「Polyester」に関連した英語例文の一覧と使い方(437ページ目) - Weblio英語例文検索

The reflection film has an A layer mainly comprising a resin composition A containing an aliphatic polyester-based resin and a fine particulate filler, and a B layer mainly comprising a resin composition B containing a polycarbonate-based resin having 30-80 g/10 min of a melt flow rate (MFR) at 300 °C based on Japanese Industrial standard JIS K7210.例文帳に追加

反射フィルムは、脂肪族ポリエステル系樹脂および微粒状充填剤を含有する樹脂組成物Ａを主成分とするＡ層と、日本工業規格ＪＩＳ Ｋ７２１０に基づく３００℃におけるメルトフローレート（ＭＦＲ）が３０〜８０ｇ／１０ｍｉｎであるポリカーボネート系樹脂を含む樹脂組成物Ｂを主成分とするＢ層とを有する。 - 特許庁

To provide a multilayered adhesion heat-resistant wrap film being a household multilayered wrap film having a layer comprising a composition (C) based on a specific aliphatic polyester resin and excelent in barrier properties, suitable for the packaging of a container (including a ceramic or plastic container) and container-free wrap packaging and especially suitable for use at the time of heating.例文帳に追加

多層状の、特定の脂肪族ポリエステル系樹脂を主成分とした組成物（C）からなる層を有する、バリヤー性にも優れた家庭用ラップフィルムであって、各種容器（磁器製およびプラスチックス製を含む。）包装用、容器無しのラッピング包装用、特に加熱使用時の用途に好適な、密着性多層耐熱ラップフィルムを提供すること。 - 特許庁

The film is obtained by subjecting the surface of a film composed of (A) a barrier resin to be selected from the group consisting of a polyvinyl alcohol resin, a polyamide resin, and a polyester resin and (B) a photocatalyst of titanium oxide or zinc oxide to a chemical treatment or a physical treatment to be selected from a solvent treatment, a flame treatment, and a corona treatment.例文帳に追加

ポリビニル系アルコール系樹脂、ポリアミド系樹脂およびポリエステル系樹脂からなる群より選択されるバリア性樹脂（Ａ）および酸化チタンまたは酸化亜鉛である光触媒（Ｂ）からなる樹脂組成物（Ｃ）でなるフィルムの表面を溶剤処理、火炎処理およびコロナ処理から選ばれる化学的処理または物理的処理してなるフィルム。 - 特許庁

This adhesive tape is fabricated such that a fabric cloth of wooly processed polyester yarns is sandwiched between a layer of high density polyethylene and low density polyethylene on one side and a layer of low density polyethylene added with a heat-fusible resin and a low density polyethylene layer on the other side, formed as a laminate by a low temperature lamination process, and an adhesive layer is provided outside thereof.例文帳に追加

ウーリー加工したポリエステル糸による織布を挟んで一方に高密度ポリエチレン及び低密度ポリエチレン層、他の一方に低密度ポリエチレンに、熱溶着樹脂を添加した層並びに低密度ポリエチレン層を、低温ラミネート形成法により積層体として形成し、その外側に粘着剤層を設けている粘着テープ。 - 特許庁

The method of manufacturing a coating material for conductive films according to the invention comprises: a pH control step for controlling a hydrogen ion density index (pH) of polyethylene dioxythiophene solution to 6 to 8 by use of amine; and a mixing step for mixing the polyethylene dioxythiophene solution subjected to pH control in the pH control step, a polyester resin, a silane coupling agent, and an enhancer.例文帳に追加

本発明の導電膜用塗料の製造方法は、アミンを使用してポリエチレンジオキシチオフェン水溶液のｐＨを６〜８に調整するｐＨ調整工程、ならびに、ｐＨ調整工程によってｐＨが調整された前記ポリエチレンジオキシチオフェン水溶液、ポリエステル樹脂、シランカップリング剤およびエンハンサーを混合する混合工程を含む。 - 特許庁

To provide a polyester fiber which has excellent heat stability and excellent environmental safety and can be applied to various fiber uses such as fibers for clothes, fibers for interiors or night clothes, such as curtains, carpets, or wadding, fibers for industrial materials such as tire cords or ropes, various woven fabrics, various knitted fabrics, staple fiber nonwoven fabrics, filament nonwoven fabrics, or the like.例文帳に追加

衣料用繊維、カーテン、カーペット、ふとんわた等に代表されるインテリア・寝装用繊維、タイヤコード、ロープ等に代表される産業資材用繊維、各種織物、各種編物、短繊維不織布、長繊維不織布用、等の各種繊維用途に適用可能な熱安定性に優れるとともに環境面からの安全性にも優れたポリエステル繊維を提供すること - 特許庁

To provide polyester staple fibers usable as a binder fiber in production of a nonwoven fabric with a dry and a wet system, imparting a high adhesion effect even in thermal adhesion at a lower temperature and improving processing speed, and preferably usable as a nonwoven fabric used in a specific field such as a filter cloth in water processing or in osmosis membrane, etc.例文帳に追加

乾式や湿式不織布の製造においてバインダー繊維として好適に用いることができ、熱接着処理温度が低くても接着効果が高く、加工速度を向上させることができ、さらには、水処理用のろ過布や浸透膜等の特殊分野に使用する不織布にも好適に用いることができるポリエステル短繊維を提供する。 - 特許庁

Since the compressed gas which does not require the addition of a stabilizer is used as the reaction solvent and the liquid-phase polymerization and flash spinning are carried out in a single consecutive process, the method is useful for producing the biodegradable polyester material employed as a biodegradable and biocompatible material useful in medical, chemical, agricultural and environmental fields, etc.例文帳に追加

安定化剤の添加を必要としない圧縮気体を反応溶媒として用い、液相重合反応とフラッシュ紡糸が単一連続工程でなされるため、医学、化学、農学、環境などの分野で有用な生分解性及び生体適合性材料として用いられる生分解性ポリエステル材料の製造に有用である。 - 特許庁

The thermoplastic resin composition comprises a minus ion generating resin (I) containing a thermoplastic resin (polyolefin-based resin, polystyrene-based resin, polyester-based resin, polyamide-based resin, etc.) having 10^14-10^2 Ω/sq surface resistivity and a minus ion generator and a decorating agent (II) composed of powder having 1-500 μm and a metallic gloss.例文帳に追加

本発明の熱可塑性樹脂組成物は、表面固有抵抗が１０^１４〜１０^２Ω／ｓｑである熱可塑性樹脂（ポリオレフィン系樹脂、ポリスチレン系樹脂、ポリエステル系樹脂、ポリアミド系樹脂等）と、マイナスイオン発生剤とを含むマイナスイオン発生樹脂（Ｉ）と、平均粒子径が１〜５００μｍの金属様光沢を有する粉体からなる加飾剤（ＩＩ）とを含有する。 - 特許庁

To provide a heat-shrinkable polyester film to be used for a heat-shrinkable label and a film suitable for a packaging material used in coating, bundling, outer covering, etc., which is lowered in shrinkage nonuniformity, is excellent in heat resistance, keeps a beautiful appearance stably, and contributes to the recycling of resources by its cutting properties.例文帳に追加

被覆、結束、外装、などに用いられる包装材として好適な熱収縮性ラベル及びフィルムに関するものであり、特に収縮むらが少なく、耐熱性に優れた収縮結果を与え、美麗な仕上がり外観を安定して保持し、カット性を有するがゆえに資源のリサイクルにも寄与する熱収縮性ポリエステル系フィルムを提供すること。 - 特許庁

The brassiere cup molding is obtained by molding non-woven fabric where the fiber webs containing ≥20 mass% of potential crimp-expressed highly-crimped fiber are entwined with one another via needle punch, and non-woven fabric to which the hot-melting type fibers comprising ε-caprolactone-copolymerized polyester are bonded by adhesive resin which is fused to the core part of the fibers.例文帳に追加

及び潜在捲縮が発現した高捲縮繊維を２０質量％以上含む繊維ウェブが、ニードルパンチによって絡合されており、しかもε−カプロラクトン共重合ポリエステルを構成成分とする熱接着性繊維が芯部まで溶融してなる接着樹脂によって結合された不織布がカップ状に成形されてなるブラジャーカップ用成形体。 - 特許庁

In the heat developable material obtained by plasma-treating a polyester base with no undercoat layer and disposing a photosensitive layer containing photosensitive silver halide grains, an organic silver salt, a reducing agent and a polyacetal binder on the base immediately after the plasma treatment, a layer containing a modified polyvinyl acetate is applied simultaneously together with the photosensitive layer between the photosensitive layer and the base.例文帳に追加

下塗り層のないポリエステル支持体をプラズマ処理直後、該支持体上に感光性ハロゲン化銀粒子、有機銀塩、還元剤及びポリアセタール結合剤を含有する感光層を設けた熱現像材料において、該感光層と支持体の間に変性ポリ酢酸ビニルを含む層を感光層と同時に塗布したことを特徴とする熱現像材料。 - 特許庁

To provide a developing device which avoids deterioration of the fluidity of toner without causing a problem in terms of miniaturization of the device or cost while using a polyester-based monocomponent magnetic toner and forms good images and is excellent in environmental stability and free of the occurrence of image defects even in a long-term use, and to provide a process cartridge with the same and an image forming apparatus.例文帳に追加

装置の小型化、コストの面での不具合を生じることなく、ポリエステル系一成分磁性トナーを用いながら、トナーの流動性の悪化を回避し、環境安定性にすぐれ、長期の使用においても画像不良の発生がなく、良好な画像を形成する現像装置、並びにそれを備えたプロセスカートリッジ、画像形成装置を提供する。 - 特許庁

This polyester resin composition, used for preparing a light- reflecting molded article by forming a light-reflecting metallic layer on a molded article obtained from the composition, is prepared by compounding (A) 100 pts.wt. polybutylene terephthalate resin with (B) 5-100 pts.wt. polyethylene terephthalate resin and (C) 1-100 pts.wt. polyalkylene naphthalate resin.例文帳に追加

ポリエステル樹脂組成物より得られる成形品に光反射金属層が形成されている光反射成形品に用いられるポリエステル樹脂組成物であって、該組成物が、(A)ポリブチレンテレフタレート樹脂100重量部に対し、(B)ポリエチレンテレフタレート樹脂５〜100重量部と(C)ポリアルキレンナフタレート樹脂1〜100重量部を含有されていることを特徴とするポリエステル樹脂組成物。 - 特許庁

To obtain a toner for electrostatic latent image development, which has excellent heat resistance in storage, controls a surface shape, has excellent chargeability, a sharp particle size distribution, excellent low-temperature fixability and high-precision reproducibility, to provide a method for producing the same, to obtain a polyester resin fine particle useful for producing the toner and to provide a method for producing the same.例文帳に追加

保管時の耐熱性が良く表面形状を制御可能であり、帯電性に優れ、粒度分布がシャープで低温定着性に優れ、しかも高精細再現性の良好な静電潜像現像用トナーと、その製造方法、及び、該トナーの作製に用いられるポリエステル樹脂微粒子とその製造方法を提供することにある。 - 特許庁

This thermoplastic resin composition for laser welding is characterized by comprising 100 pts.wt. of a thermoplastic resin (A) containing at least one polyester resin or polyamide resin, and 10 to 150 pts.wt. of glass fibers (B) whose each cross section vertical in the longitudinal direction of the fibers has a flat shape having a flatness ratio of ≥1.5 by the following expression.例文帳に追加

少なくとも１種のポリエステル樹脂又はポリアミド樹脂を含む熱可塑性樹脂（Ａ）１００重量部に対して、繊維長さ方向に垂直な断面が下記式による扁平率１．５以上の扁平形状であるガラス繊維（Ｂ）１０〜１５０重量部を配合してなることを特徴とする、レーザー溶着用熱可塑性樹脂組成物。 - 特許庁

To provide a thermoplastic resin pellet having a sheath-core structure, containing a carbodiimide compound in the core component at a high concentration difficult to be attained by conventional technique and free from the problem of environmental pollution in the production of pellet by the decomposition product of the carbodiimide compound and the evaporation of impurities and to provide a method for producing a molded polyester article such as fiber by using the pellet.例文帳に追加

従来技術では困難であった高濃度のカルボジイミド化合物を芯成分に含有し、ペレットの調製時にカルボジイミド化合物の分解生成物や不純物の揮発による環境汚染を招くことがない芯鞘構造の熱可塑性樹脂製ペレット、およびこのペレットを使用して繊維などのポリエステル成形体を製造する方法の提供。 - 特許庁

To provide a polyester elastomer retaining excellent heat resistance and exhibiting sufficient mechanical strengths such as flexibility, elasticity- restoring properties and the like, and excellent stability to changes with time enough to retain performances such as tensile strength and the like without undergoing changes even in the case of being exposed to a high temperature environment for a long period, and to provide its production method.例文帳に追加

本発明は、優れた耐熱性を維持し、十分な柔軟性および弾性回復性等の機械強度を有し、かつ引張強度等の物性が長期間高温にさらされた場合であっても変化しにくいといった、経時的変化に対する安定性を有するポリエステル系エラストマーおよびその製造方法を提供することにある。 - 特許庁

The suppor for the magnetic recording medium has a layer (layer M) containing a metal based inorganic compound, formed on at least one surface of a polyester film, wherein the layer M has 50 to 200 nm thickness, at least the one layer M has 15 to 40 nm arithmetic average roughness Ra and 150 to 300 nm maximum sectional height Rt.例文帳に追加

ポリエステルフィルムの少なくとも片面に金属系無機化合物を含む層（Ｍ層）が設けられ、Ｍ層の厚みが５０〜２００ｎｍである磁気記録媒体用支持体であって、少なくとも一方のＭ層の算術平均粗さＲａが１５〜４０ｎｍであり、最大断面高さＲｔが１５０〜３００ｎｍである磁気記録媒体用支持体とする。 - 特許庁

The writing plane 143 is constructed by a smooth resin sheet material of a polyester, polyvinyl chloride or acrylic resin and a coating of a resin such as a melanin resin or a fluorine contained resin is applied thereon, whereby the radiographic information can be put thereon with writing instruments including a water-color ink and erased by wiping with a soft article such as a cloth or a tissue paper.例文帳に追加

筆記面１４３は、ポリエステル、ポリ塩化ビニル、アクリル樹脂等の滑面な樹脂シート材で構成し、その上をメラニン系樹脂や含フッ素系樹脂等の樹脂でコーティングすることで、水性インク等の筆記具で撮影情報を記入でき、布やテッシュペーパ等の柔らかいもので拭き取ることで撮影情報を消去できる。 - 特許庁

The thermoplastic resin composition is one obtained by a dynamic cross-linking treatment on a mixture comprising (I) a specific addition polymerization type block copolymer, (II) a specific functionalized addition polymerization type block copolymer, (III) a thermoplastic polyester type polymer, (IV) a cross-linking agent and (V) a softening agent for a rubber at a specific ratio under melting conditions.例文帳に追加

熱可塑性樹脂組成物は、特定の付加重合系ブロック共重合体（Ｉ）、特定の官能化付加重合系ブロック共重合体（ＩＩ）、熱可塑性ポリエステル系重合体（ＩＩＩ）、架橋剤（ＩＶ）及びゴム用軟化剤（Ｖ）を特定の配合比で含有する混合物を、溶融条件下で動的に架橋処理してなるものである。 - 特許庁

In the substrate for the magnetic recording medium, wherein a thin film consisting of a material selected from the group consisting of metal, semimetal, alloy, the oxides of these and composites of these is formed on one side surface of a polyester film, the substrate has ≥70% IR reflectance and the surface of the thin film is the surface for forming the ferromagnetic metal film.例文帳に追加

ポリエステルフイルムの片側表面上に、金属、半金属及び合金並びにこれらの酸化物及び複合物から選ばれた材料からなる薄膜が形成されてなる磁気記録媒体用支持体であって、この支持体の赤外線反射率が７０％以上であり、かつ、薄膜の表面が強磁性金属膜形成用の面である。 - 特許庁

This self-deposit type coating composition is characterized by comprising one or more resins (for example, an anionic polyester resin obtained by the condensation reaction of a polyhydric alcohol with an acid) selected from the group of water-dispersible or soluble organic resins, an acid component (for example, hydrogen fluoride), a metal ion (for example, iron ion), and a lubricant component (for example, polytetrafluoroethylene).例文帳に追加

水分散性および水溶性の有機樹脂の群の中から選ばれる１種又は２種以上の樹脂（例えば、多価アルコールと酸との縮合反応により得られたアニオン性のポリエステル樹脂）と、酸成分（例えば、フッ化水素）と、金属イオン（例えば、鉄イオン）と、潤滑剤成分（例えば、ポリテトラフルオロエチレン）とを含有する自己析出型被覆組成物。 - 特許庁

A cellulose acylate film is produced by a method involving a casting process by which a cellulose acylate composition comprising a cellulose acylate, a monofunctional polyester macromonomer (M) having a functional group at either end of the principle polymer chain and a weight average molecular weight of ≤2×10^4, a polymerizable monomer (A) and a photopolymerization initiator (L) is cast, and a photoirradiation process.例文帳に追加

セルロースアシレート、重合体主鎖の片末端に重合性基を有し、かつ重量平均分子量２×１０^４以下の一官能性ポリエステルマクロモノマー（Ｍ）、重合性モノマー（Ａ）、及び光重合開始剤（Ｌ）を含有するセルロースアシレート組成物を流延する流延工程と光照射の工程と含む工程により、セルロースアシレートフィルムを製造する。 - 特許庁

At least on one surface of a polyester film wherein a crystallization orientation has not been completed, a coated layer for which a water dispersive or water-based coating liquid containing a resin wherein polyalkylene oxide of which the repeating unit is 10-100 is copolymerized, is applied, dried, drawn, and in addition, a heat-treatment is applied is provided.例文帳に追加

本発明は、結晶配向が完了する前のポリエステルフイルムの少なくとも片面に、繰り返し単位が１０〜１００であるポリアルキレンオキシドが共重合された樹脂を含む水分散性または水性塗布液を塗布し、乾燥、延伸、更に熱処理を施された塗布層を有する昇華型感熱転写用インキ易接着ポリエステルフイルムである。 - 特許庁

To provide a method for manufacturing a resin molded product capable of obtaining the resin molded product in which an impact resistance, a compression resistance and a molded product appearance of disadvantages are improved even when the molded product is formed at least in a complicated shape including at least a mesh part when a recycled polyester resin is utilized to manufacture the resin molded product.例文帳に追加

再生ポリエステル樹脂を活用して樹脂成形品を製造したとき、この樹脂成形品が少なくともメッシュ部分を含むような複雑な形状をしていても、その欠点である耐衝撃性、耐圧縮性および成形品外観を改良した樹脂成形品を得ることができる樹脂成形品の製造方法を提供すること。 - 特許庁

To provide a polyester composition which is excellent in transparency, slipperiness and wear resistance, can be used adequately for magnetic recording media, electrical insulation, general industries, food packaging and the like, and particularly combines various characteristics such as flavoriness, adhesion and impact resistance suitable as a film for food packaging and a metal plate laminating film for metallic cans for beverages and foods.例文帳に追加

透明性、滑り性、耐摩耗性に優れ、磁気記録媒体用、電気絶縁用、一般工業用、食品包装用等に好適に使用でき、特には食品包装用および飲料、食料用金属缶等のための金属板貼り合わせ用フィルムとして好適なフレーバ性、接着性、耐衝撃性等の各種特性を兼備したポリエステル組成物を得る。 - 特許庁

This fiber for the rubber reinforcement is obtained by attaching 0.2-0.6 wt.% lubricant, 0.05-0.15 wt.% emulsifier and 0.05-0.3 wt.% epoxy compound to a fiber composed of a polyester comprising at least 90 mol% ethylene 2,6-naphthalate unit based on the whole repeating units, and having 2-5 dtex single fiber size.例文帳に追加

全繰り返し単位中の少なくとも９０モル％がエチレン−２，６−ナフタレート単位であるポリエステルから形成された、単糸繊度が２〜５ｄｔｅｘの繊維上に、繊維重量に対して平滑剤が０．２〜０．６重量％、乳化剤が０．０５〜０．１５重量％、エポキシ化合物が０．０５〜０．３重量％付着しているゴム補強用繊維とする。 - 特許庁

This method for manufacturing the toner for electrophotography includes a process (1) for preparing a diffusion liquid including toner particles containing polyester under the presence of surface active agent in an aqueous medium and a process (2) for washing the toner particles prepared in the process (1) by using an alcohol aqueous solution containing 0.1 wt.% or more and less than 5 wt.% of 1-5C alcohol.例文帳に追加

（１）水系媒体中で、界面活性剤存在下、ポリエステルを含むトナー粒子の分散液を得る工程、及び（２）工程（１）で得られたトナー粒子を、炭素数１〜５のアルコールを０.１重量％以上５重量％未満含有するアルコール水溶液で洗浄する工程、を有する電子写真用トナーの製造方法である。 - 特許庁

The fiber dyed woven fabric is woven by using composite yarns composed of blended yarns of polyester fibers dyed at 125-135°C and rayon fibers or wool fibers dyed at 80-100°C or spun yarns of the wool fibers, the polyurethane elastic fibers composed of a diamine compound such as a polyether diol having a side chain and the blended yarns or the spun yarns as warp yarns and/or weft yarns.例文帳に追加

１２５〜１３５℃で染色されたポリエステル繊維と８０〜１００℃で染色されたレーヨン繊維またはウール繊維の混紡糸、または該ウール繊維の紡績糸、側鎖を有するポリエーテルジオール等のジアミン化合物からなるポリウレタン弾性繊維と該混紡糸または該紡績糸との複合糸を経糸および／または緯糸に用いて製織した先染め織物。 - 特許庁

The dispersing agent composed of an aliphatic polyester having low molecular weight is a substance having a number- average molecular weight of 500-30,000 and a weight-average molecular weight of 1,000-60,000 and selected from low-molecular polycaprolactone, low-molecular polyethylene succinate, low-molecular polybutylene succinate and low-molecular polybutylene succinate adipate, their mixture and their copolymer.例文帳に追加

低分子量脂肪族ポリエステル系分散剤は数平均分子量５００〜３0,０００、重量平均分子量１,0００〜６0,０００の、それぞれ、低分子量ポリカプロラクトン、低分子量ポリエチレンサクシネート、低分子量ポリブチレンサクシネートおよび低分子量ポリブチレンサクシネートアジペートの群から選ばれた単独または複数の混合物、またはこれらの共重合体である。 - 特許庁

The laminated film of the present invention is characterized in that it is a laminated film of at least two layers having a layer X of a resin composition C comprising an aliphatic polyester resin composition A and a plasticizer B, and a layer Y of a resin composition D comprising a polyvinylidene chloride resin and/or a polyvinylidene chloride copolymer resin.例文帳に追加

本発明の積層フィルムは、脂肪族ポリエステル樹脂組成物Ａと可塑剤Ｂを含む樹脂組成物Ｃからなる層Ｘと、ポリ塩化ビニリデン樹脂および／またはポリ塩化ビニリデン共重合樹脂を含む樹脂組成物Ｄからなる層Ｙを有する、少なくとも２層以上の積層フィルムであることを特徴とするものである。 - 特許庁

This polyester yarn is characterized in that the yarn is a multifilament yarn substantially composed of polytrimethylene terephthalate and has ≥3 cN/dtex strength, ≤25 cN/dtex Young's modulus and ≤10 cN/dtex minimum value of differential Young's modulus at 3-10% elongation in the stress-strain curve and ≥90% elastic recovery ratio after elongated to 10%.例文帳に追加

実質的にポリトリメチレンテレフタレートからなるマルチフィラメント糸であって、ストレス−ストレイン曲線での強度が３ｃＮ／ｄｔｅｘ以上、ヤング率が２５ｃＮ／ｄｔｅｘ以下であるとともに、伸度３〜１０％での微分ヤング率の最小値が１０ｃＮ／ｄｔｅｘ以下を示し、１０％伸長後の弾性回復率が９０％以上であることを特徴とするポリエステル糸。 - 特許庁

This biodegradable foamed self-adhesive tape is obtained by coating an adhesive having self adhesion on one surface of a foamed sheet substrate composed of a biodegradable aliphatic polyester and having ≥87.5 porosity, and has ≥0.4 and ≤3 mm thickness, ≥4.9 N/cm2 tensile strength, ≥4.9 and ≤200 N/cm tear strength.例文帳に追加

生分解性脂肪族ポリエステルからなり気孔率が８７．５％以上である発泡シート基材の片面に、自己粘着性を有する粘着剤が塗工され、０．４ｍｍ以上３ｍｍ以下の厚みを有し、引っ張り強度が４．９Ｎ／ｃｍ^2以上、引き裂き強度が４．９Ｎ／ｃｍ以上２００Ｎ／ｃｍ以下である生分解性発泡粘着テープ。 - 特許庁

The composition of the sound isolating material for automobiles is made by adding, to a composition having a rubber, a polypropylene resin and a polyethylene resin, 0.1-10 mass% of the paint waste products composed of main raw materials of an acrylic melamine resin and a polyester melamine resin and having such a particle size as 90% or more thereof passes through an 80 μm mesh classifier.例文帳に追加

自動車用防音材料の組成物は、ゴム、ポリプロピレン樹脂、及びポリエチレン樹脂を有する組成物に、アクリルメラニン及びポリエステルメラニン樹脂を主原料とする８０μｍメッシュの分級機を９０％以上が通過する粒度の塗料廃棄物を０．１質量％〜１０質量％混合してなることを特徴とする。 - 特許庁

In the water cut-off polyurethane foam formed by expanding a soft polyurethane foam raw material including at least a polyol, a poly isocyanate, a foam adjusting agent, a catalyst, an expanding agent and a viscosity reducing agent, wherein the polyol component is a polyester polyol originating from a dimer acid and the foam adjusting agent is a reactive silicone having an active hydrogen group.例文帳に追加

少なくともポリオール、ポリイソシアネート、整泡剤、触媒、発泡剤、減粘剤とを含む軟質ポリウレタンフォーム原料を発泡させてなる止水性ポリウレタンフォームであって、前記ポリオール成分が、ダイマー酸由来ポリエステルポリオールであって、前記整泡剤が活性水素基を有する反応性シリコーンであることを特徴とする止水性ポリウレタンフォーム。 - 特許庁

The flame-retardant polyester-based artificial hair having the above-mentional various properties is obtained by melt-spinning a composition containing a bromine-containing flame retardant, zinc borate and/or zinc stannate, preferably, a composition containing organic fine particles and/or inorganic fine particles besides them.例文帳に追加

ポリエステルに臭素含有難燃剤、ホウ酸亜鉛および／または錫酸亜鉛を含んでなる組成物、さらには、有機微粒子および／または無機微粒子を含んでなる組成物を溶融紡糸することにより、通常のポリエステル繊維の耐熱性、強伸度など繊維物性を維持し、セット性、触感、光沢、透明性に優れた難燃性ポリエステル系人工毛髪が得られる。 - 特許庁

In the waterproof sheet with the pressure-sensitive layer constituted by successively laminating the pressure-sensitive layer 12 containing unvulacanized rubber comprising butyl rubber and a release sheet to the rear surface of a waterproof sheet layer 10 containing vulcanized rubber comprising ethylene/propylene rubber and/or butyl rubber, a reinforcing net 14 comprising a polyester fiber is provided between the waterproof sheet layer 10 and the pressure-sensitive layer 12.例文帳に追加

エチレンプロピレンゴム及び／又はブチルゴムからなる加硫ゴムを含有する防水シート層１０の裏面に、ブチルゴムからなる未加硫ゴムを含有する粘着層１２と離型シート１６とを順に積層した粘着層付き防水シートであって、防水シート層１０と粘着層１２との間に、ポリエステル繊維からなる補強ネット１４を設ける。 - 特許庁

This cleaner is formed by integrating the synthetic resin fibers 1, 1,... of the polyester, etc., solidifying and molding these fibers to a prescribed shape, then cutting the fibers from a direction perpendicular to the synthetic resin fibers 1,1,... and forming the cut surfaces as the dirt removing surfaces, thereby allowing the ends of the synthetic resin fibers 1 to appear at the dirt removing surfaces.例文帳に追加

本発明は、ポリエステルなどの合成樹脂繊維１、１、・・を集積して所定形状に固着成型した後、上記合成樹脂繊維１、１、・・に対して直角方向より切断してその切断面を汚れ落とし面３、３’とすることにより同汚れ落とし面３、３’に合成樹脂繊維１端部が現出したクリ−ナ−。 - 特許庁

To provide a copolyester resin pellet which shows a favorable solution stability, even when dissolved in general-purpose solvents, and can be safely stored for a long period without blocking by effectively preventing blocking of the pellet of a poorly crystalline copolymer polyester resin having a high adhesive property and a glass transition temperature of ≤40°C, and a method for producing the same.例文帳に追加

粘着性が高いガラス転移点が４０℃以下の貧結晶性共重合ポリエステル樹脂ペレットのブロッキングを効果的に防止し、かつ、長期にわたってブロッキングすることなく安全に保存することができ、さらには、汎用溶剤に溶解しても溶液安定性が良好な共重合ポリエステル樹脂ペレットとその製造方法を提供する。 - 特許庁

To provide a method capable of producing an approximately cylindrical aromatic polyester-based resin pre-expanded bead having good surface state and cellular state, excellent in appearance and in-mold expansion moldability, having low crystallinity and so capable of forming expanded products having high mechanical strength and good appearance by in-mold expansion-molding.例文帳に追加

表面状態および気泡状態が良好で、外観および型内発泡成形性に優れる上、結晶化度が小さいために、型内発泡成形によって高強度でかつ外観の良好な発泡成形体を形成することが可能な略円柱状の芳香族ポリエステル系樹脂予備発泡粒子を、安定して製造しうる製造方法を提供する。 - 特許庁

To provide an unsaturated polyester resin composition which has a molding shrinkage factor in the range of 0.3-0.5% and thereby enables a solenoid coil molded article to be easily demolded from a mold having no draft and which has a low coefficient of linear expansion and can thereby prevent the occurrence of cracks caused by thermal impact; and to provide a solenoid coil molded article using the same.例文帳に追加

成形収縮率を０．３〜０．５％の範囲内にすることで、抜き勾配の無い金型からソレノイドコイル成形品を容易に脱型することを可能とすると共に、線膨張係数を低く抑えることで熱衝撃によるクラックの発生を防止することが可能な不飽和ポリエステル樹脂組成物とそれを用いたソレノイドコイル成形品を提供する。 - 特許庁

The false-twist polyester textured yarns thus obtained are stable in false-twist processability and have scarce fluffs.例文帳に追加

酸化アルミニウム粒子を０．０５重量％以上５重量％以下含有したポリエステルフィルムを再生原料とした溶融紡糸を行うとともに、油剤中に重量平均分子量が４，０００以上のポリエーテル成分を５重量％以上５０重量％以下含有するポリエーテル系紡糸油剤を糸条に対し０．３重量％以上１．５重量％付与させる。 - 特許庁

This resin paste contains an aromatic liquid-crystalline polyester, a magnetic or conductive filler, and a solvent containing a halogen-substituted phenol compound of formula (I) (wherein A is a halogen atom or a tri-halogenated methyl group; i is an integer of 1-5; if i is not less than 2, all A can be the same or different.).例文帳に追加

芳香族液晶ポリエステルと、磁性フィラーまたは導電性フィラーと、下記式（Ｉ）（式中、Ａはハロゲン原子を表わすか、トリハロゲン化メチル基を表わし、ｉは１〜５の整数を表わし、ｉが２以上の場合、Ａは同一でも異なっていてもよい。）で示されるハロゲン置換フェノール化合物を含む溶媒とを含有することを特徴とする樹脂ペースト。 - 特許庁

The mold release film includes: a coating layer containing at least two kinds of organic compounds containing an aluminum element, a titanium element, and a zirconium element, and an organic silicon compound on one surface of a polyester film extended at least in one axial direction; a mold release layer on the coating layer; and the coating layer on a film surface at the opposite side.例文帳に追加

少なくとも一軸方向に延伸されたポリエステルフィルムの片面に、アルミニウム元素、チタン元素、またはジルコニウム元素を含む有機化合物の少なくとも２種と有機珪素化合物とを含有する塗布層を有し、当該塗布層上に離型層を有し、反対側のフィルム面に塗布層を有することを特徴とする離型フィルム。 - 特許庁