The silicon carbide-based porous structure material coated with a ceramic is obtained by removing excess carbon by calcining a silicon carbide-based, heat-resistant porous structure material, obtained by impregnating silicon into a silicon carbide-based porous structure material having open pores, in the air, then impregnating it with a solution which gives an oxide ceramic when it is fired, and firing the impregnated porous structure material.例文帳に追加

開気孔を生成させた炭化ケイ素系多孔質構造体にシリコンを溶融含浸して得た炭化ケイ素系耐熱性多孔質構造体を、空気中で仮焼して過剰の炭素を除いた後、焼成して酸化物セラミックスとなる溶液を含浸させ、それを焼成することにより、セラミックスで被覆された炭化ケイ素系多孔質構造材を得る。 - 特許庁

The ceramic material for dentistry is manufactured by mixing 0.001-5 wt.% pink coloring material of a solid solution of aluminum oxide and manganese oxide and 0.001-5 wt.% yellow coloring material of a solid solution of zirconium oxide and vanadium oxide with zirconium oxide containing a stabilizer in which 0.1-30 wt.% aluminum oxide is incorporated if need and firing.例文帳に追加

必要に応じて更に酸化アルミニウムを０.１〜３０重量％含有させた安定化材を含む酸化ジルコニウムに、酸化アルミニウムに酸化マンガンを固溶したピンク色の着色材と、酸化ジルコニウムに酸化バナジウムを固溶した黄色の着色材とをそれぞれ０.００１〜５重量％の範囲内で混合し、焼成して歯科用セラミックス材を作製する。 - 特許庁

Li_2TiO_3 is recovered as a fine powder suitable for manufacturing ceramics by dissolving lithium titanate (Li_2TiO_3), which is a monoclinic ceramic, in a hydrogen peroxide (H_2O_2) solution, stabilizing the solution by adding a water-soluble diligand or triligand chelate reagent, controlling the lithium isotope ratio, concentrating, drying, and finally heating.例文帳に追加

単斜晶相のセラミックであるチタン酸リチウム（Li_2TiO_3）を過酸水素（H_2O_2）水で溶解させ、水溶性の２配位子もしくは３配位子のキレート試薬を加えることにより、この溶液を安定化処理した後にリチウムの同位体比を調整し、濃縮した後に乾燥及び加熱することにより、Li_2TiO_3をセラミックスの製造に適した微粉末として回収する。 - 特許庁

The method for forming the casting mold includes a step of: forming body by kneading ceramic powder containing silicon nitride powder and a first binder solution; a step of: forming slurry by adding a second binder solution to the body; and a step of forming a mold releasing layer by applying the slurry to the surface of a casting mold base body.例文帳に追加

窒化珪素粉末を含むセラミック粉末と、第一バインダー溶液と、を混練して、坏土を形成する工程と、前記坏土に第二バインダー溶液を添加して、スラリーを形成する工程と、前記スラリーを鋳型用基体の表面に付着させて、離型層を形成する工程と、を備えることを特徴とする鋳型の形成方法とする。 - 特許庁

A silver salt solution is applied to the surface of a carrier such as natural or synthetic fiber, glass, ceramic, metal oxide and sintered metal oxide and the solution is reduced with an active hydrogen reducing agent or by the irradiation with ultraviolet rays having a wavelength of ≤400 nm to form ultrafine silver particles having excellent antibacterial property and supported on the surface of the carrier.例文帳に追加

天然あるいは合成繊維、ガラス、セラミックス、金属酸化物、金属酸化物焼結体等の坦体の表面に銀塩溶液を塗布し、次いでこれを活性水素系還元剤、あるいは波長４００ｎｍ以下の紫外線照射による還元処理により、当該坦体の表面に抗菌性に優れた銀微細粒子を生成及び坦持させる。 - 特許庁

The conductive porous ceramic essentially composed of titanium silicide is manufactured by forming a composite film from a film-forming raw material solution obtained by highly filling titanium silicide TiSi_2 powder in an organic solvent solution of a polymer substance and firing the obtained composite film in vacuum or inactive atmosphere in a heating range of ≥400°C.例文帳に追加

珪素化チタンTiSi_2粉末を高分子物質の有機溶媒溶液中に高充填した製膜原液から複合膜を製膜し、得られた複合膜を少くとも400℃以上の加熱温度範囲では真空または不活性雰囲気環境下で焼成することによって、珪素化チタンを主成分として形成される導電性多孔質セラミックスを製造する。 - 特許庁

The apparatus for treating the waste water 1 includes a first treatment tank 11 having submersible pump means 21 which sucks the floating milk fat along with the waste water via a suction port 17 and brings it into contact with ceramic 18 to emulsify it to make an emulsified water solution, which is discharged via a delivery port 19.例文帳に追加

排水処理装置１は、浮上乳脂肪分を排水とともに吸込口部17から吸い込んでセラミック18と接触させて乳化水溶液にして吐出口部19から吐き出す水中ポンプ手段21を配置した第１処理槽11を備える。 - 特許庁

The solidified molded product is spray-coated with a borate aqueous solution, subjected to a high heat treatment at ≥1,000°C with a gas burner to form the strong structure having a 2 to 3 centimeter glass crystal fine ceramic layer.例文帳に追加

固化後構造体表面にホウ酸水溶液を塗付してガスバーナーで１０００℃以上の高温処理をし、表面２〜３センチをガラス上結晶のファインセラミック化し強固な構造にすると共に内部の有意の物質が徐々に浸食放出される。 - 特許庁

The H_2S removing material after use of the H_2S removing material made of the ceramic honeycomb carrying the composite metal oxide containing Mn is subjected to washing treatment in a heated alkali aqueous solution or heat treatment in a vacuum to remove S (sulfur) deposed on a surface.例文帳に追加

Ｍｎを含む複合酸化物を担持したセラミックスハニカム製Ｈ_2Ｓ除去材の使用後のＨ_2Ｓ除去材を、加熱アルカリ水溶液中で洗浄処理するか、あるいは真空中で加熱処理して、表面に沈着したＳ（硫黄）を除去する。 - 特許庁

To provide a silicon nitride porous body which has a porous structure with a large average pore size and large thermal conductivity and small thermal expansivity of a cut-off test piece, and is preferably used for a gas and/or solution purification part of a ceramic filter or the like.例文帳に追加

平均細孔径が大きな多孔構造を有するとともに、切り出した試験片の熱伝導率が高く熱膨張率が小さな、セラミックフィルタ等のガス及び／又は溶液浄化部品に好適に用いられる窒化珪素多孔体を提供する。 - 特許庁

The technical field of the specified invention (Claim 1) is "dissolving a ceramic material in an article which is vulnerable to attack by a caustic alkali solution ", whereas that of the related invention (Claim 2) is "dissolving the core made of a ceramics material of a light metal or a light alloy casting". 例文帳に追加

（請求項１）の技術分野は「苛性アルカリ溶液の攻撃を受け易い物品内のセラミック材料の溶解」であり、関連発明（請求項２）の技術分野は「軽金属又は軽合金鋳物のセラミック材料よりなる中子の溶解」である。 - 特許庁

The electrolytic tin plating solution for the ceramic electronic component contains stannous ion and a chelating agent, and whose pH is controlled between 6-9, and whose value of the relation (molar concentration of the chelate agent)/(molar concentration of stannous ion) is controlled higher than 2.4 and 4.5 or less.例文帳に追加

本実施形態に係るめっき液は、セラミック電子部品用の電気スズめっき液であって、スズイオン及びキレート剤を含み、ｐＨが６以上９以下であり、キレート剤のモル濃度／スズイオンのモル濃度の値が２．４より大きく、４．５以下である。 - 特許庁

The tin electroplating solution for the ceramic electronic component contains tin ion and has pH≥5 and ≤8, ≤0.3 mol/L concentration of ammonia and ammonium ion, and (molar concentration of chelate agent)/(molar concentration of tin ion) of ≤2.5.例文帳に追加

本実施形態に係るめっき液は、セラミック電子部品用の電気スズめっき液であって、スズイオンを含み、ｐＨが５以上８以下であり、アンモニアおよびアンモニウムイオンの濃度が０．３ｍｏｌ／Ｌ以下であり、キレート剤のモル濃度／スズイオンのモル濃度が２．５以下である。 - 特許庁

Solution of the coloring matter separated from safflowers is sold in a white ceramic bowl with a lid which prevents the color of beni from being worn out, a sake cup (light cannot enter the cup as long as it is turned over), or a seashell, after being spread with a number of coats on such a container and dried up. 例文帳に追加

紅花から分離した色素の溶液を、紅が退色しないように蓋が付いた白色の陶器の椀や猪口（伏せておけば光が入らないため）、あるいは貝殻に何度も塗り重ねて乾燥させた状態で販売されている。 - Wikipedia日英京都関連文書対訳コーパス

On the other hand, the new matter corresponding to the problems to be solved of the specified invention, i.e. to "make a ceramic material include the substance containing hydrogen donors and make a ceramic material immerse in the anhydrous caustic alkaline solution", is equivalent to the substantial part of the matters in the claim of the related invention. Therefore, the substantial parts of matters in the claims of the two inventions are the same. 例文帳に追加

一方、関連発明において、特定発明の解決しようとする課題に対応した新規な事項である「セラミック材料内に水素供与基を含有する物質を包含させ、無水苛性アルカリ浴中に浸漬する」点を請求項に記載する事項の主要部としているので、両発明の請求項に記載する事項の主要部は同一である。 - 特許庁

The silicon carbide-based porous structure material coated with a ceramic is obtained by removing excess carbon by calcining a silicon carbide-based porous structure material in which open pores resulting from the volume reduction reaction that occurs when silicon reacts with carbon to form silicon carbide are formed, in the air, then impregnating it with a solution which gives an oxide ceramic when it is fired, and firing the impregnated porous structure material.例文帳に追加

シリコンと炭素が反応して炭化ケイ素が生成する体積減少反応に起因する開気孔が生成された炭化ケイ素系多孔質構造体を空気中で仮焼して過剰の炭素を除いた後、焼成して酸化物セラミックスとなる溶液を含浸させ、それを焼成することにより、セラミックス被覆された炭化ケイ素系多孔質構造材を得る。 - 特許庁

This film is formed by mixing a ceramic material which does not react with the molten aluminum alloy and aqueous solution of 25-35 wt.% sodium silicate water glass of Na_2O-nSiO_2 (2.1≤n≤3.2), coating the mixed material in which 45-80 wt.% ceramic material is contained, and burning at 250-800°C.例文帳に追加

この被膜は、アルミニウム合金の溶融物と反応しないセラミックス材と、Ｎａ_2Ｏ・ｎＳｉＯ_2（２．１≦ｎ≦３．２）の珪酸ソーダ水ガラスの２５重量％以上３５重量％以下の水溶液とを混合させ、上記セラミックス材が４５重量％以上８０重量％以下になるようにした混合物を塗布してから２５０℃以上８００℃以下で焼成させることで形成されたものである。 - 特許庁

The method includes: a step of forming a polymide film on a supporter; a step of forming the ceramic film such as ITO or titania on the polymide film by applying a solution of a metal salt such as a metal alkoxide or metal chloride salt to the polymide film and heating it to 500°C or higher; and a step of transferring the ceramic film on the low heat-resistant substrate such as a plastic.例文帳に追加

支持体上にポリイミド膜を形成する工程と、 その上に金属アルコキシドや金属塩化物塩などの金属塩の溶液を塗布した後、５００℃以上に加熱することにより、前記ポリイミド膜上にＩＴＯやチタニアなどのセラミック膜を形成する工程と、 前記セラミック膜をプラスチック等の低耐熱性の基材上に転写する工程とを備えることを特徴とする。 - 特許庁

In particular, such substrate is impregnated or coated with a mixture of a peroxo-containing ceramic precursor and a colloidal conductive ultramicroparticle solution, and the ceramic precursor is crystallized to obtain an insulation structure in which the substrate has a volume resistivity of 10^8 to 10^12 Ωcm and the formed surface resistance layer has a surface resistivity of 10^7 to 10^11 Ω/square.例文帳に追加

即ち、基板にペルオキソ基を持つセラミックス前駆体とコロイド状の導電性超微粒子溶液の混合物を含浸または塗布し、前記セラミックス前駆体を結晶化させて、前記基板の体積比抵抗が１０^８〜１０^１２Ω・ｃｍであると共に表面比抵抗が１０^７〜１０^１１Ω／□である表面抵抗層を形成したことを特徴とする絶縁構造体である。 - 特許庁

The method of manufacturing the thermoelectric conversion element includes a step of obtaining composite particles by drying a particulate matter produced by dripping first strong alkaline solution containing a reducing agent and ceramic particles into second strong acid solution containing a salt of an element composing a thermoelectric conversion material, and a step of obtaining a thermoelectric conversion element by sintering the composite particles.例文帳に追加

還元剤とセラミックス粒子とを含有する強アルカリ性の第一の溶液を、熱電変換材料を構成する元素の塩を含有する強酸性の第二の溶液に滴下し、得られた粒子状物質を乾燥させることで複合粒子を得る工程；および 該複合粒子を焼結し熱電変換素子を得る工程、を含むことを特徴とする熱電変換素子の製造方法。 - 特許庁

The method of manufacturing the thermoelectric conversion element includes a step of producing composite particles by drying particulate matter obtained by dripping first solution containing a salt of an element composing a thermoelectric conversion material into second solution containing a reducing agent and ceramic particles and conditioned to have pH10-14, and a step of obtaining a thermoelectric conversion element by sintering the composite particles.例文帳に追加

熱電変換材料を構成する元素の塩を含有する第一の溶液を、還元剤とセラミックス粒子とを含有するｐＨ１０〜１４に調整された第二の溶液に滴下し、得られた粒子状物質を乾燥させることで複合粒子を得る工程；およびこの複合粒子を焼結し熱電変換素子を得る工程、を含む、熱電変換素子を製造する方法。 - 特許庁

Alternatively, after weighing the hardly soluble ceramic sample into the decomposition vessel, sulfuric acid and phosphoric acid are added thereto, and the vessel is plugged, stored in the pressure vessel, and irradiated with a microwave, to thereby decompose the sample; and mercury concentration in the solution acquired thereby is measured.例文帳に追加

または、難溶性のセラミック試料を分解容器に秤量した後、硫酸およびリン酸を加えて密栓しこれを耐圧容器内に収め、マイクロ波を照射して試料を分解することによって得られた溶液中の水銀濃度を測定する。 - 特許庁

To prevent solder solution of a thick film conductor as much as possible while ensuring solder wettability in a packaging method of a semiconductor chip arranged to connect a semiconductor chip consisting of a silicon semiconductor onto the thick film conductor on a ceramic substrate by solder die bonding.例文帳に追加

セラミック基板上の厚膜導体の上に、シリコン半導体よりなる半導体チップをはんだダイボンドにより、接続するようにした半導体チップの実装方法において、はんだ濡れ性を確保しつつ、厚膜導体のはんだ食われを極力防止する。 - 特許庁

The manufacturing method includes a process A in which the glass powder or glass ceramic mixture powder, the resin, and the solvent are stirred, mixed and kneaded, and a process B in which a gel solution containing an organic thixotropic agent is further added to the kneaded object obtained by the process A and mixed, stirred, and kneaded.例文帳に追加

製造方法は、ガラス粉末又はガラス・セラミック混合粉末と、樹脂と、溶媒とを攪拌・混合し、混練する工程Ａと、工程Ａで得られた混練物に、さらに無機揺変剤を含有するゲル溶液を添加して攪拌・混合し、混練する工程Ｂを有する。 - 特許庁

A cover glass for a solar cell has a ceramic layer containing SiO_2, which is formed of a solution containing at least one element selected from a group consisting of organo silica sol and colloidal silica and condensate of organo alkoxysilane, as a main element.例文帳に追加

基材とするガラスの表面に、オルガノシリカゾル及びコロイダルシリカからなる群から選ばれた少なくとも一種の成分と、オルガノアルコキシシランの縮合物を含有する溶液から形成されるSiO_2を主成分とするセラミックス層を有する、太陽電池用カバーガラス。 - 特許庁

To provide a nickel powder-dispersed aqueous solution having excellent dispersibility, to provide a nickel powder-dispersed organic solvent having excellent dispersibility and long-term preservability, to provide their production methods, and to provide electroconductive paste suitable for the internal electrode of a multilayer ceramic capacitor obtained therefrom.例文帳に追加

分散性が優れているニッケル粉末分散水溶液と分散性及び長期保管性に優れたニッケル粉末分散有機溶剤、それらの製造方法及びそれよりなる積層セラミックコンデンサー内部電極用として好適な導電ペーストを提供する。 - 特許庁

A work composed of the ceramic element 12 and the burned electrode 20 formed thereon is dipped into a processing solution 42 containing a surface treating agent that includes adsorption radicals and water-repellent radicals so as to undergo a surface treatment, and thereafter the plating electrode is formed on the burned electrode 20.例文帳に追加

吸着基と撥水基とを含む表面処理剤を含む処理溶液４２の中に、セラミック素体１２に焼付け電極２０を形成したワークを浸漬して表面処理を行い、その後、焼付け電極２０上にめっき電極を形成する。 - 特許庁

In the aqueous liquid electrostatic coating method, the ceramic complex formed by sintering polymer initial condensate of silicon dioxide and tourmaline is dispersed into water, and silicon oxide aqueous solution obtained by applying mechanical stimulation is spray-coated onto the grounded coating surface.例文帳に追加

本発明の水性液体静電塗装方法は、二酸化ケイ素の高分子初期縮合物と電気石とを焼結したセラミックス複合体を水に分散し、機械的刺激を与えて得られた酸化ケイ素水溶液をアースされた塗装面に噴射塗装する。 - 特許庁

The piezoelectric/electrostrictive ceramic composition mainly consists of a Pb(Mg_1/3Nb_2/3)O_3-PbTiO_3-PbZrO_3 three-component solid solution composition and contains 0.05 to 3.0 mass% (in terms of NiO) Ni and 0.003 to 0.01 mass% (in terms of SiO_2) Si.例文帳に追加

Ｐｂ（Ｍｇ_1/3Ｎｂ_2/3）Ｏ_3−ＰｂＴｉＯ_3−ＰｂＺｒＯ_3三成分固溶系組成物を主成分とし、ＮｉをＮｉＯ換算で０．０５〜３．０質量％、及びＳｉをＳｉＯ_2換算で０．００３〜０．０１質量％それぞれ含有する圧電／電歪磁器組成物である。 - 特許庁

In a dielectric ceramic composed of a perovskite type crystal as an essential crystalline phase, the perovskite type crystal is a solid solution composed of a multiple oxide of Ba, Sr, W and RE (RE represents rare earth element).例文帳に追加

ペロブスカイト型結晶を主結晶相とする誘電体磁器において、前記ペロブスカイト型結晶が少なくともＢａ、Ｓｒ、Ｍｇ、ＷおよびＲＥ（ＲＥは稀土類元素）の複合酸化物からなる固溶体であることを特徴とする誘電体磁器とする。 - 特許庁

An aqueous slurry obtained by mixing powdery ceramic materials with an aqueous solution of an aluminum hydroxide sol is foamed to prepare a foamed slurry, this foamed slurry is filled into a mold, dried and calcined to form a calcined molding, a plurality of such calcined moldings are joined using the above foamed slurry to form an integrated molding, and this molding is fired to obtain the objective lightweight ceramic molding.例文帳に追加

セラミックス原料粉末と水酸化アルミニウムゾル水溶液を混合して得た水性スラリーを発泡させて発泡スラリーを作製し、該発泡スラリーを型に充填し、乾燥後仮焼することにより仮焼成形体を作製し、該仮焼成形体の複数個を上記発泡スラリーを用いて接合することにより一体の成形体を作製し、その後、該成形体を焼成して軽量セラミックス成形体を得る。 - 特許庁

The dielectric ceramic composition is characterized in that it has a main component containing BaTiO_3, SrTiO_3 and CaTiO_3, and at least a part of the BaTiO_3, SrTiO_3 and CaTiO_3 being present in the composition does not form a solid solution each other.例文帳に追加

ＢａＴｉＯ_３ 、ＳｒＴｉＯ_３ およびＣａＴｉＯ_３ を含む主成分を有する誘電体磁器組成物であって、前記ＢａＴｉＯ_３ 、ＳｒＴｉＯ_３ およびＣａＴｉＯ_３ の少なくとも一部が、互いに固溶していないことを特徴とする誘電体磁器組成物。 - 特許庁

The corrosion-resistant coating method of the turbine casing comprises a coating step S2 of coating a solution with metal being dispersed therein on an inner surface of the turbine casing, and a baking step S3 of forming a ceramic thin film on the inner surface of the turbine casing by drying the coated metal for heat stabilization.例文帳に追加

タービンケーシングの耐食コーティング処理方法は、タービンケーシングの内表面に金属を分散させた溶液を塗布する塗布工程Ｓ２と、この塗布した金属を乾燥し加熱安定化させてタービンケーシングの内表面にセラミックスの薄膜を形成する焼付け工程Ｓ３と、を有する。 - 特許庁

The ceramic fired body is produced by first preparing a porous body containing a synthetic zeolite by adding coal ash to an alkali treating liquid prepared by reacting the aluminum dross in an alkali aqueous solution, adding the porous granular and powdery body containing the synthetic zeolite to a clay, kneading and drying it, followed by firing.例文帳に追加

アルミドロスをアルカリ水溶液中で反応させたアルカリ処理液に石炭灰を加え加熱、反応させて合成ゼオライトを含む多孔質体を得、該合成ゼオライトを含む多孔質粒粉体を粘土に加えて混練、乾燥した後、焼成して得られたセラミック焼成体。 - 特許庁

Provided is the method for producing the aluminum titanate-based ceramic, in which deposits are precipitated preferably by a coprecipitation process, from a solution containing titanium and aluminum elements, and then the obtained deposits are made into powder, and raw material powder containing the powder is fired.例文帳に追加

チタン元素とアルミニウム元素を含む溶液から、好ましくは共沈操作で析出物を析出させ、得られた析出物を粉末とした析出物粉末を含む原材料粉末を用いて焼成することを特徴とするチタン酸アルミニウム系セラミックスの製造方法とする。 - 特許庁

When performing electroless Ni plating of the conductive part 4 formed on the surface of the ceramic prime field 1 containing the borosilicate glass, an amine compound such as glycine is added as a complexing agent to the electroless Ni plating solution used to form an Ni-P coating 5 on the conductive part 4.例文帳に追加

ホウケイ酸系ガラスを含有したセラミック素体１の表面に導電部４を形成し、該導電部４に無電解Ｎｉめっきを施す場合、錯化剤としてグリシン等のアミン化合物が添加された無電解Ｎｉめっき液を使用し、導電部４にＮｉ−Ｐ皮膜５を形成する。 - 特許庁

Magnetic particles are coated with a brazing filler metal containing at least one kind among Cu, Ni, Ag, and Au, and Ti and/or Zr, and then coated with at least one kind between inorganic sol and a ceramic precursor solution, thereafter a plurality of magnetic particles are compressed and compacted, and heat-treated.例文帳に追加

磁性粒子を、Ｃｕ、Ｎｉ、ＡｇおよびＡｕの少なくとも１種と、Ｔｉおよび／またはＺｒとを含有するろう材により被覆した後、無機ゾルおよびセラミックス前駆体溶液の少なくとも１種により被覆し、その後、複数の磁性粒子を加圧成形し、熱処理する。 - 特許庁

Ceramic, sand, glass, charcoal or the like is coated or covered with an aqueous solution of a compound of metal having high catalytic action and an organic acid as a working liquid and is heat-treated.例文帳に追加

触媒作用の高い金属と有機酸との化合物の水溶液を加工液とし、セラミック、砂、ガラス、炭等に均一に塗布またはコーティングし、加熱処理を行うことにより、ＮＯｘ等の環境汚染ガスを効率よく軽減させ、なおかつ持続性の高い触媒材を提供できる。 - 特許庁

To provide electrolyte having high ionic conductivity and sufficient mechanical strength even having thin thickness by impregnating a nonaqueous electrolytic solution in a medium including glass-ceramic powder of lithium ion conductivity.例文帳に追加

媒体中に非水系電解液を含浸してなる電解質において、高いイオン伝導性を有し、かつ厚みを薄くした場合においても十分な機械的強度を有する電解質、および電池容量が高く、充放電サイクル特性も良好で、長期的に安定して使用できるリチウム二次電池を提供する。 - 特許庁

A complex solution of the ceramic mixture mixed with a titanium phosphate-based compound and a vegetable essential oil diluted with a solvent such as water and alcohol, which is selected according to a target industrial product, is obtained and its powder is obtained by drying it.例文帳に追加

リン酸チタニウム系化合物水溶液と混合させたセラミック混合物は混合させる工業製品に合わせ水やアルコールなど溶剤を使用し希釈調性した植物精油製品の複合溶液が得られ、混合された溶液は乾燥加工することによって粉体も得られる。 - 特許庁

The glaze of a ceramic is melted in an aqueous solution, which is prepared by mixing 30-90% of a water glass with 70-10% of water, so as to adhere to the veining of leaves, the mesophyll of which is processed with a sodium hydroxide or a resin-based varnish in order to from worked veining.例文帳に追加

水ガラス１０％〜８０％に対して、水９０％〜２０％を混合したの水溶液をつくり、この水溶液に陶磁器の釉薬を溶いて、これを水酸化ナトリュウムで葉肉を処理した木の葉の葉脈に付着させ樹脂系ニスを付着させて、加工済葉脈を作る。 - 特許庁

To provide a method and apparatus for drying a slurry-like or solution-like material by which the substantial operation rate of the drying apparatus is improved, the generation of defective products is decreased and the production of dried powder is increased, and to provide a method of manufacturing a ceramic sintered compact to obtain the ceramic sintered compact having excellent quality by molding and sintering the dried powder manufacturing in this way.例文帳に追加

乾燥装置の実質的な稼動率を上昇させるとともに、不良品の発生量を減少させ、乾燥粉末の生産量を増大させることのできるスラリー状又は溶液状材料の乾燥方法及びスラリー状又は溶液状材料の乾燥装置及びそのようにして製造される乾燥粉末を成形・焼結して品質のよいセラミック焼結体を得るセラミック焼結体の製造方法を提供する。 - 特許庁

The method, that is for producing an organic vehicle for preparing a paste to be used in case of producing multilayered ceramic electronic parts or a plasma display, comprises effecting the solution polymerization of a monomer whose main component is alkyl(meth)acrylate in an organic solvent that does not erode a green sheet and serves as a solvent of the paste.例文帳に追加

多層セラミック電子部品またはプラズマディスプレイを製造する際に使用されるペースト用の有機ビヒクルの製造方法であって、ペーストの溶剤となるグリーンシートを侵食しない有機溶剤中で、アルキル（メタ）アクリル酸エステルを主成分とする単量体を溶液重合させる有機ビヒクルの製造方法。 - 特許庁

In a process of forming a printing pattern of ceramic electronic components with the use of an ink jet printer, a wall face of the path for the water-based ink 4 of the ink jet printer is coated with a wettability improvement aqueous solution before the water-based ink 4 is filled, and then the water-based ink 4 is jetted from the ink jet head 1.例文帳に追加

インクジェット印刷装置を用いてセラミック電子部品の印刷パターンを形成する工程において、水系インク４を充填する前に前記インクジェットヘッド印刷装置の水系インク４の経路を濡れ性向上水溶液にて壁面を被覆した後、前記水系インク４をインクジェットヘッド１から吐出させる。 - 特許庁

This conductive paste is used to form internal electrodes of the laminated ceramic electronic component and contains a conductive inorganic component and an organic vehicle composed of an organic binder and an organic solvent; and the organic solvent contains isobomyl acetate and/or noryl acetate having a <8.5 solution parameter.例文帳に追加

本発明の導電性ペーストは、積層セラミック電子部品の内部電極形成に供される導電性ペーストであって、導電性無機成分と、有機バインダと有機溶剤とからなる有機ビヒクルと、を含有し、有機溶剤は、溶解パラメータが８．５未満であるイソボニルアセテートまたは／およびノピルアセテートを含有することを特徴とする。 - 特許庁