the nonuniform distribution of the composition within the crystal, when evaluating the structure of the crystal through X-ray diffraction.例文帳に追加

Ｘ線回折により結晶構造評価を行う際、測定されるピークの拡がり形状が、結晶中の組成が不均一に分布していることを反映して決まっているか否かを、簡便に判定できる、結晶の構造解析方法を提供する。 - 特許庁

The production method for a crystal polymorphism A (Fig.1: X-ray powder diffraction pattern) of a pitavastatin hemicalcium salt (formula) comprises allowing a sodium salt of pitavastatin to react with CaCl_2 in an aqueous reaction medium, separating a formed crystal, and drying it so that the water content is adjusted to 3-12%.例文帳に追加

ピタバスタチンのナトリウム塩とＣａＣｌ_2とを水性反応媒体中で反応させ、生成した結晶を分離し、乾燥して含水量を３〜１２％に調節する、ピタバスタチンヘミカルシウム塩（下式）の結晶多形Ａ（図１：Ｘ線粉末回折図形）の製造方法。 - 特許庁

To provide a structural analysis method of a crystal for easily deciding whether the spread shape of a peak to be measured is determined, by reflecting the nonuniform distribution of the composition in the crystal, when evaluating the structure of the crystal by X-ray diffraction.例文帳に追加

Ｘ線回折により結晶構造評価を行う際、測定されるピークの拡がり形状が、結晶中の組成が不均一に分布していることを反映して決まっているか否かを、簡便に判定できる、結晶の構造解析方法を提供する。 - 特許庁

According to this method, the dendrite structure of the casting 1 composed of coarse crystal grains can be fined at the surface layer part 2, so that an X-ray diffraction phenomenon can be well generated to stably obtain the correct residual stress.例文帳に追加

この方法によれば、粗大な結晶粒からなる鋳物１の樹枝状晶組織を、その表層部２で微細化することができるため、Ｘ線の回折現象を良好に生じさせることができ、正しい残留応力を安定して求めることができ得る。 - 特許庁

The engine additive comprises a BN powder having an average particle diameter of above 1.0 to 3.0 μm, a maximum particle diameter of at most 15 μm, a graphitization index (GI) of 4.0 or below as measured by a powder X-ray diffraction method, and a boron oxide content of 0.5-5 mass %.例文帳に追加

平均粒径１．０μｍ超３．０μｍ以下、最大粒径１５μｍ以下、粉末Ｘ線回折法による黒鉛化指数（ＧＩ）４．０以下、酸化ほう素含有率０．５〜５質量％のＢＮ粉末からなることを特徴とするエンジンオイル添加剤。 - 特許庁

The control of the density of the dislocation is carried out by suppressing the width of a half value in the X-ray diffraction of a base powder to low, or by the method of not applying a pressure of >100 kgf/cm2 in the steps before obtaining the sintered compact, or by sintering with nitrifying reaction of Si powder.例文帳に追加

転位密度の制御は、原料粉末のＸ線回折における半価幅を低く抑えるか、焼結体を得るまでの工程で１００ｋｇｆ／ｃｍ^2を越える圧力を加えない方法、又はＳｉ粉末の窒化反応焼結による。 - 特許庁

The invention provides a fine carbon fiber having a layer spacing d_002 of 0.337 nm measured by X-ray diffraction method, a fiber diameter of ≤1,000 nm and a compact specific resistance of ≤0.02 Ω.cm and a fine carbon fiber having a metal content of ≤500 mass ppm.例文帳に追加

Ｘ線回折法で求めた層面間隔ｄ_002が０．３３７ｎｍを超え、繊維径１０００ｎｍ以下、圧密比抵抗が０．０２Ω・ｃｍ以下の微細な炭素繊維及び金属含有量が５００質量ｐｐｍ以下である微細な炭素繊維である。 - 特許庁

Requirement (1): Carbon powder obtained by subjecting the binder (B), which can be graphitized, to graphitization treatment has a spacing (d002) on the 002 face by the X-ray wide-angle diffraction method of 0.3357 nm or greater and 0.34 nm or less, and an Lc (004) of 10 nm or greater and 500 nm or less.例文帳に追加

条件（１）：黒鉛化可能なバインダー（Ｂ）を黒鉛化処理して得られた炭素粉末のＸ線広角回折法による００２面の面間隔（ｄ００２）が０．３３５７ｎｍ以上０．３４ｎｍ以下、且つＬｃ（００４）が１０ｎｍ以上５００ｎｍ以下である。 - 特許庁

To provide a method for early determining whether there is a risk of occurrence of the delayed formation of ettringite after service by powder X-ray diffraction, in a cured article using a cement composition such as concrete or mortar receiving high-temperature ageing at the initial stage of hydration.例文帳に追加

水和初期に高温養生を受けたコンクリート、モルタル等のセメント組成物を用いた硬化物において、供用後生じる恐れがあるエトリンガイトの遅延生成の発生有無を粉末Ｘ線回折によって早期に判定する方法を提供する。 - 特許庁

After removing the respective portions of the growth layers 32-34 in the object region to be measured 41, the lattice constants of the semiconductor substrate 23 and growth layers 24-31 in the object region to be measured 41 are obtained, by using X-ray diffraction method.例文帳に追加

このように測定対象領域内４１で、前記成長層３２〜３４の各一部が除去された後、Ｘ線回折法によって、前記測定対象領域４１内の半導体基板２３および成長層２４〜３１の格子定数が求められる。 - 特許庁

The electrostatic charge image developing toner used in an image forming method in which an electrostatic charge image formed on a photoreceptor containing oxy-titanium phthalocyanine having the maximum diffraction peak at 27.3° Bragg angle (2θ±0.2°) in its X-ray diffraction spectrum with CuKα rays is developed with toner, contains a calix arene compound of formula (1).例文帳に追加

ＣｕＫα線によるＸ線回折スペクトルにおいてブラッグ角（２θ±０．２°）２７．３°に最大回折ピークを有するオキシチタニウムフタロシアニンを含有する感光体上に形成された静電荷像をトナーにより現像する画像形成方法に用いられるトナーであって、該トナーが下記構造式（１）で表されるカリックスアレン化合物を含有する静電荷像現像用トナー。 - 特許庁

The carbon structure is characterized in that it has a peak in the XRD (X-ray diffraction) diffraction pattern within the range of 19°-26°, a density by the He method of ≥1.4 g/cm^3, and a volume resistivity of ≤1 Ωcm, and it is prepared from graphite oxide by removing a part of oxygen which is covalently bonded through calcination.例文帳に追加

本発明の炭素構造体は、酸化黒鉛の焼成により共有結合した酸素の一部を取り除き、ＸＲＤ（Ｘ線回析）の回折パターンのピークが１９°から２６°の範囲に有しているとともに、Ｈｅ法による密度が１．４ｇ／ｃｍ^３以上、体積固有抵抗値が１Ω・ｃｍ以下であることを特徴としている。 - 特許庁

To attain a method and program for measuring/analyzing X-ray diffraction capable of performing sufficiently accurate profile analysis by fitting of a specific satellite peak based on known information and measured data, and to two-dimensionally display a match state globally with a good view without losing generality.例文帳に追加

既知情報及び実測データに基づく特定サテライトピークのフィッティングにより、十分な精度のプロファイル解析が行えるＸ線回折測定解析方法及びプログラムを実現し、また、一致状態を一般性を失うことなく大局的に見通しよく２次元表示する。 - 特許庁

This method for determining amosite contained in the sample into which hornblende minerals and calcite are compounded is characterized by solid-liquid-separating the sample after acid treatment, and determining amosite with an X-ray diffraction peak of d=3.1A for solid contents.例文帳に追加

角閃石系鉱物及びカルサイトが配合された試料に含まれるアモサイトを定量する方法であって、前記試料を、酸処理した後、固液分離し、固形分についてｄ＝３．１ＡのＸ線回折ピークでアモサイトを定量することを特徴とするアモサイトの定量方法。 - 特許庁

In this carbon material, an average particle diameter (D50) is 6-20 μm, a specific surface area measured with a BET method is 3 m^2/g or below, an interlayer distance d value (002) in X-ray diffraction is 0.3360-0.3395 nm, and a thickness La of a crystallite in an α-axis direction is 60-300 nm.例文帳に追加

この炭素材は、平均粒径（Ｄ５０）が６〜２０μｍ、ＢＥＴ法により測定される比表面積が３ｍ^２／ｇ以下、Ｘ線回折における層間距離ｄ値（００２）が０．３３６０〜０．３３９５ｎｍ、ａ軸方向の結晶子の厚みＬａが６０〜３００ｎｍである。 - 特許庁

The Ti-Al-based alloy target obtained by this method comprises 45 to 65 atomic% Al, and has at least two or more phases of Ti_3Al, TiAl, TiAl_2 and TiAl_3 upon analysis by X-ray diffraction, and in which metal Ti and metal Al as simple substances are not left upon EPMA (Electron Probe Micro Analysis).例文帳に追加

これにより得られたＴｉ−Ａｌ系合金ターゲットは、Ａｌを４５〜６５原子％含有し、Ｘ線回折で分析したときにＴｉ_３Ａｌ，ＴｉＡｌ，ＴｉＡｌ_２，ＴｉＡｌ_３の少なくとも２種以上の相を含み、ＥＰＭＡ分析をしたときに単体の金属Ｔｉ及び金属Ａｌが残存していない。 - 特許庁

In the thermoplastic resin composition comprising at least a carbon fiber and a thermoplastic resin, the size of the crystals of the carbon fiber measured by the broad-angle X-ray diffraction method is within a range of 1.4-4.5 nm and the diameter of the cross section of the fiber is within a range of 3-15 μm.例文帳に追加

少なくとも炭素繊維と熱可塑性樹脂とを含む熱可塑性樹脂組成物において、広角Ｘ線回折法で測定した炭素繊維の結晶サイズが1.4〜4.5nmの範囲内であり、かつ繊維断面の直径が3〜15μmの範囲内であることを特徴とする熱可塑性樹脂組成物。 - 特許庁

The anti-blocking agent comprises (A) aluminosilicate particles having an X-ray diffraction image characteristic in kaolin and (B) amorphous silica particles at a weight ratio of (A)/(B)=70/30-10/90 and substantially does not cause segregation, when the agent is subjected to the tapping treatment according to the tapping type bulk density testing method.例文帳に追加

（Ａ）カオリンに特有のＸ線回折像を有するアルミノケイ酸塩粒子と（Ｂ）非晶質シリカ粒子とを、重量比で、（Ａ）：（Ｂ）＝７０：３０乃至１０：９０の割合で含有してなり、タタキコミカサ比重試験法にしたがってタッピング処理を行ったときに実質上偏析が生じないアンチブロッキング剤。 - 特許庁

In a solid-phase synthesis method to manufacture the composite oxide powders of barium titanate and the like, a titanium oxide having a rutile content determined by X-ray diffraction of higher than 90% and 100% or less and having a specific surface area of 150-300 m^2/g is used as a raw material titanium oxide.例文帳に追加

チタン酸バリウム等の複合酸化物粉末を製造する固相合成法において、原料のチタン酸化物として、Ｘ線回折法により求められるルチル化率が９０％より高く、１００％以下であり、比表面積が１５０〜３００ｍ^２／ｇであるチタン酸化物を用いる。 - 特許庁

In the method of forming an image which uses at least a photoreceptor and a toner, the electrophotographic photoreceptor has a photosensitive layer containing oxytitanium phthalocyanine, having the maximum diffraction peak at the Bragg angle (2θ±0.2) 27.3° in X-ray diffraction by CuKα line, and the toner has 3 to 8 μm volume average particle size and 20 mm or lower fluidity index.例文帳に追加

少なくとも感光体及びトナーを用いる画像形成方法において、該電子写真感光体が、ＣｕＫα線によるＸ線回折においてブラッグ角（２θ±０．２）２７．３゜に最大回折ピークを有するオキシチタニウムフタロシアニンを含有する感光層を有し、該トナーが体積平均粒径が３〜８μmであり且つ流動性指数が２０ｍｍ以下であることを特徴とする画像形成方法。 - 特許庁

This method for producing the oxidized compound comprises a process of oxidizing an organic compound by reacting the organic compound with an oxidizing agent in the presence of a titanosilicate (I) obtained by making contact of a titanosilicate (II) having the following X-ray diffraction pattern with a structure-regulating agent, or its silylated compound.例文帳に追加

下記Ｘ線回折パターンを有するチタノシリケート（ＩＩ）と構造規定剤とを接触させることにより得られるチタノシリケート（Ｉ）又はそのシリル化物の存在下に、有機化合物と酸化剤とを反応させることにより、前記有機化合物を酸化させる工程を含む酸化化合物の製造方法の提供。 - 特許庁

The hard coating has residual stress in the range of about -0.4 to about -3 GPa when measured by an XRD Sin^2ψ method and a crystal orientation characterized by a ratio of (200) peak intensity to (111) peak intensity by X-ray diffraction being in the range of about 1 to about 14.例文帳に追加

ハードコーティングはまた、ＸＲＤ Ｓｉｎ^２ψ法によって測定される場合約−０．４〜約−３ＧＰａの範囲の残留応力と、Ｘ線回折による（１１１）ピーク強度に対する（２００）ピーク強度の比が約１〜約１４の範囲であることによって特徴付けられる結晶方位とを有する。 - 特許庁

The negative electrode material for a nonaqueous secondary battery includes a nitrogen-containing carbon compound containing 1 mass% or more and 20 mass% or less of nitrogen and having a graphite structure where a spacing on the d002 face measured by means of a powder X-ray diffraction method is 3.40 Å or more and 4.00 Å or less.例文帳に追加

１質量％以上２０質量％以下の窒素を含有し、粉末Ｘ線回折法により測定されるｄ００２面の間隔が３．４０Å以上４．００Å以下であるグラファイト構造を有する含窒素炭素化合物を含む非水系二次電池用負極材料とする。 - 特許庁

The protein crystallization method comprises adding a reagent necessary for protein crystallization to a protein solution to form a sample solution and causing the crystal of the protein to deposit while applying to the sample solution a voltage that heightens resolution of X-ray diffraction of the deposited crystal.例文帳に追加

本発明に係るタンパク質の結晶化方法は、タンパク質溶液に、タンパク質の結晶化に必要な試薬を添加してサンプル溶液を生成し、該サンプル溶液に、析出した結晶のＸ線回折の解像度が高くなる電圧を印加しながらタンパク質の結晶を析出させることを特徴とする。 - 特許庁

Regarding the positive electrode component in which the main component is lithium manganate, this has a crystallite size measuring process to measure the crystallite size of the positive electrode active material for the lithium secondary battery based on an X-ray diffraction method, and a presumption process to presume the positive electrode capacity from the crystallite size is provided.例文帳に追加

マンガン酸リチウムを主成分とする正極活物質について、Ｘ線回折法に基づき該リチウム二次電池用正極活物質の結晶子サイズを測定する結晶子サイズ測定工程と、該結晶子サイズから正極容量を推定する推定工程と、を有することを特徴とする。 - 特許庁