「POLYLACTIC ACID」に関連した英語例文の一覧と使い方(52ページ目) - Weblio英語例文検索

To provide a polylactic acid-based resin composition having rich flexibility, having good transparency, formability, and color, capable of being produced at a relatively reduced cost, having safety without having an effect on the environment or the like, and excellent in biodegradability.例文帳に追加

柔軟性に富み、透明性、成形性、色相の良好な、比較的低価格で製造可能な、環境問題などの影響のない安全な、生分解性に優れたポリ乳酸系樹脂組成物を提供する。 - 特許庁

The toner is produced by a production method of the toner including a melting and mixing step of melting and mixing a lignin compound and a polylactic acid for inducing a transesterification between the lignin compound and the polylactic acid to obtain a reaction product as a binder resin; and a particle forming step of forming particles from a colorant and the binder resin obtained in the melting and mixing step, with the obtained particles containing the colorant dispersed in the binder resin.例文帳に追加

リグニン系化合物とポリ乳酸とを溶融させて混合することによって、該リグニン系化合物と該ポリ乳酸との間でエステル交換反応を生じさせ、反応生成物を結着樹脂として得る溶融混合工程と、着色剤と前記溶融混合工程によって得られる結着樹脂とから、該結着樹脂中に該着色剤が分散した粒子を形成する粒子形成工程とを含むトナーの製造方法によってトナーを製造する。 - 特許庁

To provide an aqueous dispersion composition which is obtained by aqueous-dispersing polylactic acid/polycaprolactone copolymer in the presence of a specific compound as a dispersant and can give polylactic acid/polycaprolactone copolymer coating films excellent in coating film physical properties such as water resistance, and to use the aqueous dispersion composition as a binder resin to provide a biodegradable water-based printing ink composition or a biodegradable water-based overprint varnish composition.例文帳に追加

乳化剤としてある特定の化合物を使用してポリ乳酸／ポリカプロラクトン共重合体を水性分散化することにより、耐水性などの塗膜物性に優れたポリ乳酸／ポリカプロラクトン共重合体皮膜を得ることが可能な水性分散組成物を提供し、さらに、それをバインダー樹脂として利用することにより、生分解性水性印刷インキ組成物や生分解性水性オーバープリントニス組成物を提供する。 - 特許庁

The polylactic resin sheet includes a film C containing a polyhydric alcohol fatty acid ester A and a water-soluble acrylic polymer B on at least one surface of a polylactic resin base material, wherein a content of the polyhydric alcohol fatty acid ester A in the film C is >20 to <50 mass% or >80 to <95 mass% with respect to 100 mass%.例文帳に追加

ポリ乳酸系樹脂基材の少なくとも片面に、多価アルコール脂肪酸エステル（Ａ）と水溶性アクリル系重合体（Ｂ）とを含有する被膜（Ｃ）を有するポリ乳酸系樹脂シートであって、多価アルコール脂肪酸エステル（Ａ）の被膜（Ｃ）１００質量％に対する含有量が２０質量％超５０質量％未満、または８０質量％超９５質量％未満であることを特徴とするポリ乳酸系樹脂シート。 - 特許庁

In the biodegradable conductive composite sheet consisting of a plurality of layers, the outer layer among a plurality of the layers is constituted of a polylactic acid polymer, biodegradable aliphatic polyester and a resin containing 3-15 wt.% of a conductive agent and the inner layer among them is constituted of the polylactic acid polymer, biodegradable aliphatic polyester and the resin containing 0.1-3 wt.% of the conductive agent.例文帳に追加

複数の層からなる生分解性導電性複合シートにおいて、上記複数層のうち外層を、ポリ乳酸系重合体、生分解性脂肪族ポリエステル、及び３〜１５重量％の導電剤を含有する樹脂から構成し、上記複数層のうち内層を、ポリ乳酸系重合体、生分解性脂肪族ポリエステル、及び０．１〜３重量％の導電剤を含有する樹脂から構成することを特徴とする。 - 特許庁

The polylactic acid resin composition having an accelerated biodegradation rate comprises 100 pts.mass polylactic polymer and 5-40 pts.mass anatase-type titanium oxide having a particle diameter of 0.05-1 μm which is non-surface treated or rutile-type titanium oxide having a particle diameter of 0.005-1 μm which is surface-treated with an inorganic substance.例文帳に追加

生分解速度が促進されたポリ乳酸系樹脂組成物であって、ポリ乳酸系重合体１００質量部に、粒径が０．０５〜１μｍでかつ表面処理されていないアナターゼ型二酸化チタン、もしくは粒径が０．００５〜１μｍでかつ表面が無機物処理されているルチル型二酸化チタンが、５〜４０質量部配合されている。 - 特許庁

The biodegradable resin composition obtained by synthesis from the regenerable resource and comprising a polylactic polymer (A) having L-lactic acid and/or D-lactic acid as the major component and the molded article therefrom comprise modified starch (B) and a glycerol fatty acid ester (C) containing ≥75 mass% diacetylmonoacyl glycerol having an 8-16C saturated fatty acid.例文帳に追加

Ｌ−乳酸及び／又はＤ−乳酸が主成分のポリ乳酸重合体（Ａ）を主体とする再生可能資源から合成されてなる生分解性樹脂組成物及びそれから成る成形品において、変性澱粉（Ｂ）、及び、炭素数８〜１６の飽和脂肪酸を有するジアセチルモノアシルグリセロールを７５質量％以上含有するグリセリン脂肪酸エステル（Ｃ）を含有することを特徴とするポリ乳酸系樹脂組成物及び成形品。 - 特許庁

The polylactic acid-based block copolymer has a segment (segment B) mainly comprising an L-lactic acid unit at the both ends of a segment mainly including an aliphatic carbonate unit via a segment (segment A) mainly comprising a D-lactic acid unit, wherein an organophosphorus compound represented by specific structure is copolymerized with at least one of the segment A and the segment B.例文帳に追加

脂肪族カーボネート単位を主として含むセグメントの両端に、主としてＤ−乳酸単位からなるセグメント（Ａセグメント）を介して、主としてＬ−乳酸単位からなるセグメント（Ｂセグメント）を有するポリ乳酸系ブロック共重合体であって、Ａセグメント、Ｂセグメントの少なくとも一方に、特定構造で表される有機リン化合物が共重合されているポリ乳酸系ブロック共重合体。 - 特許庁

This release-controlled local administration agent is an agent applied in the body, where a micro-capsule, of at least one medicine, using a polylactic acid or a copolymer of lactic acid and glycolic acid is sealed into a space surrounded by a regenerated cellulose membrane or a regenerated cellulose porous membrane, to be usable without requiring decomposition of a regenerated cellulose.例文帳に追加

体内に適用する徐放化局所投与剤であって、少なくとも一の薬剤をポリ乳酸あるいは乳酸とグリコール酸の共重合体を用いたマイクロカプセルを再生セルロース膜および再生セルロース多孔膜に囲まれた空間に封入してその再生セルロースの分解を必要としないままで使用できることを特徴とする徐放化局所投与剤。 - 特許庁

The packaging material for receiving and holding an ink jet head and/or an ink tank is constituted of a biodegradable film comprising at least one kind selected among biodegradable polymers including a polyamino acid, starch, polylactic acid, polycaprolactone, polyglycolic acid and Bionol, and at least one of silicon oxide (SiO2) and aluminum oxide (Al2O3) which is metallized on the biodegradable film.例文帳に追加

インクジェットヘッド及び／又はインクタンクを収納保持する包装材料であって、ポリアミノ酸、デンプン、ポリ乳酸、ポリカプロラクトン、ポリグリコール酸、及びビオノールからなる生分解性ポリマー群より選択される少なくとも一種を含有する生分解性フィルム上に、酸化ケイ素（ＳｉＯ_2）及び酸化アルミニウム（Ａｌ_2Ｏ_3）の少なくとも一方を蒸着させてなることを特徴とする包装材料である。 - 特許庁

The polyester resin composition is (1) a composition which has polylactic acid as its main component and contains, as a plasticizer, diglycerol acetate with its acetylation rate not less than 50% or (2) a composition which contains diglycerol acetate and diacetylmonoacyl glycerol having, as a constituent fatty acid, an aliphatic fatty acid containing not less than eight carbons.例文帳に追加

ポリエステル樹脂組成物において、（１）ポリ乳酸を主成分とするポリエステル樹脂組成物において、アセチル化率５０％以上のジグリセロール酢酸エステルを可塑剤として含有すること、（２）ジグリセロール酢酸エステルと炭素数８以上の脂肪族脂肪酸を構成脂肪酸とするジアセチルモノアシルグリセロールとを含有すること、を各々特徴とするポリエステル樹脂組成物である。 - 特許庁

This aliphatic polyester composition comprises a polylactic acid (A) and an aliphatic polyester polyether copolymer (B), wherein a content of the aliphatic polyester polyether copolymer (B) is ≥1 pt.wt. to ≤60 pts.wt. based on 100 pts.wt. of the total amount of the poly lactic acid (A) and the aliphatic polyester polyether copolymer (B).例文帳に追加

ポリ乳酸（Ａ）と脂肪族ポリエステルポリエーテル共重合体（Ｂ）とを含有してなる組成物であって、脂肪族ポリエステルポリエーテル共重合体（Ｂ）の含有量が、ポリ乳酸（Ａ）と脂肪族ポリエステルポリエーテル共重合体（Ｂ）との合計１００重量部中、１重量部以上６０重量部以下である脂肪族ポリエステル組成物。 - 特許庁

There is provided a method for manufacturing the composition characterized in that an excipient selected from the group of a polylactic acid, a hyaluronic acid, a collagen, and a poly(lactide-co-glycolide) is dissolved in a protein having a physiological activity in carbon dioxide gas in a supercritical or subcritical state to obtain a uniform mixture, and the mixture is solidified in a needle-like shape.例文帳に追加

超臨界又は亜臨界状態の炭酸ガス中に，ポリ乳酸，ヒアルロン酸，コラーゲン，ポリ（ラクチド−ｃｏ−グリコリド）からなる群から選択される賦形剤と，生理活性を有する蛋白質を溶解して均質な混合物とし，ついで該混合物を針状に固化することを特徴とする，組成物の製造方法。 - 特許庁

The laminate comprises at least paper and a filmlike material composed mainly of a copolymer of polylactic acid and an oxycarboxylic acid, and the filmlike material comprises a laminar structure composed of laminated layers of different crystalinities to make a layer of lower crystalinity, among the outer two layers, overlie paper.例文帳に追加

ポリ乳酸又は乳酸とオキシカルボン酸とのコポリマーを主成分とするフィルム状物及び紙を少なくとも有する積層体において、上記フィルム状物は、結晶性の異なる層からなる積層構造を有し、かつ、上記フィルム状物を構成する２つの外層のうち、結晶性がより低い層を紙と積層させる。 - 特許庁

The implant is formed by dispersing steroid (in especially, anti-inflammatory agent, dexamethasone) in a matrix of PLGA copolymer (polylactic acid/polyglycolic acid copolymer) as the eye disease treatment agent, and the implant is a medicine delivery apparatus having a shape selected from a group consisting of a fiber, a sheet, a film, a micro sphere, a sphere, a disk and a plaque.例文帳に追加

眼病治療剤としてステロイド（特に、抗炎症剤デキサメタゾン）がＰＬＧＡコポリマー（ポリ乳酸／ポリグリコール酸コポリマー）のマトリックス中に分散されたインプラントであり、該インプラントはファイバー、シート、フィルム、微小球、球、円板、及びプラークからなる群から選ばれる形状を有する医薬デリバリー装置である。 - 特許庁

This resin composition is obtained by blending (A) an aliphatic-aromatic copolyester-based resin, (B) a polylactic acid-based resin or an aliphatic polyester-based resin and (C) 10-150 pts.wt. ester-based plasticizer having an aromatic carboxylic acid component and aliphatic alcoholic component based on 100 pts.wt. total amount of the (A)+(B).例文帳に追加

（Ａ）脂肪族−芳香族共重合ポリエステル系樹脂、（Ｂ）ポリ乳酸系樹脂または脂肪族ポリエステル系樹脂、及び（Ａ）＋（Ｂ）の合計量１００重量部に対して、（Ｃ）芳香族カルボン酸成分及び脂肪族アルコール成分を有するエステル系可塑剤を１０〜１５０重量部配合してなる樹脂組成物。 - 特許庁

In the resin composition, the thermoplastic resin (A) is preferably at least one kind of biodegradable resin selected from the group consisting of a resin obtained by using a polylactic acid, a polycaprolactone, an aliphatic dicarboxylic acid and a polyhydric alcohol as main raw materials, a polyester resin synthesized from a microorganism or a plant, starch and modified starch.例文帳に追加

また、熱可塑性樹脂（Ａ）がポリ乳酸、ポリカプロラクトン、脂肪族ジカルボン酸と多価アルコールを主原料として得られる樹脂、微生物または植物より合成されたポリエステル樹脂、澱粉、変性澱粉からなる群から選択される少なくとも１種の微生物崩壊性樹脂である樹脂組成物。 - 特許庁

The composition containing polylactic acid is obtained by melt ring-opening polymerization under specific condition, using a metal compound as a catalyst containing at least one metal selected from tin, aluminum, zinc, calcium, titanium, germanium, manganese, magnesium, and rare earth elements, under coexistence of lactide and a specific phosphorous acid compound.例文帳に追加

ラクチドと特定の亜リン酸化合物との共存下、スズ、アルミニウム、亜鉛、カルシウム、チタン、ゲルマニウム、マンガン、マグネシウム及び稀土類元素より選択される少なくとも一種の金属を含有する金属化合物を触媒として用い、特定の条件下に溶融開環重合させてポリ乳酸含有組成物を得る。 - 特許庁

The biodegradable resin composition comprises: 100 pts.mass of a biodegradable polyester resin that contains 50 mass% or more of a polylactic acid; 0.5-10 pts.mass of a phyllosilicate; and 0.1-15 pts.mass of a jojoba oil.例文帳に追加

ポリ乳酸を５０質量％以上含有した生分解性ポリエステル樹脂１００質量部と、層状珪酸塩０．５〜１０質量部と、ホホバ油０．１〜１５質量部とを含有することを特徴とする生分解性樹脂組成物。 - 特許庁

To provide a polylactic acid resin type molding which can control the deterioration of a surface caused by hydrolysis, and in which the formation of a dry area and/or the generation a crack can be suppressed, and which can improve the durability, and a method of manufacturing it.例文帳に追加

表面部における加水分解による劣化が抑制され、これにより荒れや亀裂の発生を抑制することができ、耐久性を高めることができるポリ乳酸樹脂系成形品とその製造方法を提供する。 - 特許庁

The fiber-based board including a natural fiber having an average fiber length of 5-100 mm and a polylactic acid resin, has an apparent density of 0.6-1.1 g/cm^3 at the surface layer of the fiber-based board.例文帳に追加

繊維系ボードは平均繊維長５〜１００ｍｍの範囲内の天然繊維とポリ乳酸樹脂とを含んで構成される繊維系ボードであって、繊維系ボードの表面層の見かけ密度が０．６〜１．１ｇ／ｃｍ^３の範囲内にある。 - 特許庁

This method for producing the molded article comprises melting the polylactic acid-based resin composition, filling the melted resin composition into a mold of a molding machine in which the molding temperature is set to a temperature not higher than a crystallization initiation temperature in DSC and not lower than the glass transition temperature and molding the resin composition while crystallizing the resin.例文帳に追加

ポリ乳酸系樹脂組成物を溶融し、ＤＳＣにおける結晶化開始温度以下ガラス転移温度以上の範囲に温度設定された成形機の金型に充填し、結晶化させながら成形する。 - 特許庁

The composition is obtained by compounding, based on (A) 100 pts.wt. of a polybutylene terephthalate resin, (B) 5-100 pts.wt. of a polylactic acid resin having melting point of 130-150°C and crystal melting heat of 0-10 J/g, and (C) 0-5 pts.wt. of a hydrolysis resistance modifier.例文帳に追加

（Ａ）ポリブチレンテレフタレート樹脂１００重量部に対して、（Ｂ）融点１３０〜１５０℃、結晶融解熱量０〜１０J／ｇのポリ乳酸樹脂５〜１００重量部、（Ｃ）耐加水分解性改良剤０〜５重量部を配合する。 - 特許庁

To confirm whether a polylactic acid resin can be used as an insulating material for a DC power cable, and find a preferable blending constitution when using the resin as the insulating material for the power cable.例文帳に追加

ポリ乳酸系樹脂が、直流電力ケーブルの絶縁材料として使用することができるか否かを確認すること、また直流電力ケーブル用の絶縁材料として使用する場合に、好ましい配合構成を見出すことにある。 - 特許庁

The polylactic acid film has a crystal melt peak in a predetermined temperature range, has predetermined stereo-formation degree, has plane-direction retardation (Re) and thickness-direction retardation (Rth) in predetermined numerical ranges, and has a predetermined thermal contraction coefficient.例文帳に追加

特定の温度範囲に結晶融解ピークを有し、特定のステレオ化度を有し、面方向の位相差（Ｒｅ）および厚み方向の位相差（Ｒｔｈ）が特定の数値範囲にあり、特定の熱収縮率を有するポリ乳酸フィルム。 - 特許庁

The resin composition comprises mainly polylactic acid, has a light transmittance of ≥50% for a wavelength of 900-940 nm and ≤40% for a wavelength of 200-700 nm, when measured on a 1mm thick plate prepared from the composition.例文帳に追加

この樹脂組成物は、ポリ乳酸を主成分とし、厚さ１ｍｍの板状にした際に、波長９００〜９４０ｎｍの光線透過率が５０％以上、２００〜７００ｎｍの光線透過率が４０％以下である。 - 特許庁

To obtain substantially noncrosslinked expandable resin beads having high expandability, polylactic acid-based resin expandable beads capable of giving a biodegradable bulk cushioning material having high cushioning performance as a foam.例文帳に追加

生分解性を有し且つ発泡体として優れた緩衝性能を有するバラ状緩衝材を与えるポリ乳酸系樹脂発泡性粒子において、実質的に無架橋で優れた発泡性を有する発泡性粒子を提供する。 - 特許庁

According to an example, powdery granulated mica (containing 0.8 wt.% urethane resin binder) obtained by granulating natural mica having 40-50 μm particle size is added to a polylactic acid in 10 wt.% and a storage elastic modulus at a high temperature is remarkably increased.例文帳に追加

実施例では、ポリ乳酸に粒径４０〜５０μｍの天然マイカを造粒した造粒雲母粉（ウレタン樹脂バインダーを０．８ｗｔ％含む）を１０ｗｔ％添加したことろ、高温時における貯蔵弾性率が大幅に向上した。 - 特許庁

In the polarizing plate, a protection film formed from a material containing polylactic acid is laminated at least on one surface of a polarizing film through an adhesive layer, wherein, the adhesive layer is formed by curing a specified radiation curable composition.例文帳に追加

偏光膜の少なくとも片面にポリ乳酸を含む材料からなる保護フィルムが接着剤層を介して積層された偏光板であって、接着剤層を特定の放射線硬化型組成物を硬化させたものとする。 - 特許庁

The polylactic acid block copolymer with weight average molecular weight of 100,000 or more can be prepared by performing solid phase polymerization of the mixture obtained by mixing with shearing or pressing.例文帳に追加

（ΔＨｍ−ΔＨｃ）＞２０（Ｊ／ｇ）さらに、混合をせん断付与あるいは加圧で行い、当該混合物を固相重合することにより、重量平均分子量が１０万以上のポリ乳酸ブロック共重合体を製造することができる。 - 特許庁

When a polylactic acid undrawn yarn having a crystal size of less than 6 nm is drawn, the drawing temperature, the heat treatment temperature, the drawing ratio are set to higher than 110°C, higher than 120°C, and in a specific range, respectively.例文帳に追加

結晶サイズが６ｎｍ未満のポリ乳酸未延伸糸を延伸するに際し、延伸温度を１１０℃以上、熱処理温度を１２０℃以上、延伸倍率（ＤＲ）を特定の範囲とするポリ乳酸繊維の製造方法。 - 特許庁

In addition, when the bathing agent is stuck between the fibers of the nonwoven fabric made from polylactic acid instead of being accommodated in the bag, the area, which the bathing agent homogeneously dispersed between the fibers sticks to, increases, and therefore the bathing agent more effectively elutes.例文帳に追加

また、入浴剤を袋に収容する代わりに、ポリ乳酸不織布の繊維間に入浴剤を付着すると、繊維間に均一分散された入浴剤の付着面積が増大するため、入浴剤の溶出効果が向上する。 - 特許庁

To give pleats to a cloth made of a cellulosic fiber, silk, or wool, by utilizing a cloth made of a polylactic acid fiber, while stable pleats are not conventionally formed thereon, unless a chemical or a resin is used.例文帳に追加

ポリ乳酸繊維からなる布帛を利用して、従来では薬剤や樹脂を使わなければ安定したプリーツが形成できなかったようなセルロース系繊維、絹または毛からなる布帛にプリーツを付与しようとするものである。 - 特許庁

To provide a polylactic acid laminated sheet having sufficient impact resistance, heat resistance and thermal bending formability without particularly increasing a sheet thickness and a tough thermally bent formed object made from the sheet withstanding distribution or storage.例文帳に追加

シート厚を特に大きくすることなく、十分な耐衝撃性、耐熱性、及び熱折り曲げ成形性を有するシート、及びこのシートから流通や保管に耐える強靭な熱折り曲げ成形体を提供することを目的とする。 - 特許庁

Also the polymer alloy shows an islands in sea structure in which the polylactic acid-based polymer forms a sea component and the copolymeric polyester polymer forms island components, and the domain size of the island components is in 0.001-0.1 μm range.例文帳に追加

またポリマーアロイは、ポリ乳酸系重合体が海成分を形成し、共重合ポリエステル重合体が島成分を形成した海島構造を呈するとともに、島成分のドメインサイズが０．００１〜０．１μｍの範囲にある。 - 特許庁

The resin composition is prepared by adding 0.1 to 10 pts.wt. carbodiimide group-containing resin as an additive to a raw material wherein mainly a polylactic acid polymer (A) is mixed with an aliphatic polyester carbonate (B).例文帳に追加

主としてポリ乳酸系重合体（Ａ）と脂肪族ポリエステルカーボネート（Ｂ）が混合されている原料に、さらに添加剤としてカルボジイミド基含有樹脂が０．１〜１０重量部含まれるようにする事で上記目的が達成される。 - 特許庁

An original yarn of PLA (polylactic acid fiber) (1010 dtex) and an original yarn of N-6 nylon (1430 dtex) are commingled by a commingler to provide a commingled yarn with PLA ratio of 41.4%.例文帳に追加

ＰＬＡ（ポリ乳酸繊維）（１０１０dtex）の原糸、及びＮ−６ナイロン（１４３０dtex）の原糸を、コーミングルにて混繊して、ＰＬＡ比率４１．４％の混繊糸を得、この混繊糸を使用して、下記の原反規格、基布及びバッキングにてパイルカーペットを作成した。 - 特許庁

To provide a thermally insulated container which is a compounded container formed by combining a container main body molded by heat-resistant polylactic acid resin made from biomass with a paper outer cylinder and has a low environmental load at the time discard.例文帳に追加

バイオマスを原料とした耐熱性のあるポリ乳酸系樹脂を成形した容器本体と紙製紙製外筒とを組合わせた複合容器であって、廃棄時における環境負荷の少ない断熱容器を提供する。 - 特許庁

To provide a manufacturing method of a woody fiber molded product constituted so that woody fibers are bonded by a polylactic acid type aliphatic polyester and superior in strength and moisture resistance.例文帳に追加

木質系繊維がポリ乳酸系脂肪族ポリエステルで結合された成形体の製造に関し、強度が高く、耐湿性に優れた木質系繊維成形体を得ることができる木質系繊維成形体の製造方法を提供する。 - 特許庁

This biodegradable headrest cover is constituted of a nonwoven filament fabric comprising a polylactic acid-based polymer and the flame retardance of the nonwoven filament fabric is ≥24 oxygen index measured according to JIS K 7201.例文帳に追加

ポリ乳酸系重合体からなる長繊維不織布で構成される生分解性ヘッドレストカバーであり長繊維不織布の難燃性がＪＩＳ Ｋ ７２０１の測定において酸素指数２４以上を有する生分解性ヘッドレストカバー。 - 特許庁

In the resin composition, the compatibility of the both of the resins is improved markedly and only one Tg having a value in the middle of the Tg's of 2 kinds of resins before the blending, becomes to be observed and the heat resistance is improved as compared with that of the polylactic acid.例文帳に追加

両樹脂の相溶性が顕著に向上し、ブレンド前の２種の樹脂のＴｇの中間の値を有する１個のＴｇのみが観測されるようになり、耐熱性がポリ乳酸樹脂と比べて向上した樹脂組成物。 - 特許庁

To provide a heat-shrinkable laminated film capable of satisfying breaking resistance of a polylactic-acid heat-shrinkable film, and suitable for applications to shrinkage package, shrinkage binding package, a shrinkage label and the like for imparting transparency and a low-temperature shrinkage characteristic.例文帳に追加

ポリ乳酸系熱収縮フィルムの耐破断性を満足させ、かつ透明性や低温収縮特性を付与する収縮包装、収縮結束包装や収縮ラベル等の用途に適した熱収縮性フィルムを得る。 - 特許庁

To provide a polylactic acid crimped yarn enabling compatibility between the process passableness in producing itself and a carpet product therefrom and the physical properties of the carpet product required in its use.例文帳に追加

本発明は、捲縮糸の製造並びにカーペット製品を製造するときの工程通過性とカーペット製品としての使用時に要求される物性との両立を可能としたポリ乳酸捲縮糸を提供せんとするものである。 - 特許庁

Biodegrading plastics, particularly a polylactic acid also has high compressive strength and a decomposition reaction is promoted quickly in an alkaline atmosphere as the decomposing sheet, and the water absorption action of the water absorbing sheet such as paper, a nonwoven fabric or the like assists the decomposition action.例文帳に追加

該分解シートには生分解性プラスチック、特にポリ乳酸系の材料が圧縮強度も高く、アルカリ性雰囲気で早急に分解反応が促進され、紙、不織布などの吸水シートの吸水作用がこれを助長する。 - 特許庁

This resin composition comprising a polylactic acid and a polycarbonate, or especially an aliphatic polyestercarbonate as a raw material, is obtained by subjecting the polymers to a crosslinking reaction by a peroxide to compatibilize the polymers.例文帳に追加

ポリ乳酸とポリカーボネート、特に脂肪族ポリエステルカーボネートを原料とし、さらに過酸化物によりポリマー同士を架橋反応させる事によりポリマー同士を相溶化させ、優れた機械特性を有する相溶性樹脂組成物を成す。 - 特許庁